CN104263096A - Furniture coating - Google Patents
Furniture coating Download PDFInfo
- Publication number
- CN104263096A CN104263096A CN201410506641.4A CN201410506641A CN104263096A CN 104263096 A CN104263096 A CN 104263096A CN 201410506641 A CN201410506641 A CN 201410506641A CN 104263096 A CN104263096 A CN 104263096A
- Authority
- CN
- China
- Prior art keywords
- powder
- calcium carbonate
- carbonate
- furniture
- coatings
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a furniture coating which is prepared from the following raw materials in parts by weight: high-density polyethylene, pentachlorophenol, acetyl tributyl citrate, dimethyl sulfoxide, ammonium dihydrogen phosphate, EVA resin, ferrous sulfate, glass-ceramic powder, light calcium carbonate, pyrophyllite, chromic carbonate, butyl hydroxy anisd, ammonium octamolybdate, polytetrafluoroethylene, graphite powder, ricinoleic acid, acrylic resin, nano calcium carbonate powder, triethanolamine, beryllium oxide, diethyleneglycolmonoethylether, dioctyl maleate, petroleum sodium sulfonate, diethanol amine, tert-butyl-p-cresol, industrial lecithin, propylene carbonate and ethyl acetate. The furniture coating disclosed by the invention has the beneficial effects that the coating is strong in coat adhesion, thick in paint membrane, and good in heat dissipation effect, is not yellowed and embrittled and can inhibit the volatilization of poisonous gas, and the raw materials such as nano calcium carbonate powder increase the anti-corrosion property of products, and the comprehensive properties of products are superior.
Description
?
technical field
The present invention relates to a kind of coating, particularly a kind of coatings for furniture.
Background technology
Human survival and make the history of painting pass up to the Stone Age, and enter the last world, various synthetic resin coating newly developed has waited until that a large amount of application model coating enters to synthesize filmogen for the main epoch.The coating of developed country per capita consumption reaches more than 10KG, and modern coatings industry becomes an important industry of modern chemical industry.Although existing coating type is various, ubiquity shortcoming miscellaneous, such as jaundice embrittlement, paint film fullness ratio is poor, volatilization toxic gas, radiating effect are poor, cannot meet the multiple demand of people.
Summary of the invention
The object of the invention is to overcome above-mentioned deficiency existing in prior art, the coatings for furniture that a kind of over-all properties is superior is provided.
In order to realize foregoing invention object, the invention provides following technical scheme:
A kind of coatings for furniture, be prepared from by the raw material of following weight: high density polyethylene(HDPE) 20-36, pentachlorophenol 1-2, tributyl acetylcitrate 5-6, dimethyl sulfoxide (DMSO) 0.5-3, primary ammonium phosphate 1-2, EVA resin 2-3, ferrous sulfate 0.2-0.5, glass-cermic powder 2-4, light calcium carbonate 7-12, agalmatolite 10-20, chromium carbonate 2-3, butylated hydroxy anisole 0.5-1.5, ammonium octamolybdate 1.2-2.5, tetrafluoroethylene 3-5, Graphite Powder 99 2-3, ricinolic acid 0.4-1, acrylic resin 15-30, nano-calcium carbonate calcium powder 0.5-2, trolamine 1-2, beryllium oxide 0.1-0.5, diethylene glycol monoethyl ether 3-5, dioctyl maleate 0.1-0.6, petroleum sodium sulfonate 0.1-0.3, diethanolamine 2-3, tertiary butyl cresols 1-2, industry Yelkin TTS 0.1-1, propylene carbonate 1-2, ethyl acetate 30-55.
Described a kind of coatings for furniture, its preparation method comprises the following steps:
Each raw material is mixed, is heated to 80-85 DEG C, stirring reaction 1-2 hour, by weight mixing and stirring under the speed of 2000-2200r/min, after when being ground to 60-70 μm, stop grinding, packaging.
compared with prior art, beneficial effect of the present invention: this coating have strong, the non-yellowing embrittlement of coating adhesion, paint film plentiful, suppress volatilization toxic gas, good heat dissipation effect, the raw materials such as nano-calcium carbonate calcium powder add the antiseptic property of product, and over-all properties is superior.
Embodiment
Below in conjunction with test example and embodiment, the present invention is described in further detail.But this should be interpreted as that the scope of the above-mentioned theme of the present invention is only limitted to following embodiment, all technology realized based on content of the present invention all belong to scope of the present invention.
Embodiment 1: a kind of coatings for furniture, be prepared from by the raw material of following weight: high density polyethylene(HDPE) 30, pentachlorophenol 1.5, tributyl acetylcitrate 5, dimethyl sulfoxide (DMSO) 1, primary ammonium phosphate 1-2, EVA resin 2.6, ferrous sulfate 0.4, glass-cermic powder 3, light calcium carbonate 10, agalmatolite 13, chromium carbonate 2.7, butylated hydroxy anisole 1.1, ammonium octamolybdate 2, tetrafluoroethylene 5, Graphite Powder 99 2, ricinolic acid 0.7, acrylic resin 20, nano-calcium carbonate calcium powder 1.2, trolamine 1, beryllium oxide 0.3, diethylene glycol monoethyl ether 4, dioctyl maleate 0.2, petroleum sodium sulfonate 0.1, diethanolamine 2.2, tertiary butyl cresols 1.6, industry Yelkin TTS 0.2, propylene carbonate 1.5, ethyl acetate 47.
A kind of preparation method of coatings for furniture comprises the following steps:
Each raw material is mixed, is heated to 80-85 DEG C, stirring reaction 1-2 hour, by weight mixing and stirring under the speed of 2000-2200r/min, after when being ground to 60-70 μm, stop grinding, packaging.
Claims (2)
1. a coatings for furniture, it is characterized in that, be prepared from by the raw material of following weight: high density polyethylene(HDPE) 20-36, pentachlorophenol 1-2, tributyl acetylcitrate 5-6, dimethyl sulfoxide (DMSO) 0.5-3, primary ammonium phosphate 1-2, EVA resin 2-3, ferrous sulfate 0.2-0.5, glass-cermic powder 2-4, light calcium carbonate 7-12, agalmatolite 10-20, chromium carbonate 2-3, butylated hydroxy anisole 0.5-1.5, ammonium octamolybdate 1.2-2.5, tetrafluoroethylene 3-5, Graphite Powder 99 2-3, ricinolic acid 0.4-1, acrylic resin 15-30, nano-calcium carbonate calcium powder 0.5-2, trolamine 1-2, beryllium oxide 0.1-0.5, diethylene glycol monoethyl ether 3-5, dioctyl maleate 0.1-0.6, petroleum sodium sulfonate 0.1-0.3, diethanolamine 2-3, tertiary butyl cresols 1-2, industry Yelkin TTS 0.1-1, propylene carbonate 1-2, ethyl acetate 30-55.
2. a kind of coatings for furniture according to claim 1, is characterized in that: preparation method comprises the following steps:
Each raw material is mixed, is heated to 80-85 DEG C, stirring reaction 1-2 hour, by weight mixing and stirring under the speed of 2000-2200r/min, after when being ground to 60-70 μm, stop grinding, packaging.