CN105462096A - 玻纤增强改性材料及其制备方法 - Google Patents
玻纤增强改性材料及其制备方法 Download PDFInfo
- Publication number
- CN105462096A CN105462096A CN201410449997.9A CN201410449997A CN105462096A CN 105462096 A CN105462096 A CN 105462096A CN 201410449997 A CN201410449997 A CN 201410449997A CN 105462096 A CN105462096 A CN 105462096A
- Authority
- CN
- China
- Prior art keywords
- district
- polyvinyl chloride
- fiberglass reinforced
- preparation
- fiber reinforced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种玻纤增强聚氯乙烯材料及其制备方法。本发明的玻纤增强抗老化聚氯乙烯材料，其组分按质量百分数配比为：聚氯乙烯50％～60％、玻璃纤维5％～15％、抗静电剂1％～3％、耐候剂0.5％～2％、抗氧剂0.1％～0.5％、润滑剂0.5％～1％、增容剂2％～5％。本发明的有益效果是，与现有技术相比，本发明制得的玻纤增强抗老化聚氯乙烯材料，具有良好的抗静电性能和耐老化性能，而且具有强度高、光泽性好、尺寸稳定、耐热耐腐蚀性能优良等优点，可广泛适用于汽车、家电、通讯、仪器仪表等领域。<!-- 2 -->
Description
技术领域
本发明属聚氯乙烯材料生产技术领域，改善聚氯乙烯原有的不足。生产出符合社会需求的产品。
背景技术
聚氯乙烯是一种新型的化学建筑材料广泛应用于工农业及日常生活等国民经济各个领域，尤其是近年建筑市场对聚氯乙烯产品的巨大需求，使氯乙烯产品成为具有相当竞争力的一个塑料品种，产量仅次于聚乙烯居第二位，因其具有节能、隔热、保温、环保、安装简便等特点，已成为我国建筑业中必不可少的新型建材。随着我国经济的持续增长，迎来了我国建筑业的黄金时期，同时也带动了化学建材业的迅速发展。
发明内容
本发明的目的是提供一种改善聚氯乙烯材料的不足的专用改性材料及其制备方法。
聚氯乙烯玻纤增强改性材料由下列重量比原料组成：
聚氯乙烯原料；65～75
无碱长玻璃纤维：25～35
硅烷偶联剂KH-550：1.5～2.5
玻璃相容剂：1.5～2.5
该聚氯乙烯玻纤增强改性材料的制备方法包括下列步骤：将无碱长玻璃纤维与KH-550共混10分钟，将聚氯乙烯干燥处理，再将上述各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为150-170℃，二区为170-220℃，三区为230-260℃，四区为250-265℃；五区为245-250℃，停留时间为1-2分钟，压力为10-15Mpa。
具体实施方式
下面通过具体实施方式对本发明做进一步的说明，以下实施例仅是对本发明进行说明而非对其加以限定。
实施例1：
(1)按重量比分分别称取各原料如下：
聚氯乙烯原料；65
无碱长玻璃纤维：25
硅烷偶联剂KH-550：1.5
玻璃相容剂：1.5
(2)将无碱长玻璃纤维与KH-550共混10分钟，将聚氯乙烯干燥处理，再将上述各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为150-170℃，二区为170-220℃，三区为230-260℃，四区为250-265℃；五区为245-250℃，停留时间为1-2分钟，压力为10-15Mpa。
实验结果：
上述实验结果表明，聚氯乙烯材料的耐热性能有明显的改善和提高。
实施例2：
(1)按重量比分分别称取各原料如下：
聚氯乙烯原料；70
无碱长玻璃纤维：30
硅烷偶联剂KH-550：2.0
玻璃相容剂：2.0
(2)将无碱长玻璃纤维与KH-550共混10分钟，将聚氯乙烯干燥处理，再将上述各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为150-170℃，二区为170-220℃，三区为230-260℃，四区为250-265℃；五区为245-250℃，停留时间为1-2分钟，压力为10-15Mpa。
实验结果：
上述实验结果表明，聚氯乙烯材料的耐热性能有明显的改善和提高。
实施例3：
(1)按重量比分分别称取各原料如下：
聚氯乙烯原料；75
无碱长玻璃纤维：35
硅烷偶联剂KH-550：2.5
玻璃相容剂：2.5
(2)将无碱长玻璃纤维与KH-550共混10分钟，将聚氯乙烯干燥处理，再将上述各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为150-170℃，二区为170-220℃，三区为230-260℃，四区为250-265℃；五区为245-250℃，停留时间为1-2分钟，压力为10-15Mpa。
实验结果：
上述实验结果表明，聚氯乙烯材料的耐热性能有明显的改善和提高。
上述实施例为本发明的举例说明，并不用来限制本发明。通过上述实验表明，其中实施例2为最优重量比，通过本方法制造的聚氯乙烯玻纤增强改性材料的拉伸强度、断裂伸长率、弯曲强度等性能得到了明显改善。
本发明所述的聚氯乙烯玻纤增强改性材料，改善聚氯乙烯原有的不足，生产出符合社会需求的产品，适用于电子电气和汽车行业、工业零件等。
Claims (5)
1.一种玻纤增强聚氯乙烯材料，其特征在于，其组分按质量百分数配比为：聚氯乙烯50％～60％、玻璃纤维5％～15％、抗静电剂1％～3％、耐候剂0.5％～2％、抗氧剂0.1％～0.5％、润滑剂0.5％～1％、增容剂2％～5％。
2.根据权利要求1所述的玻纤增强聚氯乙烯材料，其特征在于，所述的玻璃纤维为直径在8～15μm、长度为3～8mm的无碱玻璃纤维，且其表面经硅烷偶联剂KH-550处理过。
3.根据权利要求1所述的玻纤增强聚氯乙烯材料，其特征在于，所述的抗静剂为抗静电剂HKD-510或抗静电剂HDC-102。
4.根据权利要求1所述的玻纤增强聚氯乙烯材料，其特征在于，所述的耐候剂为质量比1：1的复合受阻胺光稳定剂HS-944和HS-622的复配物。
5.根据权利要求1所述的玻纤增强聚氯乙烯材料的制备方法，其特征在于，包括以下步骤：
先将上述各种原料在高速混合器中干混3-4分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为120-130℃，二区为140-160℃，三区为185-205℃，四区为180-200℃；五区为170-190℃，停留时间为1-2分钟，压力为10-15Mpa。