CN105440917A - 一种易施工贝母漆及其制备方法 - Google Patents
一种易施工贝母漆及其制备方法 Download PDFInfo
- Publication number
- CN105440917A CN105440917A CN201610001754.8A CN201610001754A CN105440917A CN 105440917 A CN105440917 A CN 105440917A CN 201610001754 A CN201610001754 A CN 201610001754A CN 105440917 A CN105440917 A CN 105440917A
- Authority
- CN
- China
- Prior art keywords
- percent
- paint
- fritillary
- bulb
- fritillaria
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种易施工贝母漆及其制备方法,按质量分数计,其组成为:合成脂肪酸树脂50~60%,流平剂0.1~0.2%,1%有机硅消泡剂0.7~2%,催干剂0.1~0.2%,20%?CAB浆5~10%,醋酸丁酯5~10%,丙二醇丁醚醋酸酯4~6%,125目珠光粉5~10%,30%透明染料1~5%。将上述各种原材料按照投料顺序投入分散缸中,混合后高速分散均匀。本发明不仅贝母效果较之原来产品有所提升,而且更易施工、生产。
Description
技术领域
本发明涉及一种易施工贝母漆及其制备方法。
背景技术
随着经济的发展,人民生活水平逐步提高,对于家具款式、颜色等的要求越来越高,尤其是橱柜、浴室柜等不仅仅局限于原来的单一颜色的产品,而是逐渐在追求各种异形产品、特殊效果的产品,贝母漆便是其中的一种。但以往生产的贝母漆不仅成本较高,且锤纹助剂的添加量对于贝母效果有着直接的影响,因而生产过程中对于助剂量的添加要求较为严格,且对于助剂的添加量需要做大量的实验才能够确定。
发明内容
本发明便是针对这一情况,采用新的助剂,不仅贝母效果较之原来产品有所提升,且生产也更易于实现。
本发明所述一种易施工贝母漆按质量分数计,其组成为:
合成脂肪酸树脂50~60%
流平剂0.1~0.2%
1%有机硅消泡剂0.7~2%
催干剂0.1~0.2%
20%CAB浆5~10%
醋酸丁酯5~10%
丙二醇丁醚醋酸酯4~6%
1250目珠光粉5~10%
30%透明染料1~5%。
所述方法包括如下步骤:将上述各种原材料按照投料顺序投入分散缸中,混合后高速分散均匀。
将制得的贝母漆搭配配套的固化剂及稀释剂均匀喷涂到工件表面。
本发明与现有技术相比具有以下优点:
本发明采用的所有原材料价格均很低廉,容易得到;材料中的20%CAB浆有高羟值,可以跟配套的固化剂发生交联反应,提高整体的耐候性和耐水性;该产品相对于以前的贝母漆,更加容易施工,更易于实现,且贝母效果更好。
具体实施方式:
为了加深对本发明的理解,下面将结合实例对本发明作进一步详述,该实施例仅用于解释本发明,并不构成对本发明保护范围的限定。
实验方法:
准备材料合成脂肪酸树脂,流平剂,1%有机硅消泡剂,催干剂,20%CAB浆,醋酸丁酯,丙二醇丁醚醋酸酯,125目珠光粉,30%透明染料,将上述各种原材料按照投料顺序投入分散缸中,高速分散均匀即可。
具体实验配比如表1。
表1
具体实验效果见表2。
表2
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 | 对比组 | |
固化时间 | 短 | 短 | 短 | 短 | 短 | 短 | 长 |
贝开现象 | 无 | 无 | 无 | 无 | 无 | 无 | 略有贝开 |
贝母纹 | 花纹均匀 | 花纹均匀 | 花纹均匀 | 花纹均匀 | 花纹均匀 | 花纹均匀 | 环纹不均 |
所述对比组采用的贝母漆为市场购买的现有贝母漆。
通过表2的实验结果可知,根据本发明生产的贝母漆,喷涂容易,实现容易,不需要做太大的调整,贝母纹都大小和密度都很均匀;而对比组的固化时间跟本发明6个实施例中的相比较,固化时间较长,通过直接喷涂,容易导致纹路不均,不易控制和操作。综上,本发明综合性能优越,在本技术领域有很高的应用价值。
以上所述仅为说明本发明的实施方式,并不用于限制本发明,对于本领域的技术人员来说,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (4)
1.一种易施工贝母漆,其特征在于:所述一种易施工贝母漆组分及质量分数为:
合成脂肪酸树脂50~60%
流平剂0.1~0.2%
1%有机硅消泡剂0.7~2%
催干剂0.1~0.2%
20%CAB浆5~10%
醋酸丁酯5~10%
丙二醇丁醚醋酸酯4~6%
1250目珠光粉5~10%
30%透明染料1~5%。
2.根据权利要求1所述的一种易施工贝母漆的制备方法,所述方法包括如下步骤:将上述各种原材料按照投料顺序投入分散缸中,混合后高速分散均匀。
3.根据权利要求1所述的一种易施工贝母漆,其特征在于:将贝母漆搭配配套的固化剂及稀释剂均匀喷涂到工件表面。
4.根据权利要求1所述的一种易施工贝母漆,其特征在于:所述流平剂、1%有机硅消泡剂、催干剂、20%CAB浆为助剂,所述醋酸丁酯、丙二醇丁醚醋酸酯为溶剂。