CN105401456A - 一种含甘草粉的pvc合成革及其生产方法 - Google Patents

一种含甘草粉的pvc合成革及其生产方法 Download PDF

Info

Publication number
CN105401456A
CN105401456A CN201510706710.0A CN201510706710A CN105401456A CN 105401456 A CN105401456 A CN 105401456A CN 201510706710 A CN201510706710 A CN 201510706710A CN 105401456 A CN105401456 A CN 105401456A
Authority
CN
China
Prior art keywords
parts
pvc
synthetic leather
powder
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510706710.0A
Other languages
English (en)
Inventor
黄浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Hongkun Auto Parts Co Ltd
Original Assignee
Wuhu Hongkun Auto Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Hongkun Auto Parts Co Ltd filed Critical Wuhu Hongkun Auto Parts Co Ltd
Priority to CN201510706710.0A priority Critical patent/CN105401456A/zh
Publication of CN105401456A publication Critical patent/CN105401456A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种含甘草粉的PVC合成革，其是由下述重量份的原料制得：PVC？SG-5？30-60，PVC？SG-8？15-30，十二烷基葡糖苷1-2，聚二甲基硅氧烷0.5-1.5，双咪唑啉季铵盐0.2-1，硅溶胶1-3，邻苯二甲酸二辛酯30-60，乙酰柠檬酸三丁酯20-40，木质素磺酸钙1-3，轻质碳酸钙10-15，硬脂酸1-2，甘草粉3-6，明矾3-6，色料5-10，改性助剂5-10；本发明的PVC合成革具有长效杀菌除臭的功效，手感及外观质量良好，符合实际需求，适合大规模生产应用。

Description

一种含甘草粉的PVC合成革及其生产方法
技术领域
本发明涉及高分子材料领域，具体涉及一种含甘草粉的PVC合成革及其生产方法。
背景技术
目前，合成革主要分为聚氯乙烯（PVC）合成革和聚氨酯（PU）合成革两种。PU合成革手感和外观质量好，但是价格偏高，使用寿命不长，且目前较成熟的PU合成革工艺需要大量使用DMF作为溶剂，环境效应不好；PVC合成革价格低，物理性能能达到质量要求，缺点是手感和外观质量稍差，且透气性差，限制了其更广泛的使用。
甘草是一种常见中草药，具有较强的杀菌抑菌功能和一定的除臭功效，添加一定量的甘草粉有助于抑制细菌在合成革表面繁殖，同时达到除臭的目的。
发明内容
本发明的目的是提供一种具有良好外观及手感、且具有良好抑菌除臭功能的含甘草粉的PVC合成革。
本发明是通过以下技术方案实现的：
一种含甘草粉的PVC合成革，包括基布层和PVC层，其中：
PVC层由下述重量份的原料制得：
PVCSG-530-60，PVCSG-815-30，十二烷基葡糖苷1-2，聚二甲基硅氧烷0.5-1.5，双咪唑啉季铵盐0.2-1，硅溶胶1-3，邻苯二甲酸二辛酯30-60，乙酰柠檬酸三丁酯20-40，木质素磺酸钙1-3，轻质碳酸钙10-15，硬脂酸1-2，甘草粉3-6，明矾3-6，色料5-10，改性助剂5-10；
其中改性助剂由下列重量份的原料制成：
木浆纤维10-15，滑石粉5-10，玉米棒芯10-15，玉米淀粉1-5，羧甲基纤维素钠3-6，六偏磷酸钠1-3，纳米二氧化钛0.2-1，聚乙烯蜡0.5-1，甘露醇1-2，油酸0.1-0.3，十二烷基二甲基苄基溴化铵1-2；
改性助剂的制备方法是：
将木浆纤维与滑石粉、十二烷基二甲基苄基溴化铵混合后加入适量5-10%醋酸溶液，600-800r/min搅拌1-2h后过滤并干燥，加入纳米二氧化钛，800-1000℃煅烧1-2h，降温至200-400℃后再处理2-4h，冷却后加入玉米棒芯和玉米淀粉，100-150℃处理2-3h后加入其余原料，混合后初步研磨均匀，60-80℃、200-400r/min搅拌2-4h，冷却后研磨至500-1000目，即得；
一种含甘草粉的PVC合成革的生产方法，包括以下步骤：
（1）将甘草粉、十二烷基葡糖苷和木质素磺酸钙加入适量3-6%醋酸溶液，400-600r/min搅拌1-3min后加入双咪唑啉季铵盐、明矾和硬脂酸，60-80℃、800-1000r/min搅拌15-30min，干燥后研磨至800-1000目，得活性粉体；
（2）将活性粉体与其余原料混合，先以200-400r/min低速搅拌15-30min，再以1000-1500r/min高速搅拌45-90min，100-200目过滤，加入密炼机，140-160℃塑化，再140-170℃开炼，得PVC层浆料；
（3）以水性聚氨酯作为粘结剂，将PVC层浆料与基布通过四辊压延机在160-180℃下压延贴合，速度为40-60米/分，冷却收卷，产品经表面效果处理，质量检验结果合格，即可出厂。
本发明的优点是：
1.本发明通过添加有效成分甘草粉，有效抑制了细菌在合成革表面繁殖，同时达到除臭的效果；
2.通过添加改性助剂，改善了PVC合成革的透气性能，使其克服不透气的缺点，具有一定的透气吸湿功效，应用范围更加广泛；
3.通过配方与工艺改进，改善了合成革的手感和外观质量，使其具有类似于天然皮革的自然舒适手感。
具体实施方式
本发明非限定实施例如下：
实施例1
一种含甘草粉的PVC合成革，包括基布层和PVC层，其中：
PVC层由下列重量（kg）的原料制成：
PVCSG-550，PVCSG-825，十二烷基葡糖苷1.5，聚二甲基硅氧烷1，双咪唑啉季铵盐0.8，硅溶胶2，邻苯二甲酸二辛酯45，乙酰柠檬酸三丁酯30，木质素磺酸钙2，轻质碳酸钙12，硬脂酸1.5，甘草粉4，明矾5，色料6，改性助剂8；
其中改性助剂由下列重量（kg）的原料制成：
木浆纤维12，滑石粉8，玉米棒芯12，玉米淀粉4，羧甲基纤维素钠5，六偏磷酸钠2，纳米二氧化钛0.5，聚乙烯蜡0.8，甘露醇1.5，油酸0.2，十二烷基二甲基苄基溴化铵1.5；
改性助剂的制备方法是：
将木浆纤维与滑石粉、十二烷基二甲基苄基溴化铵混合后加入适量5%醋酸溶液，600r/min搅拌2h后过滤并干燥，加入纳米二氧化钛，1000℃煅烧1h，降温至400℃后再处理2h，冷却后加入玉米棒芯和玉米淀粉，100℃处理2h后加入其余原料，混合后初步研磨均匀，60℃、400r/min搅拌2h，冷却后研磨至800目，即得；
其生产方法包括以下步骤：
（1）将甘草粉、十二烷基葡糖苷和木质素磺酸钙加入适量4%醋酸溶液，400r/min搅拌2min后加入双咪唑啉季铵盐、明矾和硬脂酸，80℃、800r/min搅拌15min，干燥后研磨至800目，得活性粉体；
（2）将活性粉体与其余原料混合，先以400r/min低速搅拌30min，再以1500r/min高速搅拌45min，100目过滤，加入密炼机，140℃塑化，再160℃开炼，得PVC层浆料；
（3）以水性聚氨酯作为粘结剂，将PVC层浆料与基布通过四辊压延机在160℃下压延贴合，速度为50米/分，冷却收卷，产品经表面效果处理，质量检验结果合格，即可出厂。
经产品性能测试，该产品经向拉伸负荷295.5N，纬向拉伸负荷238.2N，经向断裂伸长率9.3%，纬向断裂伸长率15.4%，经向撕裂负荷18.2N，纬向撕裂负荷24.7N，老化试验不开裂，符合产业标准的要求。

Claims (2)

1.一种含甘草粉的PVC合成革，包括基布层和PVC层，其特征在于：
所述的PVC层由下述重量份的原料制得：
PVCSG-530-60，PVCSG-815-30，十二烷基葡糖苷1-2，聚二甲基硅氧烷0.5-1.5，双咪唑啉季铵盐0.2-1，硅溶胶1-3，邻苯二甲酸二辛酯30-60，乙酰柠檬酸三丁酯20-40，木质素磺酸钙1-3，轻质碳酸钙10-15，硬脂酸1-2，甘草粉3-6，明矾3-6，色料5-10，改性助剂5-10；
所述改性助剂由下列重量份的原料制成：
木浆纤维10-15，滑石粉5-10，玉米棒芯10-15，玉米淀粉1-5，羧甲基纤维素钠3-6，六偏磷酸钠1-3，纳米二氧化钛0.2-1，聚乙烯蜡0.5-1，甘露醇1-2，油酸0.1-0.3，十二烷基二甲基苄基溴化铵1-2；
所述改性助剂的制备方法是：
将木浆纤维与滑石粉、十二烷基二甲基苄基溴化铵混合后加入适量5-10%醋酸溶液，600-800r/min搅拌1-2h后过滤并干燥，加入纳米二氧化钛，800-1000℃煅烧1-2h，降温至200-400℃后再处理2-4h，冷却后加入玉米棒芯和玉米淀粉，100-150℃处理2-3h后加入其余原料，混合后初步研磨均匀，60-80℃、200-400r/min搅拌2-4h，冷却后研磨至500-1000目，即得。
2.根据权利要求1所述的一种含甘草粉的PVC合成革的制备方法，其特征在于，包括以下步骤：
（1）将甘草粉、十二烷基葡糖苷和木质素磺酸钙加入适量3-6%醋酸溶液，400-600r/min搅拌1-3min后加入双咪唑啉季铵盐、明矾和硬脂酸，60-80℃、800-1000r/min搅拌15-30min，干燥后研磨至800-1000目，得活性粉体；
（2）将活性粉体与其余原料混合，先以200-400r/min低速搅拌15-30min，再以1000-1500r/min高速搅拌45-90min，100-200目过滤，加入密炼机，140-160℃塑化，再140-170℃开炼，得PVC层浆料；
（3）以水性聚氨酯作为粘结剂，将PVC层浆料与基布通过四辊压延机在160-180℃下压延贴合，速度为40-60米/分，冷却收卷，产品经表面效果处理，质量检验结果合格，即可出厂。
CN201510706710.0A 2015-10-27 2015-10-27 一种含甘草粉的pvc合成革及其生产方法 Pending CN105401456A (zh)