CN105401407A - Non-ironing three-proofing finishing process of pure-cotton fabric - Google Patents
Non-ironing three-proofing finishing process of pure-cotton fabric Download PDFInfo
- Publication number
- CN105401407A CN105401407A CN201510861702.3A CN201510861702A CN105401407A CN 105401407 A CN105401407 A CN 105401407A CN 201510861702 A CN201510861702 A CN 201510861702A CN 105401407 A CN105401407 A CN 105401407A
- Authority
- CN
- China
- Prior art keywords
- ironing
- cotton fabric
- prevention finishing
- pure cotton
- prevention
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a non-ironing three-proofing finishing process of a pure-cotton fabric. The technological process sequentially includes material preparation, liquid ammonia finishing, non-ironing three-proofing finishing, baking, baking and washing, stentering, preshrinking and acceptance check. By the adoption of the non-ironing three-proofing finishing process of the pure-cotton fabric, the technological process is shortened, the cost is reduced, pure cotton is non-ironing and three-proofing and can be produced in a batched mode, the non-ironing level is above Level 3.5, and the pure-cotton fabric is oil-proof, water-proof and anti-stain and meets the AATCC standard.
Description
Technical field
The present invention relates to a kind of non-ironing three-prevention finishing technique of pure cotton fabric, belong to technical field of textile printing.
Background technology
Along with the cry of human society back to nature is day by day strong, people increase gradually to natural fiber clothes fabric demand, cotton, as one of the representative of natural fabric, it has the comfortable characteristic of nature, wash and wear, three anti-effect tripartite face advantages, therefore be more and more subject to the favor of people, but the major defect of cotton creases easily, wash rear shrink; Therefore for improving this shortcoming, textile wrinkle resistance arranges and seems particularly important, at present, nearly all non-ironing+three-prevention finishing all adopts and pads resin, then bake under the hot conditions of 150 DEG C-180 DEG C, adding non-ironing auxiliary agent, then the method that 150 DEG C of high temperature bakes reaches textile noniron finish and three anti-effects; But cotton fiber and resin react under high temperature drying, same three anti-baking also are react under high temperature drying, therefore study how non-ironing with three anti-processing one baths, with three, resin bakes prevents that baking a step realizes, be the Main way of this technical study, save flow process, reduce costs.
Summary of the invention
The object of the invention is to overcome above-mentioned defect, provide a kind of non-ironing three-prevention finishing technique of pure cotton fabric, shortened process, reduces costs, make textile non-ironing+three to prevent, can produce in batches, easy-care properties reaches more than 3.5 grades, grease proofing, waterproof, antifouling arrival AATCC standard.
The non-ironing three-prevention finishing technique of a kind of pure cotton fabric of the present invention, technological process is followed successively by fabric preparation, liquid ammonia finishing, non-ironing three-prevention finishing, bakes, bakes washing, tentering, preshrunk and test dress.
, the component of non-ironing three-prevention finishing liquid and weight proportion are resin EFR100-200g/l, catalyst 53150-100g/l, fiber protection agent HDP30-50g/l, three anti-auxiliary agent HPU60-120g/l, hydrochloric acid 1-2g/l, and all the other are water.
Fabric pH value after liquid ammonia finishing controls at 6-7.
Non-ironing three-prevention finishing is for padding non-ironing three-prevention finishing liquid, and in non-ironing three-prevention finishing, bake out temperature controls at 80-100 DEG C, and cloth surface temperature controls at 35-40 DEG C, and cropping humidity is between 6-6.6%.
Finally by fabric in the clot of cropping place.
The bath on stenter of non-ironing three-prevention finishing is carried out.
Baking temperature controls at 150-160 DEG C, bakes the speed of a motor vehicle and controls at 40-50m/min.
Bake washing: on rinsing machine, carry out 60-70 DEG C of cleaning, adjuvant used component and weight proportion are soda ash 8-12g/l, acetic acid 1-5g/l, nonionic detergent 2-4g/l, and all the other are water.
The component that tentering is adjuvant used and weight proportion are acetic acid 1-3g/l, and all the other are water, 110-150 DEG C, and tentering speed is 50m/min.
Preshrunk washing shrinkage controls at more than 0--2%.
The non-ironing rank of fabric after process reaches U.S. AATCC124 standard more than 3.5 grades, content of formaldehyde reaches below International Environmental Protection standard 75ppm, grease proofing effect reaches U.S.'s AATCC118-2007 standard and washes first 5 grades, wash 4 grades 5 times, waterproof effect reaches U.S.'s AATCC22-2010 standard and washes first 100 points, wash latter 70 points for 5 times, anti-fouling effect reaches U.S.'s AATCC193-2007 standard and washes first 6 grades, washes 4 grades 5 times.And more non-ironing three-prevention finishing normal process flow process: non-ironing---bake---bake and wash---wash after three prevent---three anti-ly to bake-preshrunk three to prevent after can saving and washing, three anti-ly bake 2 road technological processes.
Operation principle is: COTTON FABRIC is when washing or by External Force Acting, cellulose macromolecule can produce slippage, fabric produces deformation, when dehydrate or external force eliminate after, cellulose macromolecule produces new intermolecular force on new position, so the deformation produced just can not recover, such fabric face just creates wrinkle, this wrinkle usually will through ironing process, cellulose macromolecule is forced to set back, to eliminate wrinkle, the why crease-resistant difference of cellulose fibre is because lack necessary cross-bond between cellulose macromolecule main chain, if at high temperature reacted by resin and cellulose hydroxyl group, between cellulose macromolecule, form stable cross-bond limit molecule relative displacement under external force, fabric is made not easily to produce permanent deformation under the effect of external force, thus make fabric have good ironing-free performance.Add non-ironing auxiliary agent when applying no-ironing resin, bake under the high temperature conditions, can reach comparatively ideal three anti-effects, shortened process, reduces costs simultaneously.
The present invention compared with prior art, has following beneficial effect:
1. noniron finish and three-prevention finishing two step are combined into a step: while adding non-ironing auxiliary agent, add three anti-auxiliary agents, realize shortening the flow process of washing rear three-prevention finishing.
2, with three, non-ironing baking prevents that baking two steps is combined into a step: while processing non-ironing baking, realize three prevent baking, and realizes the anti-flow process baking arrangement of shortening three.
3, adopt the fabric after process of the present invention soft, wrinkle resistance, three anti-excellent result, easy-care properties reaches U.S. AATCC124 standard more than 3.5 grades, and grease proofing effect reaches U.S.'s AATCC118-2007 standard and washes first 5 grades, washes 4 grades 5 times, waterproof effect reaches U.S.'s AATCC22-2010 standard and washes first 100 points, wash latter 70 points for 5 times, anti-fouling effect reaches U.S.'s AATCC193-2007 standard and washes first 6 grades, washes 4 grades 5 times.Content of formaldehyde reaches below International Environmental Protection standard 75ppm, the clothes made of this fabric, wrinkle resistant in wearing process, can keep good credential status, namely eliminate ironing condition after washing is dried, before washing simultaneously, and three anti-excellent result after washing.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
Fabric specification is: 3/1 twill fabric of CM30*CM30*130*70*57/58.
Fabric non-ironing+three-prevention finishing technological process is:
1, fabric prepares: grey cloth stand seam requires that positive and negative is consistent, margin to seam place is straight, firm, procedure calls of singing is singed totally, the destarch of destarch kiering procedure calls is clean, and destarch rate reaches more than 98%, and after kiering, capillary effect reaches 2in/30min, to ensure non-ironing effect and feel, fabric whiteness CIE numerical value under d 65 illuminant after bleaching requires bleaching reaches 87, alkali mercerizedly requires mercerising abundant, and cloth cover pH value is 7.
2, liquid ammonia finishing: adopt conventional liquid ammonia finishing, the fabric pH value after liquid ammonia finishing is decided to be 6.
3, non-ironing: in non-ironing process, to add non-ironing auxiliary agent; the component of non-ironing auxiliary agent and weight proportion are resin EFR160g/l, catalyst 53148g/l, fiber protection agent HDP30g/l, non-ironing auxiliary agent HPU60g/l hydrochloric acid 1.5g/l; all the other are water; drying room temperature controls at 82 ± 3 DEG C; cloth surface temperature controls between 35 ± 3 DEG C; cropping humidity between 6-6.6%, finally by fabric in the clot of cropping place.
4, high temperature bakes: by the fabric of clot on baker 160 DEG C, the speed of baking is that 40m/min bakes.
5, washing is baked: on rinsing machine, carry out 70 DEG C of cleanings, adjuvant used component and weight proportion are soda ash 10g/l, acetic acid 3g/l, nonionic detergent 3g/l, and all the other are water.
6, tentering: carry out on stenter, adjuvant used component and weight proportion are acetic acid 2g/l, and all the other are water, 130 DEG C, and tentering speed is 50m/min processing.
7, preshrunk: for meeting the shrink requirement of fabric, preshrinking machine carries out, and washing shrinkage controls at AATCC135-2004 method 0--1.5%.
After tested, the non-ironing rank of fabric after process of the present invention is adopted to reach U.S. AATCC124 standard 3.5 grades, grease proofing effect reaches U.S.'s AATCC118-2007 standard and washes first 5 grades, wash 4 grades 5 times, waterproof effect reaches U.S.'s AATCC22-2010 standard and washes first 100 points, wash latter 70 points for 5 times, anti-fouling effect reaches U.S.'s AATCC193-2007 standard and washes first 6 grades, washes 4 grades 5 times.Content of formaldehyde reaches International Environmental Protection standard 20ppm.
Embodiment 2
The specification of fabric is: the plain fabric of CM40*CM30*114*70*61/62.
The iron-free finishing process flow process of fabric is:
1, fabric prepares: grey cloth stand seam requires that positive and negative is consistent, margin to seam place is straight, firm, procedure calls of singing is singed totally, the destarch of destarch kiering procedure calls is clean, and destarch rate reaches more than 98%, and after kiering, capillary effect reaches 2in/30min, to ensure non-ironing effect and feel, fabric whiteness CIE numerical value under d 65 illuminant after bleaching requires bleaching reaches 87, alkali mercerizedly requires mercerising abundant, and cloth cover pH value is between 6.5.
2, liquid ammonia finishing: adopt conventional liquid ammonia finishing, the fabric pH value after liquid ammonia finishing is decided to be 7.
3, non-ironing; non-ironing auxiliary agent is added in non-ironing process; the component of non-ironing auxiliary agent and weight proportion are resin EFR200g/l, catalyst 531100g/l, fiber protection agent HDP50g/l, non-ironing auxiliary agent HPU120g/l hydrochloric acid 1.5g/l; all the other are water; drying room temperature controls at 90 ± 3 DEG C; cloth surface temperature controls between 40 ± 3 DEG C, cropping humidity between 6-6.6%, finally by fabric in the clot of cropping place.
4, high temperature bakes reaction: by the fabric of clot on baker 150 degree, baking the speed of a motor vehicle is 50m/min.
5, washing is baked: on rinsing machine, carry out 70 DEG C of cleanings, adjuvant used component and weight proportion are soda ash 10g/l, acetic acid 3g/l, nonionic detergent 3g/l, and all the other are water.
6, tentering: carry out on stenter, adjuvant used component and weight proportion are acetic acid 2g/l, and all the other are water, and 130 DEG C of tentering speed are 50m/min processing.
7, preshrunk: for meeting the shrink requirement of fabric, preshrinking machine carries out, and washing shrinkage controls at AATCC135-2004 method 0--1.5%.
After tested, the non-ironing rank of fabric after process of the present invention is adopted to reach U.S. AATCC124 standard 3.0 grades, grease proofing effect reaches U.S.'s AATCC118-2007 standard and washes first 5 grades, wash 4 grades 5 times, waterproof effect reaches U.S.'s AATCC22-2010 standard and washes first 100 points, wash latter 70 points for 5 times, anti-fouling effect reaches U.S.'s AATCC193-2007 standard and washes first 6 grades, washes 4 grades 5 times.Content of formaldehyde reaches International Environmental Protection standard 20ppm.
Embodiment 3
The specification of fabric is: the plain fabric of CM40*CM30*114*70*61/62.
The iron-free finishing process flow process of fabric is:
1, fabric prepares: grey cloth stand seam requires that positive and negative is consistent, margin to seam place is straight, firm, procedure calls of singing is singed totally, the destarch of destarch kiering procedure calls is clean, and destarch rate reaches more than 98%, and after kiering, capillary effect reaches 5cm/5min, to ensure non-ironing effect and feel, fabric whiteness CIE numerical value under d 65 illuminant after bleaching requires bleaching reaches 87, alkali mercerizedly requires mercerising abundant, and cloth cover pH value is 7.
2, liquid ammonia finishing: adopt conventional liquid ammonia finishing, the fabric pH value after liquid ammonia finishing is decided to be 6.
3, non-ironing; non-ironing auxiliary agent is added in non-ironing process; the component of non-ironing auxiliary agent and weight proportion are resin EFR100g/l, catalyst 53160g/l, fiber protection agent HDP30g/l, non-ironing auxiliary agent HPU80g/l hydrochloric acid 1g/l; all the other are water; drying room temperature controls at 90 ± 3 DEG C; cloth surface temperature controls between 40 ± 3 DEG C, cropping humidity between 6-6.6%, finally by fabric in the clot of cropping place.
4, high temperature bakes reaction: by the fabric of clot on baker 150 degree, baking the speed of a motor vehicle is 50m/min.
5, washing is baked: on rinsing machine, carry out 60 DEG C of cleanings, adjuvant used component and weight proportion are soda ash 8g/l, acetic acid 2g/l, nonionic detergent 2g/l, and all the other are water.
6, tentering: carry out on stenter, adjuvant used component and weight proportion are acetic acid 3g/l, and all the other are water, and 130 DEG C of stenter speed of a motor vehicle are 50m/min processing.
7, preshrunk: for meeting the shrink requirement of fabric, preshrinking machine carries out, and washing shrinkage controls at AATCC135-2004 method 0--1.5%.
After tested, the non-ironing rank of fabric after process of the present invention is adopted to reach U.S. AATCC124 standard 3.0 grades, grease proofing effect reaches U.S.'s AATCC118-2007 standard and washes first 5 grades, wash 4 grades 5 times, waterproof effect reaches U.S.'s AATCC22-2010 standard and washes first 100 points, wash latter 70 points for 5 times, anti-fouling effect reaches U.S.'s AATCC193-2007 standard and washes first 6 grades, washes 4 grades 5 times.Content of formaldehyde reaches International Environmental Protection standard 20ppm.
Claims (9)
1. a non-ironing three-prevention finishing technique for pure cotton fabric, is characterized in that: technological process is followed successively by fabric preparation, liquid ammonia finishing, non-ironing three-prevention finishing, bakes, bake washing, tentering, preshrunk and test dress.
2. the non-ironing three-prevention finishing technique of pure cotton fabric according to claim 1; it is characterized in that; the component of non-ironing three-prevention finishing liquid and weight proportion are resin EFR100-200g/l, catalyst 53150-100g/l, fiber protection agent HDP30-50g/l, three anti-auxiliary agent HPU60-120g/l; hydrochloric acid 1-2g/l, all the other are water.
3. the non-ironing three-prevention finishing technique of pure cotton fabric according to claim 1, is characterized in that, the fabric pH value after liquid ammonia finishing controls at 6-7.
4. the non-ironing three-prevention finishing technique of pure cotton fabric according to claim 1, it is characterized in that, non-ironing three-prevention finishing is for padding non-ironing three-prevention finishing liquid, and in non-ironing three-prevention finishing, bake out temperature controls at 80-100 DEG C, cloth surface temperature controls at 35-40 DEG C, and cropping humidity is between 6-6.6%.
5. the non-ironing three-prevention finishing technique of pure cotton fabric according to claim 1, is characterized in that, the bath on stenter of non-ironing three-prevention finishing is carried out.
6. the non-ironing three-prevention finishing technique of pure cotton fabric according to claim 1, it is characterized in that, baking temperature controls at 150-160 DEG C, bakes the speed of a motor vehicle and controls at 40-50m/min.
7. the non-ironing three-prevention finishing technique of pure cotton fabric according to claim 1, is characterized in that, bake washing: on rinsing machine, carry out 60-70 DEG C of cleaning, adjuvant used component and weight proportion are soda ash 8-12g/l, acetic acid 1-5g/l, nonionic detergent 2-4g/l, all the other are water.
8. the non-ironing three-prevention finishing technique of pure cotton fabric according to claim 1, is characterized in that, the component that tentering is adjuvant used and weight proportion are acetic acid 1-3g/l, and all the other are water, 110-150 DEG C, and tentering speed is 50m/min.
9. the non-ironing three-prevention finishing technique of pure cotton fabric according to claim 1, it is characterized in that, preshrunk washing shrinkage controls at more than 0--2%.