CN110468585A - A kind of ready-made non-ironing garment cool feeling finishing technique - Google Patents
A kind of ready-made non-ironing garment cool feeling finishing technique Download PDFInfo
- Publication number
- CN110468585A CN110468585A CN201910750357.4A CN201910750357A CN110468585A CN 110468585 A CN110468585 A CN 110468585A CN 201910750357 A CN201910750357 A CN 201910750357A CN 110468585 A CN110468585 A CN 110468585A
- Authority
- CN
- China
- Prior art keywords
- ready
- cool feeling
- parts
- agent
- clothing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ready-made non-ironing garment cool feeling finishing techniques, are related to technical field of textile afterfinish, its key points of the technical solution are that a kind of ready-made non-ironing garment cool feeling finishing technique, includes the following steps: spraying, preliminary drying, drying, pressing, bakes sizing, cooling;The noniron finish liquid takes water as a solvent preparation, contains following components: modified dihydroxy bisethylene urea crosslinking agent, catalyst, wear-resistant finishing agent, three-proof finishing agent, silicon class softening agent and clothing cool feeling agent.The present invention can increase the submissive smooth sense of ready-made clothes by the addition of silicon class softening agent, can reduce the temperature of clothing by the cooperation of itself and clothing cool feeling agent, to reduce feeling of oppression and heat, increase the comfort for wearing clothing.
Description
Technical field
The present invention relates to technical field of textile afterfinish, more specifically, it is related to a kind of ready-made non-ironing garment cool feeling arrangement
Technique.
Background technique
Cotton fabric is also known as cotton, is using cotton yarn as the woven fabric of raw material.Cotton fabric because its water imbibition it is strong, it is wear-resisting it is washable,
Soft comfortable and ventilative the features such as feeling nice and cool, it is widely used in garment material, drapery and TECHNICAL FABRIC;Using pure-cotton fabric
The shirt of production has good comfort and ventilative sense, therefore very popular, but due to the elasticity of cotton shirt
It is poor, washing shrinkage is larger, is easy corrugated defect brings worries again, and iron-free finishing process then can be very good to solve
The problem of pure-cotton fabric easily wrinkles.
Noniron finish is that the blended fabric of the cotton after washing or cotton and chemical fibre is instigated to have quick drip-dry, do not need ironing just
It is able to maintain a kind of finishing technique of relatively flat appearance very, principle is using the crease-shedding finishing agents such as Lauxite or double hydroxyethyl sulfone
Initial reduced body, under alkaline condition with cellulose occur catalytic crosslinking react, make the active group and fiber of finishing agent macromolecular
Hydroxy functional group crosslinking in plain macromolecular, deposition, improve cellulose dry state and hygrometric state resilience, show in wearability
Improve crease resistant finishing.
In the prior art, Authorization Notice No. is the Chinese patent of CN105780494B, and it is formaldehydeless to disclose a kind of cotton fabric
Ironing and anti-crease treatment process, it includes the following steps: the 1) cotton fabric after kiering is bleached or is dyed, is first placed on preshrinking machine
Shrunk finish is carried out, finishing process is then fed into;2) configuration of organosilicon ironing and anti-crease finishing fluid;3) cotton fabric is by padding
Process makes organosilicon noniron finish liquid evenly into cotton fabric;4) cotton fabric after arranging removes cotton by baking process and knits
Moisture on object;5) cotton fabric after drying bakes the cotton fabric for obtaining and having ironing and anti-crease by high temperature.Traditional fabric is non-ironing
The process flow of arrangement is relatively easy, and comes then more complicated relatively to the non-ironing treatment process of ready-made clothes.
In the prior art, application publication number is the patent application document of CN104594038A, discloses a kind of pure cotton dress ornament
Non-ironing environmentally friendly finishing technique, step includes: (1) no-ironing resin finishing technique formula: LF-2 resin: 100-130g/L, chlorine
Change magnesium series catalysts: 25g/L, double amido organosilicon lotions: 40-60g/L, nonionic penetrant: 2-4g/L, bath raio 1:5-10,
10-20min of room temperature.(2) process flow: clothing dipping after be dehydrated (liquid carrying rate 70% -80%) → drying (65 DEG C or less are dried to
Containing damp rate 5%-10%) → whole boiling hot setting → hanger bakes (150-160 DEG C, 5-15min).
The aesthetics of cotton shirt by non-ironing processing increases substantially, and cotton dress ornament has good gas permeability
With having a good sweat property, sweat on human skin and micro- sweat can be adsorbed, compares and is suitble to wear in summer, but the cotton clothes after absorbing sweat
The rate of drying of decorations is slow, and the clothes after absorbing sweat is easy patch on the skin, increases feeling of oppression and heat and sense of discomfort.
Summary of the invention
The purpose of the present invention is to provide a kind of ready-made non-ironing garment cool feeling finishing techniques, can by the addition of silicon class softening agent
To increase the submissive smooth sense of ready-made clothes, the temperature of clothing can be reduced by the cooperation of itself and clothing cool feeling agent, to reduce bored
Thermal sensation increases the comfort for wearing clothing.
Above-mentioned technical purpose of the invention has the technical scheme that
A kind of ready-made non-ironing garment cool feeling finishing technique, includes the following steps:
S1, spraying: noniron finish liquid is sprayed on ready-made clothes after atomization, liquid carrying rate 80-100%;
S2, preliminary drying: carrying out preliminary drying processing to the ready-made clothes after spraying, it is made to contain damp rate 70-80%;
S3, drying: carrying out drying and processing to pre-baked ready-made clothes, it is made to contain damp rate 8-15%;
S4, pressing: pressing sizing is carried out to double sleeves of ready-made clothes, neck, preceding width, back panel, yoke;
S5, it bakes sizing: the ready-made clothes after pressing being carried out to bake sizing;
S6, cooling: cooling treatment is carried out to ready-made clothes after molding is baked;
The noniron finish liquid takes water as a solvent preparation, the component of following mass-volume concentration is contained in noniron finish liquid: modified
Dihydroxy bisethylene urea crosslinking agent 80-100g/L, catalyst 20-25g/L, wear-resistant finishing agent 30-60g/L, three-proof finishing agent 30-
60g/L, silicon class softening agent 30-60g/L and clothing cool feeling agent 60-80g/L.
By using above-mentioned technical proposal, arrangement by noniron finish liquid to ready-made clothes can solve cotton ready-made clothes and easily wrinkle
Defect, to improve its aesthetics;Using the characteristic of cotton material absorbing sweat, the sweat of skin surface can be quickly absorbed,
And the addition of silicon class softening agent can increase the submissive smooth sense of ready-made clothes, can reduce clothing by the cooperation of itself and clothing cool feeling agent
The temperature of object increases the comfort for wearing clothing to reduce feeling of oppression and heat.
Further, the clothing cool feeling agent is made of the raw material of following parts by weight: amino-polyether polysiloxane block is total
30-40 parts of polymers, 15-20 parts of emulsifier, 3-5 parts of Capmul MCM C8,2-4 parts of xylitol, 1-2 parts of jade powder, alkyl glycosides
1-2 parts, 1-1.4 parts of glacial acetic acid and 60-70 parts of water.
By using above-mentioned technical proposal, using amino-polyether polysiloxane block copolymers as primary raw material, cooperate with list
Clothing cool feeling agent made from glycerol caprylate, xylitol, jade powder and alkyl glycosides can make after its clothing organization
The feel of fabric is fine and smooth, submissive, smooth and have cooling feeling, by its with after three-proof finishing agent and the cooperation of silicon class softening agent,
The submissive comfort of clothing can be increased, and the evaporation of moisture on clothes can be accelerated, prevent clothing and skin adhesion, improved
Wear the comfort of cotton ready-made clothes.
Further, the clothing cool feeling agent is prepared with the following method: based on parts by weight, 1. taking 30 parts of water, Xiang Qi
3-5 parts of middle addition Capmul MCM C8,2-4 parts of xylitol, 1-2 parts of jade powder, 1-2 parts of alkyl glycosides, after mixing evenly, obtain
Mixed liquor;
2. taking 30-40 parts of amino-polyether polysiloxane block copolymers and 15-20 parts of emulsifiers, 60-70 is warming up to after mixing
DEG C, 30-40min is stirred with the speed of 2000-3000r/min, is then cooled to 30-40 DEG C, be added 0.5-0.7 part glacial acetic acid with
10 parts of water, after stirring 10-20min with the speed of 400-1000r/min;0.5-0.7 parts of glacial acetic acid and 20-30 parts of water are added,
Then 15-25min is stirred with the speed of 400-1000r/min;Mixed liquor is added, then is stirred with the speed of 400-1000r/min
10-30min is mixed, clothing cool feeling agent is obtained.
Further, the catalyst is mixed by 16 hydrazine aluminum sulfates and citric acid that weight ratio is 19:1.
It, can be with by the catalyst that is mixed by 16 hydrazine aluminum sulfates and citric acid by using above-mentioned technical proposal
Group of the modified dihydroxy bisethylene urea crosslinking agent at relatively mild temperature and on cotton fiber is reacted, so that ready-made clothes
Tearing resistance retains significantly.
Further, the preliminary drying temperature in S2 is 60-70 DEG C, time 20-30min.
By using above-mentioned technical proposal, 60-70 DEG C at a temperature of, preliminary drying processing is carried out to ready-made clothes, it is lower in temperature
Preliminary drying at a temperature of, can prevent resin or coating from quickly causing male and female face and surface resin to fabric surface migration.
Further, the drying temperature in S3 is 110-130 DEG C, drying time 5-6min.
Further, the pressing temperature in S4 is 150-180 DEG C, and unit cloth surface pressure is 0.3-0.4kg/cm2, when pressing
Between be 40-60s.
By using above-mentioned technical proposal, pressing is carried out to ready-made clothes and handles the fold that can be reduced on ready-made clothes, improves ready-made clothes
Aesthetics.
Further, the baking temperature in S5 is 140-160 DEG C, bakes time 3-6min.
By using above-mentioned technical proposal, ready-made clothes is baked at 140-160 DEG C, noniron finish liquid can be made pre-
Contracting body under the effect of the catalyst, is crosslinked with fiber and is reacted, and increases the pliability of ready-made clothes fabric, and can be reduced and be torn
The loss of strength.
Further, the cooling temperature in S6 be 10-15 DEG C, cooling time 4-8min.
In conclusion the present invention has the advantages that compared with the prior art
1. can solve the defect that cotton ready-made clothes easily wrinkles, to improve its aesthetics by arrangement of the noniron finish liquid to ready-made clothes;
Using the characteristic of cotton material absorbing sweat, the sweat of skin surface can be quickly absorbed, and the addition of silicon class softening agent can increase
The submissive smooth sense of addition clothing can reduce the temperature of clothing by it with the cooperation of clothing cool feeling agent, and will be so that accelerating
The evaporation of sweat, to reduce feeling of oppression and heat, increases the comfort for wearing clothing so that the inner surface of clothing keeps dry sensation;
2. cooperating using amino-polyether polysiloxane block copolymers as primary raw material with Capmul MCM C8, xylitol, jade powder
And clothing cool feeling agent made from alkyl glycosides can make the feel of fabric fine and smooth, submissive, smooth after its clothing organization
And there is cooling feeling, by it with after three-proof finishing agent and the cooperation of silicon class softening agent, the submissive comfort of clothing can be increased,
And the evaporation that can accelerate moisture on clothes prevents clothing and skin adhesion, improves the comfort for wearing cotton ready-made clothes.
Detailed description of the invention
Fig. 1 is ready-made non-ironing garment cool feeling finishing technique flow chart in embodiment 1.
Specific embodiment
Invention is further described in detail below.
One, the preparation example of clothing cool feeling agent
Amino-polyether polysiloxane block copolymers in following preparation example are selected from what Dongguan City Han Feng chemical science and technology company provided
The terpolymer block silicone oil crude oil of model H790;Emulsifier is selected from the model that Hai Tianyuan Chemical Co., Ltd. in Nantong provides
The amino silicone oil emulsifying agent of HTY-2.
The preparation example 1 of clothing cool feeling agent: 1. taking 30kg water, and Capmul MCM C8 3kg, xylitol 2kg, jade are added thereto
Mountain flour 1kg, alkyl glycosides 1kg obtain mixed liquor after mixing evenly;
2. taking 30kg amino-polyether polysiloxane block copolymers and 15kg emulsifier, 60 DEG C are warming up to after mixing, with
The speed of 2000r/min stirs 30min, is then cooled to 30 DEG C, 0.5kg glacial acetic acid and 10kg water is added, with 400r/min's
After speed stirs 10min;0.5kg glacial acetic acid and 20kg water is added, 15min is then stirred with the speed of 400r/min;Again plus
Enter mixed liquor, then 10min is stirred with the speed of 400r/min, obtains clothing cool feeling agent.
The preparation example 2 of clothing cool feeling agent: 1. taking 30kg water, and Capmul MCM C8 4kg, xylitol 3kg, jade are added thereto
Mountain flour 1.5kg, alkyl glycosides 1.5kg obtain mixed liquor after mixing evenly;
2. taking 35kg amino-polyether polysiloxane block copolymers and 17.5kg emulsifier, 65 DEG C are warming up to after mixing, with
The speed of 2500r/min stirs 35min, is then cooled to 35 DEG C, 0.6kg glacial acetic acid and 10kg water is added, with 700r/min's
After speed stirs 15min;0.6kg glacial acetic acid and 25kg water is added, 20min is then stirred with the speed of 700r/min;Again plus
Enter mixed liquor, then 20min is stirred with the speed of 700r/min, obtains clothing cool feeling agent.
The preparation example 3 of clothing cool feeling agent: 1. taking 30kg water, and Capmul MCM C8 5kg, xylitol 4kg, jade are added thereto
Mountain flour 2kg, alkyl glycosides 2kg obtain mixed liquor after mixing evenly;
2. taking 40kg amino-polyether polysiloxane block copolymers and 20kg emulsifier, 70 DEG C are warming up to after mixing, with
The speed of 3000r/min stirs 40min, is then cooled to 40 DEG C, 0.7kg glacial acetic acid and 10kg water is added, with 1000r/min's
After speed stirs 20min;0.7kg glacial acetic acid and 30kg water is added, 25min is then stirred with the speed of 1000r/min;Again plus
Enter mixed liquor, then 30min is stirred with the speed of 1000r/min, obtains clothing cool feeling agent.
The preparation example 4 of clothing cool feeling agent: the preparation example 1 of this preparation example and the agent of clothing cool feeling the difference is that, raw material
In be not added with Capmul MCM C8, xylitol and jade powder.
Two, the preparation example of noniron finish liquid
Modification dihydroxy bisethylene urea crosslinking agent in following preparation example is selected from the KNITTEX RCT that Hensel steps;Wear-resistant finishing agent
The TURPEX ACN NEW stepped selected from Hensel;Three-proof finishing agent is selected from the MEGASOFT CEC of Du Pont's teflon;Silicon class softening agent
The ULTRATEX SI stepped selected from Hensel.
The preparation example 1 of noniron finish liquid: contain the component of following mass-volume concentration in noniron finish liquid: modified dihydroxy
Bisethylene urea crosslinking agent 80g/L, 16 hydrazine aluminum sulfate 19g/L, citric acid 1g/L, wear-resistant finishing agent 30g/L, three-proof finishing agent
30g/L, silicon class softening agent 30g/L and the agent of clothing cool feeling (preparation example 1 selected from clothing cool feeling agent) 60g/L, surplus is water.
The preparation example 2 of noniron finish liquid: contain the component of following mass-volume concentration in noniron finish liquid: modified dihydroxy
Bisethylene urea crosslinking agent 90g/L, 16 hydrazine aluminum sulfate 21.375g/L, citric acid 1.125g/L, wear-resistant finishing agent 45g/L, three
Anti- finishing agent 45g/L, silicon class softening agent 45g/L and the agent of clothing cool feeling (preparation example 2 selected from clothing cool feeling agent) 70g/L, it is remaining
Amount is water.
The preparation example 3 of noniron finish liquid: contain the component of following mass-volume concentration in noniron finish liquid: modified dihydroxy
Bisethylene urea crosslinking agent 100g/L, 16 hydrazine aluminum sulfate 23.75g/L, citric acid 1.25g/L, wear-resistant finishing agent 60g/L, three
Anti- finishing agent 60g/L, silicon class softening agent 60g/L and the agent of clothing cool feeling (preparation example 3 selected from clothing cool feeling agent) 80g/L, it is remaining
Amount is water.
The preparation example 4 of noniron finish liquid: the preparation example 1 of this preparation example and noniron finish liquid the difference is that, raw material
In do not include the agent of clothing cool feeling.
The preparation example 5 of noniron finish liquid: the preparation example 1 of this preparation example and noniron finish liquid the difference is that, raw material
In do not include the agent of clothing cool feeling and silicon class softener.
The preparation example 6 of noniron finish liquid: the preparation example 1 of this preparation example and noodles finishing fluid the difference is that, clothing
The preparation example 4 that cool feeling agent is selected from the agent of clothing cool feeling is prepared, and the preparing of the clothing cool feeling agent is not added with single octanoic acid in raw material sweet
Grease, xylitol and jade powder.
Two, embodiment
Embodiment 1: a kind of ready-made non-ironing garment cool feeling finishing technique includes the following steps:
S1, spraying: noniron finish liquid (preparation example 1 selected from noniron finish liquid) is sprayed on ready-made clothes after atomization, band liquid
Rate is 100%;
S2, preliminary drying: carrying out preliminary drying processing to the ready-made clothes after spraying, and preliminary drying temperature is 60 DEG C, time 20min, it is made to contain damp rate
It is 80%;
S3, drying: drying and processing is carried out to pre-baked ready-made clothes, drying temperature is 110 DEG C, and drying time 5min contains it
Damp rate is 15%;
S4, pressing: pressing sizing is carried out to double sleeves of ready-made clothes, neck, preceding width, back panel, yoke, pressing temperature is 150 DEG C, unit cloth
Surface pressure is 0.3kg/cm2, the pressing time is 40s;
S5, it bakes sizing: the ready-made clothes after pressing being carried out to bake sizing, baking temperature is 140 DEG C, bakes time 3min;
S6, cooling: carrying out cold front heavy rain processing to ready-made clothes after molding is baked, and cooling temperature is 10 DEG C, cooling time 4min.
Embodiment 2: a kind of ready-made non-ironing garment cool feeling finishing technique includes the following steps:
S1, spraying: noniron finish liquid (preparation example 2 selected from noniron finish liquid) is sprayed on ready-made clothes after atomization, band liquid
Rate is 90%;
S2, preliminary drying: carrying out preliminary drying processing to the ready-made clothes after spraying, and preliminary drying temperature is 65 DEG C, time 25min, it is made to contain damp rate
It is 75%;
S3, drying: drying and processing is carried out to pre-baked ready-made clothes, drying temperature is 120 DEG C, and drying time 5min contains it
Damp rate is 12%;
S4, pressing: pressing sizing is carried out to double sleeves of ready-made clothes, neck, preceding width, back panel, yoke, pressing temperature is 165 DEG C, unit cloth
Surface pressure is 0.35kg/cm2, the pressing time is 50s;
S5, it bakes sizing: the ready-made clothes after pressing being carried out to bake sizing, baking temperature is 150 DEG C, bakes time 4min;
S6, cooling: carrying out cooling treatment to ready-made clothes after molding is baked, and cooling temperature is 13 DEG C, cooling time 6min.
Embodiment 3: a kind of ready-made non-ironing garment cool feeling finishing technique includes the following steps:
S1, spraying: noniron finish liquid (preparation example 3 selected from noniron finish liquid) is sprayed on ready-made clothes after atomization, band liquid
Rate is 80%;
S2, preliminary drying: carrying out preliminary drying processing to the ready-made clothes after spraying, and preliminary drying temperature is 70 DEG C, time 30min, it is made to contain damp rate
It is 70%;
S3, drying: drying and processing is carried out to pre-baked ready-made clothes, drying temperature is 130 DEG C, and drying time 6min contains it
Damp rate is 8%;
S4, pressing: pressing sizing is carried out to double sleeves of ready-made clothes, neck, preceding width, back panel, yoke, pressing temperature is 180 DEG C, unit cloth
Surface pressure is 0.4kg/cm2, the pressing time is 60s;
S5, it bakes sizing: the ready-made clothes after pressing being carried out to bake sizing, baking temperature is 160 DEG C, bakes time 6min;
S6, cooling: carrying out cooling treatment to ready-made clothes after molding is baked, and cooling temperature is 15 DEG C, cooling time 8min.
Four, comparative example
Comparative example 1: this comparative example difference from example 1 is that, noniron finish liquid be selected from noniron finish liquid preparation example 4
It prepares, the agent of clothing cool feeling is not included in the noniron finish liquid.
Comparative example 2: this comparative example difference from example 1 is that, noniron finish liquid be selected from noniron finish liquid system
Prepared by standby example 5, the agent of clothing cool feeling and silicon class softener are not included in the noniron finish liquid.
Comparative example 3: this comparative example difference from example 1 is that, noniron finish liquid be selected from noniron finish liquid system
Prepared by standby example 6, the preparation example 4 that the clothing cool feeling agent in the noniron finish liquid is selected from the agent of clothing cool feeling is prepared, and the clothing is cool
Preparing for agent of sense is not added with Capmul MCM C8, xylitol and jade powder in raw material.
Five, performance test
Finished product physicochemical property: according to the regulation in GB/T2660-2017 " shirt ", to using embodiment 1-3 and comparative example 1-3
The finished product physicochemical property of treated pure cotton shirt is detected.Creasy recovery angle: according to AATCC 66-2014, " woven fabric is rolled over
Wrinkle recovery: replying horn cupping " measurement.To using embodiment 1-3 and comparative example 1-3 treated pure cotton shirt from flexibility,
Smooth feeling and cooling feeling carry out feel grading, are divided into 5 grades, and 1 grade worst, and 5 grades best;To using embodiment 1-3 and comparison
Example 1-3 treated pure cotton shirt carries out wearing feeling grading from comfort and drying time, wherein test environment is at 30 DEG C
At a temperature of, comfort after wearing the shirt perspired and the time that is completely dried of perspiration shirt is counted, comfortably
Sense grading is divided into 5 grades, and 1 grade worst, and 5 grades best.Test result is shown in table 1.
Table 1
There is good ironing-free performance, physicochemical property using the shirt of process of the invention it can be seen from 1 data of table
Meet the requirement of Grade A in GB/T2660-2017 " shirt ", and there is excellent flexibility, smooth feeling and cooling feeling,
After hot weather dress, shirt absorbing sweat and can reduce the temperature of wearer rapidly, furthermore have shorter drying time,
Cotton shirt rapid draing after enabling absorbing sweat reduces feeling of oppression and heat and sense of discomfort.
Prepared by the preparation example 4 that the noniron finish liquid of comparative example 1 is selected from noniron finish liquid, clothing is not included in the noniron finish liquid
Object cool feeling agent;Compared to embodiment 1, the smooth feeling and cooling feeling of the shirt after the arrangement of comparative example 1 are decreased obviously, and are worn
Comfort be substantially reduced and drying time is obviously prolonged, illustrate that the addition of clothing cool feeling agent in noniron finish liquid can be obvious
The feel and comfort of shirt are improved, and helps to shorten the drying time of cotton shirt.
Prepared by the preparation example 5 that the noniron finish liquid of comparative example 2 is selected from noniron finish liquid, clothing is not included in the noniron finish liquid
The agent of object cool feeling and silicon class softener;Compared to embodiment 1, the flexibility of the shirt after the arrangement of comparative example 2, smooth feeling with
And cooling feeling is decreased obviously, the comfort of dress is substantially reduced and drying time is obviously prolonged, and illustrates noniron finish liquid underpants
The agent of object cool feeling and the addition of silicon class softening agent can significantly improve the feel and comfort of shirt, and help to shorten cotton
The drying time of matter shirt.
Prepared by the preparation example 6 that the noniron finish liquid of comparative example 3 is selected from noniron finish liquid, the clothing in the noniron finish liquid is cool
The preparation example 4 that sense agent is selected from the agent of clothing cool feeling is prepared, and preparing for the clothing cool feeling agent is not added with single sad glycerol in raw material
Ester, xylitol and jade powder;Cooling feeling compared to embodiment 1, the shirt after the arrangement of comparative example 3 is decreased obviously, and is worn
Comfort be substantially reduced and drying time is obviously prolonged, illustrate to be added to Capmul MCM C8, xylitol and jade
Clothing cool feeling agent made from powder is to clothing cool feeling better effect.
This specific embodiment is only explanation of the invention, is not limitation of the present invention, those skilled in the art
Member can according to need the modification that not creative contribution is made to the present embodiment after reading this specification, but as long as at this
All by the protection of Patent Law in the scope of the claims of invention.
Claims (9)
1. a kind of ready-made non-ironing garment cool feeling finishing technique, characterized by the following steps:
S1, spraying: noniron finish liquid is sprayed on ready-made clothes after atomization, liquid carrying rate 80-100%;
S2, preliminary drying: carrying out preliminary drying processing to the ready-made clothes after spraying, it is made to contain damp rate 70-80%;
S3, drying: carrying out drying and processing to pre-baked ready-made clothes, it is made to contain damp rate 8-15%;
S4, pressing: pressing sizing is carried out to double sleeves of ready-made clothes, neck, preceding width, back panel, yoke;
S5, it bakes sizing: the ready-made clothes after pressing being carried out to bake sizing;
S6, cooling: cooling treatment is carried out to ready-made clothes after molding is baked;
The noniron finish liquid takes water as a solvent preparation, the component of following mass-volume concentration is contained in noniron finish liquid: modified
Dihydroxy bisethylene urea crosslinking agent 80-100g/L, catalyst 20-25g/L, wear-resistant finishing agent 30-60g/L, three-proof finishing agent 30-
60g/L, silicon class softening agent 30-60g/L and clothing cool feeling agent 60-80g/L.
2. a kind of ready-made non-ironing garment cool feeling finishing technique according to claim 1, it is characterised in that: the clothing cool feeling agent by
The raw material of following parts by weight is made: 30-40 parts of amino-polyether polysiloxane block copolymers, 15-20 parts of emulsifier, single octanoic acid are sweet
3-5 parts of grease, 2-4 parts of xylitol, 1-2 parts of jade powder, 1-2 parts of alkyl glycosides, 1-1.4 parts of glacial acetic acid and 60-70 parts of water.
3. a kind of ready-made non-ironing garment cool feeling finishing technique according to claim 2, it is characterised in that: the clothing cool feeling agent is adopted
It prepares with the following method: based on parts by weight, 1. taking 30 parts of water, Capmul MCM C8 3-5 parts, xylitol 2-4 are added thereto
Part, 1-2 parts of jade powder, 1-2 parts of alkyl glycosides, after mixing evenly, obtain mixed liquor;
2. taking 30-40 parts of amino-polyether polysiloxane block copolymers and 15-20 parts of emulsifiers, 60-70 is warming up to after mixing
DEG C, 30-40min is stirred with the speed of 2000-3000r/min, is then cooled to 30-40 DEG C, be added 0.5-0.7 part glacial acetic acid with
10 parts of water, after stirring 10-20min with the speed of 400-1000r/min;0.5-0.7 parts of glacial acetic acid and 20-30 parts of water are added,
Then 15-25min is stirred with the speed of 400-1000r/min;Mixed liquor is added, then is stirred with the speed of 400-1000r/min
10-30min is mixed, clothing cool feeling agent is obtained.
4. a kind of ready-made non-ironing garment cool feeling finishing technique according to claim 1, it is characterised in that: the catalyst is by weight
Than being mixed for 16 hydrazine aluminum sulfates and citric acid of 19:1.
5. a kind of ready-made non-ironing garment cool feeling finishing technique according to claim 1, it is characterised in that: the preliminary drying temperature in S2 is
60-70 DEG C, time 20-30min.
6. a kind of ready-made non-ironing garment cool feeling finishing technique according to claim 1, it is characterised in that: the drying temperature in S3 is
110-130 DEG C, drying time 5-6min.
7. a kind of ready-made non-ironing garment cool feeling finishing technique according to claim 1, it is characterised in that: the pressing temperature in S4 is
150-180 DEG C, unit cloth surface pressure is 0.3-0.4kg/cm2, the pressing time is 40-60s.
8. a kind of ready-made non-ironing garment cool feeling finishing technique according to claim 1, it is characterised in that: the baking temperature in S5 is
140-160 DEG C, bake time 3-6min.
9. a kind of ready-made non-ironing garment cool feeling finishing technique according to claim 1, it is characterised in that: the cooling temperature in S6 is
10-15 DEG C, cooling time 4-8min.