CN105400063A - 纳米超细滑石粉增强聚丙烯材料 - Google Patents
纳米超细滑石粉增强聚丙烯材料 Download PDFInfo
- Publication number
- CN105400063A CN105400063A CN201410449384.5A CN201410449384A CN105400063A CN 105400063 A CN105400063 A CN 105400063A CN 201410449384 A CN201410449384 A CN 201410449384A CN 105400063 A CN105400063 A CN 105400063A
- Authority
- CN
- China
- Prior art keywords
- polypropylene
- nanometer
- talcum powder
- ultrafine
- district
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
聚丙烯(PP)为非极性的结晶塑料，是五大类通用塑料之一，原料来料丰富、价格便宜、易于加工成型等等，因此用途非常广泛。尽管聚丙烯有众多优点，但是，也存在一些不足之处。最大的缺点是耐寒性差。低温易断，且收缩率大，抗蠕变性差，制品尺寸稳定性差，易变性。通过纳米改性来补足PP本身不足之处。纳米超细滑石粉增强聚丙烯材料，由下列重量比的原料组成：聚丙烯：80～90；超细滑石粉：5～15；硅烷偶联剂：0.5～1.5；抗氧剂：1.0～3.0；光稳定剂：1.0～2.0；分散剂：1.0～2.0。<!-- 2 -->
Description
技术领域
本发明属聚丙烯材料生产技术领域，改善聚丙烯原有的不足。生产出符合社会需求的产品。
背景技术
聚丙烯(PP)为非极性的结晶塑料，是五大类通用塑料之一，原料来料丰富、价格便宜、易于加工成型等等，因此用途非常广泛。尽管聚丙烯有众多优点，但是，也存在一些不足之处。最大的缺点是耐寒性差。低温易断，且收缩率大，抗蠕变性差，制品尺寸稳定性差，易变性。通过纳米改性来补足PP本身不足之处。
发明内容
本发明的目的是提供一种不影响材料的力学性能，环保的聚丙烯专用改性料。纳米超细滑石粉增强聚丙烯材料，由下列重量比的原料组成：
聚丙烯：80～90；
超细滑石粉：5～15；
硅烷偶联剂：0.5～1.5；
抗氧剂：1.0～3.0；
光稳定剂：1.0～2.0；
分散剂：1.0～2.0。
本发明中，所述抗氧剂为乙烯-辛烯的共聚物，所述分散剂为工业白油10#。
所述纳米超细滑石粉增强聚丙烯材料的制备方法为：
将各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为90-100℃，二区为150-180℃，三区为200-210℃，四区为200-205℃；五区为190-200℃，停留时间为1-2分钟，压力为10-15Mpa。
具体实施方式
下面通过具体实施方式对发明做进一步说明，以下实施例是对本发明进行说明而非加以限定。
实施例1
(1)按重量比分别称取各原料如下：
聚丙烯：80；
超细滑石粉：5；
硅烷偶联剂：0.5；
抗氧剂：1.0；
光稳定剂：1.0；
分散剂：1.0。
(2)将各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为90-100℃，二区为150-180℃，三区为200-210℃，四区为200-205℃；五区为190-200℃，停留时间为1-2分钟，压力为10-15Mpa。
实验结果
实施例2
(1)按重量比分别称取各原料如下：
聚丙烯：85；
超细滑石粉：10；
硅烷偶联剂：1.0；
抗氧剂：2.0；
光稳定剂：1.5；
分散剂：1.5。
(2)将各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为90-100℃，二区为150-180℃，三区为200-210℃，四区为200-205℃；五区为190-200℃，停留时间为1-2分钟，压力为10-15Mpa。
实验结果
实施例3
(1)按重量比分别称取各原料如下：
聚丙烯：90；
超细滑石粉：15；
硅烷偶联剂：1.5；
抗氧剂：3.0；
光稳定剂：2.0；
分散剂：2.0。
(2)将各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为90-100℃，二区为150-180℃，三区为200-210℃，四区为200-205℃；五区为190-200℃，停留时间为1-2分钟，压力为10-15Mpa。
实验结果
Claims (3)
1.纳米超细滑石粉增强聚丙烯材料，其特征在于，由下列重量比的原料组成：
聚丙烯：80～90；
超细滑石粉：5～15；
硅烷偶联剂：0.5～1.5；
抗氧剂：1.0～3.0；
光稳定剂：1.0～2.0；
分散剂：1.0～2.0。
2.根据权利要求1所述的纳米超细滑石粉增强聚丙烯材料，其特征在于，最优重量比原料组成为：
聚丙烯：85；
超细滑石粉：10；
硅烷偶联剂：1.0；
抗氧剂：2.0；
光稳定剂：1.5；
分散剂：1.5。
3.根据权利要求1所述的纳米超细滑石粉增强聚丙烯材料，其特征在于，所述抗氧剂为乙烯-辛烯的共聚物，所述分散剂为工业白油10#。