CN105400053A - 一种微渗透性低粘度pe合金材料及其制备方法 - Google Patents
一种微渗透性低粘度pe合金材料及其制备方法 Download PDFInfo
- Publication number
- CN105400053A CN105400053A CN201511004639.8A CN201511004639A CN105400053A CN 105400053 A CN105400053 A CN 105400053A CN 201511004639 A CN201511004639 A CN 201511004639A CN 105400053 A CN105400053 A CN 105400053A
- Authority
- CN
- China
- Prior art keywords
- resin
- low viscosity
- alloy material
- micro
- perviousness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种微渗透性低粘度PE合金材料,其组成,按照重量百分比为:(1)PE树脂65-75%,(2)PA6树脂10-15%,(3)PP树脂5-10%,(4)矿物填充体系4-5%,(5)相容剂4-6%,(6)抗氧剂0.2-0.5%。本发明的微渗透性低粘度PE合金材料将满足了客户小型特殊化工瓶的需求,具备微渗透性、易加工性能等性能,满足小型吹瓶级产品的要求。另外,本发明还提供了一种微渗透性低粘度PE合金材料的制备方法。
Description
技术领域
本发明涉及一种高分子材料技术领域,尤其是涉及一种微渗透性低粘度PE合金材料及其制备方法。
背景技术
PE树脂常用于吹瓶,利用PE/PP树脂同PA树脂的相容性较差,易出现一部分分层,在利用二氧化硅等矿物质扩大层与层之间的缝隙,以达到亲水和亲油性的溶液缓慢的渗透。
PE合金材料保留PE的吹瓶性能,利用PP和PA易加工性,已达到低粘度PE合金材料。
发明内容
针对上述现有技术存在的缺点,本发明旨在提供一种微渗透性低粘度PE合金材料及其制备方法,来满足客户越来越高的需求。
本发明采用的技术方案:本发明公开的一种微渗透性低粘度PE合金材料,其组成按照重量百分比为:(1)PE树脂65-75%,(2)PA6树脂10-15%,(3)PP树脂5-10%,(4)矿物填充体系4-5%,(5)相容剂4-6%,(6)抗氧剂0.2-0.5%。
本发明还包括有以下:
PE树脂为高密度聚乙烯树脂,PA6树脂为尼龙树脂,PP树脂为聚丙烯树脂。
矿物填充体系为:包括二氧化硅等。
相容剂为以PP和LLDPE为主体,多单体(马来酸酐,丙烯酸)。
本发明还提供了一种制备微渗透性低粘度PE合金材料的方法,该方法包括以下步骤:
原材料的处理及混合:
将PE树脂PA树脂和PP树脂、相容剂等在高速混料机中110℃混合3分钟,使各组分充分搅拌分散均匀;再加入A物料混合3分钟;
A物料:矿物填充体系、抗氧剂等在高速混料机180℃中混合30分钟,使各组分充分搅拌分散均匀;
熔融挤出:
将混合好的物料加入双螺杆挤出机中熔融挤出,熔融挤出温度在190-210℃之间,螺杆转速为300转/分;
造粒及后处理:
对挤出的物料进行冷却、风干、切粒、过强磁、包装得到成品。
具体的是,其中所述的微渗透性低粘度PE合金材料,E树脂为高密度聚乙烯树脂,PA6树脂为尼龙树脂,PP树脂为聚丙烯树脂;矿物填充体系为:包括硫酸钙、滑石粉等。相容剂为以PP和LLDPE为主体,多单体(马来酸酐,丙烯酸)。
本发明的微渗透性低粘度PE合金材料将满足了客户小型特殊化工瓶的需求,具备微渗透性、易加工性能等性能,满足小型吹瓶级产品的要求。
具体实施方式
下面结合实施例来具体说明本发明。
实施例1
70%重量PE和10%重量PA与10%重量的PP、5%重量的矿物填充体系、4.9%重量的相容剂体系、0.1%重量的主抗氧剂四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯(1010)和0.2%辅助抗氧剂三(2,4-二叔丁基苯基)亚磷酸酯(168)。
实施例2
65%重量PE和15%重量PA与10%重量的PP、4.9%重量的矿物填充体系、5%重量的相容剂体系、0.1%重量的主抗氧剂四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯(1010)和0.2%辅助抗氧剂三(2,4-二叔丁基苯基)亚磷酸酯(168)。
实施例的制备方法及工艺如下:
(1)原材料的处理及混合
将PE树脂PA树脂和PP树脂、相容剂等在高速混料机中110℃混合3分钟,使各组分充分搅拌分散均匀;再加入A物料混合3分钟。
A物料:矿物填充体系、抗氧剂等在高速混料机180℃中混合30分钟,使各组分充分搅拌分散均匀;
(2)熔融挤出
将混合好的物料加入双螺杆挤出机中熔融挤出,熔融挤出温度在190-210℃之间,螺杆转速为300转/分;
(3)造粒及后处理
对挤出的物料进行冷却、风干、切粒、过强磁、包装得到成品。
对实施例1和实施例2所得的微渗透性低粘度PE合金材料的性能如下表格:
综上所述,是本发明的较佳实施例,凡依本发明技术方案所作出的改变,所产生的功能作用未能超出本发明技术方案的范围时,均属于本发明的保护范围。
Claims (5)
1.一种微渗透性低粘度PE合金材料,其特征在于,按重量百分比由以下组分组成:
2.如权利要求1所述的一种微渗透性低粘度PE合金材料,其特征在于:PE树脂为高密度聚乙烯树脂,PA6树脂为尼龙树脂,PP树脂为聚丙烯树脂。
3.如权利要求1所述的一种微渗透性低粘度PE合金材料,其特征在于:矿物填充体系为:包括二氧化硅等。
4.如权利要求1所述的一种微渗透性低粘度PE合金材料,其特征在于:相容剂为以PP和LLDPE为主体,多单体(马来酸酐,丙烯酸)。
5.一种制备如权利要求1-4任何一项所述的微渗透性低粘度PE合金材料的方法,其特征在于,该方法包括以下步骤:
(1)原材料的处理及混合:
将PE树脂PA树脂和PP树脂、相容剂等在高速混料机中110℃混合3分钟,使各组分充分搅拌分散均匀;再加入A物料混合3分钟;
A物料:矿物填充体系、抗氧剂等在高速混料机180℃中混合30分钟,使各组分充分搅拌分散均匀;
(2)熔融挤出:
将混合好的物料加入双螺杆挤出机中熔融挤出,熔融挤出温度在190-210℃之间,螺杆转速为300转/分;
(3)造粒及后处理:
对挤出的物料进行冷却、风干、切粒、过强磁、包装得到成品。