CN105386148A - 可反射红外线的汽车用凉感有色涤纶长丝及其制备方法 - Google Patents
可反射红外线的汽车用凉感有色涤纶长丝及其制备方法 Download PDFInfo
- Publication number
- CN105386148A CN105386148A CN201510700936.XA CN201510700936A CN105386148A CN 105386148 A CN105386148 A CN 105386148A CN 201510700936 A CN201510700936 A CN 201510700936A CN 105386148 A CN105386148 A CN 105386148A
- Authority
- CN
- China
- Prior art keywords
- polyester filament
- colored polyester
- infrared
- automotive
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种可反射红外线的汽车用凉感有色涤纶长丝及其制备方法,涉及纺织制造技术领域,应用本发明本身带有几种颜色的反射红外线型高分子材料参与有色母粒的共混配色,通过双螺杆挤出造粒,然后应用高速纺丝设备制成汽车用凉感涤纶有色长丝,让产生热量的红外光不要在面料表面积聚,从而得到一定的温差效果,达到降低汽车内饰面料表面的温度的目的。利用现有设备,通过工艺调整,投资少,最关键的指标是,采用TSR,太阳光的总反射率以百分数表示,该类产品的TSR至少是普通产品的1.5倍-2倍。
Description
技术领域:
本发明涉及纺织制造技术领域,具体涉及一种可反射红外线的汽车用凉感有色涤纶长丝及其制备方法。
背景技术:
目前,市场上使用玉石粉制作功能母粒,所得涤纶长丝制作的面料通过玉石粉的快速导热原理,可使面料附近的温度降低1-2℃。但有缺点,含玉石粉的纤维导热的同时也在吸热,用此类材料制作的面料用在汽车内饰中,在光照强的车内更容易吸热。
据测试,夏日高温,密闭车内的温度可达60-70℃,与人体接触面积最大的汽车座椅上积聚的热量给人体带来非常不舒服的感受,甚至引发人体汗腺失控。
为了降低汽车内饰面料表面的温度,本发明引入反射红外线的原理,让产生热量的红外光不要在面料表面积聚,从而得到一定的温差效果,而这种效果,在汽车空调打开后,对比更明显。
发明内容:
本发明所要解决的技术问题在于,提供一种可反射红外线的汽车用凉感有色涤纶长丝及其制备方法,应用本发明本身带有几种颜色的反射红外线型高分子材料参与有色母粒的共混配色,通过双螺杆挤出造粒,然后应用高速纺丝设备制成汽车用凉感涤纶有色长丝,让产生热量的红外光不要在面料表面积聚,从而得到一定的温差效果,达到降低汽车内饰面料表面的温度的目的。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种可反射红外线的汽车用凉感有色涤纶长丝,其特征在于,所述长丝由以下重量份的配方配比组成:
基本树脂:90-95%
带颜色母粒:1-10%
反射红外线型高分子料:0.1-5%
所述基本树脂为聚酯类;
所述带颜色母粒是市场为有色涤纶长丝制备的基本配方,包括复合氧化物,金属络合物,有机或无机组成的颜色体系;
所述反射红外线型高分子料,主要指通过硅处理的无机物颗粒,通过反射红外线型高分子料,使得产生热量的红外光不在面料表面积聚,从而得到一定的温差效果,达到降低汽车内饰面料表面的温度的目的。
一种可反射红外线的汽车用凉感有色涤纶长丝的制备方法,其特征在于以下步骤:
1)、通过测色仪器与软件,选定0.1-5%相对含量的反射红外线型高分子料的颜色,根据需要与1-10%相对含量的带颜色母粒复配,得到两者的质量配比;
2)、通过双螺杆挤出机,采用侧喂料方式,将上述带颜色母粒和反射红外线型高分子料按纤维浓度需要的最终比例喂入螺杆内,熔融,剪切,混炼,挤出,造粒,得到成品母粒;所述挤出温度设定在200-280℃,螺杆转速为200转-500转/分;
3)、利用高速纺有色涤纶纺丝装置,母粒注入部分则使用第二步骤的成品母粒;所述纺丝速度从2500-3300米/分调节,通过侧风冷却,油嘴上油,卷取机构卷装成型,得到可反射红外线的汽车用凉感有色涤纶长丝。
本发明的有益效果为:提供一种可反射红外线的汽车用凉感有色涤纶长丝及其制备方法,本发明的反射红外线型高分子材料作为复配色母粒中的单色,省去一定的母粒成本;利用现有设备,通过工艺调整,投资少,即可获得特殊的反射红外线型有色涤纶长丝。通过本发明制得的可反射红外线的汽车用凉感有色涤纶长丝,最关键的指标是,采用TSR,太阳光的总反射率以百分数表示,该类产品的TSR至少是普通产品的1.5倍-2倍。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
成分(质量分数) | 实施例1 | 实施例2 | 对比例 |
基本树脂 | 96.5% | 95% | 97% |
带颜色母粒 | 3% | 3.5% | 3% |
反射红外线型高分子料 | 0.5% | 1.5% | -- |
红外反射率TSR | 15% | 20% | 10% |
从上表可知,通过本发明制得的可反射红外线的汽车用凉感有色涤纶长丝,采用TSR,太阳光的总反射率以百分数表示,该类产品的TSR至少是普通产品的1.5倍-2倍。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (5)
1.一种可反射红外线的汽车用凉感有色涤纶长丝,其特征在于,所述长丝由以下重量份的配方配比组成:
基本树脂:90-95%
带颜色母粒:1-10%
反射红外线型高分子料:0.1-5%。
2.根据权利要求1所述的一种可反射红外线的汽车用凉感有色涤纶长丝,其特征在于,所述基本树脂为聚酯类。
3.根据权利要求1所述的一种可反射红外线的汽车用凉感有色涤纶长丝,其特征在于,所述带颜色母粒是市场为有色涤纶长丝制备的基本配方,包括复合氧化物,金属络合物,有机或无机组成的颜色体系。
4.根据权利要求1所述的一种可反射红外线的汽车用凉感有色涤纶长丝,其特征在于,所述反射红外线型高分子料,主要指通过硅处理的无机物颗粒。
5.一种可反射红外线的汽车用凉感有色涤纶长丝的制备方法,其特征在于以下步骤:
1)、通过测色仪器与软件,选定0.1-5%相对含量的反射红外线型高分子料的颜色,根据需要与1-10%相对含量的带颜色母粒复配,得到两者的质量配比;
2)、通过双螺杆挤出机,采用侧喂料方式,将上述带颜色母粒和反射红外线型高分子料按纤维浓度需要的最终比例喂入螺杆内,熔融,剪切,混炼,挤出,造粒,得到成品母粒;所述挤出温度设定在200-280℃,螺杆转速为200转-500转/分;
3)、利用高速纺有色涤纶纺丝装置,母粒注入部分则使用第二步骤的成品母粒;所述纺丝速度从2500-3300米/分调节,通过侧风冷却,油嘴上油,卷取机构卷装成型,得到可反射红外线的汽车用凉感有色涤纶长丝。