CN105367064A - 一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料及其制备方法 - Google Patents

一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料及其制备方法 Download PDF

Info

Publication number
CN105367064A
CN105367064A CN201510706674.8A CN201510706674A CN105367064A CN 105367064 A CN105367064 A CN 105367064A CN 201510706674 A CN201510706674 A CN 201510706674A CN 105367064 A CN105367064 A CN 105367064A
Authority
CN
China
Prior art keywords
silicon carbide
powder
circuit board
interference
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510706674.8A
Other languages
English (en)
Inventor
王丹丹
王乐平
夏运明
涂聚友
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI LONGDUO ELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
HEFEI LONGDUO ELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI LONGDUO ELECTRONIC TECHNOLOGY Co Ltd filed Critical HEFEI LONGDUO ELECTRONIC TECHNOLOGY Co Ltd
Priority to CN201510706674.8A priority Critical patent/CN105367064A/zh
Publication of CN105367064A publication Critical patent/CN105367064A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料，该碳化硅基陶瓷基板以微米级的碳化硅粉体与氟金云母粉复合使用，可有效降低碳化硅的烧结温度，获得更好的绝缘性，而含有纳米陶瓷粉透明液体的聚乙二醇复合溶剂对粉体间的浸润性和粘结能力强，可使得各物料间均匀分散粘合，形成致密紧凑的坯体，加入的胶体石墨导热性佳，有一定的防止电磁干扰的功效，可提高电路板的使用性能，制得的坯体在相对较低的烧结温度下即可得到高致密度、高强度、高导热性的复合陶瓷基板，应用潜力巨大。

Description

一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料及其制备方法
技术领域
本发明涉及碳化硅陶瓷制备技术领域，尤其涉及一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料及其制备方法。
背景技术
随着电子元器件功率和密度的增大，致使单位体积发热量也随之增加，对电路基板的综合性能要求越来越高，其中陶瓷基板具备良好的综合性能，在绝缘性、导热性以及热膨胀性、化学稳定性等方面表现突出，逐渐被广泛的应用于基板材料中，其中沿用较久的主要是以氧化铝、氧化铍作为基板原料，然而氧化铝陶瓷片存在热导率低、热膨胀系数与Si不相匹配等缺点，氧化铍陶瓷虽然综合性能较为优良，但是其生产成本较高、有毒，氮化铝陶瓷虽然综合性能较为优良，但生产成本较高，应用也受到限制，反之以碳化硅作为基板材料在使用性能上则具有较为明显的优势。
虽然碳化硅陶瓷基板的应用前景广阔，然而在实际生产过程中存在烧结致密度低、原料利用率低、绝缘性有待提高等等问题，制约着这类材料的大规模使用，急需从原料配制及生产工艺上做进一步的改进。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料及其制备方法。
本发明是通过以下技术方案实现的：
一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料，该材料由以下重量份的原料制成：碳化硅60-70、氟金云母粉8-10、胶体石墨1-2、固含量为10-15%的硅溶胶5-8、硝酸钇1-2、硅烷偶联剂kh5501-2、甘油8-10、乙二醇5-6、聚乙二醇1-2、纳米陶瓷粉透明液体10-12、去离子水50-60。
所述的一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料的制备方法为：
（1）先将碳化硅、氟金云母粉球磨分散12-15h，随后加入胶体石墨、硅溶胶、硅烷偶联剂kh550继续混合球磨分散4-5h后，加入其它剩余物料，密闭混合球磨分散4-5h，将所得浆料完全干燥后过200-300目筛；
（2）将上述过筛粉体投入模具中压制成型，所得坯体在400-500℃下进行排胶处理，处理结束后将坯体送入真空电阻炉中，其中氮气和氢气的流量比为1:0.5-0.6，并在氮气和氢气混合气体氛围下以1500-1650℃的温度保温烧结4-6h，烧结结束后自然冷却至室温，即得所述复合陶瓷基板材料。
本发明制备的碳化硅基陶瓷基板以微米级的碳化硅粉体与氟金云母粉复合使用，可有效降低碳化硅的烧结温度，获得更好的绝缘性，而含有纳米陶瓷粉透明液体的聚乙二醇复合溶剂对粉体间的浸润性和粘结能力强，可使得各物料间均匀分散粘合，形成致密紧凑的坯体，加入的胶体石墨导热性佳，有一定的防止电磁干扰的功效，可提高电路板的使用性能，制得的坯体在相对较低的烧结温度下即可得到高致密度、高强度、高导热性的复合陶瓷基板，应用潜力巨大。
具体实施方式
该实施例陶瓷基板材料由以下重量份的原料制成：碳化硅60、氟金云母粉8、胶体石墨1、固含量为10%的硅溶胶5、硝酸钇1、硅烷偶联剂kh5501、甘油8、乙二醇5、聚乙二醇1、纳米陶瓷粉透明液体10、去离子水50。
该陶瓷基板的制备方法为：
（1）先将碳化硅、氟金云母粉球磨分散12h，随后加入胶体石墨、硅溶胶、硅烷偶联剂kh550继续混合球磨分散4h后，加入其它剩余物料，密闭混合球磨分散4h，将所得浆料完全干燥后过200目筛；
（2）将上述过筛粉体投入模具中压制成型，所得坯体在400℃下进行排胶处理，处理结束后将坯体送入真空电阻炉中，其中氮气和氢气的流量比为1:0.5，并在氮气和氢气混合气体氛围下以1600℃的温度保温烧结5h，烧结结束后自然冷却至室温，即得所述复合陶瓷基板材料。
该实施例制得的基板的性能测试结构为：
体积密度：3.20g/cm3；弯曲强度：512MPa；热导率：153.6（W/m.k）。

Claims (2)

1.一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料，其特征在于，该材料由以下重量份的原料制成：碳化硅60-70、氟金云母粉8-10、胶体石墨1-2、固含量为10-15%的硅溶胶5-8、硝酸钇1-2、硅烷偶联剂kh5501-2、甘油8-10、乙二醇5-6、聚乙二醇1-2、纳米陶瓷粉透明液体10-12、去离子水50-60。
2.如权利要求1所述的一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料及其制备方法，其特征在于，所述的制备方法为：
（1）先将碳化硅、氟金云母粉球磨分散12-15h，随后加入胶体石墨、硅溶胶、硅烷偶联剂kh550继续混合球磨分散4-5h后，加入其它剩余物料，密闭混合球磨分散4-5h，将所得浆料完全干燥后过200-300目筛；
（2）将上述过筛粉体投入模具中压制成型，所得坯体在400-500℃下进行排胶处理，处理结束后将坯体送入真空电阻炉中，其中氮气和氢气的流量比为1:0.5-0.6，并在氮气和氢气混合气体氛围下以1500-1650℃的温度保温烧结4-6h，烧结结束后自然冷却至室温，即得所述复合陶瓷基板材料。
CN201510706674.8A 2015-10-27 2015-10-27 一种防电磁干扰高导热的碳化硅基陶瓷电路板基板材料及其制备方法 Pending CN105367064A (zh)