CN105367028A - 一种抗弯折防渗蒸压加气混凝土砌块及其制作方法 - Google Patents
一种抗弯折防渗蒸压加气混凝土砌块及其制作方法 Download PDFInfo
- Publication number
- CN105367028A CN105367028A CN201510754489.6A CN201510754489A CN105367028A CN 105367028 A CN105367028 A CN 105367028A CN 201510754489 A CN201510754489 A CN 201510754489A CN 105367028 A CN105367028 A CN 105367028A
- Authority
- CN
- China
- Prior art keywords
- hour
- aerated concrete
- block
- add
- seepage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗弯折防渗蒸压加气混凝土砌块,通过对剑麻短纤维、罗布麻纤维进行乙酰化反应封闭了纤维素中游离的羟基,提高了材料的疏水性能和热稳定性,再配合物理改性方法添加其他有效成分,改善了纤维在蒸压加气混凝土中耐久性和分散性,添加的纳米二氧化钛增加了砌块的抗菌性,添加的液体石蜡提高了砌块的防潮性能,添加的废砂浆解决了环境污染的问题,降低了生产成本,并且实现节能环保、变废为宝的主题,本发明加气砌块具有抗弯折、防渗耐水性、使用寿命长的优点。
Description
技术领域
本发明涉及加气砌块技术领域,具体涉及一种抗弯折防渗蒸压加气混凝土砌块及其制作方法。
背景技术
作为新型墙体材料的重要品种之一,蒸压加气混凝土砌块与传统的黏土烧结砖相比具有保温隔热效果好、防火性能好、隔音、质轻、环保等众多优点。然而,加气混凝土砌块体积变形系数偏大、强度偏低、吸水率大,且砌筑成墙体时,墙体易出现裂缝,抹灰层易产生大面积龟裂、空鼓和脱落现象,表现出明显的脆性,在一定程度上阻碍了蒸压加气混凝土砌块的进一步应用和推广。纤维作为一种很好的水泥基体增强材料自20世纪起就被广泛的应用到传统的普通混凝土制品中,其相关理论也得到了较为充足和深入的研究。然而由于蒸压加气混凝土砌块在产业化生产过程中,一般采用钢丝对初凝后的加气混凝土进行切割成型,掺入过多的纤维会对加气混凝土的切割有所影响,使得纤维在蒸压加气混凝土中应用效果不是特别显著,阻碍了其在蒸压加气混凝土砌块中应用范围,也严重影响了蒸压加气混凝土砌块的产品质量和性能。
发明内容
本发明的目的就是提供一种抗弯折防渗蒸压加气混凝土砌块及其制作方法,以克服现有技术的不足。
本发明的目的是这样实现的:
一种抗弯折防渗蒸压加气混凝土砌块,其特征在于,由下列重量份的原料制成:偏高岭土40-42、生石灰16-18、废砂浆34-36、水泥5-7、铝粉膏0.08-0.12、四硼酸钠0.3-0.5、液体石蜡4-6、乙酸酐55-58、纳米二氧化钛2-4、藕粉6-8、罗布麻纤维3-5、剑麻短纤维5-6、腈纶纤维6-8、乙烯基三乙氧基硅烷3-4、适量水。
所述的一种抗弯折防渗蒸压加气混凝土砌块的制备方法,其特征在于包括以下步骤:
(1)将剑麻短纤维、罗布麻纤维放入烘箱中于105℃干燥1-2小时,同时用汽蒸预处理20-40分钟放入反应罐中,加入乙酸酐、纳米二氧化钛搅拌混匀静置3-5小时,然后加热至100-140℃反应2-3小时,用清水漂洗至中性烘干,喷洒雾状液体石蜡干燥;
(2)将生石灰、废砂浆、偏高岭土用5-8%盐酸溶液浸泡3-4小时,洗涤至中性,于650-770℃下煅烧4-5小时,冷却至120-130℃加入乙烯基三乙氧基硅烷研磨30-50分钟;
(3)将步骤(2)物料投入搅拌机中,加水搅拌成浆,加入步骤(1)物料、腈纶纤维搅拌2min,加入水泥搅拌1min,再加入铝粉膏及其他剩余成分搅拌30s制得浆料,水料比为0.53;
(4)将步骤(3)制得的浆料入模,静置发气初养2-4小时,切除超出模具部分,脱模放入反应釜内,控制温度150-170℃进行高温蒸养8-12小时,出料。
本发明有以下有益效果:本发明通过对剑麻短纤维、罗布麻纤维进行乙酰化反应封闭了纤维素中游离的羟基,提高了材料的疏水性能和热稳定性,再配合物理改性方法添加其他有效成分,改善了纤维在蒸压加气混凝土中耐久性和分散性,添加的纳米二氧化钛增加了砌块的抗菌性,添加的液体石蜡提高了砌块的防潮性能,添加的废砂浆解决了环境污染的问题,降低了生产成本,并且实现节能环保、变废为宝的主题,本发明加气砌块具有抗弯折、防渗耐水性、使用寿命长的优点。
具体实施方式
所述的一种抗弯折防渗蒸压加气混凝土砌块,其特征在于,由下列重量份的原料制成:偏高岭土41、生石灰16、废砂浆34、水泥5、铝粉膏0.09、四硼酸钠0.3、液体石蜡4、乙酸酐57、纳米二氧化钛2、藕粉8、罗布麻纤维3、剑麻短纤维5、腈纶纤维6、乙烯基三乙氧基硅烷3、适量水。
制作方法包括以下步骤:
(1)将剑麻短纤维、罗布麻纤维放入烘箱中于105℃干燥1-2小时,同时用汽蒸预处理20-40分钟放入反应罐中,加入乙酸酐、纳米二氧化钛搅拌混匀静置3-5小时,然后加热至100-140℃反应2-3小时,用清水漂洗至中性烘干,喷洒雾状液体石蜡干燥;
(2)将生石灰、废砂浆、偏高岭土用5-8%盐酸溶液浸泡3-4小时,洗涤至中性,于650-770℃下煅烧4-5小时,冷却至120-130℃加入乙烯基三乙氧基硅烷研磨30-50分钟;
(3)将步骤(2)物料投入搅拌机中,加水搅拌成浆,加入步骤(1)物料、腈纶纤维搅拌2min,加入水泥搅拌1min,再加入铝粉膏及其他剩余成分搅拌30s制得浆料,水料比为0.53;
(4)将步骤(3)制得的浆料入模,静置发气初养2-4小时,切除超出模具部分,脱模放入反应釜内,控制温度150-170℃进行高温蒸养8-12小时,出料。
本发明制得的蒸压加气混凝土砌块的技术指标如下:
(1)平均容重为560kg/m3;
(2)导热系数(W/m·k):0.092,有良好的保温隔热性能;
(3)抗压强度:7.3MPa;
(4)劈裂抗拉强度提高17.3%。
Claims (2)
1.一种抗弯折防渗蒸压加气混凝土砌块,其特征在于,由下列重量份的原料制成:偏高岭土40-42、生石灰16-18、废砂浆34-36、水泥5-7、铝粉膏0.08-0.12、四硼酸钠0.3-0.5、液体石蜡4-6、乙酸酐55-58、纳米二氧化钛2-4、藕粉6-8、罗布麻纤维3-5、剑麻短纤维5-6、腈纶纤维6-8、乙烯基三乙氧基硅烷3-4、适量水。
2.根据权利要求1所述的一种抗弯折防渗蒸压加气混凝土砌块的制作方法,其特征在于包括以下步骤:
(1)将剑麻短纤维、罗布麻纤维放入烘箱中于105℃干燥1-2小时,同时用汽蒸预处理20-40分钟放入反应罐中,加入乙酸酐、纳米二氧化钛搅拌混匀静置3-5小时,然后加热至100-140℃反应2-3小时,用清水漂洗至中性烘干,喷洒雾状液体石蜡干燥;
(2)将生石灰、废砂浆、偏高岭土用5-8%盐酸溶液浸泡3-4小时,洗涤至中性,于650-770℃下煅烧4-5小时,冷却至120-130℃加入乙烯基三乙氧基硅烷研磨30-50分钟;
(3)将步骤(2)物料投入搅拌机中,加水搅拌成浆,加入步骤(1)物料、腈纶纤维搅拌2min,加入水泥搅拌1min,再加入铝粉膏及其他剩余成分搅拌30s制得浆料,水料比为0.53;
(4)将步骤(3)制得的浆料入模,静置发气初养2-4小时,切除超出模具部分,脱模放入反应釜内,控制温度150-170℃进行高温蒸养8-12小时,出料。