CN105363990A - 一种长杆类整体式传动轴锻造工艺 - Google Patents

一种长杆类整体式传动轴锻造工艺 Download PDF

Info

Publication number
CN105363990A
CN105363990A CN201510839906.7A CN201510839906A CN105363990A CN 105363990 A CN105363990 A CN 105363990A CN 201510839906 A CN201510839906 A CN 201510839906A CN 105363990 A CN105363990 A CN 105363990A
Authority
CN
China
Prior art keywords
blank
forging
transmission shaft
bending
length
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510839906.7A
Other languages
English (en)
Other versions
CN105363990B (zh
Inventor
葛玉林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kunshan Huizhong Machine Co Ltd
Original Assignee
Kunshan Huizhong Machine Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan Huizhong Machine Co Ltd filed Critical Kunshan Huizhong Machine Co Ltd
Priority to CN201510839906.7A priority Critical patent/CN105363990B/zh
Publication of CN105363990A publication Critical patent/CN105363990A/zh
Application granted granted Critical
Publication of CN105363990B publication Critical patent/CN105363990B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种长杆类整体式传动轴锻造工艺，包括如下步骤：（1）坯料选取，选择直径为21mm，长度为225mm的长棒型坯料；（2）坯料加热，对95mm长度部分的坯料进行感应加热至800℃-900℃；（3）双向折弯，对坯料加热部分进行双向折弯，对坯料40mm及65mm处折弯，折弯方向相反，折弯后形状为扭曲S状；（4）精锻，将折弯后的坯料放入精锻型腔中，对加热头部进行成型，锻造零件精确外形；（5）切边，将精锻后的锻件放入切边模具中，利用零件与下模具剪切作用使锻件与飞边分离；（6）冷却，将锻造后的锻件放入保温箱中，缓慢冷却至室温；（7）热处理，将锻件加热至677-732℃保温，后随炉冷却。采用加热、弯曲、锻造、切边的工艺流程，保证了产品的精确性，提高了产品性能。

Description

一种长杆类整体式传动轴锻造工艺
技术领域
本发明涉及了一种长杆类整体式传动轴锻造工艺，属于锻造加工技术领域。
背景技术
长杆类一体式轴类齿头零件的形状为一端长杆状，另一端为较短粗的圆柱凸台，两圆心不同轴，中间以扁平状长方台连接。作为重型卡车的传动部件，此类零件工作环境为重载强磨损，因此对于零件的性能要求非常高。零件一般采用硬度很高的不锈钢，因此，现有的锻造工艺在材料锻造时流动性较差，锻造温度范围小，容易产生折叠、开裂等缺陷，锻造难度大。
发明内容
本发明所要解决的技术问题是提供一种长杆类整体式传动轴锻造工艺，采用加热、弯曲、锻造、切边的工艺流程，保证了产品的精确性，提高了产品性能。
为了解决上述技术问题，本发明所采用的技术方案是：
一种长杆类整体式传动轴锻造工艺，包括如下步骤：
（1）坯料选取，选择直径为21mm，长度为225mm的长棒型坯料；
（2）坯料加热，对95mm长度部分的坯料进行感应加热至800℃-900℃；
（3）双向折弯，对坯料加热部分进行双向折弯，对坯料40mm及65mm处折弯，折弯方向相反，折弯后形状为扭曲S状；
（4）精锻，将折弯后的坯料放入精锻型腔中，对加热头部进行成型，锻造零件精确外形；
（5）切边，将精锻后的锻件放入切边模具中，利用零件与下模具剪切作用使锻件与飞边分离；
（6）冷却，将锻造后的锻件放入保温箱中，缓慢冷却至室温；
（7）热处理，将锻件加热至677-732℃保温，后随炉冷却。
前述的一种长杆类整体式传动轴锻造工艺，其特征在于：所述步骤（3）中双向折弯的温度在650℃-750℃之间。
前述的一种长杆类整体式传动轴锻造工艺，其特征在于：所述步骤（5）中的精锻温度在550℃-650℃之间。
前述的一种长杆类整体式传动轴锻造工艺，其特征在于：所述坯料为高碳马氏体不锈钢。
本发明的有益效果是：本工艺设计采用加热、弯曲、锻造、切边的工艺流程，解决了在锻造时流动性较差，锻造温度范围小，容易产生折叠、开裂等缺陷，保证了产品的精确性，提高了产品性能。
具体实施方式
下面将结合具体实施方式，对本发明做进一步的说明。
一种长杆类整体式传动轴锻造工艺，其特征在于：包括如下步骤：
（1）坯料选取，选择直径为21mm，长度为225mm的长棒型坯料；
（2）坯料加热，对95mm长度部分的坯料进行感应加热至800℃-900℃；
（3）双向折弯，对坯料加热部分进行双向折弯，对坯料40mm及65mm处折弯，折弯方向相反，折弯后形状为扭曲S状；
（4）精锻，将折弯后的坯料放入精锻型腔中，对加热头部进行成型，锻造零件精确外形；
（5）切边，将精锻后的锻件放入切边模具中，利用零件与下模具剪切作用使锻件与飞边分离；
（6）冷却，将锻造后的锻件放入保温箱中，缓慢冷却至室温；
（7）热处理，将锻件加热至677-732℃保温，后随炉冷却。
本工艺设计采用加热、弯曲、锻造、切边的工艺流程，解决了在锻造时流动性较差，锻造温度范围小，容易产生折叠、开裂等缺陷，保证了产品的精确性，提高了产品性能。
经过反复试验，所述步骤（3）中双向折弯的温度在650℃-750℃之间，所述步骤（5）中的精锻温度在550℃-650℃之间时，产品的性能最佳。
本实施例中，坯料为高碳马氏体不锈钢，其硬度能够满足折弯、锻造时的流动性要求，且最后成型的零件性能也能符合要求。
综上所述，本发明提供的一种长杆类整体式传动轴锻造工艺，采用加热、弯曲、锻造、切边的工艺流程，保证了产品的精确性，提高了产品性能。
以上显示和描述了本发明的基本原理、主要特征及优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界。

Claims (4)

1.一种长杆类整体式传动轴锻造工艺，其特征在于：包括如下步骤：
（1）坯料选取，选择直径为21mm，长度为225mm的长棒型坯料；
（2）坯料加热，对95mm长度部分的坯料进行感应加热至800℃-900℃；
（3）双向折弯，对坯料加热部分进行双向折弯，对坯料40mm及65mm处折弯，折弯方向相反，折弯后形状为扭曲S状；
（4）精锻，将折弯后的坯料放入精锻型腔中，对加热头部进行成型，锻造零件精确外形；
（5）切边，将精锻后的锻件放入切边模具中，利用零件与下模具剪切作用使锻件与飞边分离；
（6）冷却，将锻造后的锻件放入保温箱中，缓慢冷却至室温；
（7）热处理，将锻件加热至677-732℃保温，后随炉冷却。
2.根据权利要求1所述的一种长杆类整体式传动轴锻造工艺，其特征在于：所述步骤（3）中双向折弯的温度在650℃-750℃之间。
3.根据权利要求1所述的一种长杆类整体式传动轴锻造工艺，其特征在于：所述步骤（5）中的精锻温度在550℃-650℃之间。
4.根据权利要求1所述的一种长杆类整体式传动轴锻造工艺，其特征在于：所述坯料为高碳马氏体不锈钢。
CN201510839906.7A 2015-11-27 2015-11-27 一种长杆类整体式传动轴锻造工艺 Active CN105363990B (zh)