CN105964853B - GCr15轴承套圈的自由锻工艺 - Google Patents

GCr15轴承套圈的自由锻工艺 Download PDF

Info

Publication number
CN105964853B
CN105964853B CN201610454948.3A CN201610454948A CN105964853B CN 105964853 B CN105964853 B CN 105964853B CN 201610454948 A CN201610454948 A CN 201610454948A CN 105964853 B CN105964853 B CN 105964853B
Authority
CN
China
Prior art keywords
forging
steel
temperature
gcr15
plug
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610454948.3A
Other languages
English (en)
Other versions
CN105964853A (zh
Inventor
吕美莲
刘春超
冯宝倪
吕俊
吕诚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Auspicious Outstanding Co Ltd Of Forging Of Anhui Province
Original Assignee
Auspicious Outstanding Co Ltd Of Forging Of Anhui Province
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Auspicious Outstanding Co Ltd Of Forging Of Anhui Province filed Critical Auspicious Outstanding Co Ltd Of Forging Of Anhui Province
Priority to CN201610454948.3A priority Critical patent/CN105964853B/zh
Publication of CN105964853A publication Critical patent/CN105964853A/zh
Application granted granted Critical
Publication of CN105964853B publication Critical patent/CN105964853B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了GCr15轴承套圈的自由锻工艺,它包括以下步骤:GCr15钢的化学成分为C为0.95‑1.05,Si为0.15‑0.35,Mn为0.25‑045,S为≤0.025,P为≤0.025,Cr为1.40‑1.65,Mo为≤0.10,Ni为≤0.30,Cu为≤0.25,Ni+Cu为≤0.50;相比以前这类锻件只能生产锻圆相比,大大降低了原材料消耗,从而降低了生产成本。

Description

GGr 15轴承套圈的自由锻工艺
技术领域
[0001] 本发明涉及冶金锻造工艺,具体涉及GCrl5轴承套圈的自由锻工艺。
背景技术
[0002] 自由锻造是利用冲击力或压力使金属在上下砧面间各个方向自由变形,不受任何 限制而获得所需形状及尺寸和一定机械性能的锻件的一种加工方法,由于自由锻造所用工 具和设备简单,通用性好,成本低。同铸造毛坯相比,自由锻消除了缩孔、缩松、气孔等缺陷, 使毛坯具有更高的力学性能。锻件形状简单,操作灵活。因此,它在重型机器及重要零件的 制造上有特别重要的意义。
[0003] 在锻造行业推动下,各种重型机械设备高速发展,但重型设备关键部位零件,技术 指标要求高,生产技术难度大,例如电机轴、船舶用曲轴、及各类大型套筒类锻件,这类零件 受力繁重、复杂、工作环境特殊,要求具有较高的组织性能,因此锻造技术水平提高迫在眉 睫,
发明内容
[0004] 为解决背景技术中所述技术问题,本发明采用以下技术方案:GCrl5轴承套圈的自 由锻工艺,它包括以下步骤:
[0005] 1) GCrl5钢的化学成分为C为0.95-1.05,Si为0.15-0.35,Mn为0.25-045,S为彡 0_025,卩为<0.025,0为1_4()-1_65,]\1〇为彡0_10,附为彡0_30,(:11为彡0.25,附+〇1为彡 0.50;
[0006] 2)将GCrl5钢放入熔炉,始锻温度应控制在钢熔点以下100-200°C,GCrl5钢在 1000-130(TC就开始出现液相相变,另外此钢y体相区较低碳钢相区狭窄,850-900°C左右 开始向奥氏体转变制成芯棒;
[0007] 3)冲孔大小要与芯棒尺寸相吻合,芯棒预热25〇-35〇°C并涂抹润滑剂,严格执行轻 重轻的锻造操作规程,在料温高时,按一压一送走六方重压拔长,带料温下降到1〇〇〇-C以下 时,钢的塑形急剧下降,要按一压一翻走六方拔长,避免冷裂产生;
[OOOS] 4)锻后空冷550°c,热装炉退火,770-790°C保温后随炉缓冷到550°C以下出炉空 冷,消除了锻造后的残余内应力,得到细小的粒状珠光体组织,为最终热处理做好组织准 备。
[0009]优选地,步骤2)适当扩大锻造温度区间,始锻熔点温度定为ll5〇°C,终锻温度定为 850 °C。
[0010]本发明的有益效果是:相比以前这类锻件只能生产锻圆相比,大大降低了原材料 消耗,从而降低了生产成本。
[0011] 说明书附图
[0012]图1为本发明中的锻造中一压一送操作示意图;
[0013]图2为本发明中的锻造中一压一翻操作示意图。
具体实施方式
[0014] 实施例一
[0015] 1) GCrl5钢的化学成分为C为0 • 95,Si为0 • 15,Mn为0 • 25,S为0 • 025,P为0 • 025,Cr为 1•40,Mo为0•10,Ni为0•30,Cu为0•2,Ni+Cu为0•50;
[0016] 2)将GCrl5钢放入熔炉,始锻温度应控制在钢熔点以下100°C,GCrl5钢始锻熔点温 度在1000°C就开始出现液相相变,Y体相区较低碳钢相区狭窄,850°C左右开始向奥氏体转 变制成芯棒;
[0017] 3)冲孔大小要与芯棒尺寸相吻合,芯棒预热250°C并涂抹润滑剂,严格执行轻重轻 的锻造操作规程,在料温高时,按一压一送走六方重压拔长,带料温下降到1000°C以下时, 钢的塑形急剧下降,要按一压一翻走六方拔长,避免冷裂产生;
[0018] 4)锻后空冷550°C,热装炉退火,77(TC保温后随炉缓冷到550°C以下出炉空冷,消 除了锻造后的残余内应力,得到细小的粒状珠光体组织,为最终热处理做好组织准备。
[0019] 实施例二
[0020] 1)6以15钢的化学成分为(:为1.05,3:1为0.35,1^为045,3为0.02,?为0.02,(:1'为 1•65,Mo为0•5,Ni为0•20,Cu为0•2,Ni+Cu为0•40;
[0021] 2)将GCrl5钢放入熔炉,始锻温度应控制在钢熔点以下20CTC,GCrl5钢始锻熔点温 度在1300°C就开始出现液相相变,Y体相区较低碳钢相区狭窄,90CTC左右开始向奥氏体转 变制成芯棒;
[0022] 3)冲孔大小要与芯棒尺寸相吻合,芯棒预热35(TC并涂抹润滑剂,严格执行轻重轻 的锻造操作规程,在料温高时,按一压一送走六方重压拔长,带料温下降到1000 °c以下时, 钢的塑形急剧下降,要按一压一翻走六方拔长,避免冷裂产生;
[0023] 4)锻后空冷550°C,热装炉退火,790°C保温后随炉缓冷到550°C以下出炉空冷,消 除了锻造后的残余内应力,得到细小的粒状珠光体组织,为最终热处理做好组织准备。
[0024] 实施例三
[0025] 1)6(^15钢的化学成分为(:为1.0,31为0.2,1«11为0.35,3为0.015,?为0.02,(^为 1•5,Mo为0•05,Ni为0•25,Cu为0•25,Ni+Cu为0•50;
[0026] 2)将GCrl5钢放入熔炉,始锻温度应控制在钢熔点以下150°C,GCrl5钢始锻熔点温 度在1200°C就开始出现液相相变,y体相区较低碳钢相区狭窄,880°C左右开始向奥氏体转 变制成芯棒;
[0027] 3)冲孔大小要与芯棒尺寸相吻合,芯棒预热300°C并涂抹润滑剂,严格执行轻重轻 的锻造操作规程,在料温高时,按一压一送走六方重压拔长,带料温下降到1000°C以下时, 钢的塑形急剧下降,要按一压一翻走六方拔长,避免冷裂产生;
[0028] 4)锻后空冷550°C,热装炉退火,78(TC保温后随炉缓冷到55(TC以下出炉空冷,消 除了锻造后的残余内应力,得到细小的粒状珠光体组织,为最终热处理做好组织准备。

Claims (2)

  1. l.GCrl5轴承套圈的自由锻工艺,其特征在于,它包括以下步骤: 1) GCrl5钢的化学成分为C为0 • 95-1 • 05,Si为0.15-0 • 35,Mn为0 • 25-045,S为彡0 • 025, P 为彡 0_025,Cr 为 1.40-1_65,1«〇为彡0.10,附为彡0_30,(:11为彡〇.25,祖+〇1为彡0_50; 2) 将GCrl5钢放入熔炉,始锻温度应控制在钢熔点以下100-2〇〇°C,GCrl5钢在1000-1300 °C就开始出现液相相变,另外此钢Y体相区较低碳钢相区狭窄,850-900 °C时开始向奥 氏体转变制成芯棒; 3) 冲孔大小要与芯棒尺寸相吻合,芯棒预热250-350°C并涂抹润滑剂,严格执行轻重轻 的锻造操作规程,在料温高时,按一压一送走六方重压拔长,待料温下降到1000T:以下时, 钢的塑形急剧下降,要按一压一翻走六方拔长,避免冷裂产生; 4) 锻后空冷550°C,热装炉退火,770-79(TC保温后随炉缓冷到550°C以下出炉空冷,消 除了锻造后的残余内应力,得到细小的粒状珠光体组织,为最终热处理做好组织准备。
  2. 2.根据权利要求1所述的GCrl5轴承套圈的自由锻工艺,其特征在于,步骤2)适当扩大 锻造温度区间,始锻熔点温度定为1150°C,终锻温度定为85(TC。
CN201610454948.3A 2016-06-20 2016-06-20 GCr15轴承套圈的自由锻工艺 Active CN105964853B (zh)