CN105344925A - 精密铸造的管道用脱模剂 - Google Patents
精密铸造的管道用脱模剂 Download PDFInfo
- Publication number
- CN105344925A CN105344925A CN201510698805.2A CN201510698805A CN105344925A CN 105344925 A CN105344925 A CN 105344925A CN 201510698805 A CN201510698805 A CN 201510698805A CN 105344925 A CN105344925 A CN 105344925A
- Authority
- CN
- China
- Prior art keywords
- parts
- releasing agent
- nano
- polystyrene
- mold releasing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种精密铸造的管道用脱模剂，包括以下物质按质量份数组成：硅油15-35份、蓖麻油22-45份、丙三醇9-21份、油酸乙酯4-12份、丙烯酸乳液5-13份、聚苯乙烯4-9份、三聚磷酸钠3-11份、液体石蜡12-23份、胶体石墨7-12份、纳米膨润土6-12份、沸石粉4-16份、壬基酚聚氧乙烯醚2-6份、二硫化钨1-7份、纳米二氧化钛4-8份和平衡水54-86份。通过上述方式，本发明精密铸造的管道用脱模剂，能够提高脱模效果，延长使用寿命，生产成本低，安全可靠。
Description
技术领域
本发明涉及精密铸造领域，特别是涉及一种精密铸造的管道用脱模剂。
背景技术
铸造是将金属熔炼成符合一定要求的液体并放进铸型里，经冷却凝固、清理处理后得到有预定形状，尺寸和性能的铸件的工艺过程。铸造毛坯因近乎成形，而达到免机械加工活少量加工的目的降低了成本并在一定程度上减少了制作时间。铸造是现代装置制造工业的基础工艺之一，然而铸造脱模时铸造工艺中比较重要的一步，直接关系到铸造的质量，脱模剂是一种用在两个彼此易于粘着的物体表面的一个界面涂层，它可使物体表面易于脱离、光滑及洁净。因此，脱模剂直接关系到铸造质量的好坏。
发明内容
本发明主要解决的技术问题是提供一种精密铸造的管道用脱模剂，能够提高脱模效果，延长使用寿命，生产成本低，安全可靠。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种精密铸造的管道用脱模剂，包括以下物质按质量份数组成：硅油15-35份、蓖麻油22-45份、丙三醇9-21份、油酸乙酯4-12份、丙烯酸乳液5-13份、聚苯乙烯4-9份、三聚磷酸钠3-11份、液体石蜡12-23份、胶体石墨7-12份、纳米膨润土6-12份、沸石粉4-16份、壬基酚聚氧乙烯醚2-6份、二硫化钨1-7份、纳米二氧化钛4-8份和平衡水54-86份。
在本发明一个较佳实施例中，包括以下物质按质量份数组成：硅油15份、蓖麻油22份、丙三醇9份、油酸乙酯4份、丙烯酸乳液5份、聚苯乙烯4份、三聚磷酸钠3份、液体石蜡12份、胶体石墨7份、纳米膨润土6份、沸石粉4份、壬基酚聚氧乙烯醚2份、二硫化钨1份、纳米二氧化钛4份和平衡水54份。
在本发明一个较佳实施例中，包括以下物质按质量份数组成：硅油20份、蓖麻油33份、丙三醇12份、油酸乙酯7份、丙烯酸乳液10份、聚苯乙烯6份、三聚磷酸钠8份、液体石蜡16份、胶体石墨11份、纳米膨润土7份、沸石粉10份、壬基酚聚氧乙烯醚4份、二硫化钨5份、纳米二氧化钛5份和平衡水77份。
在本发明一个较佳实施例中，包括以下物质按质量份数组成：硅油35份、蓖麻油45份、丙三醇21份、油酸乙酯12份、丙烯酸乳液13份、聚苯乙烯9份、三聚磷酸钠11份、液体石蜡23份、胶体石墨12份、纳米膨润土12份、沸石粉16份、壬基酚聚氧乙烯醚6份、二硫化钨7份、纳米二氧化钛8份和平衡水86份。
本发明的有益效果是：本发明精密铸造的管道用脱模剂，能够提高脱模效果，延长使用寿命，生产成本低，安全可靠。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例1，一种精密铸造的管道用脱模剂，包括以下物质按质量份数组成：硅油15份、蓖麻油22份、丙三醇9份、油酸乙酯4份、丙烯酸乳液5份、聚苯乙烯4份、三聚磷酸钠3份、液体石蜡12份、胶体石墨7份、纳米膨润土6份、沸石粉4份、壬基酚聚氧乙烯醚2份、二硫化钨1份、纳米二氧化钛4份和平衡水54份。
实施例2，一种精密铸造的管道用脱模剂，包括以下物质按质量份数组成：硅油20份、蓖麻油33份、丙三醇12份、油酸乙酯7份、丙烯酸乳液10份、聚苯乙烯6份、三聚磷酸钠8份、液体石蜡16份、胶体石墨11份、纳米膨润土7份、沸石粉10份、壬基酚聚氧乙烯醚4份、二硫化钨5份、纳米二氧化钛5份和平衡水77份。
实施例3，一种精密铸造的管道用脱模剂，包括以下物质按质量份数组成：硅油35份、蓖麻油45份、丙三醇21份、油酸乙酯12份、丙烯酸乳液13份、聚苯乙烯9份、三聚磷酸钠11份、液体石蜡23份、胶体石墨12份、纳米膨润土12份、沸石粉16份、壬基酚聚氧乙烯醚6份、二硫化钨7份、纳米二氧化钛8份和平衡水86份。
区别于现有技术，本发明精密铸造的管道用脱模剂，能够提高脱模效果，延长使用寿命，生产成本低，安全可靠。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (4)
1.一种精密铸造的管道用脱模剂，其特征在于，包括以下物质按质量份数组成：硅油15-35份、蓖麻油22-45份、丙三醇9-21份、油酸乙酯4-12份、丙烯酸乳液5-13份、聚苯乙烯4-9份、三聚磷酸钠3-11份、液体石蜡12-23份、胶体石墨7-12份、纳米膨润土6-12份、沸石粉4-16份、壬基酚聚氧乙烯醚2-6份、二硫化钨1-7份、纳米二氧化钛4-8份和平衡水54-86份。
2.根据权利要求1所述的精密铸造的管道用脱模剂，其特征在于，包括以下物质按质量份数组成：硅油15份、蓖麻油22份、丙三醇9份、油酸乙酯4份、丙烯酸乳液5份、聚苯乙烯4份、三聚磷酸钠3份、液体石蜡12份、胶体石墨7份、纳米膨润土6份、沸石粉4份、壬基酚聚氧乙烯醚2份、二硫化钨1份、纳米二氧化钛4份和平衡水54份。
3.根据权利要求1所述的精密铸造的管道用脱模剂，其特征在于，包括以下物质按质量份数组成：硅油20份、蓖麻油33份、丙三醇12份、油酸乙酯7份、丙烯酸乳液10份、聚苯乙烯6份、三聚磷酸钠8份、液体石蜡16份、胶体石墨11份、纳米膨润土7份、沸石粉10份、壬基酚聚氧乙烯醚4份、二硫化钨5份、纳米二氧化钛5份和平衡水77份。
4.根据权利要求1所述的精密铸造的管道用脱模剂，其特征在于，包括以下物质按质量份数组成：硅油35份、蓖麻油45份、丙三醇21份、油酸乙酯12份、丙烯酸乳液13份、聚苯乙烯9份、三聚磷酸钠11份、液体石蜡23份、胶体石墨12份、纳米膨润土12份、沸石粉16份、壬基酚聚氧乙烯醚6份、二硫化钨7份、纳米二氧化钛8份和平衡水86份。