CN105330165A - 一种用于加工防眩玻璃的蚀刻液及其制备方法 - Google Patents
一种用于加工防眩玻璃的蚀刻液及其制备方法 Download PDFInfo
- Publication number
- CN105330165A CN105330165A CN201510679445.1A CN201510679445A CN105330165A CN 105330165 A CN105330165 A CN 105330165A CN 201510679445 A CN201510679445 A CN 201510679445A CN 105330165 A CN105330165 A CN 105330165A
- Authority
- CN
- China
- Prior art keywords
- etching solution
- acid
- control temperature
- parts
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于加工防眩玻璃的蚀刻液及其制备方法,该蚀刻液包括以下组分氟化氢、氟化铵、硫酸、硝酸、硫酸钾、硝酸铵、硫酸铜、酸雾抑制剂、烷基酚聚氧乙烯醚、烷基苯磺酸钠、烷基磺酸钠、乙二醇、去离子水。将氟化氢、氟化铵、硫酸、硝酸、硫酸钾、硝酸铵、硫酸铜、烷基酚聚氧乙烯醚、烷基苯磺酸钠、烷基磺酸钠、乙二醇、去离子水加入至搅拌釜中,调节搅拌釜转速至2400转/分钟,控制温度在5-15℃,搅拌10-15min后,加入酸雾抑制剂并缓慢降低搅拌釜的转速至800转/分钟,控制温度在5-10℃,搅拌30-40min后,即制得本发明的蚀刻液。本发明的蚀刻液不仅制造成本低,且其制造过程中很少产生酸雾,对空气污染少,对环境友好。
Description
技术领域
本发明涉及玻璃制造领域,特别涉及一种用于加工防眩玻璃的蚀刻液及其制备方法。
背景技术
目前,防眩玻璃的应用十分的广泛,不仅可以应用于手机、平板电脑、超级本等电子设备,而且还广泛的应用于汽车挡风玻璃、后视镜等汽车玻璃之中。而电子设备和汽车是我国正在大力发展的两大支柱产业,所以对防眩玻璃的研究是相当有必要的。
现有技术中,已经出现了酸蚀防眩玻璃的加工工艺,该工艺的关键点在于其中的蚀刻液的制备,但现有技术中的蚀刻液的制备有以下两个缺点。其一,现有技术中会使用较为昂贵的原材料制备,如会采用硝酸银、阿拉伯树胶粉(专利公开号为CN101215097的专利中有所记载)。其二,在制备蚀刻液的过程之中,会产生大量的酸性气体,不仅会对生产的设备产生腐蚀,且会对环境造成很大的污染。
发明内容
本发明的目的,就是为了解决上述问题而提供了一种制造原材料价格低、制造成本低,且生产过程中产生的酸性气体少的于加工防眩玻璃的蚀刻液。
本发明的另一个目的还在于提供了一种上述蚀刻液的制备方法。
为实现上述目的,本发明的技术方案实施如下:
一种用于加工防眩玻璃的蚀刻液,该蚀刻液包括以下组分及其重量份:
上述的一种用于加工防眩玻璃的蚀刻液,其中,所述酸雾抑制剂包括以下组分及其重量份:
本发明还提供了一种用于加工防眩玻璃的蚀刻液的制备方法,包括以下步骤:
步骤1:按照以下组分及其重量份准备制备酸雾抑制剂的原材料:
步骤2:将油酸和异丙醇加入至搅拌机中,控制温度在35-45℃,搅拌30min后,在搅拌机中加入咪唑啉季铵盐和一半重量份的异构醇聚氧乙烯醚,控制温度在45-55℃,搅拌30min后,将剩余原材料加入搅拌机,控制温度在35-45℃,再搅拌30min,冷却至室温即制得所述酸雾抑制剂。
步骤3:按照以下组分及其重量份准备制备蚀刻液的原材料:
步骤4:将氟化氢、氟化铵、硫酸、硝酸、硫酸钾、硝酸铵、硫酸铜、烷基酚聚氧乙烯醚、烷基苯磺酸钠、烷基磺酸钠、乙二醇、去离子水加入至搅拌釜中,调节搅拌釜转速至2400转/分钟,控制温度在5-15℃,搅拌10-15min后,加入酸雾抑制剂并缓慢降低搅拌釜的转速至800转/分钟,控制温度在5-10℃,搅拌30-40min后,即制得本发明的蚀刻液。
本发明的有益效果如下:
本发明与现有技术相比,采用了硫酸钾、硝酸铵等金属盐类替代了硝酸银作为制备本发明蚀刻液的催化剂,这种替代降低了制备本发明蚀刻液原材料的价格,从而降低了制备本发明的成本。同时,为了解决现有技术之中,生产蚀刻液过程中会产生大量酸雾的情况,本发明中加入了特制的酸雾抑制剂,并且控制反应在较低的温度下进行,在保证反应充分完成的前提之下,将生产本发明的蚀刻液时产生的酸雾降低到最少。
具体实施方式
下面将结合实施例,对本发明作进一步说明。
实施例1
一种用于加工防眩玻璃的蚀刻液的制备方法,包括以下步骤:
步骤1:按照以下组分及其重量份准备制备酸雾抑制剂的原材料:咪唑啉季铵盐12份、油酸4份、异丙醇6份、异构醇聚氧乙烯醚14份和去离子水35份。
步骤2:将4份油酸和6份异丙醇加入至搅拌机中,控制温度在35℃,搅拌30min后,在搅拌机中加入12份咪唑啉季铵盐和7份异构醇聚氧乙烯醚,控制温度在45℃,搅拌30min后,将7份异构醇聚氧乙烯醚和35份去离子水加入搅拌机,控制温度在45℃,再搅拌30min,冷却至室温即制得酸雾抑制剂。
步骤3:按照以下组分及其重量份准备制备蚀刻液的原材料:氟化氢12份、氟化铵6份、硫酸9份、硝酸15份、硫酸钾0.25份、硝酸铵0.1份、硫酸铜0.25份、酸雾抑制剂0.05份、烷基酚聚氧乙烯醚0.15份、烷基苯磺酸钠0.6份、烷基磺酸钠0.55份、乙二醇0.35份、去离子水42份。
步骤4:将12份氟化氢、6份氟化铵、9份硫酸、15份硝酸、0.25份硫酸钾、0.1份硝酸铵、0.25份硫酸铜、0.15份烷基酚聚氧乙烯醚、0.6份烷基苯磺酸钠、0.55份烷基磺酸钠、0.35份乙二醇、42份去离子水加入至搅拌釜中,调节搅拌釜转速至2400转/分钟,控制温度在10℃,搅拌10min后,加入0.05份酸雾抑制剂并缓慢降低搅拌釜的转速至800转/分钟,控制温度在5℃,搅拌35min后,即制得本发明的蚀刻液。
实施例2
一种用于加工防眩玻璃的蚀刻液的制备方法,包括以下步骤:
步骤1:按照以下组分及其重量份准备制备酸雾抑制剂的原材料:咪唑啉季铵盐15份、油酸5份、异丙醇8份、异构醇聚氧乙烯醚12份;去离子水33份。
步骤2:将5份油酸和8份异丙醇加入至搅拌机中,控制温度在40℃,搅拌30min后,在搅拌机中加入15份咪唑啉季铵盐和6份异构醇聚氧乙烯醚,控制温度在50℃,搅拌30min后,将6份异构醇聚氧乙烯醚和33份去离子水加入搅拌机,控制温度在40℃,再搅拌30min,冷却至室温即制得所述酸雾抑制剂。
步骤3:按照以下组分及其重量份准备制备蚀刻液的原材料:
氟化氢13份、氟化铵9份、硫酸10份、硝酸15份、硫酸钾0.15份、硝酸铵0.22份、硫酸铜0.35份、酸雾抑制剂0.07份、烷基酚聚氧乙烯醚0.055份、烷基苯磺酸钠0.65份、烷基磺酸钠0.7份、乙二醇0.3份、去离子水55份。
步骤4:将13份氟化氢、9份氟化铵、10份硫酸、15份硝酸、0.15份硫酸钾、0.22份硝酸铵、0.35份硫酸铜、0.055份烷基酚聚氧乙烯醚、0.65份烷基苯磺酸钠、0.7份烷基磺酸钠、0.3份乙二醇、55份去离子水加入至搅拌釜中,调节搅拌釜转速至2400转/分钟,控制温度在5℃,搅拌12min后,加入0.07份酸雾抑制剂并缓慢降低搅拌釜的转速至800转/分钟,控制温度在5℃,搅拌40min后,即制得本发明的蚀刻液。
通过实施例1和实施例2所生产的蚀刻液具有很大的市场竞争力,原因有二:其一,目前我国正大力发展环保产业,原先污染严重的工艺必将被新的工艺所替代,本发明的蚀刻液生产过程中由于加入了酸雾抑制剂,所以产生的酸雾非常少,相比现有工艺对环境友好。其二,本发明中使用的原材料较现有技术中的原材料成本要低,故降低了生产成本,具有市场竞争力。
以上实施例仅供说明本发明之用,而非对本发明的限制,有关技术领域的技术人员,在不脱离本发明的精神和范围的情况下,还可以作出各种变换或变型,因此所有等同的技术方案也应该属于本发明的范畴,应由各权利要求所限定。
Claims (3)
1.一种用于加工防眩玻璃的蚀刻液,其特征在于,该蚀刻液包括以下组分及其重量份:
2.如权利要求1所述的一种用于加工防眩玻璃的蚀刻液,其特征在于,所述酸雾抑制剂包括以下组分及其重量份:
3.一种如权利要求1所述的用于加工防眩玻璃的蚀刻液的制备方法,其特征在于,包括以下步骤:
步骤1:按照以下组分及其重量份准备制备酸雾抑制剂的原材料:
步骤2:将油酸和异丙醇加入至搅拌机中,控制温度在35-45℃,搅拌30min后,在搅拌机中加入咪唑啉季铵盐和一半重量份的异构醇聚氧乙烯醚,控制温度在45-55℃,搅拌30min后,将剩余原材料加入搅拌机,控制温度在35-45℃,再搅拌30min,冷却至室温即制得所述酸雾抑制剂。
步骤3:按照以下组分及其重量份准备制备蚀刻液的原材料:
步骤4:将氟化氢、氟化铵、硫酸、硝酸、硫酸钾、硝酸铵、硫酸铜、烷基酚聚氧乙烯醚、烷基苯磺酸钠、烷基磺酸钠、乙二醇、去离子水加入至搅拌釜中,调节搅拌釜转速至2400转/分钟,控制温度在5-15℃,搅拌10-15min后,加入酸雾抑制剂并缓慢降低搅拌釜的转速至800转/分钟,控制温度在5-10℃,搅拌30-40min后,即制得本发明的蚀刻液。