CN105314946A - Interior wall ceramic tile joint mixture - Google Patents
Interior wall ceramic tile joint mixture Download PDFInfo
- Publication number
- CN105314946A CN105314946A CN201510705049.1A CN201510705049A CN105314946A CN 105314946 A CN105314946 A CN 105314946A CN 201510705049 A CN201510705049 A CN 201510705049A CN 105314946 A CN105314946 A CN 105314946A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- powder
- water
- ceramic tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an interior wall ceramic tile joint mixture which comprises the following components in parts by mass: 50-150 parts of cement, 5-10 parts of shining powder, 5-10 parts of a fluorescent agent, 20-35 parts of quartz sand, 5-10 parts of a slow-release agent, 15-20 parts of latex powder, 10-20 parts of magnesium silicate, 20-30 parts of limestone powder, 5-10 parts of an antioxidant, 5-10 parts of a thickening water-retaining agent, 5-10 parts of an alkali efflorescence resistant agent, 5-10 parts of an anti-crack waterproof agent and 45-60 parts of water. After filling is finished, the joint mixture is relatively rapid to dry, relatively high in adhesiveness and low in falling-off possibility; the joint mixture has the characteristic of low alkalinity, so as to avoid damage to the human body; the shining powder and the fluorescent agent are added in the joint mixture, so that the aesthetic degree of gaps can be improved, and personal aesthetic requirements can be met.
Description
Technical field
The present invention relates to a kind of inner-wall ceramic tile spackling.
Background technology
Current at building industry high speed development, during tackiness agent is widely used in building brick material stickup on, the stickup of brick material needs to coordinate spackling.Because tackiness agent and spackling itself are containing water soluble alkali, salt etc., when rainy weather, when moisture infiltrates in material, these soluble ingredient can be dissolved in the water, infiltrate brick material pore and joint filling not crucial point, form water channel and ooze out surface, then contact with the CO2 in air, acid rain etc., generate undissolved white thing and the accumulation of salt in the surface soil.
It is attractive in appearance that the accumulation of salt in the surface soil can affect buildings, gives unsafe sensation; The accumulation of salt in the surface soil can affect and whitewash quality, delamination easily occurs and makes finishing failure; The accumulation of salt in the surface soil can cause structure crack, makes textural anomaly dilatation fissure; The common mould of the accumulation of salt in the surface soil has head mold, Mucor, aspergillus and mould etc., easily causes tetter and respiratory tract disease, even may bring out cancer.
Spackling of the prior art comparatively unsightly simultaneously, therefore cannot meet actual aesthetic needs.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of inner-wall ceramic tile spackling, the present invention is after full-filling completes, drying is comparatively rapid, wall attached is better simultaneously, difficult drop-off, and the present invention simultaneously has the special of low alkalinity, avoid causing damage to human body, add bright powder and fluorescent agent in the present invention simultaneously, the aesthetic measure in gap can be increased, meet individual aesthetic needs.
For solving the problem, the present invention adopts following technical scheme:
A kind of inner-wall ceramic tile spackling, comprises the component of following mass fraction:
Cement 50-150 part
Bright powder 5-10 part
Fluorescent agent 5-10 part
Quartz sand 20-35 part
Sustained release dosage 5-10 part
Latex powder 15-20 part
Magnesium Silicate q-agent 10-20 part
Limestone powder 20-30 part
Antioxidant 5-10 part
Thickening water-holding agent 5-10 part
Anti-accumulation of salt in the surface soil agent 5-10 part
Anti-crack water-proof agent 5-10 part
Water 45-60 part.
As preferred technical scheme, comprise the component of following mass fraction: cement 150 parts, 5 parts, bright powder, fluorescent agent 5 parts, quartz sand 20 parts, sustained release dosage 5 parts, latex powder 15 parts, Magnesium Silicate q-agent 10 parts, limestone powder 20 parts, antioxidant 5 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 45 parts, water.
As preferred technical scheme, comprise the component of following mass fraction: cement 50 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 10 parts, latex powder 20 parts, Magnesium Silicate q-agent 20 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 10 parts, anti-accumulation of salt in the surface soil agent 10 parts, anti-crack water-proof agent 10 parts, 60 parts, water.
As preferred technical scheme, comprise the component of following mass fraction: cement 50 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 5 parts, latex powder 15 parts, Magnesium Silicate q-agent 10 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 60 parts, water.
As preferred technical scheme, comprise the component of following mass fraction: cement 100 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 10 parts, latex powder 20 parts, Magnesium Silicate q-agent 20 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 60 parts, water.
As preferred technical scheme, the particle diameter of described bright powder is 300-500 order.
As preferred technical scheme, the particle diameter of described quartz sand is 400-600 order.
As preferred technical scheme, the particle diameter of described latex powder is 300-400 order.
As preferred technical scheme, the particle diameter of described limestone powder is 600-700 order.
As preferred technical scheme, described cement is silicate cement.
The invention has the beneficial effects as follows: the present invention is after full-filling completes, drying is comparatively rapid, wall attached is better simultaneously, difficult drop-off, the present invention simultaneously has the special of low alkalinity, avoids causing damage to human body, adds bright powder and fluorescent agent in the present invention simultaneously, the aesthetic measure in gap can be increased, meet individual aesthetic needs.
Embodiment
Below the preferred embodiments of the present invention are described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
A kind of inner-wall ceramic tile spackling, comprises the component of following mass fraction:
Cement 50-150 part
Bright powder 5-10 part
Fluorescent agent 5-10 part
Quartz sand 20-35 part
Sustained release dosage 5-10 part
Latex powder 15-20 part
Magnesium Silicate q-agent 10-20 part
Limestone powder 20-30 part
Antioxidant 5-10 part
Thickening water-holding agent 5-10 part
Anti-accumulation of salt in the surface soil agent 5-10 part
Anti-crack water-proof agent 5-10 part
Water 45-60 part.
Comprise the component of following mass fraction: cement 150 parts, 5 parts, bright powder, fluorescent agent 5 parts, quartz sand 20 parts, sustained release dosage 5 parts, latex powder 15 parts, Magnesium Silicate q-agent 10 parts, limestone powder 20 parts, antioxidant 5 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 45 parts, water.
Comprise the component of following mass fraction: cement 50 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 10 parts, latex powder 20 parts, Magnesium Silicate q-agent 20 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 10 parts, anti-accumulation of salt in the surface soil agent 10 parts, anti-crack water-proof agent 10 parts, 60 parts, water.
Comprise the component of following mass fraction: cement 50 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 5 parts, latex powder 15 parts, Magnesium Silicate q-agent 10 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 60 parts, water.
Comprise the component of following mass fraction: cement 100 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 10 parts, latex powder 20 parts, Magnesium Silicate q-agent 20 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 60 parts, water.
The particle diameter of described bright powder is 300-500 order.
The particle diameter of described quartz sand is 400-600 order.
The particle diameter of described latex powder is 300-400 order.
The particle diameter of described limestone powder is 600-700 order.
Described cement is silicate cement.
The invention has the beneficial effects as follows: the present invention is after full-filling completes, drying is comparatively rapid, wall attached is better simultaneously, difficult drop-off, the present invention simultaneously has the special of low alkalinity, avoids causing damage to human body, adds bright powder and fluorescent agent in the present invention simultaneously, the aesthetic measure in gap can be increased, meet individual aesthetic needs.
Embodiment 1
Choose the component of following mass fraction: cement 150 parts, 5 parts, bright powder, fluorescent agent 5 parts, quartz sand 20 parts, sustained release dosage 5 parts, latex powder 15 parts, Magnesium Silicate q-agent 10 parts, limestone powder 20 parts, antioxidant 5 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 45 parts, water.
After above each component is carried out mixing 10-25min by mixing machine, namely obtain spackling of the present invention;
Spackling of the present invention has preferably outward appearance after tested, and simultaneously the accumulation of salt in the surface soil is lower, less to body effect, not easy to crack and drop after adhering to metope simultaneously.
Embodiment 2
Choose the component of following mass fraction: cement 50 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 10 parts, latex powder 20 parts, Magnesium Silicate q-agent 20 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 10 parts, anti-accumulation of salt in the surface soil agent 10 parts, anti-crack water-proof agent 10 parts, 60 parts, water.
After above each component is carried out mixing 10-25min by mixing machine, namely obtain spackling of the present invention;
Spackling of the present invention has preferably outward appearance after tested, and simultaneously the accumulation of salt in the surface soil is lower, less to body effect, not easy to crack and drop after adhering to metope simultaneously.
Embodiment 3
Choose the component of following mass fraction: cement 50 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 5 parts, latex powder 15 parts, Magnesium Silicate q-agent 10 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 60 parts, water.
After above each component is carried out mixing 10-25min by mixing machine, namely obtain spackling of the present invention;
Spackling of the present invention has preferably outward appearance after tested, and simultaneously the accumulation of salt in the surface soil is lower, less to body effect, not easy to crack and drop after adhering to metope simultaneously.
Embodiment 4
Choose the component of following mass fraction: cement 100 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 10 parts, latex powder 20 parts, Magnesium Silicate q-agent 20 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 60 parts, water.
After above each component is carried out mixing 10-25min by mixing machine, namely obtain spackling of the present invention;
Spackling of the present invention has preferably outward appearance after tested, and simultaneously the accumulation of salt in the surface soil is lower, less to body effect, not easy to crack and drop after adhering to metope simultaneously.
More than show and describe ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; the present invention also has various changes and modifications without departing from the spirit and scope of the present invention, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (10)
1. an inner-wall ceramic tile spackling, is characterized in that: the component comprising following mass fraction:
Cement 50-150 part
Bright powder 5-10 part
Fluorescent agent 5-10 part
Quartz sand 20-35 part
Sustained release dosage 5-10 part
Latex powder 15-20 part
Magnesium Silicate q-agent 10-20 part
Limestone powder 20-30 part
Antioxidant 5-10 part
Thickening water-holding agent 5-10 part
Anti-accumulation of salt in the surface soil agent 5-10 part
Anti-crack water-proof agent 5-10 part
Water 45-60 part.
2. inner-wall ceramic tile spackling according to claim 1, is characterized in that: the component comprising following mass fraction: cement 150 parts, 5 parts, bright powder, fluorescent agent 5 parts, quartz sand 20 parts, sustained release dosage 5 parts, latex powder 15 parts, Magnesium Silicate q-agent 10 parts, limestone powder 20 parts, antioxidant 5 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 45 parts, water.
3. inner-wall ceramic tile spackling according to claim 1, is characterized in that: the component comprising following mass fraction: cement 50 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 10 parts, latex powder 20 parts, Magnesium Silicate q-agent 20 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 10 parts, anti-accumulation of salt in the surface soil agent 10 parts, anti-crack water-proof agent 10 parts, 60 parts, water.
4. inner-wall ceramic tile spackling according to claim 1, is characterized in that: the component comprising following mass fraction: cement 50 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 5 parts, latex powder 15 parts, Magnesium Silicate q-agent 10 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 60 parts, water.
5. inner-wall ceramic tile spackling according to claim 1, is characterized in that: the component comprising following mass fraction: cement 100 parts, 10 parts, bright powder, fluorescent agent 10 parts, quartz sand 35 parts, sustained release dosage 10 parts, latex powder 20 parts, Magnesium Silicate q-agent 20 parts, limestone powder 30 parts, antioxidant 10 parts, thickening water-holding agent 5 parts, anti-accumulation of salt in the surface soil agent 5 parts, anti-crack water-proof agent 5 parts, 60 parts, water.
6. inner-wall ceramic tile spackling according to claim 1, is characterized in that: the particle diameter of described bright powder is 300-500 order.
7. inner-wall ceramic tile spackling according to claim 1, is characterized in that: the particle diameter of described quartz sand is 400-600 order.
8. inner-wall ceramic tile spackling according to claim 1, is characterized in that: the particle diameter of described latex powder is 300-400 order.
9. inner-wall ceramic tile spackling according to claim 1, is characterized in that: the particle diameter of described limestone powder is 600-700 order.
10. inner-wall ceramic tile spackling according to claim 1, is characterized in that: described cement is silicate cement.