CN103880331A - Epoxy resin plaster for building jointing and preparation method thereof - Google Patents
Epoxy resin plaster for building jointing and preparation method thereof Download PDFInfo
- Publication number
- CN103880331A CN103880331A CN201310557403.1A CN201310557403A CN103880331A CN 103880331 A CN103880331 A CN 103880331A CN 201310557403 A CN201310557403 A CN 201310557403A CN 103880331 A CN103880331 A CN 103880331A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- epoxy resin
- talcum powder
- joint filling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses epoxy resin plaster for building jointing. The epoxy resin plaster comprises a first component and a second component, wherein the first component comprises the following materials in parts by weight: 80-120 parts of bisphenol A epoxy resin, 10-30 parts of an active diluting flexibilizer, 5-10 parts of fumed silica and 160-180 parts of talcum powder; and the second component comprises the following materials in parts by weight: 10-30 parts of an active diluted flexibilizer, 40-50 parts of an alicyclic amine curing agent, 200-220 parts of talcum powder and 2-6 parts of an accelerant. The epoxy resin plaster is low in cost, convenient to operate by workers, quick to cure and high in flexibility, and can be cured in a wet environment.
Description
Technical field
The present invention relates to a kind of building spackling, relate in particular to a kind of building joint filling epoxy resin daub and preparation method thereof.
Background technology
Ceramic tile, floor tile gap filler are a kind of high-quality environment protective type high molecular polymer cement based compoiste adhering materials.It is taking high grade quartz sand, cement as aggregate, selects high molecular polymer rubber powder to be equipped with multiple additives and stirs all mixed powdery matrix materials forming through mixing machine, is mainly used in various glaze the inside brick, marble, the brick material filleting use such as granite, filleting width, thickness can be selected according to user.
With ceramic tile floor tile gap filler filleting, can ensure that institute's filleting road flawless produces, and there is good water-impervious performance, can prevent that humidity and rain penetration from, to body of wall inside, particularly winter, infiltering the moisture content freezing and expansion in seam road, thereby causing the brick that is stuck to come off.In addition with also reducing separating out of sand-cement slurry Free Calcium after ceramic tile floor tile gap filler, and do not affect the attractive in appearance of decoration.
Summary of the invention
Goal of the invention: the object of the invention is to for the deficiencies in the prior art, a kind of building joint filling epoxy resin daub and preparation method thereof is provided, this clay cost is low, workman is easy to operate, quick solidifying, toughness is high, and can under moist environment, solidify.
Technical scheme: a kind of building joint filling epoxy resin daub of the present invention, comprise first component and second component, described first component comprises following mass parts material: dihydroxyphenyl propane epoxy resin 80-120 part, active dilution toughner 10-30 part, aerosil 5-10 part, talcum powder 160-180 part; Described second component comprises following mass parts material: active dilution toughner 10-30 part, aliphatic cyclic amine solidifying agent 40-50 part, talcum powder 200-220 part, promotor 2-6 part.
Further improve technique scheme, described active dilution toughner is ethylene glycol diglycidylether, benzyl glycidyl ether or alicyclic glycidyl ether.
Described aliphatic cyclic amine solidifying agent be the Meng alkane diamines, isophorone diamine or diamino hexylamine in one or more.
Further, described promotor is 2,4,6-tri-(dimethylamino methyl) phenol.
As preferably: above-mentioned building joint filling is with in epoxy resin daub, and described first component comprises following mass parts material: 80 parts of dihydroxyphenyl propane epoxy resins, 20 parts of ethylene glycol diglycidylethers, 6 parts of aerosils, 160 parts of talcum powder; Described second component comprises following mass parts material: 20 parts of ethylene glycol diglycidylethers, the Meng 40 parts of alkane diamines, 200 parts of talcum powder, 2 parts of promotor.
As preferably: above-mentioned building joint filling is with in epoxy resin daub, and described first component comprises following mass parts material: 100 parts of dihydroxyphenyl propane epoxy resins, 30 parts of benzyl glycidyl ethers, 8 parts of aerosils, 170 parts of talcum powder; Described second component comprises following mass parts material: 30 parts of benzyl glycidyl ethers, 50 parts of isophorone diamines, 220 parts of talcum powder, 5 parts of promotor.
A preparation method for epoxy resin daub for above-mentioned building joint filling, comprises the steps:
(1) preparation of first component: the dihydroxyphenyl propane epoxy resin of first component, active dilution toughner, aerosil, talcum powder are added in three-roller successively, stir 10-15 minute, make its even mixing obtain first component;
(2) preparation of second component: activity dilution toughner, aliphatic cyclic amine solidifying agent, talcum powder and the promotor of second component are added in another three-roller successively, stir 10-15 minute, evenly mixing obtains second component;
(3) mixed preparing: the second component that the first component that step (1) is made and step (2) make in mass ratio 1:1-1.2 three-roller stirring makes described clay.
Compared with prior art, its beneficial effect is in the present invention: cost of the present invention is low, workman is easy to operate, quick solidifying, and toughness is high, and can under moist environment, solidify.
Embodiment
Below technical solution of the present invention is elaborated, but protection scope of the present invention is not limited to described embodiment.
Embodiment 1: a kind of building joint filling epoxy resin daub, comprise first component and second component, described first component comprises following mass parts material: 80 parts of dihydroxyphenyl propane epoxy resins, 20 parts of ethylene glycol diglycidylethers, 6 parts of aerosils, 160 parts of talcum powder; Described second component comprises following mass parts material: 20 parts of ethylene glycol diglycidylethers, the Meng 40 parts of alkane diamines, 200 parts of talcum powder, 2 parts of promotor.
The preparation method of epoxy resin daub for above-mentioned building joint filling, comprises the steps:
(1) preparation of first component: the dihydroxyphenyl propane epoxy resin of first component, ethylene glycol diglycidylether, aerosil, talcum powder are added in three-roller successively, stir 15 minutes, make its even mixing obtain first component;
(2) preparation of second component: by the ethylene glycol diglycidylether of second component, the Meng alkane diamines, talcum powder and promotor add successively in another three-roller, stir 15 minutes, evenly mixing obtains second component;
(3) mixed preparing: the second component that the first component that step (1) is made and step (2) make in mass ratio 1:1 three-roller stirring makes described clay.
Embodiment 2: a kind of building joint filling epoxy resin daub, comprise first component and second component, described first component comprises following mass parts material: 100 parts of dihydroxyphenyl propane epoxy resins, 30 parts of benzyl glycidyl ethers, 8 parts of aerosils, 170 parts of talcum powder; Described second component comprises following mass parts material: 30 parts of benzyl glycidyl ethers, 50 parts of isophorone diamines, 220 parts of talcum powder, 5 parts of promotor.
The preparation method of epoxy resin daub for above-mentioned building joint filling, comprises the steps:
(1) preparation of first component: the dihydroxyphenyl propane epoxy resin of first component, benzyl glycidyl ether, aerosil, talcum powder are added in three-roller successively, stir 12 minutes, make its even mixing obtain first component;
(2) preparation of second component: the benzyl glycidyl ether of second component, isophorone diamine, talcum powder and promotor are added in another three-roller successively, stir 12 minutes, evenly mixing obtains second component;
(3) mixed preparing: the second component that the first component that step (1) is made and step (2) make in mass ratio 1:1.2 three-roller stirring makes described clay.
The clay making can be constructed in 40 minutes, can be completely curing in 22 hours.
As mentioned above, although represented and explained the present invention with reference to specific preferred embodiment, it shall not be construed as the restriction to the present invention self.Not departing under the spirit and scope of the present invention prerequisite of claims definition, can make in the form and details various variations to it.
Claims (7)
1. a building joint filling epoxy resin daub, is characterized in that, comprises first component and second component, described first component comprises following mass parts material: dihydroxyphenyl propane epoxy resin 80-120 part, active dilution toughner 10-30 part, aerosil 5-10 part, talcum powder 160-180 part; Described second component comprises following mass parts material: active dilution toughner 10-30 part, aliphatic cyclic amine solidifying agent 40-50 part, talcum powder 200-220 part, promotor 2-6 part.
2. a kind of building joint filling epoxy resin daub according to claim 1, is characterized in that, described active dilution toughner is ethylene glycol diglycidylether, benzyl glycidyl ether or alicyclic glycidyl ether.
3. a kind of building joint filling epoxy resin daub according to claim 2, is characterized in that, described aliphatic cyclic amine solidifying agent be the Meng alkane diamines, isophorone diamine or diamino hexylamine in one or more.
4. a kind of building joint filling epoxy resin daub according to claim 1, is characterized in that, described promotor is 2,4,6-tri-(dimethylamino methyl) phenol.
5. a kind of building joint filling epoxy resin daub according to claim 3, it is characterized in that, described first component comprises following mass parts material: 80 parts of dihydroxyphenyl propane epoxy resins, 20 parts of ethylene glycol diglycidylethers, 6 parts of aerosils, 160 parts of talcum powder; Described second component comprises following mass parts material: 20 parts of ethylene glycol diglycidylethers, the Meng 40 parts of alkane diamines, 200 parts of talcum powder, 2 parts of promotor.
6. a kind of building joint filling epoxy resin daub according to claim 3, is characterized in that, described first component comprises following mass parts material: 100 parts of dihydroxyphenyl propane epoxy resins, 30 parts of benzyl glycidyl ethers, 8 parts of aerosils, 170 parts of talcum powder; Described second component comprises following mass parts material: 30 parts of benzyl glycidyl ethers, 50 parts of isophorone diamines, 220 parts of talcum powder, 5 parts of promotor.
7. a preparation method for epoxy resin daub for building joint filling claimed in claim 1, is characterized in that, comprises the steps:
(1) preparation of first component: the dihydroxyphenyl propane epoxy resin of first component, active dilution toughner, aerosil, talcum powder are added in three-roller successively, stir 10-15 minute, make its even mixing obtain first component;
(2) preparation of second component: activity dilution toughner, aliphatic cyclic amine solidifying agent, talcum powder and the promotor of second component are added in another three-roller successively, stir 10-15 minute, evenly mixing obtains second component;
(3) mixed preparing: the second component that the first component that step (1) is made and step (2) make in mass ratio 1:1-1.2 three-roller stirring makes described clay.