CN105314617A - 一种制备炭分子筛的方法 - Google Patents
一种制备炭分子筛的方法 Download PDFInfo
- Publication number
- CN105314617A CN105314617A CN201410361978.0A CN201410361978A CN105314617A CN 105314617 A CN105314617 A CN 105314617A CN 201410361978 A CN201410361978 A CN 201410361978A CN 105314617 A CN105314617 A CN 105314617A
- Authority
- CN
- China
- Prior art keywords
- carrying
- molecular sieve
- temperature
- carbon
- petroleum coke
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开一种制备炭分子筛的方法,其特征在于,首先将石油焦预粉碎,然后釆用氧化剂和插层剂对原料进行浸渍氧化插层膨胀处理,样品进一步细粉碎,再加入适量粘结剂、粘结助剂及水进行捏合,捏合均匀后将该捏合物进行成型处理,成型处理物经干燥处理后进行炭化,然后根据需要进行控制物理活化以及碳沉积调孔处理,获得本发明所述的炭分子筛。本发明对石油焦进行插层预处理使其微晶尺度减小,层片间距成d002值变大,使其具有较发达的微孔,且改变石油焦的表面结构,有利于进一步的活化调孔处理,所得产品强度高,微孔丰富,孔径分布窄,产品可用于PSA法空气分离制氮,以及瓦斯气或天然气中甲烷的富集。
Description
技术领域
本发明涉及一种化工生产技术领域,主要涉及一种制备炭分子筛的方法。
背景技术
炭分子筛(CMS)是指具有接近被吸附分子大小的孔隙且孔径分布均匀的微孔炭材料,广泛应用于吸附分离、净化和催化等领域,主要作为变压吸附(PSA)工艺的吸附剂,广泛应用于中小规模的空气分离以制备富N2气体。CMS性能及其制造成本很大程度上由所用原料和采用的工艺过程所决定。对于工业生产CMS来说,开发新的原料以降低生产成本将带来巨大的经济效益和社会效益。用于制备CMS的原料很广,由含炭植物或矿物(煤、沥青等)到合成高分子聚合物等,均可用来制造炭分子筛。石油加工副产品石油焦是制备CMS可供选择的原料之一。
随着石油焦产量的不断上升和市场需求趋于饱和,为石油焦寻找新的利用途径越来越受到人们的重视。以石油焦为原料合成CMS,是一条石油焦增值和利用的新途径。石油焦具有价格低廉、来源广泛、固定炭含量高,灰分低等优点,但石油焦微观结构致密、易石墨化,限制了其应用。一般认为只有原料本身或原料经过适当的处理所得的中间产物具有较均匀的发达微孔结构时,才能制备出性能优良的CMS。
中国专利CN1631775A以石油焦为原料,经预炭化后,加3〜8倍质量的氢氧化钾活化,制得髙比表面积活性炭,再经过高温热缩聚,制得高比表面积纳米孔碳分子筛。由于石油焦 微观结构致密,需要大量的活化剂(氢氧化钾)活化,因此造成生产成本较高,设备腐蚀严重,污染大;中国专利CN1462650A以石油焦为原料,以石油沥青、乙烯裂解焦油或煤焦油为粘结剂,加水捏合后成型,干燥炭化后经过控制活化与两组份孔隙调整法的组合法的孔径处理工艺,获得微孔丰富的CMS。采用焦油或沥青粘结剂,含有害物质较多,污染环境;采用苯类或汽油类浸渍剂浸渍法调孔,难以实现微孔尺度和孔容的精细调控;采用物理活化法难以打开石油焦致密的微孔结构,所生产的CMS孔径分布宽,不适用于分子尺度相近的混合组分如空气的分离。以石油焦为原料生产CMS的国外专利未见报道。
发明内容
为解决上述现有的缺点,本发明的主要目的在于提供一种实用的制备炭分子筛的方法,通过插层预处理来改变石油焦的内部结构,使其适用于制备空分或富集甲烷用CMS的方法。由该方法制得的CMS灰分低,微孔丰富,孔径分布范围窄,气体分离性能优良且生产成本低,环境污染小。
为达成以上所述的目的,本发明的一种制备炭分子筛的方法采取如下技术方案:
一种制备炭分子筛的方法,其特征在于,该方法步骤为:
(1)首先将石油焦预粉碎至过100目的筛网;
(2)将插层剂与氧化剂混合均匀,然后加入石油焦粉中搅拌均匀,石油焦、插层剂和氧化剂的质量比为1: 0.05〜0.2:0.8〜2.0,在30〜60℃的温度下,反应0.5〜3h,再用去离子水洗至pH值为5〜6,在60〜80
℃干燥1〜6小时,最后在600-900 ℃温度下 快速膨胀;
(3)将上述样品进一步细粉碎至粒径小于5〜10μm,其中90%小于5μm;再加入粘结剂、粘结助剂及水进行捏合,再挤压成型。捏合成型时物料的质量比为石油焦粉:粘结剂:粘结助剂:水为1: 0.2〜0.7:0.02〜0.1:0.4〜0.8;
(4)成型处理物经干燥处理后进行炭化、活化和碳沉积调孔处理,即获得本发明所述的炭分子筛,炭化条件为:转炉炭化,升温速率为2〜10℃/min,温度为800〜900℃,氮气或氩气保护;活化条件为:活化剂为水蒸气或二氧化碳,体积浓度为30〜80%,载气为氮气或氩气,活化温度为800〜900℃,活化时间为0.5〜3
h;碳沉积调孔条件为:碳沉积试剂为苯或甲烷,体积浓度3〜20%,载气为氮气或氩气,沉积温度为700〜800℃,时间为0.5〜3h。
所述石油焦的灰分≤1.00%,水分≤5.0 %,挥发分≤18%,含碳量≥90%;所述的氧化剂为浓度为10〜30wt%H2O2溶液或浓度为10〜40
wt%H2O2溶液;所述的插层剂为浓度为95〜98 wt%H2SO4溶液;所述的快速膨胀过程可以是在自由落下床中惰性气氛N2或Ar或反应性气氛空气中完成,加热速率为500〜1000℃/s,也可以是在固定床中惰性气氛N2或Ar中进行,加热速率为10〜
50℃/min;所述的粘结剂为热固性酚醛树脂,其性能符合如下指标:黏度为0.3〜1.5Pa·s/20℃,固含量为55〜75%。所述的粘结助剂为水溶性淀粉或羧甲基纤维素。
采用如上技术方案的本发明,具有如下有益效果:
1、对石油焦进行插层预处理可以使其微晶尺度减小,层片间距成d002值变大,使其具有较发达的微孔,且改变石油焦的表面结构,有利于进一步的活化调孔处理。同时,预处理后的石油焦易于细粉碎。
2、插层预处理在低温下进行,容易操作控制,且所用的插层剂和氧化剂可以回收再利用。采用酚醛树脂为粘结剂,产生的污染较小;采用淀粉、羧甲基纤维素等为粘结助剂,生产成本较低。
3、所生产的CMS灰分低,强度高,微孔丰富,孔径分布范围窄,分离(变压吸附空分制氮或瓦斯气或天然气中甲烷富集)性能优良。
具体实施方式
为了进一步说明本发明,下面结合实施例对本发明作进一步说明。
实施例1:
取粉碎后的石油焦原料3008,加入粘结剂(热固性酚醛树脂)、助剂(淀粉)和水混捏均匀,其中焦粉:粘结剂:助剂:水=1:0.2: 0.05:0.6,再挤压成型。在110℃烘干2h,制成直径2㎜,长3~5㎜的圆柱体小颗粒。成型烘干后的颗粒在电热转炉中以5℃/min的 升温速率升到800℃,炭化1h,载气N2流速130ml/min;炭化后再以0.45 ml/min速率通入水活化0.5h最后在温度750℃时通入苯1h进行调孔,苯流速0.135 ml/min,冷却后即获得CMS。所制得的CMS用转鼓测定的强度达到99.5%,N2吸附测定的总孔容积为0.021 ml/g,双塔变压吸附装置测定的空分性能N2的出口浓度为88%。同等条件下商品炭分子筛的测试结果为:转鼓强度99.0%,总孔容积为0.030 ml/g,N2浓度为97.9%。
实施例2
取300g焦粉与98%浓硫酸300ml及30%双氧水30ml搅拌混合均匀,反应1h,然后用去离子水洗至pH值为5~6,在80℃左右干燥2h,最后在钢甑中以10~20℃/min加热速率快速升温至750℃,停留0.5h,载气N2流速100 ml/min,制得预处理石油焦粉。接着按照实施例1的成型、炭化、活化、沉积步骤进行。所制得的CMS用转鼓测定的强度达到99.4%,N2吸附测定的总孔容积为0.043 ml/g,双塔变压吸附装置测定的空分性能队的出口浓度为 96.8%。
实施例3
取300g焦粉与98%浓硫酸300ml及30%双氧水15ml搅拌混合均匀,反应1h,然后用去离子水洗至pH值为5〜6,在80℃左右干燥2h,最后在钢甑中以10~20℃/min加热速率快速升温至750℃,停留0.5h,载气N2流速100ml/min,制得预处理的石油焦粉。接着按照实施例1的成型、炭化、活化、沉积步骤进行。所制得的CMS用转鼓测定的强度达到 99.6%,N2吸附测定的总孔容积为0.048ml/g,双塔变压吸附装置测定的空分性能N2的出口浓度为98.1%。
实施例4
取300g焦粉与98 %浓硫酸300ml及30%双氧水15ml搅拌混合均匀,反应1h,然后用去离子水洗至pH值为5~6,在80℃左右干燥2h,最后在800℃下自由落下床中快速落下,颗粒的升温约600℃/s,载气N2流速200ml/min,制得预处理的石油焦粉。接着按照实施例1的成型、炭化、活化、沉积步骤进行。所制得的CMS用转鼓测定的强度达到99.3%,N2吸附测定的总孔容积为0.052ml/g,双塔变压吸附装置测定的空分性能N2的出口浓度为 98.7%。
Claims (2)
1.一种制备炭分子筛的方法,其特征在于,该方法步骤为:
(1)首先将石油焦预粉碎至过100目的筛网;
(2)将插层剂与氧化剂混合均匀,然后加入石油焦粉中搅拌均匀,石油焦、插层剂和氧化剂的质量比为1: 0.05〜0.2:0.8〜2.0,在30〜60℃的温度下,反应0.5〜3h,再用去离子水洗至pH值为5〜6,在60〜80 ℃干燥1〜6小时,最后在600-900 ℃温度下 快速膨胀;
(3)将上述样品进一步细粉碎至粒径小于5〜10μm,其中90%小于5μm,再加入粘结剂、粘结助剂及水进行捏合,再挤压成型,捏合成型时物料的质量比为石油焦粉:粘结剂:粘结助剂:水为1: 0.2〜0.7:0.02〜0.1:0.4〜0.8;
(4)成型处理物经干燥处理后进行炭化、活化和碳沉积调孔处理,即获得本发明所述的炭分子筛,炭化条件为:转炉炭化,升温速率为2〜10℃/min,温度为800〜900℃,氮气或氩气保护;活化条件为:活化剂为水蒸气或二氧化碳,体积浓度为30〜80%,载气为氮气或氩气,活化温度为800〜900℃,活化时间为0.5〜3 h;碳沉积调孔条件为:碳沉积试剂为苯或甲烷,体积浓度3〜20%,载气为氮气或氩气,沉积温度为700〜800℃,时间为0.5〜3h。
2.根据权力要求1所述的一种制备炭分子筛的方法,其特征在于, 所述石油焦的灰分≤1.00%,水分≤5.0 %,挥发分≤18%,含碳量≥90%,所述的氧化剂为浓度为10〜30wt%H2O2溶液或浓度为10〜40 wt%H2O2溶液,所述的插层剂为浓度为95〜98 wt%H2SO4溶液,所述的快速膨胀过程可以是在自由落下床中惰性气氛N2或Ar或反应性气氛空气中完成,加热速率为500〜1000℃/s,也可以是在固定床中惰性气氛N2或Ar中进行,加热速率为10〜 50℃/min,所述的粘结剂为热固性酚醛树脂,其性能符合如下指标:黏度为0.3〜1.5Pa·s/20℃,固含量为55〜75%,所述的粘结助剂为水溶性淀粉或羧甲基纤维素。