CN105295393A - Halogenated butyl rubber membrane covering rubber plug for injection - Google Patents
Halogenated butyl rubber membrane covering rubber plug for injection Download PDFInfo
- Publication number
- CN105295393A CN105295393A CN201510697620.XA CN201510697620A CN105295393A CN 105295393 A CN105295393 A CN 105295393A CN 201510697620 A CN201510697620 A CN 201510697620A CN 105295393 A CN105295393 A CN 105295393A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- butyl rubber
- rubber
- parched
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A halogenated butyl rubber membrane covering rubber plug for injection is prepared from 60-70 parts of brominated butyl rubber, 30-40 parts of calcined kaolin, 3-5 parts of zinc oxide, 89-99 parts of epoxy resin E-42, 89-99 parts of phenol-nitrile butadiene rubber copolymers, 66-75 parts of acetone, 10-15 parts of ethidene diamine, 100-120 parts of soybean protein, 5-7 parts of turpentine, 15-20 parts of 50% sodium hydroxide aqueous solution, 40-50 parts of whitewash, 400-450 parts of chrysanthemum water, 10-20 parts of floral water, 30-50 parts of flower and plant roots and stems, 5-10 parts of ginseng, 5-10 parts of atractylodes macrocephala koidz, 5-10 parts of raw rice sprouts, 50-60 parts of water, 5-10 parts of scorched hawthorn fruit, 5-10 parts of medicated leaven, 5-7 parts of radix polygonati officinalis, 9-12 parts of rhizoma arisasmatis, 15-18 parts of calamendiol, 15-18 parts of wood bits and 100-120 parts of soycheese water. The rubber plug has the advantages that the rubber plug prepared through the process can make direct contact with medicine, an inner cover of a combined cover can be omitted, the penetration force and the chipping falling rate are decreased, and cover assembling cost is reduced for pharmaceutical factories as well.
Description
Technical field:
The present invention relates to medicinal rubber manufacture method technical field, be specifically related to injection liquid halogenated butyl rubber coated rubber plug.
Background technology:
Along with the development of society, the rubber item kind being applied to medicine and hygiene fields gets more and more, as various flask for medicinal preparations plug, asepsis injector piston, injection sealant sealing, flexible pipe, conduit, medical air cushion, antiseptic rubber medical gloves, baby nipple, tube for blood transfusion,latex etc.Desirable druggist rubber sundries not only needs to have good physicals, also must ensure nontoxic and have unreactiveness, particularly in body rubber item should have not pathogenic, do not damage adjacent tissue, do not cause the features such as allergy, aging resistance are good.
Traditional druggist rubber sundries is under high temperature, condition of high voltage, and its vulcanization system easily produces and pollutes human body, the exudate of medicament, volatile matter, thus is difficult to prepare the druggist rubber sundries meeting medicine extra best best standard.Existing druggist rubber sundries and preparation method thereof, its complex technical process, the product feature of environmental protection is poor, and safety in utilization is not strong, and work-ing life is lower.
Summary of the invention:
Technical problem to be solved by this invention is to provide a kind of directly to contact medicine, can save the inner cap of combination cover, reduce puncture force and exfoliation probability and can to the replaced injection liquid halogenated butyl rubber coated rubber plug of pharmaceutical factory's reduction group lid cost.
Technical problem to be solved by this invention adopts following technical scheme to realize:
Injection liquid halogenated butyl rubber coated rubber plug, is made up of following component:
Brominated butyl rubber 60-70 part, calcined kaolin 30-40 part, zinc oxide 3-5 part, E-42 epoxy resin 89-99 part, phenolic aldehyde-nitrile rubber multipolymer 89-99 part, acetone 66-75 part, quadrol 10-15 part, soy-protein 100-120 part, turps 5-7 part, 50% aqueous sodium hydroxide solution 15-20 part, liming 40-50 part, chrysanthemum water 400-450 part, toilet water 10-20 part, flowers and plants rhizome 30-50 root, ginseng 5-10 part, bighead atractylodes rhizome 5-10 part, raw rice sprout 5-10 part, water 50-60 part, Fructus Crataegi (parched to brown) 5-10 part, Divine Comedy 5-10 part, radix polygonati officinalis 5-7 part, Rhizoma Arisaematis 9-12 part, calamus 15-18 part, wood chip 15-18 part, bean curd water 100-120 part.
Injection liquid halogenated butyl rubber coated rubber plug, its preparation method mainly comprises the following steps:
Get ginseng, the bighead atractylodes rhizome, raw rice sprout, pulverize, mixing water, is sprayed on Fructus Crataegi (parched to brown), until Fructus Crataegi (parched to brown) moisture content higher than 50% time, take out Fructus Crataegi (parched to brown) and be placed in sealed can 1-2 hour;
To spray remaining liquid again, wood chip, Divine Comedy, radix polygonati officinalis, Rhizoma Arisaematis smash into powder to pieces with calamus, pour in liquid, stir, take out Fructus Crataegi (parched to brown) simultaneously and be placed in liquid, seal 1 hour, then under being placed in the sun, be exposed to the sun to the complete evaporate to dryness of liquid, take out remaining powder agglomates, smash to pieces, sieve, mix with bean curd water, obtain mixed solution;
Soy-protein is under agitation added in chrysanthemum water;
After stirring into serum, add 50% aqueous sodium hydroxide solution, stir rapidly, obtain A mixture;
Get E-42 epoxy resin and phenolic aldehyde-nitrile rubber multipolymer, instillation toilet water, adds 30%A mixture simultaneously, stirs;
Cooling, natural evaporate to dryness, instills turps in evaporate to dryness process, obtains dry block;
Get 70%A mixture and calcined kaolin, be placed in stirrer, heat, add liming simultaneously, 90 DEG C are not stopped heated and stirred;
Get brominated butyl rubber to add fast in stirrer, within 1-2 minute, extract out, be placed in sealed can, stand-by, in sealed can tank, the end, is equipped with flowers and plants rhizome;
Being mixed with zinc oxide, acetone, quadrol by dry block adds in stirrer again, stirs 1-2 hour;
Empty the brominated butyl rubber in sealed can and flowers and plants rhizome after 1-2 hour, pour in sealed can, add mixed solution by the mixed solution in stirrer, cooling stripping and slicing, obtains plug.
In this processing method, its key is agitating procedure, because the plug after stirring has better clarity and ensure that sterility and inside are without bacteriotoxin and noresidue moisture, cleaning in addition after extracting can make the clarity of product, particulate and silicone oil reach processing requirement, such plug directly can contact medicine, and can save combination cover inner cap, reduce puncture force and exfoliation probability, on the other hand reduce group lid cost to pharmaceutical factory; And medical rubber plug needs and plastic combination cover assembling uses, medical rubber plug directly can not contact medicine, and plastic combination cover must have inner cap, uses and also relatively bothers.
The invention has the beneficial effects as follows: plug prepared by this technique directly can contact medicine, and can save the inner cap of combination cover, reduce puncture force and exfoliation probability, reduce group lid cost to pharmaceutical factory on the other hand.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with concrete example, setting forth the present invention further.
Specific embodiment 1: injection liquid halogenated butyl rubber coated rubber plug, is made up of following component:
Brominated butyl rubber 60 parts, calcined kaolin 30 parts, 3 parts, zinc oxide, E-42 epoxy resin 89 parts, phenolic aldehyde-nitrile rubber multipolymer 89 parts, 66 parts, acetone, quadrol 10 parts, soy-protein 100 parts, 5 parts, turps, 50% aqueous sodium hydroxide solution 15 parts, liming 40 parts, chrysanthemum water 400 parts, toilet water 10 parts, 30, flowers and plants rhizome, ginseng 5 parts, the bighead atractylodes rhizome 5 parts, raw rice sprout 5 parts, 50 parts, water, Fructus Crataegi (parched to brown) 5 parts, Divine Comedy 5 parts, radix polygonati officinalis 5 parts, Rhizoma Arisaematis 9 parts, calamus 15 parts, wood chip 15 parts, 100 parts, bean curd water.
Specific embodiment 2: injection liquid halogenated butyl rubber coated rubber plug, is made up of following component:
Brominated butyl rubber 70 parts, calcined kaolin 40 parts, 5 parts, zinc oxide, E-42 epoxy resin 99 parts, phenolic aldehyde-nitrile rubber multipolymer 99 parts, 75 parts, acetone, quadrol 15 parts, soy-protein 120 parts, 7 parts, turps, 50% aqueous sodium hydroxide solution 20 parts, liming 50 parts, chrysanthemum water 450 parts, toilet water 20 parts, 50, flowers and plants rhizome, ginseng 10 parts, the bighead atractylodes rhizome 10 parts, raw rice sprout 10 parts, 60 parts, water, Fructus Crataegi (parched to brown) 10 parts, Divine Comedy 10 parts, radix polygonati officinalis 7 parts, Rhizoma Arisaematis 12 parts, calamus 18 parts, wood chip 18 parts, 120 parts, bean curd water.
Injection liquid halogenated butyl rubber coated rubber plug, its preparation method mainly comprises the following steps:
Get ginseng, the bighead atractylodes rhizome, raw rice sprout, pulverize, mixing water, is sprayed on Fructus Crataegi (parched to brown), until Fructus Crataegi (parched to brown) moisture content higher than 50% time, take out Fructus Crataegi (parched to brown) and be placed in sealed can 1-2 hour;
To spray remaining liquid again, wood chip, Divine Comedy, radix polygonati officinalis, Rhizoma Arisaematis smash into powder to pieces with calamus, pour in liquid, stir, take out Fructus Crataegi (parched to brown) simultaneously and be placed in liquid, seal 1 hour, then under being placed in the sun, be exposed to the sun to the complete evaporate to dryness of liquid, take out remaining powder agglomates, smash to pieces, sieve, mix with bean curd water, obtain mixed solution;
Soy-protein is under agitation added in chrysanthemum water;
After stirring into serum, add 50% aqueous sodium hydroxide solution, stir rapidly, obtain A mixture;
Get E-42 epoxy resin and phenolic aldehyde-nitrile rubber multipolymer, instillation toilet water, adds 30%A mixture simultaneously, stirs;
Cooling, natural evaporate to dryness, instills turps in evaporate to dryness process, obtains dry block;
Get 70%A mixture and calcined kaolin, be placed in stirrer, heat, add liming simultaneously, 90 DEG C are not stopped heated and stirred;
Get brominated butyl rubber to add fast in stirrer, within 1-2 minute, extract out, be placed in sealed can, stand-by, in sealed can tank, the end, is equipped with flowers and plants rhizome;
Being mixed with zinc oxide, acetone, quadrol by dry block adds in stirrer again, stirs 1-2 hour;
Empty the brominated butyl rubber in sealed can and flowers and plants rhizome after 1-2 hour, pour in sealed can, add mixed solution by the mixed solution in stirrer, cooling stripping and slicing, obtains plug.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (2)
1. injection liquid halogenated butyl rubber coated rubber plug, is characterized in that: have following component:
Brominated butyl rubber 60-70 part, calcined kaolin 30-40 part, zinc oxide 3-5 part, E-42 epoxy resin 89-99 part, phenolic aldehyde-nitrile rubber multipolymer 89-99 part, acetone 66-75 part, quadrol 10-15 part, soy-protein 100-120 part, turps 5-7 part, 50% aqueous sodium hydroxide solution 15-20 part, liming 40-50 part, chrysanthemum water 400-450 part, toilet water 10-20 part, flowers and plants rhizome 30-50 root, ginseng 5-10 part, bighead atractylodes rhizome 5-10 part, raw rice sprout 5-10 part, water 50-60 part, Fructus Crataegi (parched to brown) 5-10 part, Divine Comedy 5-10 part, radix polygonati officinalis 5-7 part, Rhizoma Arisaematis 9-12 part, calamus 15-18 part, wood chip 15-18 part, bean curd water 100-120 part.
2., according to the halogenated butyl rubber coated rubber plug of the injection liquid described in claim 1, it is characterized in that: its preparation method mainly comprises the following steps:
Get ginseng, the bighead atractylodes rhizome, raw rice sprout, pulverize, mixing water, is sprayed on Fructus Crataegi (parched to brown), until Fructus Crataegi (parched to brown) moisture content higher than 50% time, take out Fructus Crataegi (parched to brown) and be placed in sealed can 1-2 hour;
To spray remaining liquid again, wood chip, Divine Comedy, radix polygonati officinalis, Rhizoma Arisaematis smash into powder to pieces with calamus, pour in liquid, stir, take out Fructus Crataegi (parched to brown) simultaneously and be placed in liquid, seal 1 hour, then under being placed in the sun, be exposed to the sun to the complete evaporate to dryness of liquid, take out remaining powder agglomates, smash to pieces, sieve, mix with bean curd water, obtain mixed solution;
Soy-protein is under agitation added in chrysanthemum water;
After stirring into serum, add 50% aqueous sodium hydroxide solution, stir rapidly, obtain A mixture;
Get E-42 epoxy resin and phenolic aldehyde-nitrile rubber multipolymer, instillation toilet water, adds 30%A mixture simultaneously, stirs;
Cooling, natural evaporate to dryness, instills turps in evaporate to dryness process, obtains dry block;
Get 70%A mixture and calcined kaolin, be placed in stirrer, heat, add liming simultaneously, 90 DEG C are not stopped heated and stirred;
Get brominated butyl rubber to add fast in stirrer, within 1-2 minute, extract out, be placed in sealed can, stand-by, in sealed can tank, the end, is equipped with flowers and plants rhizome;
Being mixed with zinc oxide, acetone, quadrol by dry block adds in stirrer again, stirs 1-2 hour; Empty the brominated butyl rubber in sealed can and flowers and plants rhizome after 1-2 hour, pour in sealed can, add mixed solution by the mixed solution in stirrer, cooling stripping and slicing, obtains plug.