CN105291675B - A kind of silver-colored bowl specification preparation method of embossment - Google Patents
A kind of silver-colored bowl specification preparation method of embossment Download PDFInfo
- Publication number
- CN105291675B CN105291675B CN201510620739.7A CN201510620739A CN105291675B CN 105291675 B CN105291675 B CN 105291675B CN 201510620739 A CN201510620739 A CN 201510620739A CN 105291675 B CN105291675 B CN 105291675B
- Authority
- CN
- China
- Prior art keywords
- silver
- colored bowl
- pattern
- rosin
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of silver-colored bowl specification preparation method of embossment, including following operating procedure：Prepare 8-10mm silver plates；Groove is pressed or beaten out at silver plate planar central position, the moulding for making silver-colored bowl is repeated several times after reheating cooling；Prepare a rosin body, with firelock or charcoal fire by the roasting fusing in rosin body upper surface centre, rosin melt is filled into silver-colored bowl with spoon handle；Then the place to be carved outside silver-colored bowl carries out the pattern that handwritten drawings want engraving；Silver-colored bowl pattern is placed on above rosin body fixed, outwards hammers system into shape with son is accounted for from the pattern of silver-colored bowl inner surface, then silver-colored bowl pattern part is reheated and is repeated several times operation after cooling down, silver-colored bowl is had rough space pattern；Carved, heated after carving is good on pattern with scorper, taken out the rosin body inside silver-colored bowl and cleaned up.The pattern stereoscopic impression of the invention for processing silver-colored bowl is strong, lines is clear, pattern is life-like.
Description
Technical field
The present invention relates to the preparation method of fine silver handicraft, especially a kind of silver-colored bowl specification preparation method of embossment.
Technical background
Silver jeweleries as a kind of cultural phenomenon in history by it is many it is national favor, the carrier exchanged as multiculture it
One, Miao ethnic group's silver jeweleries complete set is made by hand, there is 30 multiple working procedures, forms founding, hammering, welds, a whole set of work such as woollen yarn knitting, washing
Skill；It is, by the process of the various filamentary silver component synthesis drawn, fine silver wire drawing to be aided with during woollen yarn knitting that the silver jeweleries of fine silver lacing technique, which makes,
The use of the techniques such as welding method, different components is fixed together welding fabrication.
But had differences in the preparation method of fine silver handicraft, unstable product quality, part fine silver handicraft is three-dimensional
Sense is poor, and lines is unintelligible, it is impossible to embody the exquisite value of handicraft.
The content of the invention
In view of the deficiencies of the prior art, the present invention is intended to provide a kind of embossment silver bowl specification preparation method, makes silver-colored bowl
Pattern stereoscopic impression is strong, lines clear, steady quality.
To reach above-mentioned purpose, the technical solution adopted by the present invention：A kind of silver-colored bowl specification preparation method of embossment, including it is as follows
Operating procedure：
1st, silver plate is first got out, silver plate thickness is 8-10mm；
2nd, a diameter of 6-8 cm iron pipe is prepared, the height of iron pipe is 3-5cm, and silver plate is fired once, treats cold
But silver plate is placed on iron pipe mouthful after and is laid flat, the pressure or hammer hammered into shape with wooden mallet or glue in the middle of silver-colored plane gently make groove, extrude
Progress grills thoroughly red with firelock after groove, carries out wooden mallet compacting again after cooling, so repeatedly several until making the moulding of silver-colored bowl；
3rd, a rosin body is prepared, with firelock or charcoal fire by the roasting fusing in rosin body upper surface centre, with spoon will
Rosin melt fills silver-colored bowl；
4th, rosin natural cooling is allowed, the position then to be carved outside silver-colored bowl carries out handwritten drawings pattern, then carries out pattern
Engraving, dissolves rosin body in silver-colored bowl external heat with firelock after engraving is good, while rinsing dry with clear water inside a silver-colored bowl
Only, the knife print in silver-colored bowl surface face is shown out of silver-colored bowl；
5th, the rosin of fusing is poured into the groove in rosin body centre, it is with firelock that rosin dignity processing is smooth,
Silver-colored bowl pattern position is placed on above rosin body and fixed, and with son is accounted for, from the pattern of silver-colored bowl inner surface, outwards slowly hammer is made after cooling,
Then silver-colored bowl pattern part is reheated, outside slowly hammer system operation is repeated after cooling, then system is hammered into shape by the firing of 3-5 times,
Just there is rough space pattern the outside of silver-colored bowl；
6th, it is again that the heating of rosin body upper surface is smooth, silver-colored bowl pattern is placed on above rosin body fixed, silver-colored bowl pattern court
On, carved, after carving is good silver-colored bowl is heated with firelock on pattern with scorper, 200-300 DEG C of heating-up temperature is taken out in silver-colored bowl
The rosin body in face is cleaned up.
Using the preparation method, make that the pattern stereoscopic impression of silver-colored bowl is strong, lines is clear, pattern is life-like.
Embodiment
1st, silver plate is first got out, thickness is 8-10mm, silver-colored bowl leak and would not split during engraving；
2nd, a diameter of 6-8 cm iron pipe is prepared, the height of iron pipe is 3-5cm, and silver plate is fired once, treats cold
But silver plate is placed on iron pipe mouthful after and is laid flat, the pressure or hammer hammered into shape with wooden mallet or glue in the middle of silver-colored plane gently make groove, extrude
Progress grills thoroughly red with firelock after groove, carries out wooden mallet or glue hammer compacting again after cooling, so repeatedly several until making silver-colored bowl
Moulding；
3rd, one piece of rosin body is prepared, the rosin body is exactly as the fixed workbench for beaing silver-colored bowl, with firelock or charcoal
The rosin of fusing is filled silver-colored bowl by fire by the roasting fusing in rosin body upper surface centre with spoon, so also just on rosin body
Centre of surface position forms a groove；
5th, rosin natural cooling is allowed, the place to be carved after cooling outside silver-colored bowl carries out the figure that handwritten drawings want engraving
Case, pattern looks for a wooden prop after finishing, silver-colored bowl is placed on wooden prop and carved, after engraving is good with firelock outside silver-colored bowl
Slowly heat, rosin body is dissolved, while being rinsed well inside silver-colored bowl with clear water, silver-colored bowl surface face is shown out of silver-colored bowl
Knife print；
6th, the rosin of fusing is poured into the groove of rosin body upper surface, with processing smooth above torch rosin body, silver
Bowl pattern position be placed on above rosin body it is fixed, after cooling with son is accounted for from the outside slowly hammer system of the pattern of silver-colored bowl inner surface, so
Silver-colored bowl pattern part is reheated afterwards, outside slowly hammer system operation is repeated after cooling, then system, silver are hammered into shape by the firing of 3-5 times
Just there is rough space pattern outside inside bowl；
7th, it is again that the heating of rosin body upper surface is smooth, silver-colored bowl pattern is placed on above rosin body fixed, silver-colored bowl pattern court
On, carved, after carving is good silver-colored bowl is heated with firelock on pattern with scorper, 200-300 DEG C of heating-up temperature is taken out in silver-colored bowl
The rosin body in face is cleaned up.
Claims (1)
1. the silver-colored bowl specification preparation method of a kind of embossment, it is characterised in that including following operating procedure：
(1) silver plate is first got out, silver plate thickness is 8-10mm；
(2) a diameter of 6-8cm iron pipe is prepared, the height of iron pipe is 3-5cm, silver plate is burnt red, after cooling silver
Plate is placed on iron pipe mouthful and balanced, and goes out groove with pressure in the middle of silver-colored plane gently of wooden mallet or glue hammer or hammering, is then burnt with firelock
Burn red thoroughly, carry out wooden mallet compacting again after cooling, be so repeated several times until making the moulding of silver-colored bowl；
(3) a rosin body is prepared, with firelock or charcoal fire by the roasting fusing in rosin body upper surface centre, with spoon by rosin
Melt fills silver-colored bowl；
(4) rosin natural cooling is allowed, the position then to be carved outside silver-colored bowl carries out handwritten drawings pattern, then carries out pattern carving
Carve, rosin body is dissolved, the rosin of fusing is poured into rosin body central part in silver-colored bowl external heat with firelock after engraving is good
In the groove of position, while being rinsed well inside silver-colored bowl with clear water, the knife print in silver-colored bowl surface face is shown out of silver-colored bowl；
(5) it is with firelock that rosin dignity processing is smooth, silver-colored bowl pattern position is placed on above rosin body and fixed, after cooling with accounting for
Son from the pattern of silver-colored bowl inner surface, outwards slowly made by hammer, and then silver-colored bowl pattern part is reheated, outwards hammer is repeated after cooling
Operation, then hammer system into shape by the firing of 3-5 times, just there is rough space pattern the outside of silver-colored bowl；
(6) rosin body upper surface heated again smooth, silver-colored bowl pattern is placed on fixation above rosin body, silver-colored bowl pattern upward,
Carved, after carving is good silver-colored bowl is heated with firelock on pattern with scorper, 200-300 DEG C of heating-up temperature is taken out inside silver-colored bowl
Rosin body is cleaned up.