CN104589198A - Pure silver lacing polishing method - Google Patents
Pure silver lacing polishing method Download PDFInfo
- Publication number
- CN104589198A CN104589198A CN201410765947.1A CN201410765947A CN104589198A CN 104589198 A CN104589198 A CN 104589198A CN 201410765947 A CN201410765947 A CN 201410765947A CN 104589198 A CN104589198 A CN 104589198A
- Authority
- CN
- China
- Prior art keywords
- lacing
- fine silver
- silver
- pure silver
- aqueous solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a pure silver lacing polishing method. The pure silver lacing polishing method includes the following steps that pure sliver lacing is placed in a miniature electric furnace to be heated and warmed, the first electric furnace temperature ranges from 400 DEG C to 500 DEG C, a power source of the electric furnace is switched off after the temperature is reached, the pure silver lacing is clamped out and placed in a sodium borate aqueous solution to be immersed for 2-5 minutes, then the pure sliver lacing is placed in the electric furnace with the temperature ranging from 600 DEG C to 650 DEG C to be heated and warmed for a second time, the power source is switched off after the temperature is reached, and after being cooled along with the furnace, the pure silver lacing is taken out and placed in an alum aqueous solution; reheating is conducted so that the alum aqueous solution can be boiled, and the pure silver lacing is immersed in the alum aqueous solution for 8-12 minutes, then take out, cleaned up with clear water, placed in a vibratory polisher to be polished in a rolling mode, taken out, washed with tap water, and immersed in boiled water for 3-5 minutes. By the adoption of the method, the shelf life of the pure silver lacing is prolonged to 12-15 months, the situation that hard spots are generated on the pure silver lacing, so that the pure silver lacing is broken is eradicated, the luster is bright, and the quality of silver ornaments is improved.
Description
Technical field
The present invention relates to fine silver lacing finishing method, the method for especially a kind of fine silver lacing polishing.
Background technology
Silver jeweleries is as a kind of cultural phenomenon in history by the favor of many nationalitys, and become one of carrier of multiculture interchange, Miao ethnic group's silver jeweleries complete set is made by hand, has 30 multiple working procedures, forms founding, hammering, welding, a whole set of techniques such as woollen yarn knitting, washing; It is the process of being synthesized by the various filamentary silver assembly drawn that the silver jeweleries of fine silver lacing technique makes, and be aided with the use of the techniques such as fine silver wire drawing welding method during woollen yarn knitting, be fixed together different assemblies welding fabrication; Finally one integral piece ornaments are put into special solution washing by soaking, remove spot polishing and become the dazzling fine silver lacing of light, this is last procedure, also extremely exquisite, existing fine silver lacing finishing method is that spot is removed in the chemical industry drug immersion washings such as one integral piece ornaments sulfuric acid, phosphoric acid, nitric acid, hydrochloric acid.There is following defect in the fine silver lacing of its polishing: the first, existing technique is stain and the material on fast processing silver jeweleries surface, and the shelf-life anti-oxidation to the fine silver lacing of lacing is too short, within 1-3 month, will be oxidized; The second, making the fine silver lacing of lacing produce pit causes filamentary silver to rupture, because the silver-colored line filamentary silver that fine silver lacing draws is very tiny; Three, the fine silver lacing after polishing also keeps slightly dark yellow, and lines is clear not, does not reach the glossiness that silver jeweleries is the distinctest.
Summary of the invention
For the deficiencies in the prior art part, the present invention aims to provide the method for a kind of fine silver lacing polishing, improves the fine silver lacing anti-oxidation time limit, removes the phenomenon of pit that fine silver lacing produces, dark yellow and fracture of wire, reaches the glossiness of silver jeweleries distinctness.
For solving the problems of the technologies described above, the method for a kind of fine silver lacing polishing that the present invention adopts, comprises the following steps:
(1) borax solution preparation: 18-22g running water and 2.6-3.0g borax are poured into and heats boiled in copper dish, treat that borax solution cools between 30-40 degree;
(2) alum solution: add 2500-3000g running water and 80-100g alum preparation alum aqueous solution at copper dish, stir;
(3) fine silver lacing is put in miniature electric furnace carry out heat temperature raising, furnace temperature is 400-500 DEG C for the first time, furnace power is turned off after temperature, with clip fine silver lacing press from both sides out put into borax solution soak 2-5 minute, then again fine silver lacing is put into electric furnace and carry out second time heat temperature raising, post bake furnace temperature is 600-650 DEG C, power supply is turned off after temperature, fine silver lacing cools with stove, after slowly cooling to 50-20 DEG C, fine silver lacing is taken out in the alum aqueous solution be put in above-mentioned copper dish;
(4) and then heating by boiled for the alum aqueous solution in copper dish, fine silver lacing soaks 8-12 minutes in copper dish, with wood chopsticks, fine silver lacing is pressed from both sides out by clean water clean, then fine silver lacing is put in vibratory finishing machine and carry out tumbling, running water 2000-2500g is added in vibratory finishing machine, the stainless shot 1500-2000g of diameter 0.1, agate particle 80-100g, polishing powder 20-30g, antirust solution 5-10g, liquid detergent 10-15g, polishing time 2-4 minute, fine silver lacing is pressed from both sides out with wood chopsticks after polishing, clean with tap water, rinse rear use 95-100 DEG C degree boiling water well and soak fine silver lacing 3-5 minutes.
The invention has the beneficial effects as follows:
Adopt the fine silver lacing after said method polishing, not only can remove stain and the pollution on silver jeweleries surface, and make the shelf-life of fine silver lacing bring up to 12-15 months, stop to cause filamentary silver to rupture because fine silver lacing produces pit, fine silver lacing after polishing has distinct glossiness, and entirety improves the quality of fine silver lacing.
Other advantages of the present invention, target and feature will be set forth to a certain extent in the following description, and to a certain extent, based on will be apparent to those skilled in the art to investigating hereafter, or can be instructed from the practice of the present invention.
Detailed description of the invention
Below will be described in detail the preferred embodiments of the present invention.Should be appreciated that preferred embodiment only in order to the present invention is described, instead of in order to limit the scope of the invention.
The method of the fine silver lacing polishing of the present embodiment, comprises the following steps:
(1) borax solution preparation: 20g running water and 2.8g borax are poured into and heats boiled in copper dish, treat that borax solution cools between 30-40 degree;
(2) alum solution: add 2500g running water and the 80g alum preparation alum aqueous solution at copper dish, stir;
(3) lacing fine silver lacing is put in miniature furnace carry out heat temperature raising, furnace temperature is 400-500 DEG C for the first time, furnace power is turned off after temperature, with clip fine silver lacing press from both sides out put into into borax solution soak 2-5 minute, then again fine silver lacing is put into electric furnace and carry out second time heat temperature raising, post bake furnace temperature is 600-650 DEG C, power supply is turned off after temperature, fine silver lacing cools with stove, after slow cooling, fine silver lacing is taken out and is put in the alum aqueous solution of above-mentioned copper dish;
(4) and then heating by boiled for the alum aqueous solution in copper dish, silver jeweleries is soaked 8-12 minutes in copper dish, with wood chopsticks, fine silver lacing is pressed from both sides out by clean water clean, then fine silver lacing is put into vibratory finishing machine and carry out tumbling, add running water 2500g inside vibratory finishing machine simultaneously, the stainless shot 12000g of diameter 0.1, agate particle 100g, polishing powder 30g, antirust solution 10g, liquid detergent 10g, polishing time 3 minutes, fine silver lacing is pressed from both sides out with wood chopsticks after polishing, clean with tap water, rinse rear use 95-100 DEG C degree boiling water well and soak silver jeweleries 3-5 minutes.
What finally illustrate is, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted, although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to technical scheme of the present invention or equivalent replacement, and not departing from aim and the scope of the technical program, it all should be encompassed in the middle of right of the present invention.
Claims (1)
1. a method for fine silver lacing polishing, is characterized in that: comprise the following steps:
(1) borax solution preparation: 18-22g running water and 2.6-3.0g borax are poured into and heats boiled in copper dish, treat that borax solution cools between 30-40 degree;
(2) alum solution: add 2500-3000g running water and 80-100g alum preparation alum aqueous solution at copper dish, stir;
(3) fine silver lacing is put in miniature electric furnace carry out heat temperature raising, furnace temperature is 400-500 DEG C for the first time, furnace power is turned off after temperature, with clip fine silver lacing press from both sides out put into borax solution soak 2-5 minute, then again fine silver lacing is put into electric furnace and carry out second time heat temperature raising, post bake furnace temperature is 600-650 DEG C, power supply is turned off after temperature, fine silver lacing cools with stove, after slowly cooling to 50-20 DEG C, fine silver lacing is taken out in the alum aqueous solution be put in above-mentioned copper dish;
(4) and then heating by boiled for the alum aqueous solution in copper dish, fine silver lacing soaks 8-12 minutes in copper dish, with wood chopsticks, fine silver lacing is pressed from both sides out by clean water clean, then fine silver lacing is put in vibratory finishing machine and carry out tumbling, running water 2000-2500g is added in vibratory finishing machine, the stainless shot 1500-2000g of diameter 0.1, agate particle 80-100g, polishing powder 20-30g, antirust solution 5-10g, liquid detergent 10-15g, polishing time 2-4 minute, fine silver lacing is pressed from both sides out with wood chopsticks after polishing, clean with tap water, rinse rear use 95-100 DEG C degree boiling water well and soak fine silver lacing 3-5 minutes.