CN102783772B - Pure-silver wiredrawing knitted flower welding method - Google Patents

Abstract

The invention discloses a pure-silver wiredrawing knitted flower welding method, which comprises the following steps of: grinding a pure-silver soldering lug or welding rod into pure-silver powder; putting the pure-silver powder in a copper disc; adding borax and pure water, wherein the mass ratio of the pure-silver powder to the borax is 10:0.8; heating the copper disc with fire; boiling water in the copper disc; after the water in the copper disc is boiled, heating for 5-10 seconds to fully dissolve the borax in the boiling water; putting a filament accessory which needs to be welded in the copper disc liquid to be dipped for 15-25 seconds; taking out the filament accessory after 15-25 seconds; welding the filament accessory on the corresponding position of a silverware; and baking with flame of 500-700DEG C. People can not see the welding mark of a silver jewelry welded with the method, and the appearance of the silver jewelry is smooth and flat.

Description

The flower welding method is compiled in the fine silver wire drawing

Technical field

The present invention relates to the processing method of fine silver, the flower welding method is compiled in especially a kind of fine silver wire drawing.

Background technology

Silver jeweleries in history once by many national favors, becomes one of carrier of multiculture interchange as a kind of cultural phenomenon, and the processing of Miao ethnic group's silver jeweleries, be to complete with the manual operations in the family workshop entirely; As required, the silversmith first the silver of melting laminate, silver bar or filamentary silver, utilize to press, few, the technique such as carve, hug, make exquisite grain pattern, and then welding or knitting forming, yet the silver jeweleries that the flower welding method obtains is compiled in existing fine silver wire drawing, and obvious weld mark is arranged, and welding position is rough smooth.

As from the foregoing, the flower welding method is compiled in above-mentioned existing fine silver wire drawing, obviously has defect and exists, and remain to be improved.

Thus, improving of the above-mentioned defect of thoughts of the present invention, be that the spy concentrates on studies and coordinates repetition test, finally proposes a kind of reasonable in design and effectively improve the invention of above-mentioned defect.

Summary of the invention

For the deficiencies in the prior art part, the present invention aims to provide a kind of fine silver wire drawing and compiles the flower welding method, and to guarantee that Silver Jewelry is not without seeing weld mark, the welding position smooth surface is smooth.

For solving the problems of the technologies described above, the flower welding method is compiled in a kind of fine silver wire drawing that the present invention adopts, and comprises the following steps:

(1) fine silver weld tabs or welding rod are worn into to the fine silver powder, described fine silver powder is put into to the copper dish, add borax and pure water, the mass ratio of fine silver powder and borax is: 10:0.8, with fiery Heated Copper dish, make the water in the copper dish boiled, heat again 5-10 seconds after the water in the copper dish is boiled, make borax fully be dissolved in boiling water;

(2) will need the filigree accessory of welding to put into above-mentioned copper dish liquid immersion taking-up afterwards in 15-25 seconds;

(3) with 500 ℃ of-700 ℃ of flames, toasted after the filigree accessory being welded on to the silverware relevant position.

Adopt the silver jeweleries of said method welding, do not see weld mark, smooth in appearance is smooth.

The specific embodiment

Embodiment 1: step is shaken, and a kind of Miao ethnic group headwear, be welded by a plurality of silver thin slices and filamentary silver, welding process

Comprise the following steps:

(1) fine silver weld tabs or welding rod are worn into to the fine silver powder, described fine silver powder is put into to the copper dish, add borax and pure water, the mass ratio of fine silver powder and borax is: 10:0.8, with fiery Heated Copper dish, make the water in the copper dish boiled, heat again 5-10 seconds after the water in the copper dish is boiled, make borax fully be dissolved in boiling water;

(2) will need the filigree accessory of welding to put into above-mentioned copper dish liquid immersion taking-up afterwards in 15-25 seconds;

(3) with 500 ℃ of-700 ℃ of flames, toasted after the filigree accessory being welded on to the silverware relevant position.

Claims (1)

1. the flower welding method is compiled in a fine silver wire drawing, it is characterized in that, comprises the following steps:

(1) fine silver weld tabs or welding rod are worn into to the fine silver powder, described fine silver powder is put into to the copper dish, add borax and pure water, the mass ratio of fine silver powder and borax is: 10:0.8, with fiery Heated Copper dish, make the water in the copper dish boiled, heat again 5-10 seconds after the water in the copper dish is boiled, make borax fully be dissolved in boiling water;

(2) will need the filigree accessory of welding to put into above-mentioned copper dish liquid immersion taking-up afterwards in 15-25 seconds;

(3) with 500 ℃ of-700 ℃ of flames, toasted after the filigree accessory being welded on to the silverware relevant position.