CN102783772A - Pure-silver wiredrawing knitted flower welding method - Google Patents

Abstract

The invention discloses a pure-silver wiredrawing knitted flower welding method, which comprises the following steps of: grinding a pure-silver soldering lug or welding rod into pure-silver powder; putting the pure-silver powder in a copper disc; adding borax and pure water, wherein the mass ratio of the pure-silver powder to the borax is 10:0.8; heating the copper disc with fire; boiling water in the copper disc; after the water in the copper disc is boiled, heating for 5-10 seconds to fully dissolve the borax in the boiling water; putting a filament accessory which needs to be welded in the copper disc liquid to be dipped for 15-25 seconds; taking out the filament accessory after 15-25 seconds; welding the filament accessory on the corresponding position of a silverware; and baking with flame of 500-700DEG C. People can not see the welding mark of a silver jewelry welded with the method, and the appearance of the silver jewelry is smooth and flat.

Description

The flower welding method is compiled in the fine silver wire drawing

Technical field

The present invention relates to the processing method of fine silver, the flower welding method is compiled in especially a kind of fine silver wire drawing.

Background technology

Silver jeweleries in history once by many national favors, becomes one of carrier of multiculture interchange as a kind of cultural phenomenon, and the processing of Miao ethnic group's silver jeweleries is to accomplish with the manual operations in the family workshop entirely; As required; The silversmith earlier the silver of melting laminate, silver bar or filamentary silver, utilize press, few, technology such as carve, hug, make exquisite grain pattern; And then welding or knitting forming; Yet the silver jeweleries that the flower welding method obtains is compiled in existing fine silver wire drawing, and tangible weld mark is arranged, and the welding position is rough smooth.

By on can know that the flower welding method is compiled in above-mentioned existing fine silver wire drawing, obviously have defective and exist, and remain to be improved.

Thus, the improving of the above-mentioned defective of thoughts of the present invention is that the spy concentrates on studies and cooperates repetition test, proposes a kind of reasonable in design and effectively improve the invention of above-mentioned defective finally.

Summary of the invention

To the weak point of prior art, the present invention aims to provide a kind of fine silver wire drawing and compiles the flower welding method, does not have the weld mark of not seeing to guarantee Silver Jewelry, and the welding position smooth surface is smooth.

For solving the problems of the technologies described above, the flower welding method is compiled in a kind of fine silver wire drawing that the present invention adopts, and may further comprise the steps:

(1) wears into the fine silver powder to fine silver weld tabs or welding rod; Put into the copper dish to said fine silver powder, add borax and pure water, the mass ratio of fine silver powder and borax is: 10:0.8; With fire heating copper dish; Make the water in the copper dish boiled, heated again 5-10 seconds after the water in the copper dish is boiled, make borax fully be dissolved in the boiling water;

The filigree accessory that (2) will weld is put into above-mentioned copper dish liquid and is soaked taking-up after 15-25 seconds;

(3) after being welded on the silverware relevant position, toasts the filigree accessory with 500 ℃ of-700 ℃ of flames.

Adopt the silver jeweleries of said method welding, do not see weld mark, smooth in appearance is smooth.

The specific embodiment

Embodiment 1: the step shakes, and a kind of Miao ethnic group headwear is welded welding process by a plurality of silver thin slices and filamentary silver

May further comprise the steps:

(1) wears into the fine silver powder to fine silver weld tabs or welding rod; Put into the copper dish to said fine silver powder, add borax and pure water, the mass ratio of fine silver powder and borax is: 10:0.8; With fire heating copper dish; Make the water in the copper dish boiled, heated again 5-10 seconds after the water in the copper dish is boiled, make borax fully be dissolved in the boiling water;

The filigree accessory that (2) will weld is put into above-mentioned copper dish liquid and is soaked taking-up after 15-25 seconds;

(3) after being welded on the silverware relevant position, toasts the filigree accessory with 500 ℃ of-700 ℃ of flames.

Claims (1)

1. the flower welding method is compiled in a fine silver wire drawing, it is characterized in that, may further comprise the steps:

(1) wears into the fine silver powder to fine silver weld tabs or welding rod; Put into the copper dish to said fine silver powder, add borax and pure water, the mass ratio of fine silver powder and borax is: 10:0.8; With fire heating copper dish; Make the water in the copper dish boiled, heated again 5-10 seconds after the water in the copper dish is boiled, make borax fully be dissolved in the boiling water;

The filigree accessory that (2) will weld is put into above-mentioned copper dish liquid and is soaked taking-up after 15-25 seconds;

(3) after being welded on the silverware relevant position, toasts the filigree accessory with 500 ℃ of-700 ℃ of flames.