CN106037184A - Silver ornament process technique - Google Patents
Silver ornament process technique Download PDFInfo
- Publication number
- CN106037184A CN106037184A CN201610539584.9A CN201610539584A CN106037184A CN 106037184 A CN106037184 A CN 106037184A CN 201610539584 A CN201610539584 A CN 201610539584A CN 106037184 A CN106037184 A CN 106037184A
- Authority
- CN
- China
- Prior art keywords
- silver
- bullion
- jeweleries
- carried out
- ornament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a silver ornament process technique. The technique comprises the steps of S1, melting silver, wherein a silver ingot is placed in a crucible, the crucible is placed on a furnace to melt the silver ingot and then clamped by lazy tongs after the silver ingot is molten, and liquid silver obtained after melting is poured into a flat copper mold; S2, taking the silver ingot in the copper mold out to be cleaned; S3, conducting wiredrawing on the silver ingot to form filamentary silver; S4, welding the filamentary silver with an external liner plate with liquid silver as welding flux to form a silver ornament; S5, placing the silver ornament in a vibrator to relieve stress through vibration; S6, soaking the silver ornament in hydrochloric acid; S7, finally placing the silver ingot in clear water to be cleaned, and then conducting inspection and packaging. By the adoption of the technique, influences on the color, quality and appearance of the silver ornament caused by constituent difference of welding powder or welding rods are avoided, and through vibration distressing and hydrochloric acid cleaning, the silver ornament has small welding stress, high firmness and high glossiness.
Description
Technical field
The present invention relates to silver jeweleries technical field, particularly relate to a kind of silver jeweleries processing technique.
Background technology
Along with growth in the living standard, people are increasing to the purchase of Silver Jewelry, and outward appearance and quality to Silver Jewelry are wanted
Asking constantly raising, due to higher demand, in prior art, the processing technique of Silver Jewelry is the most chaotic, causes the silver processed
Ornaments low in glossiness, the welding defect such as unsightly, cause a lot of substandard products to need again and melt down, cause unnecessary damage to manufacturer
Lose.
Summary of the invention
The present invention mainly solves the technical problem in the presence of prior art, thus provides that a kind of glossiness is good, welding
Silver jeweleries processing technique attractive in appearance.
The above-mentioned technical problem of the present invention is mainly addressed by following technical proposals:
The silver jeweleries processing technique that the present invention provides, it comprises the following steps:
S1, molten silver, put into silver bullion in crucible, crucible is placed on stove thawing silver bullion, after silver bullion melts, uses long handle clamp
Crucible is stated in residence, and the liquid silver after dissolving is cast in the copper mold of flat；
S2, the silver bullion taken out in described copper mold are carried out；
S3, described silver bullion is carried out wire drawing formed filamentary silver；
S4, employing liquid silver are that described filamentary silver is carried out welding formation silver jeweleries by solder with outside liner plate；
S5, described silver jeweleries is put into vibrator is carried out vibrate destressing；Vibration duration is 1-2 minute；
S6, then by described silver jeweleries use soak with hydrochloric acid, soak time and temperature are respectively as follows: 30 ± 2 seconds and 0 ± 5 DEG C；
S7, finally described silver bullion is put into clear water is carried out after, check and pack.
Further, further comprise the steps of: after described step S1
S10, described silver bullion is beaten 50-100 time repeatedly, black or impurity occur to surface.
Further, described step S2 is further comprising the steps of:
S21, described silver bullion is put into hydrochloric acid carries out decontamination previous cleaning；
S22, more described silver bullion putting into copper dish, the mass ratio adding Borax and pure water, silver bullion and Borax is: 10:
0.8；
S23, Heated Copper dish, after boiled for the water in copper dish, the continuous heating 5-10 second, make Borax be completely dissolved in boiled water
In；
S24, take out described silver bullion.
The beneficial effects of the present invention is: form flat silver bullion by carrying out mold after being melted by silver bullion, once purged
Carry out wire drawing and form filamentary silver, be finally that solder is welded on liner plate by filamentary silver by liquid silver, the liquid silver solder of the present invention and
Filamentary silver combines together, and it not only avoid because the composition difference of welding powder or welding rod causes the impact of silver jeweleries quality, quality and outward appearance,
And by vibration destressing and the cleaning of hydrochloric acid, the welding stress making silver jeweleries is little, fastness good and glossiness more preferably.
Detailed description of the invention
Below the preferred embodiments of the present invention are described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
The silver jeweleries processing technique of the present invention, it comprises the following steps:
S1, molten silver, put into silver bullion in crucible, crucible is placed on stove thawing silver bullion, after silver bullion melts, uses long handle clamp
Living crucible, the liquid silver after dissolving is cast in the copper mold of flat；
S2, the silver bullion taken out in copper mold are carried out；
S3, silver bullion is carried out wire drawing formed filamentary silver；
S4, employing liquid silver are that filamentary silver is carried out welding formation silver jeweleries by solder with outside liner plate；
S5, silver jeweleries is put in vibrator carry out vibrate destressing；Vibration duration is 1-2 minute；
S6, then silver jeweleries use soak with hydrochloric acid, soak time and temperature are respectively as follows: 30 ± 2 seconds and 0 ± 5 DEG C；
S7, finally silver bullion is put into clear water is carried out after, check and pack.
The present invention by will silver bullion melt after carry out mold and form flat silver bullion, once purged carry out wire drawing and form silver
Silk, is finally that solder is welded on liner plate by filamentary silver by liquid silver, and the liquid silver solder of the present invention combines together with filamentary silver, its
Not only avoid the impact of the silver jeweleries quality, quality and the outward appearance that cause because of the composition difference of welding powder or welding rod, and by vibration
Destressing and the cleaning of hydrochloric acid, the welding stress making silver jeweleries is little, fastness good and glossiness more preferably.
Specifically, further comprise the steps of: after step S1
S10, silver bullion is beaten 50-100 time repeatedly, black or impurity occur to surface.So it is easy to remove silver bullion
Internal impurity, improves the purity of silver bullion, and the silver jeweleries for high-quality lays the foundation.
It is also preferred that the left step S2 is further comprising the steps of:
S21, silver bullion is put in hydrochloric acid and carry out decontamination previous cleaning；
S22, again silver bullion putting into copper dish, the mass ratio adding Borax and pure water, silver bullion and Borax is: 10:0.8；
In the present invention, Borax acts not only as abluent and is carried out silver bullion, and is also used as cosolvent, improves filamentary silver
Welding effect.
S23, Heated Copper dish, after boiled for the water in copper dish, the continuous heating 5-10 second, make Borax be completely dissolved in boiled water
In；
S24, taking-up silver bullion.
Above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, any without
Cross change or replacement that creative work is expected, all should contain within protection scope of the present invention.Therefore, the protection of the present invention
Scope should be as the criterion with the protection domain that claims are limited.
Claims (3)
1. a silver jeweleries processing technique, it is characterised in that comprise the following steps:
S1, molten silver, put into silver bullion in crucible, crucible is placed on stove thawing silver bullion, after silver bullion melts, clamps institute with lazy tongs
Stating crucible, the liquid silver after dissolving is cast in the copper mold of flat；
S2, the silver bullion taken out in described copper mold are carried out；
S3, described silver bullion is carried out wire drawing formed filamentary silver；
S4, employing liquid silver are that described filamentary silver is carried out welding formation silver jeweleries by solder with outside liner plate；
S5, described silver jeweleries is put into vibrator is carried out vibrate destressing；Vibration duration is 1-2 minute；
S6, then by described silver jeweleries use soak with hydrochloric acid, soak time and temperature are respectively as follows: 30 ± 2 seconds and 0 ± 5 DEG C；
S7, finally described silver bullion is put into clear water is carried out after, check and pack.
2. silver jeweleries processing technique as claimed in claim 1, it is characterised in that further comprise the steps of: after described step S1
S10, described silver bullion is beaten 50-100 time repeatedly, black or impurity occur to surface.
3. silver jeweleries processing technique as claimed in claim 1 or 2, it is characterised in that described step S2 is further comprising the steps of:
S21, described silver bullion is put into hydrochloric acid carries out decontamination previous cleaning；
S22, more described silver bullion putting into copper dish, the mass ratio adding Borax and pure water, silver bullion and Borax is: 10:0.8；
S23, Heated Copper dish, after boiled for the water in copper dish, the continuous heating 5-10 second, make Borax be completely dissolved in boiled water；
S24, take out described silver bullion.