CN105212453A - The hollow necklace preparation method of a kind of fine silver - Google Patents
The hollow necklace preparation method of a kind of fine silver Download PDFInfo
- Publication number
- CN105212453A CN105212453A CN201510692698.2A CN201510692698A CN105212453A CN 105212453 A CN105212453 A CN 105212453A CN 201510692698 A CN201510692698 A CN 201510692698A CN 105212453 A CN105212453 A CN 105212453A
- Authority
- CN
- China
- Prior art keywords
- pipe
- silver
- parchment covering
- parchment
- wooden stick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the hollow necklace preparation method of a kind of fine silver, comprise following operating procedure: parchment covering heating is popular in Slow cooling again; Parchment covering is pressed into round tubular with wooden stick; Shaping parchment covering pipe is carried out second time heating, 2 carry out second time compacting, reparation; Parchment covering pipe is carried out third time heating, then freeze with the joint area of firelock at parchment covering pipe, after having welded, welding slag, solder joint polishing totally; Rosin is melted completely for liquid is poured in silver-colored pipe, after allowing silver-colored pipe bend out necklace, slowly heats in the outside surrounding of silver-colored pipe, allow the rosin condensed in silver-colored pipe dissolve and flow out, cleaner by clean water, dry up, just become the hollow necklace of a standard.The hollow necklace of silver adopting technique scheme to produce is not yielding, wrinkling, cracking, and the product simultaneously produced is smooth, embodies the fineness of handicraft.
Description
Technical field
The present invention relates to the preparation method of fine silver handicraft, the hollow necklace preparation method of especially a kind of fine silver.
Technical background
Silver jeweleries is as a kind of cultural phenomenon in history by the favor of many nationalitys, and become one of carrier of multiculture interchange, Miao ethnic group's silver jeweleries complete set is made by hand, has 30 multiple working procedures, forms founding, hammering, welding, a whole set of techniques such as woollen yarn knitting, washing; It is the process of being synthesized by the various filamentary silver assembly drawn that the silver jeweleries of fine silver lacing technique makes, and be aided with the use of the techniques such as fine silver wire drawing welding method during woollen yarn knitting, be fixed together different assemblies welding fabrication.
But there are differences in the preparation method of fine silver handicraft, unstable product quality, part fine silver handicraft third dimension is poor, and lines is unintelligible, and the fineness that can not embody handicraft is worth.
Summary of the invention
For the deficiencies in the prior art part, the present invention aims to provide the hollow necklace preparation method of a kind of fine silver, and the product produced is not yielding, wrinkling, cracking, and third dimension is strong.
For reaching above-mentioned purpose, the technical solution used in the present invention: the hollow necklace preparation method of a kind of fine silver, comprises following operating procedure:
1, with firelock, parchment covering is heated to be popular in completely, then allows parchment covering slowly cool;
2, being placed in the middle of parchment covering by wooden stick, take wooden stick as model, with hand the both sides of parchment covering slowly along wooden stick pressure, first two is extruded circular, and then wooden stick is moved to centre extrudes, when parchment covering is pressed into round tubular completely, then take out wooden stick;
3, shaping parchment covering pipe is carried out second time heating, heating-up temperature is 300-400 degree, allows parchment covering pipe slowly grill thoroughly, after parchment covering pipe cool naturally, then wooden stick put into parchment covering pipe carry out second time suppress, reparation, taking-up wooden stick after completing;
4, parchment covering pipe is carried out third time heating, after cooling, parchment covering pipe is placed on smooth work top, push away and roll and extrude gently, make parchment covering pipe joint flat smooth, then freeze with the joint area of firelock at parchment covering pipe, after having welded, welding slag, solder joint polishing totally;
5, in steel basin, put into the rosin grain of 200 grams-230 grams, and slowly heat at basin bottom part with charcoal fire, when temperature reaches 300-400 DEG C, rosin grain melts for liquid completely, poured in silver-colored pipe by rosin liquid, treat 25-30 minutes, rosin condenses, make silver pipe bending, after silver pipe bends out necklace, slowly heat in the outside surrounding of silver-colored pipe, allow the rosin condensed in silver-colored pipe dissolve and flow out, again clean by clean water, dry up, just become the hollow necklace of a standard.
Employing technique scheme, the product that the operating procedure of specification can be produced is not yielding, wrinkling, cracking, and the product simultaneously produced is smooth, embodies the fineness of handicraft.
concrete implementation
1, with firelock, parchment covering is heated to be popular in completely, then allows parchment covering slowly cool, make its deliquescing;
2, being placed in the middle of parchment covering by wooden stick, take wooden stick as model, with hand the both sides of parchment covering slowly along wooden stick pressure, first two is extruded circular, and then wooden stick slowly moves to centre and extrudes, and when parchment covering is pressed into round tubular completely, more slowly takes out wooden stick;
3, shaping parchment covering pipe is carried out second time heating, heating-up temperature is 350 DEG C, allows parchment covering pipe slowly grill thoroughly, after parchment covering pipe cool naturally, then wooden stick slowly put into parchment covering pipe carry out second time suppress, reparation, taking-up wooden stick after completing;
4, parchment covering pipe is carried out third time heating, after cooling, parchment covering pipe is placed on smooth work top, pushes away and roll and extrude gently, make parchment covering pipe joint flat smooth, then freeze with the joint area of firelock at parchment covering pipe, will note joint area to freeze when freezing full, weldering water flow is even, after having welded, with fine grinding wheel clean to welding slag, solder joint polishing, it is made to form smooth shinny, the silver pipe of not seeing seam;
5, in Stainless steel basin, suitably put into the rosin grain of 200 grams, and slowly heat at basin bottom part with charcoal fire, when temperature reaches 320 DEG C, rosin grain melts completely for liquid, then is managed in silver-colored pipe by rosin liquid, treats 25-30 minutes, rosin condenses, and now, silver pipe can be allowed bending, after silver pipe bends out necklace, slowly heat in the outside surrounding of silver-colored pipe, allow the rosin condensed in silver-colored pipe dissolve and flow out, after completing, clean by clean water, dry up, just become the hollow necklace of a standard.
Claims (1)
1. the hollow necklace preparation method of fine silver, is characterized in that comprising following operating procedure:
1), with firelock parchment covering is heated to be popular in completely, then allows parchment covering slowly cool;
2), by wooden stick being placed in the middle of parchment covering, take wooden stick as model, with hand the both sides of parchment covering slowly along wooden stick pressure, first two is extruded circular, and then wooden stick is moved to centre extrudes, when parchment covering is pressed into round tubular completely, then take out wooden stick;
3), by shaping parchment covering pipe undertaken second time heating, heating-up temperature is 300-400 degree, allows parchment covering pipe slowly grill thoroughly, after parchment covering pipe cool naturally, then wooden stick put into parchment covering pipe carry out second time suppress, reparation, taking-up wooden stick after completing;
4), by parchment covering pipe carry out third time heating, after cooling, parchment covering pipe is placed on smooth work top, push away and roll and extrude gently, make parchment covering pipe joint flat smooth, then freeze with the joint area of firelock at parchment covering pipe, after having welded, welding slag, solder joint polishing totally;
5), in steel basin, put into the rosin grain of 200 grams-230 grams, and slowly heat at basin bottom part with charcoal fire, when temperature reaches 300-400 DEG C, rosin grain melts for liquid completely, poured in silver-colored pipe by rosin liquid, treat 25-30 minutes, rosin condenses, make silver pipe bending, after silver pipe bends out necklace, slowly heat in the outside surrounding of silver-colored pipe, allow the rosin condensed in silver-colored pipe dissolve and flow out, again clean by clean water, dry up, just become the hollow necklace of a standard.