CN105290312A - 一种阀门消失模铸造用泡沫塑料粘结剂 - Google Patents

一种阀门消失模铸造用泡沫塑料粘结剂 Download PDF

Info

Publication number
CN105290312A
CN105290312A CN201510692773.5A CN201510692773A CN105290312A CN 105290312 A CN105290312 A CN 105290312A CN 201510692773 A CN201510692773 A CN 201510692773A CN 105290312 A CN105290312 A CN 105290312A
Authority
CN
China
Prior art keywords
parts
added
20min
valve
land plaster
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510692773.5A
Other languages
English (en)
Inventor
黎宏
黎思瑶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEXIAN KEJIA VALVE CASTING CO Ltd
Original Assignee
HEXIAN KEJIA VALVE CASTING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEXIAN KEJIA VALVE CASTING CO Ltd filed Critical HEXIAN KEJIA VALVE CASTING CO Ltd
Priority to CN201510692773.5A priority Critical patent/CN105290312A/zh
Publication of CN105290312A publication Critical patent/CN105290312A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阀门消失模铸造用泡沫塑料粘结剂，涉及阀门制造技术领域，由如下重量份数的原料制成：聚合松香70-80份、双马来酰亚胺15-20份、改性淀粉13-18份、煅烧高岭土11-15份、聚丙烯酸钠10-13份、麦芽糊精10-13份、石膏粉8-12份、纳米氧化铝6-10份、棕榈蜡6-10份、田菁胶5-8份、二月桂酸二丁基锡3-6份、枸橼酸钠2-4份、正丁醇40-50份、水60-70份。本发明所制粘结剂具有生产成本低、粘结效果好、用量少和发气量少的特点，并且气化迅速，无残留物，适用于阀门消失模铸造用泡沫塑料的粘结。

Description

一种阀门消失模铸造用泡沫塑料粘结剂
技术领域：
本发明涉及阀门制造技术领域，具体涉及一种阀门消失模铸造用泡沫塑料粘结剂。
背景技术：
消失模铸造是将与铸件尺寸形状相似的泡沫模型粘结组合成模型簇，刷涂耐火涂料并烘干后，埋在干石英砂中振动造型，在负压下浇注，使模型气化，液体金属占据模型位置，凝固冷却后形成铸件的新型铸造方法。与传统铸造技术相比，消失模铸造具有铸件质量好、成本低、尺寸精度高、表面光洁的特点，可实现大规模、大批量生产，降低劳动强度和减少能源消耗。
在消失模铸造过程中，泡沫塑料模型的制备尤为重要。在模型制备时如果粘结剂选择不当，或粘结剂使用量过多或过少，不仅影响制模效率，还会增加浇注时的发气量和燃烧后的残留物，以及使模型各部分结合不良，导致铸件表面出现凹痕或毛刺缺陷。因此，为了获得优质的铸件，需要所用粘结剂气化迅速、无残留物。
发明内容：
本发明所要解决的技术问题在于提供一种粘结效果好、用量少，且发气量少、气化迅速和无残留物的阀门消失模铸造用泡沫塑料粘结剂。
本发明所要解决的技术问题采用以下的技术方案来实现：
一种阀门消失模铸造用泡沫塑料粘结剂，由如下重量份数的原料制成：
聚合松香70-80份、双马来酰亚胺15-20份、改性淀粉13-18份、煅烧高岭土11-15份、聚丙烯酸钠10-13份、麦芽糊精10-13份、石膏粉8-12份、纳米氧化铝6-10份、棕榈蜡6-10份、田菁胶5-8份、二月桂酸二丁基锡3-6份、枸橼酸钠2-4份、正丁醇40-50份、水60-70份；
其制备方法如下：
(1)向聚合松香中加入纳米氧化铝和正丁醇，混合均匀后于微波频率2450MHz、功率600W下微波处理15-20min，待温度降至70-80℃后再加入双马来酰亚胺和聚丙烯酸钠，保温搅拌20-30min，即得物料I；
(2)将改性淀粉加入水中打浆，待形成均匀浆体后加入棕榈蜡和田菁胶，升温至60-70℃保温搅拌15-20min，即得物料II；
(3)向物料II中加入煅烧高岭土和石膏粉，于超声频率40kHz、温度40-50℃下超声处理15-20min，然后加入物料I、麦芽糊精、二月桂酸二丁基锡和枸橼酸钠，继续超声处理10-15min，即得粘结剂。
所述改性淀粉由如下重量份数的原料制成：植物淀粉90-100份、茶多酚15-20份、纳米氧化铝8-12份、芒硝10-13份、三聚磷酸钠5-8份、柠檬酸7-10份、水200-250份，其制备方法为：先将植物淀粉加入水中打浆，待形成均匀浆体后加入茶多酚和纳米氧化铝，然后于超声频率40kHz、温度50-60℃下超声处理25-30min，再向处理液中加入三聚磷酸钠和柠檬酸，研磨15-20min后加入芒硝，混合均匀后于0-5℃下放置8-12h，最后经冷冻干燥后粉碎成粉末。
所述石膏粉由如下重量份数的原料制成：α-石膏粉60-70份、β-石膏粉40-50份、纳米陶瓷粉8-11份、纳米玻璃纤维4-7份、滑石粉10-15份、羧甲基壳聚糖10-15份、活性炭6-9份、瓜尔豆胶3-5份、水120-150份，其制备方法为：先将α-石膏粉、β-石膏粉和纳米玻璃纤维加入水中，分散均匀后于微波频率2450MHz、功率600W下微波处理15-20min，然后加入纳米陶瓷粉和滑石粉，继续微波处理5-10min，待温度降至60-70℃后加入活性炭、羧甲基壳聚糖和瓜尔豆胶，保温搅拌15-20min，最后经冷冻干燥后粉碎成粉末。
本发明的有益效果是：本发明以聚合松香为主要原料，利用纳米氧化铝对其进行改性，并辅以多种助剂，制得的粘结剂具有生产成本低、粘结效果好、用量少和发气量少的特点，并且气化迅速，无残留物，适用于阀门消失模铸造用泡沫塑料的粘结。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
(1)向70份聚合松香中加入7份纳米氧化铝和42份正丁醇，混合均匀后于微波频率2450MHz、功率600W下微波处理15min，待温度降至70℃后再加入16份双马来酰亚胺和10份聚丙烯酸钠，保温搅拌30min，即得物料I；
(2)将14份改性淀粉加入60份水中打浆，待形成均匀浆体后加入7份棕榈蜡和5份田菁胶，升温至70℃保温搅拌15min，即得物料II；
(3)向物料II中加入12份煅烧高岭土和10份石膏粉，于超声频率40kHz、温度50℃下超声处理20min，然后加入物料I、10份麦芽糊精、4份二月桂酸二丁基锡和2份枸橼酸钠，继续超声处理10-15min，即得粘结剂。
改性淀粉的制备：先将95份植物淀粉加入200份水中打浆，待形成均匀浆体后加入16份茶多酚和8份纳米氧化铝，然后于超声频率40kHz、温度55℃下超声处理30min，再向处理液中加入6份三聚磷酸钠和7份柠檬酸，研磨15min后加入10份芒硝，混合均匀后于0-5℃下放置12h，最后经冷冻干燥后粉碎成粉末。
石膏粉的制备：先将62份α-石膏粉、45份β-石膏粉和5份纳米玻璃纤维加入130份水中，分散均匀后于微波频率2450MHz、功率600W下微波处理15min，然后加入9份纳米陶瓷粉和12份滑石粉，继续微波处理10min，待温度降至70℃后加入6份活性炭、10份羧甲基壳聚糖和4份瓜尔豆胶，保温搅拌20min，最后经冷冻干燥后粉碎成粉末。
实施例2
(1)向75份聚合松香中加入8份纳米氧化铝和45份正丁醇，混合均匀后于微波频率2450MHz、功率600W下微波处理15min，待温度降至80℃后再加入18份双马来酰亚胺和12份聚丙烯酸钠，保温搅拌30min，即得物料I；
(2)将15份改性淀粉加入65份水中打浆，待形成均匀浆体后加入8份棕榈蜡和7份田菁胶，升温至70℃保温搅拌20min，即得物料II；
(3)向物料II中加入13份煅烧高岭土和10份石膏粉，于超声频率40kHz、温度50℃下超声处理20min，然后加入物料I、12份麦芽糊精、5份二月桂酸二丁基锡和3份枸橼酸钠，继续超声处理15min，即得粘结剂。
改性淀粉的制备：先将95份植物淀粉加入240份水中打浆，待形成均匀浆体后加入18份茶多酚和11份纳米氧化铝，然后于超声频率40kHz、温度55℃下超声处理30min，再向处理液中加入7份三聚磷酸钠和9份柠檬酸，研磨15min后加入12份芒硝，混合均匀后于0-5℃下放置12h，最后经冷冻干燥后粉碎成粉末。
石膏粉的制备：先将65份α-石膏粉、45份β-石膏粉和6份纳米玻璃纤维加入150份水中，分散均匀后于微波频率2450MHz、功率600W下微波处理15min，然后加入10份纳米陶瓷粉和13份滑石粉，继续微波处理10min，待温度降至70℃后加入8份活性炭、13份羧甲基壳聚糖和4份瓜尔豆胶，保温搅拌20min，最后经冷冻干燥后粉碎成粉末。
实施例3
(1)向80份聚合松香中加入10份纳米氧化铝和50份正丁醇，混合均匀后于微波频率2450MHz、功率600W下微波处理15min，待温度降至80℃后再加入18份双马来酰亚胺和10份聚丙烯酸钠，保温搅拌30min，即得物料I；
(2)将18份改性淀粉加入70份水中打浆，待形成均匀浆体后加入9份棕榈蜡和6份田菁胶，升温至70℃保温搅拌20min，即得物料II；
(3)向物料II中加入12份煅烧高岭土和12份石膏粉，于超声频率40kHz、温度50℃下超声处理20min，然后加入物料I、13份麦芽糊精、5份二月桂酸二丁基锡和4份枸橼酸钠，继续超声处理15min，即得粘结剂。
改性淀粉的制备：先将100份植物淀粉加入250份水中打浆，待形成均匀浆体后加入20份茶多酚和11份纳米氧化铝，然后于超声频率40kHz、温度60℃下超声处理30min，再向处理液中加入8份三聚磷酸钠和10份柠檬酸，研磨20min后加入10份芒硝，混合均匀后于0-5℃下放置12h，最后经冷冻干燥后粉碎成粉末。
石膏粉的制备：先将70份α-石膏粉、50份β-石膏粉和6份纳米玻璃纤维加入150份水中，分散均匀后于微波频率2450MHz、功率600W下微波处理15min，然后加入10份纳米陶瓷粉和15份滑石粉，继续微波处理10min，待温度降至70℃后加入7份活性炭、15份羧甲基壳聚糖和5份瓜尔豆胶，保温搅拌20min，最后经冷冻干燥后粉碎成粉末。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.一种阀门消失模铸造用泡沫塑料粘结剂，其特征在于，由如下重量份数的原料制成：
聚合松香70-80份、双马来酰亚胺15-20份、改性淀粉13-18份、煅烧高岭土11-15份、聚丙烯酸钠10-13份、麦芽糊精10-13份、石膏粉8-12份、纳米氧化铝6-10份、棕榈蜡6-10份、田菁胶5-8份、二月桂酸二丁基锡3-6份、枸橼酸钠2-4份、正丁醇40-50份、水60-70份；
其制备方法如下：
(1)向聚合松香中加入纳米氧化铝和正丁醇，混合均匀后于微波频率2450MHz、功率600W下微波处理15-20min，待温度降至70-80℃后再加入双马来酰亚胺和聚丙烯酸钠，保温搅拌20-30min，即得物料I；
(2)将改性淀粉加入水中打浆，待形成均匀浆体后加入棕榈蜡和田菁胶，升温至60-70℃保温搅拌15-20min，即得物料II；
(3)向物料II中加入煅烧高岭土和石膏粉，于超声频率40kHz、温度40-50℃下超声处理15-20min，然后加入物料I、麦芽糊精、二月桂酸二丁基锡和枸橼酸钠，继续超声处理10-15min，即得粘结剂。
2.根据权利要求1所述的阀门消失模铸造用泡沫塑料粘结剂，其特征在于，所述改性淀粉由如下重量份数的原料制成：植物淀粉90-100份、茶多酚15-20份、纳米氧化铝8-12份、芒硝10-13份、三聚磷酸钠5-8份、柠檬酸7-10份、水200-250份，其制备方法为：先将植物淀粉加入水中打浆，待形成均匀浆体后加入茶多酚和纳米氧化铝，然后于超声频率40kHz、温度50-60℃下超声处理25-30min，再向处理液中加入三聚磷酸钠和柠檬酸，研磨15-20min后加入芒硝，混合均匀后于0-5℃下放置8-12h，最后经冷冻干燥后粉碎成粉末。
3.根据权利要求1所述的阀门消失模铸造用泡沫塑料粘结剂，其特征在于，所述石膏粉由如下重量份数的原料制成：α-石膏粉60-70份、β-石膏粉40-50份、纳米陶瓷粉8-11份、纳米玻璃纤维4-7份、滑石粉10-15份、羧甲基壳聚糖10-15份、活性炭6-9份、瓜尔豆胶3-5份、水120-150份，其制备方法为：先将α-石膏粉、β-石膏粉和纳米玻璃纤维加入水中，分散均匀后于微波频率2450MHz、功率600W下微波处理15-20min，然后加入纳米陶瓷粉和滑石粉，继续微波处理5-10min，待温度降至60-70℃后加入活性炭、羧甲基壳聚糖和瓜尔豆胶，保温搅拌15-20min，最后经冷冻干燥后粉碎成粉末。
CN201510692773.5A 2015-10-21 2015-10-21 一种阀门消失模铸造用泡沫塑料粘结剂 Pending CN105290312A (zh)