CN105583357A - 一种泵体铸造用消失模涂料 - Google Patents
一种泵体铸造用消失模涂料 Download PDFInfo
- Publication number
- CN105583357A CN105583357A CN201610074601.6A CN201610074601A CN105583357A CN 105583357 A CN105583357 A CN 105583357A CN 201610074601 A CN201610074601 A CN 201610074601A CN 105583357 A CN105583357 A CN 105583357A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- add
- mix
- pump body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种泵体铸造用消失模涂料，涉及泵铸造技术领域，由如下重量份数的原料制成：环氧树脂50-60份、松香树脂20-30份、矿石粉12-17份、棕榈油10-15份、白炭黑10-15份、椰糠8-12份、石棉粉6-10份、米糠蜡6-10份、聚丙烯酸钠5-8份、纳米二氧化钛3-6份、过氧化二异丙苯3-6份、附着力促进剂2-4份、异丙醇30-40份、水250-300份。本发明所制涂料附着力强，在填砂震动时不会出现涂层剥落现象，并且膨胀系数小，与高温金属液体接触时不会受热膨胀而导致泵体粘砂；涂层强度高、耐火性好且发气量小，不会造成泵体砂眼、气孔、碳渣等缺陷。
Description
技术领域：
本发明涉及泵铸造技术领域，具体涉及一种泵体铸造用消失模涂料。
背景技术：
消失模铸造，是将与铸件尺寸形状相似的石蜡或泡沫模型粘结组合成模型簇，刷涂耐火涂料并烘干后，埋在干石英砂中振动造型，在负压下浇注，使模型气化，液体金属占据模型位置，凝固冷却后形成铸件的新型铸造方法。传统的铸造涂料只是在铸件和铸型中间起到阻挡隔离作用，达到防粘砂目的，但普通铸造涂料高温下由于附着力差、强度低、耐火差、发气量大，容易造成铸件产生粘砂、砂眼、气孔、碳渣等缺陷。
发明内容：
本发明所要解决的技术问题在于提供一种附着力强、强度高、耐火性好、发气量小的泵体铸造用消失模涂料。
本发明所要解决的技术问题采用以下的技术方案来实现：
一种泵体铸造用消失模涂料，由如下重量份数的原料制成：
环氧树脂50-60份、松香树脂20-30份、矿石粉12-17份、棕榈油10-15份、白炭黑10-15份、椰糠8-12份、石棉粉6-10份、米糠蜡6-10份、聚丙烯酸钠5-8份、纳米二氧化钛3-6份、过氧化二异丙苯3-6份、附着力促进剂2-4份、异丙醇30-40份、水250-300份；
其制备方法如下：
(1)向水中加入环氧树脂、松香树脂和过氧化二异丙苯，混合均匀后于微波频率2450MHz、功率600W下微波处理10min，再加入聚丙烯酸钠和纳米二氧化钛，继续微波处理5min，即得物料I；
(2)向棕榈油中加入米糠蜡，加热至80-85℃保温混合15min，冷却至室温后再加入椰糠和异丙醇，继续保温混合10min，即得物料II；
(3)向物料I中加入物料II、矿石粉、白炭黑、石棉粉和附着力促进剂，混合均匀后加入球磨机中，球磨至细度小于30μm。
所述矿石粉由如下重量份数的原料制成：煤矸石粉20-25份、硅藻土10-15份、沸石粉8-13份、石膏粉6-11份、硬脂酸5-9份、石蜡油5-9份、纳米胶粉4-7份、氯化钠3-5份、聚丙烯酰胺2-4份、蛭石粉2-4份、氧化锌1-2份、雄黄1-2份，其制备方法为：先将煤矸石粉和硅藻土加入5倍重量乙醇中，浸泡1h后加入硬脂酸和纳米胶粉，再于微波频率2450MHz、功率600W下微波处理15min，自然冷却至室温后加入氯化钠和聚丙烯酰胺，混合均匀后置于0-5℃静置30min，过滤，滤渣经真空干燥后粉碎成粉末，然后加入沸石粉、石膏粉、石蜡油、蛭石粉、氧化锌和雄黄，充分混合均匀。
所述蛭石粉使用前需要经过预处理，其处理方法为：将100-120份蛭石粉和25-35份马来酸酐加入200-250份异丙醇中，混合物先于超声频率40kHz、功率50W下超声处理30min，再加热至回流状态保温15min，待冷却至室温后加入7-11份羧甲基纤维素钠和3-6份苏打粉，混合均匀后静置1h，然后送入真空干燥机，所得固体经粉碎机制成粉末。
本发明的有益效果是：
(1)所制涂料附着力强，在填砂震动时不会出现涂层剥落现象，并且膨胀系数小，与高温金属液体接触时不会受热膨胀而导致泵体粘砂；
(2)涂料成分稳定，不会与高温金属液体发生化学反应；
(3)涂层强度高、耐火性好且发气量小，不会造成泵体砂眼、气孔、碳渣等缺陷；
(4)制备方法简单，所用原料易得。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
(1)向250份水中加入50份环氧树脂、30份松香树脂和3份过氧化二异丙苯，混合均匀后于微波频率2450MHz、功率600W下微波处理10min，再加入7份聚丙烯酸钠和3份纳米二氧化钛，继续微波处理5min，即得物料I；
(2)向10份棕榈油中加入8份米糠蜡，加热至80-85℃保温混合15min，冷却至室温后再加入8份椰糠和30份异丙醇，继续保温混合10min，即得物料II；
(3)向物料I中加入物料II、15份矿石粉、10份白炭黑、6份石棉粉和3份附着力促进剂，混合均匀后加入球磨机中，球磨至细度小于30μm。
矿石粉的制备：先将20份煤矸石粉和10份硅藻土加入5倍重量乙醇中，浸泡1h后加入6份硬脂酸和5份纳米胶粉，再于微波频率2450MHz、功率600W下微波处理15min，自然冷却至室温后加入3份氯化钠和3份聚丙烯酰胺，混合均匀后置于0-5℃静置30min，过滤，滤渣经真空干燥后粉碎成粉末，然后加入8份沸石粉、6份石膏粉、8份石蜡油、3份蛭石粉、2份氧化锌和1份雄黄，充分混合均匀。
蛭石粉的预处理：将100份蛭石粉和25份马来酸酐加入200份异丙醇中，混合物先于超声频率40kHz、功率50W下超声处理30min，再加热至回流状态保温15min，待冷却至室温后加入8份羧甲基纤维素钠和4份苏打粉，混合均匀后静置1h，然后送入真空干燥机，所得固体经粉碎机制成粉末。
实施例2
(1)向300份水中加入60份环氧树脂、20份松香树脂和5份过氧化二异丙苯，混合均匀后于微波频率2450MHz、功率600W下微波处理10min，再加入5份聚丙烯酸钠和5份纳米二氧化钛，继续微波处理5min，即得物料I；
(2)向15份棕榈油中加入10份米糠蜡，加热至80-85℃保温混合15min，冷却至室温后再加入10份椰糠和40份异丙醇，继续保温混合10min，即得物料II；
(3)向物料I中加入物料II、12份矿石粉、12份白炭黑、8份石棉粉和4份附着力促进剂，混合均匀后加入球磨机中，球磨至细度小于30μm。
矿石粉的制备：先将25份煤矸石粉和15份硅藻土加入5倍重量乙醇中，浸泡1h后加入9份硬脂酸和4份纳米胶粉，再于微波频率2450MHz、功率600W下微波处理15min，自然冷却至室温后加入5份氯化钠和2份聚丙烯酰胺，混合均匀后置于0-5℃静置30min，过滤，滤渣经真空干燥后粉碎成粉末，然后加入10份沸石粉、8份石膏粉、5份石蜡油、4份蛭石粉、1份氧化锌和2份雄黄，充分混合均匀。
蛭石粉的预处理：将110份蛭石粉和30份马来酸酐加入250份异丙醇中，混合物先于超声频率40kHz、功率50W下超声处理30min，再加热至回流状态保温15min，待冷却至室温后加入10份羧甲基纤维素钠和6份苏打粉，混合均匀后静置1h，然后送入真空干燥机，所得固体经粉碎机制成粉末。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.一种泵体铸造用消失模涂料，其特征在于，由如下重量份数的原料制成：
环氧树脂50-60份、松香树脂20-30份、矿石粉12-17份、棕榈油10-15份、白炭黑10-15份、椰糠8-12份、石棉粉6-10份、米糠蜡6-10份、聚丙烯酸钠5-8份、纳米二氧化钛3-6份、过氧化二异丙苯3-6份、附着力促进剂2-4份、异丙醇30-40份、水250-300份；
其制备方法如下：
(1)向水中加入环氧树脂、松香树脂和过氧化二异丙苯，混合均匀后于微波频率2450MHz、功率600W下微波处理10min，再加入聚丙烯酸钠和纳米二氧化钛，继续微波处理5min，即得物料I；
(2)向棕榈油中加入米糠蜡，加热至80-85℃保温混合15min，冷却至室温后再加入椰糠和异丙醇，继续保温混合10min，即得物料II；
(3)向物料I中加入物料II、矿石粉、白炭黑、石棉粉和附着力促进剂，混合均匀后加入球磨机中，球磨至细度小于30μm。
2.根据权利要求1所述的泵体铸造用消失模涂料，其特征在于，所述矿石粉由如下重量份数的原料制成：煤矸石粉20-25份、硅藻土10-15份、沸石粉8-13份、石膏粉6-11份、硬脂酸5-9份、石蜡油5-9份、纳米胶粉4-7份、氯化钠3-5份、聚丙烯酰胺2-4份、蛭石粉2-4份、氧化锌1-2份、雄黄1-2份，其制备方法为：先将煤矸石粉和硅藻土加入5倍重量乙醇中，浸泡1h后加入硬脂酸和纳米胶粉，再于微波频率2450MHz、功率600W下微波处理15min，自然冷却至室温后加入氯化钠和聚丙烯酰胺，混合均匀后置于0-5℃静置30min，过滤，滤渣经真空干燥后粉碎成粉末，然后加入沸石粉、石膏粉、石蜡油、蛭石粉、氧化锌和雄黄，充分混合均匀。
3.根据权利要求2所述的泵体铸造用消失模涂料，其特征在于：所述蛭石粉使用前需要经过预处理，其处理方法为：将100-120份蛭石粉和25-35份马来酸酐加入200-250份异丙醇中，混合物先于超声频率40kHz、功率50W下超声处理30min，再加热至回流状态保温15min，待冷却至室温后加入7-11份羧甲基纤维素钠和3-6份苏打粉，混合均匀后静置1h，然后送入真空干燥机，所得固体经粉碎机制成粉末。