CN105273359B - High silica containing Mo-phenolic resin of carbon residue and preparation method thereof - Google Patents
High silica containing Mo-phenolic resin of carbon residue and preparation method thereof Download PDFInfo
- Publication number
- CN105273359B CN105273359B CN201510577652.6A CN201510577652A CN105273359B CN 105273359 B CN105273359 B CN 105273359B CN 201510577652 A CN201510577652 A CN 201510577652A CN 105273359 B CN105273359 B CN 105273359B
- Authority
- CN
- China
- Prior art keywords
- phenolic resin
- phenol
- carbon residue
- preparation
- silica containing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of high silica containing Mo-phenolic resin of carbon residue and preparation method thereof, the molecular structure of the Mo-phenolic resin is shown in formula I:
Description
Technical field
The present invention relates to technical field of chemistry, more particularly to field of material technology.
Background technology
Phenolic resin poor heat resistance, decomposed seriously in 500 DEG C or so of temperature ranges, matter carbon easily aoxidizes under high temperature
Decarburized layer is formed, which has limited its application on refractory material.Certain metallic element is introduced in high-polymer molecular chain, makes it
It is present in the chemical bond of high bond energy in phenolic resin molecular backbone, is one of effective way for improving phenolic resin heat resistance.
It is domestic successively to have developed boron bakelite resin, W-phenolic resin and Mo-phenolic resin.Wherein Mo-phenolic resin can be used as high temperature ablation
Material, friction material, adhesive etc., application prospect is extensive.However, Mo-phenolic resin is present, fragility is big, impact strength is weak
Shortcoming needs to overcome.
The content of the invention
First aspect technical problem to be solved by this invention is to provide a kind of high carbon residue Mo-phenolic resin containing silica.
In order to solve the above-mentioned technical problem, the present invention provides a kind of high silica containing Mo-phenolic resin of carbon residue, and it is special
Sign is that the molecular structure of the Mo-phenolic resin is shown in formula I:
Wherein, the n is 2-12 natural number, and preferably n is 3,4,5,6,7, and more preferably n is 4,5.
In the preferred technical solution of the present invention, described silica is nano silicon.
In the preferred technical solution of the present invention, it is 0.5- that described silica, which accounts for Mo-phenolic resin total amount percentage,
5wt%.
The second aspect of the present invention is to provide the preparation method of the above-mentioned silica containing Mo-phenolic resin of high carbon residue, and it is wrapped
Include following steps:
(1) SiO 2 powder, phenol, formaldehyde are placed in reaction bulb, the mol ratio 1 of phenol and formaldehyde:0.6~0.9,
Heating allows phenol to be completely dissolved, and stirring three is well mixed, and adds acidic catalyst, adjusts pH value 1.5-3.0, continues to heat
To 60-85 DEG C, insulated and stirred reaction 0.5-3 hours, phenol under acidic catalyst, occurs polycondensation reaction and forms hydroxyl first with formaldehyde
Base phenol homologue,
(2) molybdic acid obtains Mo-phenolic resin with hydroxymethyl phenol generation esterification:Molybdic acid is added in system, molybdic acid adds
Amount accounts for Mo-phenolic resin percentage by weight 2-12%, temperature rising reflux 4-5 hours, neutralization reaction system, last decompression dehydration, produces
To the Mo-phenolic resin containing Nano particles of silicon dioxide.
In the preferred technical solution of the present invention, the acid catalyst that adds in the step (1) include organic acid catalyst and
Inorganic acid catalyst.Organic acid catalyst includes but is not limited to acetic acid;Inorganic acid catalyst includes but is not limited to hydrochloric acid, nitric acid,
Sulfuric acid.
In the preferred technical solution of the present invention, described SiO 2 powder is nanometer silicon dioxide material.
In the preferred technical solution of the present invention, in the step (1), reaction system regulation to pH value to 2.0 continues to add
Heat to 70 DEG C, react 1 hour by insulated and stirred.
In the preferred technical solution of the present invention, the mol ratio of phenol and formaldehyde is preferably 1:0.75~0.82.
The advantages of the present invention are:
Mo-phenolic resin of silica of the present invention and preparation method thereof can make nano material introducing phenolic resin
The composite of standby excellent performance.Nano silicon because specific surface area is big, activity is high, can exist with phenolic resin as matrix resin compared with
Strong active force, toughness reinforcing enhancing effect is obvious, while also significantly improves the heat resistance of resin.
High carbon residue Mo-phenolic resin containing silica high temperature resistant that the present invention is prepared, resistance to ablation, carbon forming rate are high, its machine
Tool intensity is high, process industrial art performance is good;Have broad application prospects:It is more to can be applied not only to casting, building materials, other resins
Functional modifier, apply also for making rocket, the contour scientific and technological thermally protective materials of guided missile.
Embodiment
To further understand the present invention, preferred scheme of the present invention is described with reference to specific embodiment, but should
Work as understanding, these descriptions are simply further explanation the features and advantages of the present invention, rather than the limit to the claims in the present invention
System.
Embodiment 1:
The 40-50 nano silicons, 282 parts by weight of phenol, 68 parts by weight of 1.56 parts by weight are contained to 37% formalin
Solution is placed in the three-necked flask with condensing unit.Heating allows phenol to be completely dissolved, and stirring three is well mixed, and is adjusted with hydrochloric acid
PH value 1.8 is saved, continues to be heated to 70 DEG C, insulated and stirred 1 hour.
Second step molybdic acid occurs esterification with hydroxymethyl phenol and obtains Mo-phenolic resin:9.72 parts by weight molybdic acids are added, are risen
Temperature backflow 4-5 hours, with sodium hydrate aqueous solution neutralization reaction system, last decompression dehydration, obtain containing silica dioxide nano particle
The Mo-phenolic resin of son 0.5%.
Embodiment 2:
3.12 parts by weight 40-50 nano silicons, 282 parts by weight of phenol, 68 parts by weight are water-soluble containing 37% formaldehyde
Liquid is placed in the three-necked flask with condensing unit.Heating allows phenol to be completely dissolved, and stirring three is well mixed, and is adjusted with hydrochloric acid
PH value 2, continue to be heated to 70 DEG C, insulated and stirred 1 hour.
Second step molybdic acid occurs esterification with hydroxymethyl phenol and obtains Mo-phenolic resin:6.48 parts by weight molybdic acids are added, are risen
Temperature backflow 4-5 hours, with sodium hydrate aqueous solution neutralization reaction system, last decompression dehydration, obtain containing silica dioxide nano particle
The Mo-phenolic resin of son 1%.
Sample carbon forming rate prepared by testing example 1,2, to being consolidated with containing 10% hexamethylene tetramine Mo-phenolic resin
Change and carry out heat analysis, and contrasted with phenolic resin, it is as a result as shown in the table;
From the results, it was seen that high carbon residue Mo-phenolic resin containing Nano particles of silicon dioxide thermal decomposition temperature prepared by the present invention
Degree, Residual carbon are obviously improved.It can be dissolved in the organic solvents such as acetone, alcohol, high temperature resistant, resistance to ablation, carbon forming rate after solidification
Height, its high mechanical strength, casting, building materials, other resin multifunctional modification agent are can be applied not only to, can also be applied to make fire
The contour scientific and technological thermally protective materials of arrow, guided missile.
The technology contents and technical characteristic of the present invention have revealed that as above, but those skilled in the art still may base
Make a variety of replacements and modification without departing substantially from spirit of the present invention, therefore, the scope of the present invention in teachings of the present invention and announcement
The content disclosed in embodiment should be not limited to, and various replacements and modification without departing substantially from the present invention should be included, and is this patent Shen
Please claim covered.
Claims (7)
1. a kind of preparation method of the silica containing Mo-phenolic resin of high carbon residue, it is characterised in that it comprises the following steps:
(1) SiO 2 powder, phenol, formaldehyde are placed in reaction bulb, the mol ratio 1 of phenol and formaldehyde:0.6~0.9, heating
Phenol is allowed to be completely dissolved, stirring three is well mixed, and adds acidic catalyst, adjusts pH value 1.5-3.0, continues to be heated to
60-85 DEG C, insulated and stirred reaction 0.5-3 hours, phenol under acidic catalyst, occurs polycondensation reaction and forms methylol with formaldehyde
Phenol homologue,
(2) molybdic acid obtains Mo-phenolic resin with hydroxymethyl phenol generation esterification:Molybdic acid is added in system, molybdic acid addition accounts for
Mo-phenolic resin percentage by weight 2-12%, temperature rising reflux 4-5 hours, neutralization reaction system, last decompression dehydration, that is, obtain height
The silica containing Mo-phenolic resin of carbon residue.
2. preparation method according to claim 1, it is characterised in that state the acid catalyst added in step (1) and include
Machine acid catalyst and inorganic acid catalyst.
3. preparation method according to claim 1, it is characterised in that in the step (1), pH is arrived into reaction system regulation
It is worth 2.0, continues to be heated to 70 DEG C, insulated and stirred is reacted 1 hour.
4. preparation method according to claim 1, it is characterised in that in the step (1), the mol ratio of phenol and formaldehyde
For 1:0.75~0.82.
5. the silica containing Mo-phenolic resin of high carbon residue that a kind of the method as described in claim 1 is prepared, its feature
It is, the molecular structure of the Mo-phenolic resin is shown in formula I:
Wherein, the n is 2-12 natural number;It is 0.5-5wt% that described silica, which accounts for Mo-phenolic resin total amount percentage,.
6. the silica containing Mo-phenolic resin of high carbon residue according to claim 5, it is characterised in that the n is 3,4,
5,6,7.
7. the silica containing Mo-phenolic resin of high carbon residue according to claim 5, it is characterised in that described titanium dioxide
Silicon is nano silicon.