CN105272312A - 一种尖晶石结合感应电炉长寿命炉衬材料 - Google Patents
一种尖晶石结合感应电炉长寿命炉衬材料 Download PDFInfo
- Publication number
- CN105272312A CN105272312A CN201510770314.4A CN201510770314A CN105272312A CN 105272312 A CN105272312 A CN 105272312A CN 201510770314 A CN201510770314 A CN 201510770314A CN 105272312 A CN105272312 A CN 105272312A
- Authority
- CN
- China
- Prior art keywords
- parts
- electric smelting
- spinel
- particle
- lining material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种尖晶石结合感应电炉长寿命炉衬材料，一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料配比而成的：3-5mm的电熔白钢玉颗粒10-25份、3-5mm的电熔富铝尖晶石颗粒10-30份、0-1mm的电熔大结晶镁砂颗粒5-10份、0-1mm的电熔白钢玉颗粒10-20份、0-1mm的电熔富铝尖晶石颗粒10-25、200目的电熔白钢玉细粉10-15份、200目的电熔富铝尖晶石细粉10-20份、200目的电熔大结晶镁砂细粉10-15份、硅线石2-8份、外加剂0.5-1.5份、氧化锆细粉1-5份，本发明一种尖晶石结合感应电炉长寿命炉衬材料，它的特殊设计使得其在较低的温度下，热面形成强度极高的釉面，同时在极高温度下，又拥有良好的松散背衬，因此具有优良的抗击渣以及抗金属的侵蚀的能力，从而能够最大限度的防止钢水穿刺和渗漏。
Description
【技术领域】
本发明涉及炉衬材料的技术领域，特别是一种尖晶石结合感应电炉长寿命炉衬材料的技术领域。
【背景技术】
目前铸造行业中频感应电炉炉衬，主要采用的是石英砂炉衬和镁砂炉衬。对于石英砂炉衬材料，在1600℃温度下耐火材料颗粒之间就会出现液相，因此理论上它只能用于熔化铸铁和低熔点有色金属。同时，从相图上也可以看到，当熔体中含有锰和镍时，要避免使用石英砂炉衬，否则，一旦出现过热现象，会产生粘稠的氧化渣，并黏挂在炉衬上，导致频繁更换炉衬。此外，从安全和健康角度来讲，石英砂会严重影响人的健康；对于镁砂炉衬，由于矿源的因素，其物理性能和化学性能存在很大的差异，而这些物理性能和化学性能能将会严重影响到炉衬寿命的稳定性。此外使用镁砂炉衬时频繁的补炉，不仅增加劳动强度，而且过多侵蚀引起的渣子，容易导致铸件的夹杂，影响到铸件的成品率。
【发明内容】
本发明的目的就是解决现有技术中的问题，提出一种尖晶石结合感应电炉长寿命炉衬材料，它的特殊设计使得其在较低的温度下，热面形成强度极高的釉面，同时在极高温度下，又拥有良好的松散背衬，因此具有优良的抗击渣以及抗金属的侵蚀的能力，从而能够最大限度的防止刚水穿刺和渗漏。
为实现上述目的，本发明提出了一种尖晶石结合感应电炉长寿命炉衬材料，其特征在于：一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料配比而成的：3-5mm的电熔白刚玉颗粒10-25份、3-5mm的电熔富铝尖晶石颗粒10-30份、0-1mm的电熔大结晶镁砂颗粒5-10份、0-1mm的电熔白刚玉颗粒10-20份、0-1mm的电熔富铝尖晶石颗粒10-25、200目的电熔白刚玉细粉10-15份、200目的电熔富铝尖晶石细粉10-20份、200目的电熔大结晶镁砂细粉10-15份、硅线石2-8份、外加剂0.5-1.5份、氧化锆细粉1-5份。
作为优选，一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料制备而成的，3-5mm的电熔白刚玉颗粒15份、3-5mm的电熔富铝尖晶石颗粒12.3份、0-1mm的电熔大结晶镁砂颗粒5.6份、0-1mm的电熔白刚玉颗粒11份、0-1mm的电熔富铝尖晶石颗粒15.8份、200目的电熔白刚玉细粉12份、200目的电熔富铝尖晶石细粉15.6份、200目的电熔大结晶镁砂细粉13份、硅线石3份、外加剂0.8份、氧化锆细粉2.3份。
作为优选，一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料制备而成的，3-5mm的电熔白刚玉颗粒20份、3-5mm的电熔富铝尖晶石颗粒25份、0-1mm的电熔大结晶镁砂颗粒6.8份、0-1mm的电熔白刚玉颗粒15份、0-1mm的电熔富铝尖晶石颗粒16份、200目的电熔白刚玉细粉11.6份、200目的电熔富铝尖晶石细粉17.3份、200目的电熔大结晶镁砂细粉11.5份、硅线石4.5份、外加剂1.2份、氧化锆细粉3.5份。
作为优选，一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料制备而成的，3-5mm的电熔白刚玉颗粒22.3份、3-5mm的电熔富铝尖晶石颗粒28.5份、0-1mm的电熔大结晶镁砂颗粒8份、0-1mm的电熔白刚玉颗粒15.6份、0-1mm的电熔富铝尖晶石颗粒18份、200目的电熔白刚玉细粉12份、200目的电熔富铝尖晶石细粉15份、200目的电熔大结晶镁砂细粉12.3份、硅线石6.8份、外加剂1.2份、氧化锆细粉3份。
作为优选，所述外加剂为硼酸、硼酐、固体水玻璃中的一种或两种及以上的任意比混合物。
本发明的有益效果：本发明一种尖晶石结合感应电炉长寿命炉衬材料，它的特殊设计使得其在较低的温度下，热面形成强度极高的釉面，同时在极高温度下，又拥有良好的松散背衬，因此具有优良的抗击渣以及抗金属的侵蚀的能力，从而能够最大限度的防止刚水穿刺和渗漏。
【具体实施方式】
实施例一
一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料制备而成的，3-5mm的电熔白刚玉颗粒15份、3-5mm的电熔富铝尖晶石颗粒12.3份、0-1mm的电熔大结晶镁砂颗粒5.6份、0-1mm的电熔白刚玉颗粒11份、0-1mm的电熔富铝尖晶石颗粒15.8份、200目的电熔白刚玉细粉12份、200目的电熔富铝尖晶石细粉15.6份、200目的电熔大结晶镁砂细粉13份、硅线石3份、外加剂0.8份、氧化锆细粉2.3份；
实施例二
一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料制备而成的，3-5mm的电熔白刚玉颗粒20份、3-5mm的电熔富铝尖晶石颗粒25份、0-1mm的电熔大结晶镁砂颗粒6.8份、0-1mm的电熔白刚玉颗粒15份、0-1mm的电熔富铝尖晶石颗粒16份、200目的电熔白刚玉细粉11.6份、200目的电熔富铝尖晶石细粉17.3份、200目的电熔大结晶镁砂细粉11.5份、硅线石4.5份、外加剂1.2份、氧化锆细粉3.5份；
实施例三
一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料制备而成的，3-5mm的电熔白刚玉颗粒22.3份、3-5mm的电熔富铝尖晶石颗粒28.5份、0-1mm的电熔大结晶镁砂颗粒8份、0-1mm的电熔白刚玉颗粒15.6份、0-1mm的电熔富铝尖晶石颗粒18份、200目的电熔白刚玉细粉12份、200目的电熔富铝尖晶石细粉15份、200目的电熔大结晶镁砂细粉12.3份、硅线石6.8份、外加剂1.2份、氧化锆细粉3份。
上述实施例是对本发明的说明，不是对本发明的限定，任何对本发明简单变换后的方案均属于本发明的保护范围。
Claims (5)
1.一种尖晶石结合感应电炉长寿命炉衬材料，其特征在于，一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料配比而成的：3-5mm的电熔白刚玉颗粒10-25份、3-5mm的电熔富铝尖晶石颗粒10-30份、0-1mm的电熔大结晶镁砂颗粒5-10份、0-1mm的电熔白刚玉颗粒10-20份、0-1mm的电熔富铝尖晶石颗粒10-25、200目的电熔白刚玉细粉10-15份、200目的电熔富铝尖晶石细粉10-20份、200目的电熔大结晶镁砂细粉10-15份、硅线石2-8份、外加剂0.5-1.5份、氧化锆细粉1-5份。
2.如权利要求1所述一种尖晶石结合感应电炉长寿命炉衬材料，其特征在于：一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料制备而成的，3-5mm的电熔白刚玉颗粒15份、3-5mm的电熔富铝尖晶石颗粒12.3份、0-1mm的电熔大结晶镁砂颗粒5.6份、0-1mm的电熔白刚玉颗粒11份、0-1mm的电熔富铝尖晶石颗粒15.8份、200目的电熔白刚玉细粉12份、200目的电熔富铝尖晶石细粉15.6份、200目的电熔大结晶镁砂细粉13份、硅线石3份、外加剂0.8份、氧化锆细粉2.3份。
3.如权利要求1所述一种尖晶石结合感应电炉长寿命炉衬材料，其特征在于：一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料制备而成的，3-5mm的电熔白刚玉颗粒20份、3-5mm的电熔富铝尖晶石颗粒25份、0-1mm的电熔大结晶镁砂颗粒6.8份、0-1mm的电熔白刚玉颗粒15份、0-1mm的电熔富铝尖晶石颗粒16份、200目的电熔白刚玉细粉11.6份、200目的电熔富铝尖晶石细粉17.3份、200目的电熔大结晶镁砂细粉11.5份、硅线石4.5份、外加剂1.2份、氧化锆细粉3.5份。
4.如权利要求1所述一种尖晶石结合感应电炉长寿命炉衬材料，其特征在于：一种尖晶石结合感应电炉长寿命炉衬材料是按如下重量份的原料制备而成的，3-5mm的电熔白刚玉颗粒22.3份、3-5mm的电熔富铝尖晶石颗粒28.5份、0-1mm的电熔大结晶镁砂颗粒8份、0-1mm的电熔白刚玉颗粒15.6份、0-1mm的电熔富铝尖晶石颗粒18份、200目的电熔白刚玉细粉12份、200目的电熔富铝尖晶石细粉15份、200目的电熔大结晶镁砂细粉12.3份、硅线石6.8份、外加剂1.2份、氧化锆细粉3份。
5.如权利要求1所述一种尖晶石结合感应电炉长寿命炉衬材料，其特征在于：所述外加剂为硼酸、硼酐、固体水玻璃中的一种或两种及以上的任意比混合物。