CN105272136A - 一种复合代木材料及其制备方法 - Google Patents

一种复合代木材料及其制备方法 Download PDF

Info

Publication number
CN105272136A
CN105272136A CN201510813538.9A CN201510813538A CN105272136A CN 105272136 A CN105272136 A CN 105272136A CN 201510813538 A CN201510813538 A CN 201510813538A CN 105272136 A CN105272136 A CN 105272136A
Authority
CN
China
Prior art keywords
oxychloride cement
magnesium
parts
magnesium oxychloride
composite wood
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510813538.9A
Other languages
English (en)
Inventor
常胜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510813538.9A priority Critical patent/CN105272136A/zh
Publication of CN105272136A publication Critical patent/CN105272136A/zh
Pending legal-status Critical Current

Abstract

<b>一种复合代木材料，</b>它由以下原材料按重量比例配合组成：废纸30-60份、氯氧镁水泥40-70份、和氯氧镁水泥改性剂1.8-3.3份，主要通过以下步骤实现：步骤1：准备废纸30-60份、氯氧镁水泥40-70份、氯氧镁水泥改性剂1.8-3.3份，步骤2：将将氯化镁用水化开，加入废纸打成浆状，分别再加入氧化镁、氯氧镁水泥改性剂搅拌成泥状，步骤3入模凝固成型、脱模、养护即成，本发明完全改变了氯氧镁水泥的硬脆特性，扩大了其使用范围，具有低碳环保、可锯、可刨、可钉、可钻、可雕刻、可粘贴防水防火造价低廉等优点。

Description

一种复合代木材料及其制备方法
技术领域
本发明涉及一种材料及其制备方法领域，特别涉及一种复合代木材料及其制备方法。
背景技术
现有的建筑代木材料大都通过是木屑或塑钢制成,在生产过程中加入大量有机化工产品造成新装修的房子里一般甲醛、苯、氨、等有害气体都会超标，同时同时还消耗大量木材,非常不环保。
氯氧镁水泥是一种特殊品种水泥，它以氧化镁为主要成分，人们习惯上又称为镁氧水泥，人们也习惯称之为菱镁胶凝材料、菱镁水泥，人们又用玻璃纤维来增强氯氧镁水泥制得无机复合材料，将此称为无机玻璃钢，至此氯氧镁水泥又有了新的称呼即无机玻璃钢，镁水泥具有高强度镁水泥可以轻易达到62.5MPa，高耐磨他的耐磨性是普通硅酸盐水泥的三倍，耐高温、低温，轻质低密度，快凝，高光泽，良好的抗渗性，另外它还具有与木屑等有机物良好的粘接性，正是因为它的这这些特性，人们常用它加入木屑等有机物生产入装饰板、家具等代木节木材料，但是由于无机材料都有的硬脆特性，使其应用受到限制。
发明内容
为解决上述问题，本发明的目的是要提供一种低碳环保、造价低廉、无毒安全、防水防火、可锯、可刨、可钉、可钻、可雕刻、可粘贴的一种复合代木材料及其制备方法。
本发明采用以下技术方案：一种复合代木材料，它由以下原材料按重量比例配合组成：废纸30-60份、氯氧镁水泥40-70份、和氯氧镁水泥改性剂1.8-3.3份。
所述的氯氧镁水泥改性剂由磷酸和硫酸亚铁组成，所述的磷酸和硫酸亚铁的重量比例配比为0.8-1.3比1-2。
一种复合代木材料的制备方法,主要通过以下步骤实现：
步骤1准备废纸30-60份、氯氧镁水泥40-70份、氯氧镁水泥改性剂1.8-3.3份，
步骤2将将氯化镁用水化开，加入废纸打成浆状，分别再加入氧化镁、氯氧镁水泥改性剂搅拌成泥状，
步骤3入模凝固成型、脱模、养护即成。
本发明的有益效果是：本发明通过在氯氧镁水泥内加入废纸打成的浆，使其制品完全改变了氯氧镁水泥的硬脆特性，扩大了其使用范围，并且实现废纸资源的综合利用，能直接模具成型，使其无需贵重设备即可实现规模化生产，具有低碳环保、可锯、可刨、可钉、可钻、可雕刻、可粘贴防水防火造价低廉等优点。
具体实施方式
下面对本发明的实施方法做进一步说明
步骤1准备废纸30-60份、氯氧镁水泥40-70份、氯氧镁水泥改性剂1.8-3.3份，
步骤2将将氯化镁用水化开，加入废纸打成浆状，分别再加入氧化镁、氯氧镁水泥改性剂搅拌成泥状，
步骤3入模凝固成型、脱模、养护即成。

Claims (3)

1.一种复合代木材料，其特征在于它由以下原材料按重量比例配合组成：废纸30-60份、氯氧镁水泥40-70份、氯氧镁水泥改性剂1.8-3.3份。
2.如权利要求1所述的一种复合代木材料,其特征在于：所述的氯氧镁水泥改性剂由磷酸和硫酸亚铁组成，所述的磷酸和硫酸亚铁的重量比例配比为0.8-1.3比1-2。
3.如权利要求1所述的一种复合代木材料的制备方法,其特征在于：主要通过以下步骤实现：
步骤1准备废纸30-60份、氯氧镁水泥40-70份、氯氧镁水泥改性剂1.8-3.3份，
步骤2将将氯化镁用水化开，加入废纸打成浆状，分别再加入氧化镁、氯氧镁水泥改性剂搅拌成泥状，
步骤3入模凝固成型、脱模、养护即成。
CN201510813538.9A 2015-11-23 2015-11-23 一种复合代木材料及其制备方法 Pending CN105272136A (zh)