CN105271989A - 一种防火保温砂浆及其制备方法 - Google Patents
一种防火保温砂浆及其制备方法 Download PDFInfo
- Publication number
- CN105271989A CN105271989A CN201510640572.0A CN201510640572A CN105271989A CN 105271989 A CN105271989 A CN 105271989A CN 201510640572 A CN201510640572 A CN 201510640572A CN 105271989 A CN105271989 A CN 105271989A
- Authority
- CN
- China
- Prior art keywords
- thermal insulation
- fireproof thermal
- mortar
- insulation mortar
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防火保温砂浆及其制备方法，由以下原料组成水泥，陶瓷碎片，玻璃碎片，硅灰石，改性粉煤灰，砂，琼脂粉，改性淀粉醚，羟丙基甲基纤维醚，聚乙烯醇和消泡剂；制备方法为将满足条件的原料混合后在一定条件下加入相应份量的水，搅拌即得。本发明相比现有技术具有以下优点：通过优化砂浆各原料间的配比，使其协同作用，使所得砂浆具有较好的耐候性和耐火性，提高砂浆的致密性能和紧实程度，吸水率≤4%，使其具有较好的保温效果和抗老化性能，施工方便，凝结时间可控制在2-4小时之间，提高了施工效率。
Description
技术领域
本发明属于建筑化学材料技术领域，具体涉及一种防火保温砂浆及其制备方法。
背景技术
砂浆在建筑工程中是用量最大，用途广泛的建筑材料之一，砂浆可把散粒材料、块状材料、片状材料等结成整体结构，也可以装饰、保护主体材料。在普通的砂浆中加入特定的功能基元，可使其不失自身的一切技术和性能的优势而具有新的功能，克服了传统砂浆功能单一、应用领域小的缺点。
为了安全以及经济的角度出发，用于建筑砂浆如果具有防火保温的功能，会相应减少额外防火材料的使用，而目前的砂浆功能较为单一，因此防火保温砂浆的研究和加工技术需要进一步的提高。
发明内容
本发明的目的是针对现有的问题，提供了一种防火保温砂浆及其制备方法。
本发明是通过以下技术方案实现的：一种防火保温砂浆，按重量份含有以下组份：水泥20-25份，陶瓷碎片5-8份，玻璃碎片4-6份，硅灰石2-4份，改性粉煤灰5-8份，砂50-60份，琼脂粉2-6份，改性淀粉醚0.1-0.3份，羟丙基甲基纤维醚0.02-0.06份，聚乙烯醇0.04-0.08份，消泡剂0.6-0.8份。
作为对上述方案的进一步改进，所述水泥为32.5或42.5的普通硅酸盐水泥。
作为对上述方案的进一步改进，所述改性粉煤灰的改性方法为：将粉煤灰进行干燥处理，使其水份＜5%；然后在60-70℃的条件下，在粉煤灰中加入20%的盐酸溶液，固液比为1:8，在恒温中搅拌2-3小时，处理完后进行过滤并用清水清洗至其PH值为中性，然后烘干备用；在40-50℃的条件下，在烘干的粉煤灰中加入10%的氢氧化钠溶液，固液比为1:6，在恒温中搅拌1-2小时，过滤后烘干即得改性粉煤灰。
作为对上述方案的进一步改进，所述砂为级配区为0.6-1.18mm的人工砂。
一种防火保温砂浆的制备方法，包括以下步骤：
（1）将陶瓷碎片，玻璃碎片，硅灰石按配比混合后再粉磨机中粉磨，粒度直径为1.2-1.5mm，然后将粉磨物放入高温炉中，先以3℃/min的速度慢速升温至600℃，保温5小时，出炉自然冷却后再放入粉磨机中粉粉磨，得到粒度直径为0.4-0.6mm的粉磨物；
（2）将其他粉状物分别粉磨至粒度直径为0.3-0.5mm；
（3）在步骤（1）中所得的粉磨物中加入其总质量2倍的水，混拌均匀后，加入水泥，改性粉煤灰和砂，在40-50℃的条件下搅拌20-40分钟；
（4）然后加入琼脂粉，改性淀粉醚，羟丙基甲基纤维素醚，聚乙烯醇和消泡剂，在常温下搅拌60-80分钟，即得防火保温砂浆。
本发明相比现有技术具有以下优点：通过优化砂浆各原料间的配比，使其协同作用，使所得砂浆具有较好的耐候性和耐火性，提高砂浆的致密性能和紧实程度，吸水率≤4%，使其具有较好的保温效果和抗老化性能，施工方便，凝结时间可控制在2-4小时之间，提高了施工效率。
具体实施方式
实施例
一种防火保温砂浆，按重量份含有以下组份：水泥22份，陶瓷碎片6份，玻璃碎片4份，硅灰石3份，改性粉煤灰6份，砂50份，琼脂粉4份，改性淀粉醚0.2份，羟丙基甲基纤维醚0.03份，聚乙烯醇0.07份，消泡剂0.7份。
其中，所述水泥为42.5的普通硅酸盐水泥。
改性粉煤灰的改性方法为：将粉煤灰进行干燥处理，使其水份＜5%；然后在60-70℃的条件下，在粉煤灰中加入20%的盐酸溶液，固液比为1:8，在恒温中搅拌2-3小时，处理完后进行过滤并用清水清洗至其PH值为中性，然后烘干备用；在40-50℃的条件下，在烘干的粉煤灰中加入10%的氢氧化钠溶液，固液比为1:6，在恒温中搅拌1-2小时，过滤后烘干即得改性粉煤灰。
其中，所述砂为级配区为0.6-1.18mm的人工砂。
一种防火保温砂浆的制备方法，包括以下步骤：
（1）将陶瓷碎片，玻璃碎片，硅灰石按配比混合后再粉磨机中粉磨，粒度直径为1.2-1.5mm，然后将粉磨物放入高温炉中，先以3℃/min的速度慢速升温至600℃，保温5小时，出炉自然冷却后再放入粉磨机中粉粉磨，得到粒度直径为0.4-0.6mm的粉磨物；
（2）将其他粉状物分别粉磨至粒度直径为0.3-0.5mm；
（3）在步骤（1）中所得的粉磨物中加入其总质量2倍的水，混拌均匀后，加入水泥，改性粉煤灰和砂，在40-50℃的条件下搅拌20-40分钟；
（4）然后加入琼脂粉，改性淀粉醚，羟丙基甲基纤维素醚，聚乙烯醇和消泡剂，在常温下搅拌60-80分钟，即得防火保温砂浆。
对本实施例中所得防火保温砂浆进行性能测试，得到以下数据：
表1
通过表1中数据可以看出，可操作时间与标准有所差距，抗压强度和软化指数与指标相近，其他指标均满足相关指标标准，说明本发明中防火保温砂浆保温性能良好，有一定的防火能力，可以广泛应用在建中工程中，由于其原料来源广泛，且价格实惠，可以有效缩减制作成本。
Claims (5)
1.一种防火保温砂浆，其特征在于，按重量份含有以下组份：水泥20-25份，陶瓷碎片5-8份，玻璃碎片4-6份，硅灰石2-4份，改性粉煤灰5-8份，砂50-60份，琼脂粉2-6份，改性淀粉醚0.1-0.3份，羟丙基甲基纤维醚0.02-0.06份，聚乙烯醇0.04-0.08份，消泡剂0.6-0.8份。
2.如权利要求1所述一种防火保温砂浆，其特征在于，所述水泥为32.5或42.5的普通硅酸盐水泥。
3.如权利要求1所述一种防火保温砂浆，其特征在于，所述改性粉煤灰的改性方法为：将粉煤灰进行干燥处理，使其水份＜5%；然后在60-70℃的条件下，在粉煤灰中加入20%的盐酸溶液，固液比为1:8，在恒温中搅拌2-3小时，处理完后进行过滤并用清水清洗至其PH值为中性，然后烘干备用；在40-50℃的条件下，在烘干的粉煤灰中加入10%的氢氧化钠溶液，固液比为1:6，在恒温中搅拌1-2小时，过滤后烘干即得改性粉煤灰。
4.如权利要求1所述一种防火保温砂浆，其特征在于，所述砂为级配区为0.6-1.18mm的人工砂。
5.根据权利要求1-4之一所述一种防火保温砂浆的制备方法，其特征在于，包括以下步骤：
（1）将陶瓷碎片，玻璃碎片，硅灰石按配比混合后再粉磨机中粉磨，粒度直径为1.2-1.5mm，然后将粉磨物放入高温炉中，先以3℃/min的速度慢速升温至600℃，保温5小时，出炉自然冷却后再放入粉磨机中粉粉磨，得到粒度直径为0.4-0.6mm的粉磨物；
（2）将其他粉状物分别粉磨至粒度直径为0.3-0.5mm；
（3）在步骤（1）中所得的粉磨物中加入其总质量2倍的水，混拌均匀后，加入水泥，改性粉煤灰和砂，在40-50℃的条件下搅拌20-40分钟；
（4）然后加入琼脂粉，改性淀粉醚，羟丙基甲基纤维素醚，聚乙烯醇和消泡剂，在常温下搅拌60-80分钟，即得防火保温砂浆。