CN104355587A - 一种轻质保温砌块及其制作方法 - Google Patents

一种轻质保温砌块及其制作方法 Download PDF

Info

Publication number
CN104355587A
CN104355587A CN201410535416.3A CN201410535416A CN104355587A CN 104355587 A CN104355587 A CN 104355587A CN 201410535416 A CN201410535416 A CN 201410535416A CN 104355587 A CN104355587 A CN 104355587A
Authority
CN
China
Prior art keywords
parts
building block
heat insulation
insulation blocks
insulation building
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410535416.3A
Other languages
English (en)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI TINGSUO ENVIRONMENTAL PROTECTION MATERIALS Co Ltd
Original Assignee
HEFEI TINGSUO ENVIRONMENTAL PROTECTION MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI TINGSUO ENVIRONMENTAL PROTECTION MATERIALS Co Ltd filed Critical HEFEI TINGSUO ENVIRONMENTAL PROTECTION MATERIALS Co Ltd
Priority to CN201410535416.3A priority Critical patent/CN104355587A/zh
Publication of CN104355587A publication Critical patent/CN104355587A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种轻质保温砌块及其制作方法，其组成原料的重量份为：陶粒95-100、沙壤土33-36、磷矿石粉20-25、木质纤维13-15、工业废油渣4-6、改性石膏粉10-12、棉子壳16-20、玉米芯8-11、木屑15-20、三氧化钨3-5、聚苯颗粒10-15、丙烯酸乳液2-4、抗氧剂10102-3、十二烷基硫酸钠1-3；本发明的保温砌块成本低廉，制成的砌块结构简单、不易老化、成本低、抗化学侵蚀性能、抗干缩、抗碳化、抗冻性能好，无材质差异所导致的使用寿命短的缺点。

Description

一种轻质保温砌块及其制作方法
 
技术领域
本发明涉及一种建材砌块，具体涉及一种轻质保温砌块及其制作方法。
 
背景技术
砌块一般是利用建筑石膏生产的新型内隔墙的墙体材料，由于其成本低、轻质、防水，并符合低碳、环保、节能降耗、制作简单、保温效果好、坚固耐用等优点被广泛应用于建筑物内隔墙，所以创造一种利用新的工业废弃物作为主原料已成为砌块发展的主导方向。
 
发明内容
本发明的目的在于提供一种轻质保温砌块及其制作方法。
本发明采用如下技术方案：
轻质保温砌块，其组成原料的重量份为：陶粒95-100、沙壤土33-36、磷矿石粉20-25、木质纤维13-15、工业废油渣4-6、改性石膏粉10-12、棉子壳16-20、玉米芯8-11、木屑15-20、三氧化钨3-5、聚苯颗粒10-15、丙烯酸乳液2-4、抗氧剂1010 2-3、十二烷基硫酸钠1-3。
轻质保温砌块，其组成原料的重量份为：陶粒95、沙壤土35、磷矿石粉22、木质纤维14、工业废油渣5、改性石膏粉11、棉子壳18、玉米芯10、木屑18、三氧化钨4、聚苯颗粒12、丙烯酸乳液3、抗氧剂1010 2.5、十二烷基硫酸钠2。
所述的改性石膏粉的制备方法为：先将石膏放入高温炉中煅烧30-40分钟，控制温度750-900℃，煅烧后取出冷却，研磨粉碎，然后加入4-5%硅烷偶联剂KH550、4-5%纳米锌粉、1-2%乌洛托品和适量去离子水，高速搅拌混合10-20分钟，过滤取滤渣，即可。
轻质保温砌块的制作方法，包括以下步骤：按组成原料的重量份称取各原料，先将各固体原料研磨粉碎，过100目筛，首先将陶粒、沙壤土、磷矿石粉混合，加入适量废机油调和成糊状，送入500-600℃的高温炉中煅烧1-2h，取出冷却，再投进球磨机磨细，将棉子壳、玉米芯、木屑燃烧成灰烬，然后与上述细粉混合，再将其他剩余组成原料加入其中混合，再经过混合模具成型、养护、脱模切割、蒸汽养护而成。
本发明的有益效果：
本发明的保温砌块成本低廉，制成的砌块结构简单、不易老化、成本低、抗化学侵蚀性能、抗干缩、抗碳化、抗冻性能好，无材质差异所导致的使用寿命短的缺点。
 
具体实施方式
实施例1：轻质保温砌块，其组成原料的重量份（kg）为：陶粒95、沙壤土35、磷矿石粉22、木质纤维14、工业废油渣5、改性石膏粉11、棉子壳18、玉米芯10、木屑18、三氧化钨4、聚苯颗粒12、丙烯酸乳液3、抗氧剂1010 2.5、十二烷基硫酸钠2。
所述的改性石膏粉的制备方法为：先将石膏放入高温炉中煅烧35分钟，控制温度850℃，煅烧后取出冷却，研磨粉碎，然后加入4.5%硅烷偶联剂KH550、4.5%纳米锌粉、1.5%乌洛托品和适量去离子水，高速搅拌混合15分钟，过滤取滤渣，即可。
轻质保温砌块的制作方法，包括以下步骤：按组成原料的重量份称取各原料，先将各固体原料研磨粉碎，过100目筛，首先将陶粒、沙壤土、磷矿石粉混合，加入适量废机油调和成糊状，送入500-600℃的高温炉中煅烧1-2h，取出冷却，再投进球磨机磨细，将棉子壳、玉米芯、木屑燃烧成灰烬，然后与上述细粉混合，再将其他剩余组成原料加入其中混合，再经过混合模具成型、养护、脱模切割、蒸汽养护而成。
本发明的保温砌块成本低廉，制成的砌块结构简单、不易老化、成本低、抗化学侵蚀性能、抗干缩、抗碳化、抗冻性能好，砌块的抗压强度为5.75MPa 以上，容重692kg/m3 左右，干燥收缩率小于0.55%，导热系数小于0.18W/m·K。

Claims (4)

1.一种轻质保温砌块，其特征在于其组成原料的重量份为：陶粒95-100、沙壤土33-36、磷矿石粉20-25、木质纤维13-15、工业废油渣4-6、改性石膏粉10-12、棉子壳16-20、玉米芯8-11、木屑15-20、三氧化钨3-5、聚苯颗粒10-15、丙烯酸乳液2-4、抗氧剂1010 2-3、十二烷基硫酸钠1-3。
2.根据权利要求1所述的轻质保温砌块，其特征在于其组成原料的重量份为：陶粒95、沙壤土35、磷矿石粉22、木质纤维14、工业废油渣5、改性石膏粉11、棉子壳18、玉米芯10、木屑18、三氧化钨4、聚苯颗粒12、丙烯酸乳液3、抗氧剂1010 2.5、十二烷基硫酸钠2。
3.根据权利要求1所述的轻质保温砌块，其特征在于，所述的改性石膏粉的制备方法为：先将石膏放入高温炉中煅烧30-40分钟，控制温度750-900℃，煅烧后取出冷却，研磨粉碎，然后加入4-5%硅烷偶联剂KH550、4-5%纳米锌粉、1-2%乌洛托品和适量去离子水，高速搅拌混合10-20分钟，过滤取滤渣，即可。
4.一种如权利要求1所述的轻质保温砌块的制作方法，其特征在于包括以下步骤：按组成原料的重量份称取各原料，先将各固体原料研磨粉碎，过100目筛，首先将陶粒、沙壤土、磷矿石粉混合，加入适量废机油调和成糊状，送入500-600℃的高温炉中煅烧1-2h，取出冷却，再投进球磨机磨细，将棉子壳、玉米芯、木屑燃烧成灰烬，然后与上述细粉混合，再将其他剩余组成原料加入其中混合，再经过混合模具成型、养护、脱模切割、蒸汽养护而成。
CN201410535416.3A 2014-10-13 2014-10-13 一种轻质保温砌块及其制作方法 Pending CN104355587A (zh)