CN105271745A - Anti-skid treatment process of floor tiles - Google Patents
Anti-skid treatment process of floor tiles Download PDFInfo
- Publication number
- CN105271745A CN105271745A CN201510782524.5A CN201510782524A CN105271745A CN 105271745 A CN105271745 A CN 105271745A CN 201510782524 A CN201510782524 A CN 201510782524A CN 105271745 A CN105271745 A CN 105271745A
- Authority
- CN
- China
- Prior art keywords
- glaze
- floor tile
- dry granular
- treatment process
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of architectural ceramics, and particularly relates to an anti-skid treatment process of floor tiles. The process comprises the steps that a dry granular glaze is melt into glass granules through a frit furnace, and then grinding is conducted, dry granular glaze powder is obtained and added to a floor tile surface glaze to be evenly stirred; the materials are evenly applied to the surfaces of floor tiles through a glaze applying machine, and the floor tiles are obtained through sintering of a kiln furnace. According to the anti-skid treatment process of the floor tiles, a floor tile surface glaze formula is regulated, and the dry granular glaze is doped into the surface glaze, so that after the floor tile surface glaze is sintered and formed, the dry granular glaze still exists on the glaze surface in a small granular state, when a person steps on the floor tiles, a large number of friction points are increased, and therefore the problem that the floor tile glaze surfaces are wet and slippery when water exists on the floor tiles is thoroughly solved; in addition, according to produced products, attractiveness of an original product is not affected, cleaning is easy, and the produced products completely meet national standards.
Description
Technical field
The invention belongs to architectural pottery technical field, be specifically related to the anti-skidding treatment process of a kind of floor tile.
Background technology
The company that present China produces floor tile is very many, carries out the room clean and bright of decorating with floor tile, durable in use, easily clears up, and therefore uses floor tile to carry out decorating and also become the first-selection of all families.But in use all inevitably run into a problem, that is exactly in kitchen and toilet because often there is water on ground, unusual cunning above people steps down in, easily falls.Particularly old man easily falls especially, annual because the sliding old man fallen and hurt oneself in ground is a lot.Therefore, produce a kind of ship-and-galley tile and just become later inexorable trend.A lot of manufacturer of China is in order to address this problem, general is all adopt to engrave recess patterns on mould, or solve by the method that screen printing technology stamps the thicker pattern of one deck at tile surface, but, due to the distinctive glass property of floor tile glaze paint itself, frictional coefficient is little, still very sliding after particularly running into water, even if therefore tile surface has some rugged patterns, the characteristic that the surface of floor tile is easily wet and slippery still fundamentally can not be solved.
Summary of the invention
The object of this invention is to provide the anti-skidding treatment process of a kind of floor tile, scientific and reasonable, simple, obtained product good antiskid effect, be easy to cleaning.
The anti-skidding treatment process of floor tile of the present invention is melted through Cinker clew furnace by dry granular glaze to become glass particle, then grinding obtains dry granular glaze powder, and dry granular glaze powder joins in floor tile cover-coat enamel and stirs, and is evenly executed the surface of floor tile by glazing machine, burn till through kiln, to obtain final product.
Described dry granular glaze is made up of the raw material of following weight percent:
The grain composition of described grinding is greater than 20 order particle≤5%, 20 order to 40 order particle 35-45%, 40 order to 60 order particle 40-50%, the above particle 10-15% of 60 order.
Described dry granular glaze powder add-on is the 10-30% of cover-coat enamel quality, also can according to the requirement adjustment additional proportion of variant production.
The fineness of described cover-coat enamel is that 325 mesh sieves tail over <1%.
Described firing temperature is 1100-1200 DEG C.
Described firing period is 35-50 minute.
Evenly executed the surface of floor tile according to the glaze volume standard of every square centimeter of 0.05-0.08 gram by glazing machine.
The chemical composition of described dry granular glaze is as follows:
SiO
269.46％，Al
2O
39.1％，CaO4.66％，MgO0.67％，
K
2O3.08％，Na
2O1.56％，Fe
2O
30.13％，BaCO
34.4％，
ZnO3.8％，B
2O
33.5％。
Want thoroughly to solve the wet and slippery problem of floor tile glaze paint, will try every possible means to increase friction in floor tile glaze paint, the present invention researches and develops a kind of dry granular glaze and joins in the cover-coat enamel of floor tile, fully sintered when burning till, can not be dissolved in cover-coat enamel, after burning till, product surface forms the dry granular glaze of one deck projection slightly, thus reaches the anti-skidding effect of glaze paint.
Dry granular glaze forms the uniform projection small-particle of one deck at floor tile glazed surface, considerably increases the frictional coefficient of floor tile glaze paint, thus is fundamentally solving the wet and slippery defect of floor tile glaze paint.
The present invention develops the dry granular glaze of applicable firing process, very convenient when using aborning, do not need to increase glazing equipment again, utilize original glazing equipment, as long as glazing machine side proportionally joins in glazing bucket on glazing line, stir.
The floor tile with skidproof effect can be produced according to technique of the present invention, and meet national standard completely, be accepted by users, product operative norm: GB/T4100-2006 annex K.
The present invention compared with prior art, has following beneficial effect:
The present invention is by adjustment floor tile cover-coat enamel formula, in cover-coat enamel, mix a kind of dry granular glaze, make floor tile cover-coat enamel burn till shaping after, dry granular glaze still exists in glaze paint with short grained state, add a large amount of friction points above people steps down in, thus thoroughly solve the wet and slippery problem of floor tile glaze paint chance water; And the product produced does not affect the attractive in appearance of original product, be easy to cleaning, the product of production is up to state standards completely.
Embodiment
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
Dry granular glaze formula: silica powder 40%, feldspar in powder 36%, calcite 5%, boric acid 5%, saltpetre 2%, barium carbonate 10%, zinc oxide 2%.Dry granular glaze of this formula, after being processed into particle, records with sub-sieve screening that to be greater than 20 mesh sieve per-cents be the above accounting 13% of 3%, 20-40 order accounting 42%, 40-60 order accounting 42%, 60 mesh sieve.
The dry granular glaze processed adds in cover-coat enamel according to 20% ratio of cover-coat enamel, stir, then on the floor tile of 30cm*30cm, glazing is carried out according to every tile 55 grams of glaze volumes, firing temperature 1150 DEG C, firing period 40 minutes, the antiskid particles of the product surface after burning till is high-visible, feel is obvious, through soil pick-up test, not soil pick-up completely, other physical and chemical index is up to state standards completely.
Embodiment 2
Dry granular glaze formula: silica powder 44%, feldspar in powder 30%, calcite 5%, boric acid 5%, saltpetre 2%, barium carbonate 10%, zinc oxide 4%.After dry granular glaze of this formula entered to be processed into particle, record with sub-sieve screening that to be greater than 20 mesh sieve per-cents be the above accounting 10.5% of 4.5%, 20-40 order accounting 44%, 40-60 order accounting 41%, 60 mesh sieve.
The dry granular glaze processed adds in cover-coat enamel according to 28% ratio of cover-coat enamel, stir, then on the floor tile of 30cm*30cm, glazing is carried out according to every tile 48 grams of glaze volumes, firing temperature 1180 DEG C, firing period 45 minutes, the antiskid particles of the product surface after burning till is intensive, high-visible, feel is protruded obviously, tests through soil pick-up, not soil pick-up completely, other physical and chemical index is up to state standards completely.
Embodiment 3
Dry granular glaze formula: silica powder 41%, feldspar in powder 36%, calcite 5%, boric acid 5%, saltpetre 2%, barium carbonate 9%, zinc oxide 2%.After dry granular glaze of this formula entered to be processed into particle, record with sub-sieve screening that to be greater than 20 mesh sieve per-cents be the above accounting 13% of 2%, 20-40 order accounting 35%, 40-60 order accounting 50%, 60 mesh sieve.
The dry granular glaze processed adds in cover-coat enamel according to 12% ratio of cover-coat enamel, stir, then on the floor tile of 30cm*30cm, glazing is carried out according to every tile 68 grams of glaze volumes, firing temperature 1120 DEG C, firing period 35 minutes, the antiskid particles of the product surface after burning till compares dispersion, particle is obviously clear, and feel protruding effect is good, tests through soil pick-up, not soil pick-up completely, other physical and chemical index is up to state standards completely.
Claims (7)
1. the anti-skidding treatment process of floor tile, it is characterized in that dry granular glaze to melt through Cinker clew furnace to become glass particle, then grinding obtains dry granular glaze powder, dry granular glaze powder joins in floor tile cover-coat enamel and stirs, evenly executed the surface of floor tile by glazing machine, burn till through kiln, to obtain final product.
2. the anti-skidding treatment process of floor tile according to claim 1, is characterized in that described dry granular glaze is made up of the raw material of following weight percent:
3. the anti-skidding treatment process of floor tile according to claim 1, is characterized in that the grain composition of described grinding is greater than 20 order particle≤5%, 20 order to 40 order particle 35-45%, 40 order to 60 order particle 40-50%, the above particle 10-15% of 60 order.
4. the anti-skidding treatment process of floor tile according to claim 1 and 2, is characterized in that described dry granular glaze powder add-on is the 10-30% of cover-coat enamel quality.
5. the anti-skidding treatment process of floor tile according to claim 1, is characterized in that the fineness of described cover-coat enamel is that 325 mesh sieves tail over <1%.
6. the anti-skidding treatment process of floor tile according to claim 1, is characterized in that described firing temperature is 1100-1200 DEG C.
7. the anti-skidding treatment process of the floor tile according to claim 1 or 6, is characterized in that described firing period is 35-50 minute.