CN105271731A - Colored glaze recipe - Google Patents
Colored glaze recipe Download PDFInfo
- Publication number
- CN105271731A CN105271731A CN201510720023.4A CN201510720023A CN105271731A CN 105271731 A CN105271731 A CN 105271731A CN 201510720023 A CN201510720023 A CN 201510720023A CN 105271731 A CN105271731 A CN 105271731A
- Authority
- CN
- China
- Prior art keywords
- percent
- oxide
- quartz sand
- coloured glaze
- dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a colored glaze recipe. The colored glaze recipe is characterized by comprising the following ingredients in percentage by weight: 35 percent to 55 percent of quartz sand with the particle size range being 0.5mm to 1.0mm, fluxing agents: 10 percent to 15 percent of calcium oxide and 2 percent to 5 percent of silicon dioxide, clarifying agents: 6 percent to 12 percent of antimony oxide and 12 percent to 18 percent of ammonium nitrate, oxidizing agents: 5 percent to 10 percent of potassium permanganate and 2 percent to 5 percent of ammonium persulfate, coloring agents: 3 percent to 8 percent of cuprous oxide, 5 percent to 10 percent of copper oxide and 2 percent to 6 percent of cobalt sesquioxide, and other auxiliaries: 2 percent to 10 percent of fatty alcohol sodium benzenesulfonate and 2 percent to 5 percent of hydrogen peroxide. The produced colored glaze color is more glaring through the corresponding recipes.
Description
Technical field
The present invention relates to a kind of coloured glaze formula, belong to coloured glaze processing technique field.
Background technology
Coloured glaze is a kind of silicate product, has a long history, and its quality is glittering and translucent, bright and glittering, changes irregularly magnificent, and fully demonstrating the exquisiteness of Oriental, exquisiteness and implicit, is a kind of important decoration element.
Coloured glaze composition is low with softening temperature, material property length for there being good characteristic, be so convenient to manufacture technics, be applicable to coloured glaze be shaped, the quality of colored glaze product is embodied in good luster, and bubble, striped, calculus are few.The softening temperature of coloured glaze, material property depend primarily on the kind of composition and ratio thereof in coloured glaze formula, and in coloured glaze basic ingredient, add finings can make that coloured glaze temperature of fusion reduces, refining quality is improved, and avoid producing the defects such as bubble, striped, calculus.Finings can release decomposition gas in coloured glaze production process, or self gasification, produces a large amount of bubbles, receives the small bubbles of periphery, promote that coloured glaze is clarified with blub rises.
Finings conventional at present has cerium dioxide, white arsenic etc., but white arsenic is highly toxic substance, threatens operator ' s health and serious environment pollution; The clarifying effect of cerium dioxide still can, but settling time is longer, and cerium is rare earth element, and cost is costly.Therefore the coloured glaze formula that a kind of softening temperature is low, material property is long, clarifying effect is good, settling time is short, product property is excellent is needed badly.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of coloured glaze formula, makes the coloured glaze color of production more dazzling by filling a prescription accordingly.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is:
A kind of coloured glaze formula, is characterized in that: its moiety and weight ratio thereof are:
Particle size range is the quartz sand 35%-55% of 0.5mm-1.0mm;
Fusing assistant: calcium oxide 10%-15% and silicon-dioxide 2%-5%;
Finings: weisspiessglanz 6%-12% and ammonium nitrate 12%-18%;
Oxygenant: potassium permanganate 5%-10% and ammonium persulphate 2%-5%;
Tinting material: Red copper oxide 3%-8%, cupric oxide 5%-10% and cobalt sesquioxide 2%-6%;
Other auxiliary agents: fatty alcohol benzene sulfonic acid sodium salt 2%-10%, hydrogen peroxide 2%-5%.
Aforesaid a kind of coloured glaze formula, is characterized in that: the particle diameter of described quartz sand is 0.8mm.
Aforesaid a kind of coloured glaze formula, is characterized in that: described quartz sand 38%, calcium oxide 10%, silicon-dioxide 3%, weisspiessglanz 6%, ammonium nitrate 12%, potassium permanganate 5% and ammonium persulphate 3%, Red copper oxide 3%, cupric oxide 6%, cobalt sesquioxide 2%.
Aforesaid a kind of coloured glaze formula, is characterized in that: described quartz sand 40%, calcium oxide 12%, silicon-dioxide 3%, weisspiessglanz 6%, ammonium nitrate 13%, potassium permanganate 5% and ammonium persulphate 3%, Red copper oxide 3%, cupric oxide 8%, cobalt sesquioxide 2%.
Aforesaid a kind of coloured glaze formula, is characterized in that: described quartz sand 40%, calcium oxide 15%, silicon-dioxide 4%, weisspiessglanz 12%, ammonium nitrate 13%, potassium permanganate 5% and ammonium persulphate 3%, Red copper oxide 3%, cupric oxide 8%, cobalt sesquioxide 5%.
Aforesaid a kind of coloured glaze formula, is characterized in that: described quartz sand 45%, calcium oxide 12%, silicon-dioxide 4%, weisspiessglanz 13%, ammonium nitrate 13%, potassium permanganate 5% and ammonium persulphate 4%, Red copper oxide 4%, cupric oxide 10%, cobalt sesquioxide 5%.
To the invention has the beneficial effects as follows: by selecting more suitable raw material type, simultaneously all kinds of material choice preferably consumption, all kinds of like this raw material, by acting in conjunction each other, can make the azure stone handicraft obtained have preferably quality.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
A kind of coloured glaze formula provided by the invention, is characterized in that: its moiety and weight ratio thereof are:
Particle size range is the quartz sand 35%-55% of 0.5mm-1.0mm;
Fusing assistant: calcium oxide 10%-15% and silicon-dioxide 2%-5%;
Finings: weisspiessglanz 6%-12% and ammonium nitrate 12%-18%;
Oxygenant: potassium permanganate 5%-10% and ammonium persulphate 2%-5%;
Tinting material: Red copper oxide 3%-8%, cupric oxide 5%-10% and cobalt sesquioxide 2%-6%;
Other auxiliary agents: fatty alcohol benzene sulfonic acid sodium salt 2%-10%, hydrogen peroxide 2%-5%.
Wherein, the particle diameter of described quartz sand is 0.8mm.
Embodiment 1
Quartz sand 38%, calcium oxide 10%, silicon-dioxide 3%, weisspiessglanz 6%, ammonium nitrate 12%, potassium permanganate 5% and ammonium persulphate 3%, Red copper oxide 3%, cupric oxide 6%, cobalt sesquioxide 2%.
Embodiment 2
Quartz sand 40%, calcium oxide 12%, silicon-dioxide 3%, weisspiessglanz 6%, ammonium nitrate 13%, potassium permanganate 5% and ammonium persulphate 3%, Red copper oxide 3%, cupric oxide 8%, cobalt sesquioxide 2%.
Embodiment 3
Quartz sand 40%, calcium oxide 15%, silicon-dioxide 4%, weisspiessglanz 12%, ammonium nitrate 13%, potassium permanganate 5% and ammonium persulphate 3%, Red copper oxide 3%, cupric oxide 8%, cobalt sesquioxide 5%.
Embodiment 4
Quartz sand 45%, calcium oxide 12%, silicon-dioxide 4%, weisspiessglanz 13%, ammonium nitrate 13%, potassium permanganate 5% and ammonium persulphate 4%, Red copper oxide 4%, cupric oxide 10%, cobalt sesquioxide 5%.
More than show and describe ultimate principle of the present invention, principal character and advantage.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is by appending claims and equivalent circle thereof.
Claims (6)
1. a coloured glaze formula, is characterized in that: its moiety and weight ratio thereof are:
Particle size range is the quartz sand 35%-55% of 0.5mm-1.0mm;
Fusing assistant: calcium oxide 10%-15% and silicon-dioxide 2%-5%;
Finings: weisspiessglanz 6%-12% and ammonium nitrate 12%-18%;
Oxygenant: potassium permanganate 5%-10% and ammonium persulphate 2%-5%;
Tinting material: Red copper oxide 3%-8%, cupric oxide 5%-10% and cobalt sesquioxide 2%-6%;
Other auxiliary agents: fatty alcohol benzene sulfonic acid sodium salt 2%-10%, hydrogen peroxide 2%-5%.
2. a kind of coloured glaze formula according to claim 1, is characterized in that: the particle diameter of described quartz sand is 0.8mm.
3. a kind of coloured glaze formula according to claim 1, is characterized in that: described quartz sand 38%, calcium oxide 10%, silicon-dioxide 3%, weisspiessglanz 6%, ammonium nitrate 12%, potassium permanganate 5% and ammonium persulphate 3%, Red copper oxide 3%, cupric oxide 6%, cobalt sesquioxide 2%.
4. a kind of coloured glaze formula according to claim 2, is characterized in that: described quartz sand 40%, calcium oxide 12%, silicon-dioxide 3%, weisspiessglanz 6%, ammonium nitrate 13%, potassium permanganate 5% and ammonium persulphate 3%, Red copper oxide 3%, cupric oxide 8%, cobalt sesquioxide 2%.
5. a kind of coloured glaze formula according to claim 2, is characterized in that: described quartz sand 40%, calcium oxide 15%, silicon-dioxide 4%, weisspiessglanz 12%, ammonium nitrate 13%, potassium permanganate 5% and ammonium persulphate 3%, Red copper oxide 3%, cupric oxide 8%, cobalt sesquioxide 5%.
6. a kind of coloured glaze formula according to claim 1, is characterized in that: described quartz sand 45%, calcium oxide 12%, silicon-dioxide 4%, weisspiessglanz 13%, ammonium nitrate 13%, potassium permanganate 5% and ammonium persulphate 4%, Red copper oxide 4%, cupric oxide 10%, cobalt sesquioxide 5%.