CN105271740A - Colored glaze formula - Google Patents
Colored glaze formula Download PDFInfo
- Publication number
- CN105271740A CN105271740A CN201510635955.9A CN201510635955A CN105271740A CN 105271740 A CN105271740 A CN 105271740A CN 201510635955 A CN201510635955 A CN 201510635955A CN 105271740 A CN105271740 A CN 105271740A
- Authority
- CN
- China
- Prior art keywords
- oxide
- coloured glaze
- quartz sand
- glaze formula
- sodiumnitrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A colored glaze formula comprises 60-76wt% of quartz sand with the granularity range of 0.5-1mm, comprises 5-8wt% of sodium nitrate as a flux, comprises 8-12wt% of antimony oxide as a clarificant, comprises 4-7wt% of cuprous oxide, 2-6wt% of copper oxide and 3-7wt% of cadmium oxide as a coloring agent, and also comprises 1wt% of talcum powder and 1wt% of diatomite. Colored glaze handicraft with excellent quality can be obtained through the colored glaze formula in practical use.
Description
Technical field
The present invention relates to inorganic amorphous technical field of material, particularly relate to a kind of coloured glaze formula.
Background technology
Coloured glaze is a kind of silicate product, has a long history, and its quality is glittering and translucent, bright and glittering, changes irregularly magnificent, and fully demonstrate the exquisiteness of Oriental, exquisiteness and implicit, be a kind of important decoration element, the main component of coloured glaze is SiO
2.(i.e. silicon-dioxide), aluminum oxide, fusing assistant plumbous oxide and pigment etc.
Coloured glaze composition is low with softening temperature, material property length for there being good characteristic, be so convenient to manufacture technics, be applicable to coloured glaze be shaped, the quality of colored glaze product is embodied in good luster, and bubble, striped, calculus are few.The softening temperature of coloured glaze, material property depend primarily on the kind of composition and ratio thereof in coloured glaze formula, and in coloured glaze basic ingredient, add finings can make that coloured glaze temperature of fusion reduces, refining quality is improved, and avoid producing the defects such as bubble, striped, calculus.Finings can release decomposition gas in coloured glaze production process, or self gasification, produces a large amount of bubbles, receives the small bubbles of periphery, promote that coloured glaze is clarified with blub rises.Finings conventional at present has cerium dioxide, white arsenic etc., but white arsenic is highly toxic substance, threatens operator ' s health and serious environment pollution; The clarifying effect of cerium dioxide still can, but settling time is longer, and cerium is rare earth element, and cost is costly.Therefore the coloured glaze formula that a kind of softening temperature is low, material property is long, clarifying effect is good, settling time is short, product property is excellent is needed badly.
Patent documentation CN201210526726.X, publication date 2013.03.06, disclose a kind of light color terra-cotta for building, described light color terra-cotta for building are in every kilogram of magnesium chloride solution, add 0.4-0.6kg magnesium oxide, stir 6-8 minute, then 0.05-0.1kg Magnesium Silicate q-agent is added successively, 0.02-0.03kg urea-formaldehyde resin, 0.06-0.1g volatile salt, 2-3g tertiary sodium phosphate and 2-3g colorant, stir 20-30 minute, then the material be stirred is poured on glasscloth, strike off compacting, obtain after spontaneous curing drying, by the way, , light color terra-cotta smooth surface for building is clean and tidy, bright in colour beautiful, will never fade, there is excellent anti-folding and anti-pressing, resistance to rapid heat cycle, acid-proof alkaline and frost resistance energy, quality is light, water-intake rate is low, and insulation and soundproof effect good, cost is low.But at present about being applicable to prepare azure stone handicraft, colory coloured glaze formula report is less.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of coloured glaze formula, adopts this coloured glaze formula can obtain the good azure stone handicraft of quality.
For solving the problems of the technologies described above, the invention provides a kind of coloured glaze formula, its moiety and weight ratio thereof are:
Size range is the quartz sand 60%-76% of 0.5-1mm; Fusing assistant: SODIUMNITRATE 5%-8%, finings: antimonous oxide 8%-12%; And tinting material: Red copper oxide 4%-7%, cupric oxide 2%-6% and Cadmium oxide 3%-7%;
Other: talcum powder 1% and diatomite 1%.
The size range of quartz sand is 0.7mm.
Quartz sand 65%, described SODIUMNITRATE 7%, antimonous oxide 10%, Red copper oxide 5%, cupric oxide 4% and Cadmium oxide 5%.
Quartz sand 70%, SODIUMNITRATE 6%, antimonous oxide 9%, Red copper oxide 6%, cupric oxide 3% and Cadmium oxide 4%.
Quartz sand 68%, SODIUMNITRATE 6.5%, antimonous oxide 11%, Red copper oxide 5.5%, cupric oxide 4% and Cadmium oxide 6%.
Quartz sand 73%, SODIUMNITRATE 5.5%, antimonous oxide 10.5%, Red copper oxide 6.5%, cupric oxide 4.5% and Cadmium oxide 5.5%.
Compared with prior art, beneficial effect of the present invention is: owing to have selected more suitable raw material type in coloured glaze formula of the present invention, simultaneously all kinds of material choice preferably consumption, all kinds of like this raw material, by acting in conjunction each other, can make the azure stone handicraft obtained have preferably quality.
Embodiment
For making the object, technical solutions and advantages of the present invention clearly understand, below in conjunction with embodiment, the present invention is described in further details.At this, exemplary embodiment of the present invention and illustrating for explaining the present invention, but not as a limitation of the invention.
A kind of coloured glaze formula of the present invention, its moiety and weight ratio thereof are:
Size range is the quartz sand 60%-76% of 0.5-1mm; Fusing assistant: SODIUMNITRATE 5%-8%, finings: antimonous oxide 8%-12%; And tinting material: Red copper oxide 4%-7%, cupric oxide 2%-6% and Cadmium oxide 3%-7%;
Other: talcum powder 1% and diatomite 1%.
The size range of quartz sand is 0.7mm.
embodiment 1:
Size range is the quartz sand 65% of 0.7mm, described SODIUMNITRATE 7%, antimonous oxide 10%, Red copper oxide 5%, cupric oxide 4% and Cadmium oxide 5%, other: talcum powder 1% and diatomite 1%.
embodiment 2:
Size range is the quartz sand 70% of 0.7mm, SODIUMNITRATE 6%, antimonous oxide 9%, Red copper oxide 6%, cupric oxide 3% and Cadmium oxide 4%, other: talcum powder 1% and diatomite 1%.
embodiment 3:
Size range is the quartz sand 68% of 0.7mm, SODIUMNITRATE 6.5%, antimonous oxide 11%, Red copper oxide 5.5%, cupric oxide 4% and Cadmium oxide 6%, other: talcum powder 1% and diatomite 1%.
embodiment 4:
Size range is the quartz sand 73% of 0.7mm, SODIUMNITRATE 5.5%, antimonous oxide 10.5%, Red copper oxide 6.5%, cupric oxide 4.5% and Cadmium oxide 5.5%, other: talcum powder 1% and diatomite 1%.
In sum, formula of the present invention not only with component about but also relevant with the content of component, concrete all kinds of component by acting in conjunction each other, can make coloured glaze have fine qualities under preferably consumption.
Claims (6)
1. a coloured glaze formula, is characterized in that, its moiety and weight ratio thereof are:
Size range is the quartz sand 60%-76% of 0.5-1mm; Fusing assistant: SODIUMNITRATE 5%-8%, finings: antimonous oxide 8%-12%; And tinting material: Red copper oxide 4%-7%, cupric oxide 2%-6% and Cadmium oxide 3%-7%;
Other: talcum powder 1% and diatomite 1%.
2. coloured glaze formula according to claim 1, is characterized in that, the size range of described quartz sand is 0.7mm.
3. coloured glaze formula according to claim 2, is characterized in that: quartz sand 65%, SODIUMNITRATE 7%, antimonous oxide 10%, Red copper oxide 5%, cupric oxide 4% and Cadmium oxide 5%.
4. coloured glaze formula according to claim 1, is characterized in that: quartz sand 70%, SODIUMNITRATE 6%, antimonous oxide 9%, Red copper oxide 6%, cupric oxide 3% and Cadmium oxide 4%.
5. coloured glaze formula according to claim 1, is characterized in that: quartz sand 68%, SODIUMNITRATE 6.5%, antimonous oxide 11%, Red copper oxide 5.5%, cupric oxide 4% and Cadmium oxide 6%.
6. coloured glaze formula according to claim 1, is characterized in that: quartz sand 73%, SODIUMNITRATE 5.5%, antimonous oxide 10.5%, Red copper oxide 6.5%, cupric oxide 4.5% and Cadmium oxide 5.5%.