CN105271463A - 用于污水处理的高效固体过滤材料及其制造方法 - Google Patents
用于污水处理的高效固体过滤材料及其制造方法 Download PDFInfo
- Publication number
- CN105271463A CN105271463A CN201510808404.8A CN201510808404A CN105271463A CN 105271463 A CN105271463 A CN 105271463A CN 201510808404 A CN201510808404 A CN 201510808404A CN 105271463 A CN105271463 A CN 105271463A
- Authority
- CN
- China
- Prior art keywords
- sewage
- sewage treatment
- filter material
- material used
- solid filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于污水处理技术领域,涉及用于污水处理的高效固体过滤材料及其制造方法。用于污水处理的高效固体过滤材料,包括以下质量百分比的组分:氢氧化钙20-25%、碳酸钙20-25%、麦饭石4-9%、滑石粉10-15%、沸石5-13%、活性炭粉8-12%、黄泥粉8-13%。用于污水处理的高效固体过滤材料的制造方法为:将材料按照配比用水混合,制成120mm*120mm*25mm的六面体,每个面中间制成4个贯通孔,直径为25mm,干燥后,经600度高温烧制成型,即可使用。本发明的用于污水处理的高效固体过滤材料放在污水中不会被污水溶解,可长期使用,能够在较长时间里有效清除污水中的氮、磷、大肠杆菌等有害物质,有效清除污水中的色素。
Description
技术领域
本发明属于污水处理技术领域,涉及用于污水处理的高效固体过滤材料及其制造方法。
背景技术
随着经济的不断发展,各种生活污水会不断增加,水质污染不断加重,而我国是世界上比较缺水的国家之一,人均水资源占有量仅为世界人均水资源占有量的1/4,水资源短缺和污染问题已严重影响了我国国民经济建设和人们的正常生活。因此,如何保护水资源免受污染,解决污水的源头治理,已成为摆在我们面前的重要课题。
发明内容
本发明的目的是为了解决水污染问题,提供一种用于污水处理的高效固体过滤材料及制造方法。
为了实现上述目的,本发明采用的技术方案是:用于污水处理的高效固体过滤材料,包括以下质量百分比的组分:氢氧化钙20-25%、碳酸钙20-25%、麦饭石4-9%、滑石粉10-15%、沸石5-13%、活性炭粉8-12%、黄泥粉8-13%。
所述的用于污水处理的高效固体过滤材料的制造方法为:将材料按照配比用水混合,制成120mm*120mm*25mm的六面体,每个面中间制成4个贯通孔,直径为25mm,干燥后,经600度高温烧制成型,即可使用。
本发明的用于污水处理的高效固体过滤材料是在污水处理过程中使用的一种固体合成材料,它能够高效清除污水中的氮、磷等可导致水体营养化的可溶性无机物,消灭大肠杆菌等有害物质,同时具有高效脱色功能,使污水达到我国中水排放相关标准。
本发明的用于污水处理的高效固体过滤材料放在污水中不会被污水溶解,可长期使用,能够在较长时间里有效清除污水中的氮、磷、大肠杆菌等有害物质,有效清除污水中的色素。
本发明是使用的多种矿物质混合配比而成型的高效过滤材料,其原理就是利用各种矿物质的不同功能,吸附各种有害物质达到净化水的作用。
麦饭石是一种中性碱半火成岩,其主要成份为二氧化硅、氧化铝。麦饭石具有双重的吸附性:一方面是因为它以硅酸盐为主,具有很好的吸附性,另一方面由于麦饭石多含高岭石等黏土矿物,是多孔性海绵状特殊结构,有较强的静电引力,在水中对重金属离子和致害毒素有很强的吸附力,可清除水中的汞、铝、镉、砷、氟等重金属及氯化物、氰化物、残余农药、三甲烷等有害物质,吸附率是同等表面活性炭的20000倍,对重金属、大肠杆菌的吸附率达96%以上,对水中余氯吸附率(浸泡一小时后)达99%。
活性炭是黑色粉末状或颗粒状的无定型炭,在元素组成方面,80%-90%以上由碳组成,这也是活性炭为疏水性吸附剂的原因。利用化学品活化的颗粒活性炭是非常多孔的,多在微孔和中孔范围,因此活性炭对有机物有较强的吸附能力,包括微生物难以降解的有机物。污水经活性炭处理后,BOD可降低99%TOC可降低1-3mg/L,同时还具有脱色除臭,吸附除浊之功能。
沸石是火山熔岩形成的一种架状结构的铝硅酸盐矿物。它具有独特的吸附性、催化性、离子的换性、离子的选择性、耐酸性、热稳定性、多成份性及很高的生物活性和抗毒性等。沸石表面粗糙,具有多孔结构,吸附力和携载能力较强,用其过滤污水,可以去除水中的氨、氮95%。
碳酸钙是一种无机化合物,主要成分为方解石。碳酸钙对油性物质有较强吸附力,同时能够中和污水的PH值。因此,用在本发明中,它起到一种中和剂的作用。
滑石粉为硅酸盐类矿物滑石,主要成份为含水硅酸镁。它具有抗黏、抗酸性、吸附能力强等优良的物理、化学特性。
黄土是在干燥气候条件下形成的多孔性具有柱状节理的黄色粉性土。黄土中的粘土矿物主要是高岭石、伊利石、蒙脱石等,此外,黄土中的碳酸盐(方解石)含量较多。黄土用在本发明中一是起到吸附作用。二是利用其黏性加工成型固体材料。
氢氧化钙又名熟石灰,具有碱的通性,用在本发明中,主要起到中和污水PH值的碱补充剂的作用以及清除磷的作用。
根据以上各种材料的不同特性,对其进行合理配比组份,使其在污水中发挥各自不同的作用,达到净化污水的目标。
具体实施方式
下面结合实施例对本发明的用于污水处理的高效固体过滤材料及其制造方法做详细的说明和描述。
实施例1用于污水处理的高效固体过滤材料,包括以下质量百分比的组分:氢氧化钙20%、碳酸钙20%、麦饭石10%、滑石粉10%、沸石15%、活性炭粉12%、黄泥粉13%。
将上述材料按配比用水混合,制成120mm*120mm*25mm的六面体,每块中间制成4个贯通孔,直径为25mm,干燥后,经600度高温烧制成型,即可使用。
实施例2用于污水处理的高效固体过滤材料,包括以下质量百分比的组分:氢氧化钙25%、碳酸钙25%、麦饭石8%、滑石粉12%、沸石10%、活性炭粉10%、黄泥粉10%。
将上述材料按配比用水混合,制成120mm*120mm*25mm的六面体,每块中间制成4个贯通孔,直径为25mm,干燥后,经600度高温烧制成型,即可使用。
实施例3用于污水处理的高效固体过滤材料,包括以下质量百分比的组分:氢氧化钙22%、碳酸钙25%、麦饭石10%、滑石粉14%、沸石12%、活性炭粉8%、黄泥粉9%。
将上述材料按配比用水混合,制成120mm*120mm*25mm的六面体,每块中间制成4个贯通孔,直径为25mm,干燥后,经600度高温烧制成型,即可使用。
为了测试氨氮、色素、大肠杆菌等物质的清除情况,我们使用标准方法测量分析了流入反应器之前的污水指标,然后将高效固体过滤材料放入污水中,24小时后再次测量污水,测定结果如表1。
表1污水处理实验结果
污水经过净化后,BOD清除率93%,COD清除率95%,氨氮清除率95%,色素清除率100%。
Claims (2)
1.用于污水处理的高效固体过滤材料,其特征在于:包括以下质量百分比的组分:氢氧化钙20-25%、碳酸钙20-25%、麦饭石4-9%、滑石粉10-15%、沸石5-13%、活性炭粉8-12%、黄泥粉8-13%。
2.如权利要1所述的用于污水处理的高效固体过滤材料的制造方法,其特征在于:将材料按照配比用水混合,制成120mm*120mm*25mm的六面体,每个面中间制成4个贯通孔,直径为25mm,干燥后,经600度高温烧制成型,即可使用。