CN105266315B - 一种贴面折扇的制作工艺 - Google Patents

一种贴面折扇的制作工艺 Download PDF

Info

Publication number
CN105266315B
CN105266315B CN201510692718.6A CN201510692718A CN105266315B CN 105266315 B CN105266315 B CN 105266315B CN 201510692718 A CN201510692718 A CN 201510692718A CN 105266315 B CN105266315 B CN 105266315B
Authority
CN
China
Prior art keywords
fan
ribs
folding
covering
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510692718.6A
Other languages
English (en)
Other versions
CN105266315A (zh
Inventor
唐道雁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Gaofeng Daily Artware Co Ltd
Original Assignee
Anhui Gaofeng Daily Artware Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Gaofeng Daily Artware Co Ltd filed Critical Anhui Gaofeng Daily Artware Co Ltd
Priority to CN201510692718.6A priority Critical patent/CN105266315B/zh
Publication of CN105266315A publication Critical patent/CN105266315A/zh
Application granted granted Critical
Publication of CN105266315B publication Critical patent/CN105266315B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种贴面折扇的制作工艺,方法步骤包括:得到扇骨防腐溶液;取竹材或木材,加工为扇骨,将所述扇骨投入扇骨防腐溶液;将扇骨防腐溶液自然冷却;将竹骨取出,用清水喷洒,去除扇骨上的附着物后,风干;将风干后的扇骨喷淋双氧水,放入烘干室中进行烘干操作,直至扇骨表面干燥为止;取若干处理后的扇骨,将所述若干扇骨的一端涂抹粘胶,得到折扇扇骨;将扇面使用套模对扇面进行套折,折后风干,切上下边,包贴边沿,压平,即可得到折扇扇面;将折扇扇骨与折扇扇面通过所述折扇扇骨上的粘胶进行粘合,得到折扇。本发明制作的贴面折扇,结构牢固,通过粘胶使扇骨与扇面牢牢固定,不易脱落。

Description

一种贴面折扇的制作工艺
技术领域
本发明涉及扇子领域,尤其是一种贴面折扇的制作工艺。
背景技术
折扇又名“纸扇”、“掐扇”,最早出现于我国公元五世纪的南北朝时期,是一种可以自由折叠和展开的扇子,用时需要展开,现在的折扇工艺一般还是沿袭古法,这种工艺方法不仅费时费力,而且往往制得折扇的过程中失败率非常高,现在折扇市场上迫切需要一种新的折扇的制作工艺。
发明内容
本发明主要解决的技术问题在于提供一种贴面折扇的制作工艺。
本发明为解决上述技术问题采用的技术方案为:
1.一种贴面折扇的制作工艺,其特征在于:方法步骤如下:
a.制备扇骨防腐溶液,按重量份包括:乙醇25-40份茶多酚3-5份菜籽油9-10份壳寡糖8-10份精蛋白3-4份,均匀混合;
按重量份包括:丁香花粉1-2份桂花粉4-5份桔梗3-4份,均匀混合,加入所述扇骨防腐溶液中;
b.取竹材或木材,加工为扇骨,将所述扇骨投入扇骨防腐溶液,将扇骨防腐溶液加热至90-95℃,煮至4-5小时;
c.将扇骨防腐溶液自然冷却;
d.重复步骤b和c,将竹骨取出,用清水喷洒,去除扇骨上的附着物后,风干;
e.将风干后的扇骨喷淋双氧水,放入烘干室中进行烘干操作,直至扇骨表面干燥为止;
f.擦拭扇骨表面,使扇骨表面出现包浆层;
g.取若干处理后的扇骨,将所述若干扇骨的一端涂抹粘胶,将所述若干扇骨另一端活动连接,得到折扇扇骨;
h.取纸材或布材裁切成若干相同的扇面纸张,取一扇面纸张喷洒水雾后刷上糊浆,盖上相同的扇面纸张后再次刷上糊浆,直至所有的扇面纸张均匀重叠得到一完整的扇面,将所述的扇面风干晾晒24-48小时;
i.将步骤h中得到的扇面使用套模对扇面进行套折,折后风干,切上下边,包贴边沿,压平,即可得到折扇扇面;
j.将步骤g中得到的折扇扇骨与步骤i中得到的折扇扇面通过所述折扇扇骨上的粘胶进行粘合,然后放入烘干房中进行烘干操作1-2小时,得到折扇。
进一步地,所述步骤d中的风干时间为12-24小时。
进一步地,所述步骤d中烘干房的温度为80℃。
进一步地,所述步骤i中的包贴边沿使用的材料为绫条。
本发明的有益效果为:
通过采用本发明制作的贴面折扇,结构牢固,通过粘胶使扇骨与扇面牢牢固定,不易脱落,进而既保证扇子可折叠放置的方便性,同时不必将扇面做厚,保证了折扇的轻便,长时间使用折扇时也不容易感到疲累,方便实用。
具体实施方式
实施例1:
一种贴面折扇的制作工艺,方法步骤如下:
a.制备扇骨防腐溶液,按重量份包括:乙醇 25份 茶多酚 3份 菜籽油 10份 壳寡糖 10份 精蛋白 3份,均匀混合;
按重量份包括:丁香花粉 1份 桂花粉 4份 桔梗 3份,均匀混合,加入所述扇骨防腐溶液中;
b.取竹材或木材,加工为扇骨,将所述扇骨投入扇骨防腐溶液,将扇骨防腐溶液加热至90℃,煮至4小时;
c.将扇骨防腐溶液自然冷却;
d.重复步骤b和c,将竹骨取出,用清水喷洒,去除扇骨上的附着物后,风干;
e.将风干后的扇骨喷淋双氧水,放入烘干室中进行烘干操作,直至扇骨表面干燥为止;
f.擦拭扇骨表面,使扇骨表面出现包浆层;
g.取若干处理后的扇骨,将所述若干扇骨的一端涂抹粘胶,将所述若干扇骨另一端活动连接,得到折扇扇骨;
h.取纸材或布材裁切成若干相同的扇面纸张,取一扇面纸张喷洒水雾后刷上糊浆,盖上相同的扇面纸张后再次刷上糊浆,直至所有的扇面纸张均匀重叠得到一完整的扇面,将所述的扇面风干晾晒24-48小时;
i.将步骤h中得到的扇面使用套模对扇面进行套折,折后风干,切上下边,包贴边沿,压平,即可得到折扇扇面;
j.将步骤g中得到的折扇扇骨与步骤i中得到的折扇扇面通过所述折扇扇骨上的粘胶进行粘合,然后放入烘干房中进行烘干操作1小时,得到折扇。
步骤d中的风干时间为12小时。
步骤d中烘干房的温度为80℃。
步骤i中的包贴边沿使用的材料为绫条。
实施例2:
a.制备扇骨防腐溶液,按重量份包括:乙醇40份茶多酚5份菜籽油9份壳寡糖8份精蛋白3份,均匀混合;
按重量份包括:丁香花粉2份桂花粉5份桔梗4份,均匀混合,加入所述扇骨防腐溶液中;
b.取竹材或木材,加工为扇骨,将所述扇骨投入扇骨防腐溶液,将扇骨防腐溶液加热至95℃,煮至5小时;
c.将扇骨防腐溶液自然冷却;
d.重复步骤b和c,将竹骨取出,用清水喷洒,去除扇骨上的附着物后,风干;
e.将风干后的扇骨喷淋双氧水,放入烘干室中进行烘干操作,直至扇骨表面干燥为止;
f.擦拭扇骨表面,使扇骨表面出现包浆层;
g.取若干处理后的扇骨,将所述若干扇骨的一端涂抹粘胶,将所述若干扇骨另一端活动连接,得到折扇扇骨;
h.取纸材或布材裁切成若干相同的扇面纸张,取一扇面纸张喷洒水雾后刷上糊浆,盖上相同的扇面纸张后再次刷上糊浆,直至所有的扇面纸张均匀重叠得到一完整的扇面,将所述的扇面风干晾晒24-48小时;
i.将步骤h中得到的扇面使用套模对扇面进行套折,折后风干,切上下边,包贴边沿,压平,即可得到折扇扇面;
j.将步骤g中得到的折扇扇骨与步骤i中得到的折扇扇面通过所述折扇扇骨上的粘胶进行粘合,然后放入烘干房中进行烘干操作1小时,得到折扇。
步骤d中的风干时间为12小时。
步骤d中烘干房的温度为80℃。
步骤i中的包贴边沿使用的材料为绫条。
通过采用本发明制作的贴面折扇,结构牢固,通过粘胶使扇骨与扇面牢牢固定,不易脱落,进而既保证扇子可折叠放置的方便性,同时不必将扇面做厚,保证了折扇的轻便,长时间使用折扇时也不容易感到疲累,方便实用。

Claims (1)

1.一种贴面折扇的制作工艺,其特征在于:方法步骤如下:
a.制备扇骨防腐溶液,按重量份包括:乙醇25-40份茶多酚3-5份菜籽油9-10份壳寡糖8-10份精蛋白3-4份,均匀混合;
按重量份包括:丁香花粉1-2份桂花粉4-5份桔梗3-4份,均匀混合,加入所述扇骨防腐溶液中;
b.取竹材或木材,加工为扇骨,将所述扇骨投入扇骨防腐溶液,将扇骨防腐溶液加热至90-95℃,煮至4-5小时;
c.将扇骨防腐溶液自然冷却;
d.重复步骤b和c,将竹骨取出,用清水喷洒,去除扇骨上的附着物后,风干,风干时间为12-24小时;
e.将风干后的扇骨喷淋双氧水,放入烘干室中进行烘干操作,直至扇骨表面干燥为止,烘干房的温度为80℃;
f.擦拭扇骨表面,使扇骨表面出现包浆层;
g.取若干处理后的扇骨,将所述若干扇骨的一端涂抹粘胶,将所述若干扇骨另一端活动连接,得到折扇扇骨;
h.取纸材或布材裁切成若干相同的扇面纸张,取一扇面纸张喷洒水雾后刷上糊浆,盖上相同的扇面纸张后再次刷上糊浆,直至所有的扇面纸张均匀重叠得到一完整的扇面,将所述的扇面风干晾晒24-48小时;
i.将步骤h中得到的扇面使用套模对扇面进行套折,折后风干,切上下边,包贴边沿,压平,即可得到折扇扇面,包贴边沿使用的材料为绫条;
j.将步骤g中得到的折扇扇骨与步骤i中得到的折扇扇面通过所述折扇扇骨上的粘胶进行粘合,然后放入烘干房中进行烘干操作1-2小时,得到折扇。
CN201510692718.6A 2015-10-21 2015-10-21 一种贴面折扇的制作工艺 Active CN105266315B (zh)