CN105238945A - 全通孔泡沫铝及制备技术 - Google Patents

全通孔泡沫铝及制备技术 Download PDF

Info

Publication number
CN105238945A
CN105238945A CN201510353198.6A CN201510353198A CN105238945A CN 105238945 A CN105238945 A CN 105238945A CN 201510353198 A CN201510353198 A CN 201510353198A CN 105238945 A CN105238945 A CN 105238945A
Authority
CN
China
Prior art keywords
hole
mould
full
aluminium alloy
sponge
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510353198.6A
Other languages
English (en)
Other versions
CN105238945B (zh
Inventor
贾维
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510353198.6A priority Critical patent/CN105238945B/zh
Publication of CN105238945A publication Critical patent/CN105238945A/zh
Application granted granted Critical
Publication of CN105238945B publication Critical patent/CN105238945B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提出了一种全通孔泡沫铝及制备技术。以往的通孔泡沫铝通孔率在60％-80％之间，用于热交换、流体过滤、流体均布效果不太理想，我发明的全通孔泡沫铝及制备技术所生产的全通孔泡沫铝通孔率大于98％，孔隙率可达90％以上，由于孔隙率、通孔率的提高全通孔泡沫铝更加适用于热交换，流体过滤、流体均布。首先准备5-60ppi(5mm-0.42mm)孔径的全通孔海绵，切割成与模具长宽一致放入模具。再将高强石膏加抗缩裂填料加溃散剂调匀加水搅均，将搅好的浆料倒入装有海绵体的模具灌实流平，晾干后模具上方加入大于海绵体积12％-30％体积的铝或铝合金，模具整体放入加热炉逐步升温加热到780℃恒温4小时后自然冷却，出模切割清洗及制得全通孔泡沫铝。

Description

全通孔泡沫铝及制备技术
技术领域：
本发明涉及一种全通孔泡沫铝及制备技术属于新材料技术领域
背景技术：
全通孔泡沫铝-泡沫铝是近年来发展起来第一种新材料，泡沫材料是原实体材料经特殊工艺制成的泡沫状材料，泡沫铝属泡沫材料泡沫金属类，泡沫铝按照孔形孔结构大致可分为通孔型泡沫铝和闭孔型泡沫铝。以往的通孔泡沫铝通孔率在60％-80％之间，用于热交换、流体过滤、流体均布效果不太理想，我发明的全通孔泡沫铝及制备技术由于工艺不同所生产的全通孔泡沫铝通孔率大于98％，孔隙率90％以上，由于孔隙率、通孔率的提高全通孔泡沫铝更加适用于热交换，流体过滤、流体均布。
全通孔泡沫铝主要技术指标及参数：
通孔率：大于98％
孔隙率：0.78％——90％
孔径：5-60ppi(5mm-0.42mm)
体积密度：0.2-0.8g/cm3
全通孔泡沫铝材料特性：
比表面积大、孔隙率高、密度小、重量轻、除此之外仍具有原基体材料铝的优良导热特性。
泡沫铝的功能及用途：
全通孔泡沫铝可用于热交换、流体过滤、流体均布、吸声、吸能、缓冲、比刚度高、力学性能好、电磁屏蔽等功能。主要可用于：精密机械设备热交换、大功率电器热交换、流体过滤、流体均布。
发明内容：
本发明主要内容：一种全通孔泡沫铝及制备技术
实现以上技术具体做法是：
1.全通孔泡沫铝及制备技术可制备5-60ppi(5mm-0.42mm)孔径的全通孔泡沫铝。
2.全通孔泡沫铝及制备技术可制备密度为0.2-0.8的全通孔泡沫铝。
3.全通孔泡沫铝及制备技术选择5-60ppi(5mm-0.42mm)孔径的全通孔海绵。
4.全通孔泡沫铝及制备技术选用：α35高强石膏占总重55％、200#石英粉占总重20％、硫酸镁占总重25％三种原料混合均匀。
5.混合料70％加30％水搅拌均匀。
6.混合浆料灌入放有海绵的模具。
7.混合浆料灌入放有海绵的模具晾干干透。
8.模具上方加入大于海绵体积12％-30％体积的铝或铝合金
9.模具整体放入加热炉逐步升温加热到780℃恒温4小时后自然冷却。
10.出模切割清洗及制得全通孔泡沫铝。
本发明优势在于：
加工工艺简便易于大批量生产，产品质量易于控制，
具体实施：
实施1、
1.选用模具规格300mm*300mm*100mm
2.选用全通孔海绵孔径20ppi(1.27mm)，规格300mm*300mm*50mm，海绵放入模具。
3.选用α35高强石膏占总重55％、200#石英粉占总重20％、硫酸镁占总重25％三种原料混合均匀为混合料。
4.混合料70％加30％水搅拌均匀为混合浆料。
6.混合浆料灌入放有海绵的模具。
7.混合浆料灌入放有海绵的模具晾干干透。
8.模具上方加入大于海绵体积15％体积的铝或铝合金
9.模具整体放入加热炉逐步升温加热到780℃恒温4小时后自然冷却。
10.出模切割清洗实施1制备出规格为300mm*300mm*50mm的全通孔泡沫铝。
11.实施1制备出孔径为20ppi(1.27mm)的全通孔泡沫铝。
12.实施1制备出密度为0.28g/cm3的全通孔泡沫铝。
实施2、
1.选用模具规格500mm*500mm*160mm
2.选用全通孔海绵孔径10ppi(2.5mm)，规格500mm*500mm*80mm，海绵放入模具。
3.选用α35高强石膏占总重55％、200#石英粉占总重20％、硫酸镁占总重25％三种原料混合均匀为混合料。
4.混合料70％加30％水搅拌均匀为混合浆料。
6.混合浆料灌入放有海绵的模具。
7.混合浆料灌入放有海绵的模具晾干干透。
8.模具上方加入大于海绵体积15％体积的铝或铝合金
9.模具整体放入加热炉逐步升温加热到780℃恒温4小时后自然冷却。
10.出模切割清洗实施1制备出规格为500mm*500mm*80mm的全通孔泡沫铝。
11.实施1制备出孔径为10ppi(1.27mm)的全通孔泡沫铝。
12.实施1制备出密度为0.3g/cm3的全通孔泡沫铝。

Claims (10)

1.全通孔泡沫铝及制备技术可制备5-60ppi(5mm-0.42mm)孔径的全通孔泡沫铝。
2.全通孔泡沫铝及制备技术可制备密度为0.2-0.8的全通孔泡沫铝。
3.全通孔泡沫铝及制备技术选择5-60ppi(5mm-0.42mm)孔径的全通孔海绵。
4.全通孔泡沫铝及制备技术选用：α35高强石膏占总重55％、200#石英粉抗缩裂填料占总重20％、硫酸镁溃散剂占总重25％三种原料混合均匀。
5.混合料70％加30％水搅拌均匀。
6.混合浆料倒入装有海绵体的模具灌实流平。
7.模具内石膏晾干干透。
8.模具上方加入大于海绵体积12％-30％体积的铝或铝合金。
9.模具整体放入加热炉逐步升温加热到780℃恒温4小时后自然冷却。
10.出模切割清洗及制得全通孔泡沫铝。
CN201510353198.6A 2015-06-25 2015-06-25 全通孔泡沫铝及制备技术 Active CN105238945B (zh)