CN105231935A - Production process of antibacterial Modal fiber towels - Google Patents
Production process of antibacterial Modal fiber towels Download PDFInfo
- Publication number
- CN105231935A CN105231935A CN201510548952.1A CN201510548952A CN105231935A CN 105231935 A CN105231935 A CN 105231935A CN 201510548952 A CN201510548952 A CN 201510548952A CN 105231935 A CN105231935 A CN 105231935A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- modal fiber
- modal fibre
- carried out
- towel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production process of antibacterial Modal fiber towels. Modal fiber is subjected to warping, the warped Modal fiber is subjected to sizing, the sized Modal fiber is spun into gray fabric, the gray fabric is soaked in a hot water tank and flushed to remove water-soluble threads, the gray fabric is boiled and bleached, the boiled and bleached gray fabric is dyed, the dyed gray fabric is dried with a drying appliance, the dried gray fabric is cut and sewn to form Modal fiber towels, the Modal fiber towels are subjected to antibacterial processing using an antibacterial finishing agent. According to the production process, antibacterial processing is carried out, and thus germ growth is prevented effectively and towel fabric is protected from contamination by microorganisms; features such as water retention and softness are retained, the towel fabric has excellent moisture-absorbing and sweat transfer performances, outstanding high temperature resistance and outstanding stink-absorbing and foul-eliminating performances and is green and long in service life, a processing technique is simple, and production efficiency is high.
Description
Technical field
The present invention relates to towel and make field, especially a kind of antibacterial Modal fibre towel manufacture craft.
Background technology
Towel surface looped pile is intensive, soft, and water suction water storage is strong, and wear-resisting, thermal property is good, and therefore can directly be used for contacting skin, be one of most important daily necessities of daily life.On market, the overwhelming majority is woven towel, and the shortcomings such as filoplume is more, feel is poor easily appear in obtained towel, and the service life of towel is not long, and manufacture craft is also comparatively complicated.People will contact towel every day continually, due to the easy moisture absorption of towel, after each, easily corroded by various harmful bacteria breeding, as cleaned not in time, the fermentations of going bad such as the mushroom on towel cloth, grease, protein, bacterium can grow fast with geometric progression, towel body is clamminess mouldy, produces peculiar smell, affect the health of people, if the amount reproduction of malignant bacteria, invade skin, after respiratory tract etc., also can the healthy living of harmful to human.After living standards of the people step into " fairly well-off " and " rich type ", the consumption idea of resident can change to some extent than ever and select, pursue and this has been human social development with the household textiles of green, environmental protection and health inexorable trend, therefore, the exploitation of anti-microbial type towel, emerge in large numbers the trend in epoch of also just having coincide, meet consumer's uphold nature, be particular about the good custom of life of health.
Summary of the invention
The technical problem to be solved in the present invention is: for overcoming above-mentioned Problems existing, provides a kind of environmental protection, soft comfortable one antibacterial Modal fibre towel manufacture craft.
The technical solution adopted for the present invention to solve the technical problems is: a kind of antibacterial Modal fibre towel manufacture craft, and technological process is as follows:
A. described Modal fibre is carried out warping process;
B. the Modal fibre after warping is carried out starching process;
C. grey cloth is woven into by through the Modal fibre described in starching process;
D. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
E. described grey cloth is processed through over-cooking drift;
F. dyeing process is carried out by through over-cooking the grey cloth after drift;
G. the grey cloth after dyeing is carried out drying and processing through drying plant;
H. the grey cloth after oven dry is carried out cutting out and sew and obtain Modal fibre towel;
I. Modal fibre towel is carried out antimicrobial treatment through antibacterial finishing agent.
Further, described dyeing process is dyeed 25 minutes at 65 DEG C of temperature.
Further, the temperature that described drying and processing adopts is 80 DEG C ~ 90 DEG C.
The invention has the beneficial effects as follows, one of the present invention antibacterial Modal fibre towel manufacture craft is through antimicrobial treatment, effectively can prevent staphylococcus aureus, Candida albicans, Escherichia coli, aspergillus niger, aspergillus flavus, variable color aspergillus, Trichoderma viride, growing of the bacteriums such as Penicillium citrinum etc. mould, towel cloth is not stain by Institute of Micro-biology, remain water imbibition, the feature such as soft, there is excellent moisture absorbing and sweat releasing performance, outstanding resistance to elevated temperatures and the smelly blowdown performance of suction, environmental protection, long service life, and processing technology is simple, production efficiency is high.
Detailed description of the invention
A kind of antibacterial Modal fibre towel manufacture craft, technological process is as follows:
A. Modal fibre is carried out warping process;
B. the Modal fibre after warping is carried out starching process;
C. grey cloth is woven into by through the Modal fibre described in starching process;
D. grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
E. grey cloth is processed through over-cooking drift;
F. dyeing process is carried out by through over-cooking the grey cloth after drift;
G. the grey cloth after dyeing is carried out drying and processing through drying plant;
H. the grey cloth after oven dry is carried out cutting out and sew and obtain Modal fibre towel;
I. Modal fibre towel is carried out antimicrobial treatment through antibacterial finishing agent.
Further, dyeing process is dyeed 25 minutes at 65 DEG C of temperature.
Further, the temperature that drying and processing adopts is 80 DEG C ~ 90 DEG C.
With above-mentioned according to desirable embodiment of the present invention for enlightenment, by above-mentioned description, relevant staff in the scope not departing from this invention technological thought, can carry out various change and amendment completely.The technical scope of this invention is not limited to the content on description, must determine its technical scope according to right.
Claims (3)
1. an antibacterial Modal fibre towel manufacture craft, it is characterized in that, technological process is as follows:
A. described Modal fibre is carried out warping process;
B. the Modal fibre after warping is carried out starching process;
C. grey cloth is woven into by through the Modal fibre described in starching process;
D. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
E. described grey cloth is processed through over-cooking drift;
F. dyeing process is carried out by through over-cooking the grey cloth after drift;
G. the grey cloth after dyeing is carried out drying and processing through drying plant;
H. the grey cloth after oven dry is carried out cutting out and sew and obtain Modal fibre towel;
I. Modal fibre towel is carried out antimicrobial treatment through antibacterial finishing agent.
2. one according to claim 1 antibacterial Modal fibre towel manufacture craft, is characterized in that: described dyeing process is dyeed 25 minutes at 65 DEG C of temperature.
3. one according to claim 1 antibacterial Modal fibre towel manufacture craft, is characterized in that: the temperature that described drying and processing adopts is 80 DEG C ~ 90 DEG C.