CN101343809A - Production method of cotton bamboo silk towel - Google Patents

Production method of cotton bamboo silk towel Download PDF

Info

Publication number
CN101343809A
CN101343809A CNA2008102121537A CN200810212153A CN101343809A CN 101343809 A CN101343809 A CN 101343809A CN A2008102121537 A CNA2008102121537 A CN A2008102121537A CN 200810212153 A CN200810212153 A CN 200810212153A CN 101343809 A CN101343809 A CN 101343809A
Authority
CN
China
Prior art keywords
towel
cotton
grey cloth
technique
yarns
Prior art date
Application number
CNA2008102121537A
Other languages
Chinese (zh)
Inventor
孙日贵
Original Assignee
孙日贵
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 孙日贵 filed Critical 孙日贵
Priority to CNA2008102121537A priority Critical patent/CN101343809A/en
Publication of CN101343809A publication Critical patent/CN101343809A/en

Abstract

The invention relates to a towel manufacturing process, which belongs to the textile field. The towel manufacturing process comprises the steps: silk yarns, bamboo fibers and long-staple cotton are mixed in proportion, and are manufactured into 12<S> cone yarns through cotton combing, strip drawing, rough spinning and fine spinning; the yarns are woven into a piece of grey cloth through normal starching and weaving; water soluble yarns are washed off at the high temperature from the grey cloth through a continuous washing and bleaching range, the natural impurities and slurries on the cotton yarns are removed through boiling and rinsing with an overflow dyeing machine, and the grey cloth is deoxidized, dyed, enzyme-washed, softened, dried by vibration and sewn into towels. Compared with the common cotton towel, the towel manufactured through the towel manufacturing process has the advantages that the hand feeling and the gloss are good, the towel is very smooth, the drapability is better, and the towel is not easy to be creased. And meanwhile the problem that the pure cotton towel becomes hard after being washed for a plurality of times is solved, and the process is simple.

Description

Production method of cotton bamboo silk towel
Technical field
The present invention relates to field of textiles, particularly a kind of technique for preparing towel.
Background technology
Move back boil rinsing combination machine five road hot water wash remove water-soluble silk, in overflow machine, add caustic soda, stabilizing agent and hydrogen peroxide solution boil float, adding citric acid neutralization again, with a short flannel of removing hair figure surface before deoxygenase deoxidation, the dyeing with the biology enzyme cellulase, use then (150% Remazol Huang+100% Remazol red+130% Remazol orchid)+glauber salt+soda ash dyeing, soap, add soft, concussion oven dry, sew to make towel with the fluffy softener of import Clariant with detergent.Wherein the Remazol Huang, Remazol is red, Remazol is blue is: a kind of REACTIVE DYES that German DYSTAR (De Sida) company produces.But the inventor finds in practice: existing technique for preparing towel flow process complexity, and the filoplume on the towel surface of making is more, and spun silk can be removed under strong alkaline condition, and alkalescence can not make grey cloth dye normally when not enough.
Summary of the invention
The embodiment of the invention provides a kind of technique for preparing towel, makes the filoplume on the towel surface of making less, and has shortened technological process.
Purpose of the present invention is achieved through the following technical solutions:
A kind of technique for preparing towel comprises step:
Spun silk, bamboo fibre, long-staple cotton in proportion behind the mixed cotton, are made 12 SThe tube yarn;
With described tube yarn, be woven into grey cloth;
Described grey cloth is immersed in moves back in the hot water storgae that boils rinsing combination machine, water-soluble silk is removed in flushing;
Described grey cloth boiled float, deoxidation, ferment are washed, dyeing, soap boiling, add soft, oscillation drying and towel is made in sewing.
Technique scheme has following technique effect: because described grey cloth is immersed in and moves back in the hot water storgae that boils rinsing combination machine, water-soluble silk is removed in flushing; , and described grey cloth boiled float, deoxidation, ferment are washed, dyeing, soap boiling, add operation such as soft and make towel, make the filoplume on the towel surface of making less; thereby this towel compares with common cotton system towel, has good hand feeling and gloss, feels very smooth; drapability is better, is not easy to fold.Improve cotton towel simultaneously and repeatedly washed the situation that the back is sent out plate, hardened, and shortened technological process.
The specific embodiment
Describe the technical scheme of the embodiment of the invention below in detail, specifically comprise step:
1, raw cotton treatment process: griping cotton machine grasps cotton piece in the spun silk, bamboo fibre, the long-staple cotton bale of cotton of proportionally discharging, through preliminary garnetting with mixes after feed opener.
2, opening and cleaning step: raw cotton is through after mixing, carry out shredding and removal of impurities with opener, the shredding of opener is that hired roughneck's (blade, brad or pin tooth) of utilizing high speed rotary hits raw cotton and cuts apart or divide comb, plays the effect that destroys the connecting forces between fiber and fiber or fiber and the impurity.Removal of impurities is that the palisade bar grid of being made up of some triangle dirt rod is housed around the hired roughneck, is subjected to fiber after the high speed rotary hired roughneck effect and impurity to be invested bar grid and bump against with the dirt rod, and fiber block is detained by the dirt rod, and impurity is then from whereabouts, dirt rod gap.Raw cotton after above-mentioned a series of machinings, the shredding that has acquired a certain degree with mix.Some bigger impurity are eliminated, but a considerable amount of broken cottonseeds are arranged still, mote and staple fibre need be done further shredding and removing through scutcher, the effect of scutcher is: continue shredding and evenly mix raw cotton, continue to remove impurity and part staple fibres such as the broken seed of leaf bits, the lap or the cotton layer of certain specification made in control and improve the vertical and horizontal uniformity of cotton layer.The fiber majority is loose cotton piece in the lap, the flock state, and contain the impurity of 40-50%.
3, carding step: lap or the cotton layer feeding carding machine made are carried out the careful comb that divides completely, make bundle fiber be separated into the filament state, and pars fibrosa is stretched.Continue to remove the impurity and the fault that remain in the cotton layer.Utilize carding machine to make between fiber and fully mix, make the even oval comb and parallel cotton fibers prior to spinning carded sliver of certain density, and clocklike circle is placed in the sliver can, uses for next procedure.
4, mixing in doubling step: the comb and parallel cotton fibers prior to spinning carded sliver of carding machine production passes through preliminary orientation, stretches, and possesses the preliminary form of sliver.But because comb and parallel cotton fibers prior to spinning carded sliver irregularity is very big, and the fiber alignment disorder in the comb and parallel cotton fibers prior to spinning carded sliver, most of fiber becomes the hook solid attitude, therefore, and further need and closing the comb and parallel cotton fibers prior to spinning carded sliver before the spinning, to improve the comb and parallel cotton fibers prior to spinning carded sliver uniformity and fiber condition.Mainly comprising of this mixing in doubling step:
(1) and close: with 6~8 comb and parallel cotton fibers prior to spinning carded slivers and close feeding pre-drawing machine, make a sliver,, improve the strip long term irregularity because thick section of each root sliver, thin segment have an opportunity to overlap.The weight unevenness of the comb and parallel cotton fibers prior to spinning carded sliver is about about 4.0%, and the weight unevenness that passes through and close the after-ripening bar should drop to below 1%.
(2) drawing-off: be about to sliver and take out long drawing-down to original degree, improve the state of fiber simultaneously through drawing-off, it is parallel that crotch and crimped fibre are further stretched, and makes little flock further be separated into filament.Through changing drafting multiple, can control the quantitative of sliver effectively.
(3) mix: use repeatedly and the further filamentary mixing of realization of the method for closing, guarantee that the mixed cotton composition of sliver is even, stablize yarn quality.
(4) slivering: the regular geosphere of sliver that drawing frame is made is placed in the sliver can, so that carrying is deposited, uses for next procedure.
5, rove operation: sliver is fed Speed frames take out 5~12 times of long drawing-downs, and it is parallel that fiber is further stretched.Because the yarn cross-section fibers radical after the Speed frames drawing-off is few, extended parallelization is good, so brute force is lower, improves brute-force of rove so need add certain twist, avoiding reeling and accident during unwinding is extended, and prepares for spinning-drafting.Reeling roving after twisting on bobbin, is made the package of definite shape and size, so that the feeding on storage, carrying and the adaptation spun yarn.
6, spinning process: rove is fed fine spining machine elongation uniformly take out thin spun yarn, the spun yarn that is spun into is wound on the bobbin by certain moulding requirement, make a yarn to desired line density.
7, destarch is boiled and is floated operation: described grey cloth is immersed in moves back in the hot water storgae that boils rinsing combination machine, with the hot water injection of 100 ℃ of temperature, speed of a motor vehicle 12m/min, to reach the purpose of removing water-soluble silk fully.
8, boil and float operation: the 550kg grey cloth is put into 6000L water with overflow dyeing machine, (the caustic soda consumption directly influences the weightlessness of spun silk to the caustic soda of adding 2ml/L, therefore the caustic soda consumption for handle common cotton yarn consumption 40%), the hydrogen peroxide of 2.7ml/L hydrogen peroxide stabilizer, 8ml/L, be under 95 ℃ the condition in temperature, circulation 50min to reach the purpose of removing cotton yarn impurity and slurry, improves the whiteness of grey cloth, capillary effect is so that improve the dye-uptake of dyestuff.
9, deoxidation step: being that the 1g/L citric acid circulates under 50 ℃ condition and made the solution pH value be neutral in 15 minutes with concentration in overflow machine, is that 0.12ml/L deoxygenase JN500 solution circulates 20 minutes to reach the deoxidation purpose under 40 ℃ of conditions with concentration then.
10, ferment is washed operation: add the 0.5g/L citric acid earlier and make solution be faintly acid (pH value is between 4.5-5.5), the cellulase that adds 1.1g/L then circulated 30 minutes under 50 ℃ of conditions, to reduce the filoplume of wool warp line.Make the towel surface hairiness few, glossy.
11, dyeing process: add the red 0.0093%+130% Remazol of the yellow 0.06%+100% Remazol of 150% Remazol orchid 0.0036%, dying material such as glauber salt 8g/L, soda ash 5g/L in overflow machine, the grey cloth colouring was carried out in circulation in 30 minutes under 60 ℃ of temperature.
12, soap boiling operation: under 90 ℃ of conditions be 0.15g/L detergent solution circulated 15 minutes to remove on the grey cloth not the dying material of set with concentration.
13, add soft operation: add 3g/L softener JWJ, under 40 ℃ of conditions of temperature, circulated 30 minutes then, make product soft more, and then make towel through oscillation drying operation, sewing operation.Wherein: a kind of softener that JWJ produces for Clariant company, its effect is to make fabric more soft in processing procedure, more fluffy.
More than a kind of technique for preparing towel that the embodiment of the invention provided is described in detail, for one of ordinary skill in the art, thought according to the embodiment of the invention, part in specific embodiments and applications all can change, in sum, the content of this specification embodiment should not be construed as limitation of the present invention.

Claims (5)

1, a kind of technique for preparing towel is characterized in that, comprises step:
After spun silk, bamboo fibre, long-staple cotton mixing, make 12 SThe tube yarn;
Described tube yarn is woven into grey cloth;
Described grey cloth is immersed in moves back in the hot water storgae that boils rinsing combination machine, water-soluble silk is removed in flushing;
Described grey cloth boiled float, deoxidation, ferment are washed, dyeing, soap boiling, add soft, oscillation drying and towel is made in sewing.
2, technique for preparing towel as claimed in claim 1 is characterized in that, and is described with after spun silk, bamboo fibre, the long-staple cotton mixing, further comprises step:
Opening and cleaning step carries out shredding and removal of impurities with opener, continues shredding and impurity elimination with scutcher, and raw cotton is made the lap or the cotton layer of certain specification;
Carding step, lap or the cotton layer feeding carding machine made are carried out the careful comb that divides completely, make bundle fiber be separated into the filament state, and pars fibrosa is stretched, make the even oval comb and parallel cotton fibers prior to spinning carded sliver of certain density, and clocklike circle is placed in the sliver can, and the comb and parallel cotton fibers prior to spinning carded sliver of carding machine production is passed through preliminary orientation, stretches, and possesses the preliminary form of sliver;
The rove operation is taken out 5~12 times of long drawing-downs with comb and parallel cotton fibers prior to spinning carded sliver feeding Speed frames, and fiber is further stretched be parallel-laid into rove, the reeling roving after the twisting on bobbin, is made web-like;
Spinning process elongates the rove of described web-like feeding fine spining machine uniformly and to take out thin spun yarn to desired line density, and the spun yarn-winding that is spun on bobbin, is made a yarn.
3, technique for preparing towel as claimed in claim 1 is characterized in that, the described solution that floats grey cloth that boils contains caustic soda, hydrogen peroxide stabilizer, hydrogen peroxide.
4, technique for preparing towel as claimed in claim 3 is characterized in that, described caustic soda, stabilizing agent, hydrogen peroxide concentration are respectively 2mL/L, 2.7mL/L, 8mL/L.
5, technique for preparing towel as claimed in claim 1, it is characterized in that, described described grey cloth is immersed in moved back in the hot water storgae that boils rinsing combination machine, water-soluble silk is removed in flushing, specifically comprise: described grey cloth is moving back under 100 ℃ of temperature and is boiling in the rinsing combination machine through a decatize case, four water washing chambers, the washing of speed of a motor vehicle 12m/min.
CNA2008102121537A 2008-09-09 2008-09-09 Production method of cotton bamboo silk towel CN101343809A (en)