CN105077610A - Manufacturing process for antibacterial socks prepared from composite fibers - Google Patents
Manufacturing process for antibacterial socks prepared from composite fibers Download PDFInfo
- Publication number
- CN105077610A CN105077610A CN201510546987.1A CN201510546987A CN105077610A CN 105077610 A CN105077610 A CN 105077610A CN 201510546987 A CN201510546987 A CN 201510546987A CN 105077610 A CN105077610 A CN 105077610A
- Authority
- CN
- China
- Prior art keywords
- grey cloth
- socks
- composite fibers
- manufacturing process
- manufacture craft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing process for antibacterial socks prepared from composite fibers. The manufacturing process comprises the following steps: mixing a bamboo fiber, a cotton pulp fiber and a modal fiber to obtain a mixture, performing opening and impurity-removing on the mixture by an opener to manufacture the mixture subjected to opening and impurity-removing into a cone yarn, and weaving the cone yarn into grey cloth used for manufacturing socks; soaking the grey cloth in a hot water tank, and removing hydrosol filaments by flushing the grey cloth; scouring and bleaching the grey cloth with hydrosol filaments being removed; dyeing the scoured and bleached grey cloth; drying and ironing the dyed grey cloth by drying equipment; soaking the dried and ironed grey cloth in an antiseptic solution; and tailoring and sewing the soaked grey cloth to obtain the socks prepared from the composite fibers. The manufacturing process has the advantages that through the antibacterial treatment, the propagation of bacteria can be effectively prevented, so that the socks are not polluted by microorganisms; the socks have the characteristics of water-absorbing quality, soft handfeel and the like, have the excellent performance of moisture absorption and sweat releasing, and the remarkable high temperature resistance and stink absorbing and pollution discharge performance, and are environment-friendly, and long in service life.
Description
Technical field
The present invention relates to socks and make field, especially a kind of antibacterial composite fibers socks manufacture craft.
Background technology
Socks are one of most important daily necessities of daily life.Socks take textile fabric as raw material, the fabric with loop construction be interweaved by three system yarns.The yarn of these three systems be hair respectively through, warp and weft yarn.Along with the development of science and technology, occurred again through compiling socks fabric, this socks looped pile consolidation jail, but form is relatively single.On market, the overwhelming majority is woven socks, and the shortcomings such as filoplume is more, feel is poor easily appear in obtained socks, and the service life of socks is not long, and manufacture craft is also comparatively complicated.Due to the easy moisture absorption of socks, easily corroded by various harmful bacteria breeding, as cleaned not in time, the fermentations of going bad such as the mushroom on socks fabric, grease, protein, bacterium can grow fast with geometric progression, socks are clamminess mouldy, produce peculiar smell, affect the health of people, if the amount reproduction of malignant bacteria, cause beriberi, the healthy living of harmful to human.After living standards of the people step into " fairly well-off " and " rich type ", the consumption idea of resident can change to some extent than ever and select, pursue and this has been human social development with the household textiles of green, environmental protection and health inexorable trend, therefore, the exploitation of anti-microbial type socks, emerge in large numbers the trend in epoch of also just having coincide, meet consumer's uphold nature, be particular about the good custom of life of health.
Summary of the invention
The technical problem to be solved in the present invention is: for overcoming above-mentioned Problems existing, provides a kind of environmental protection, soft comfortable a kind of antibacterial composite fibers socks manufacture craft.
The technical solution adopted for the present invention to solve the technical problems is: a kind of antibacterial composite fibers socks manufacture craft, and technological process is as follows:
A. a yarn is made after the mixing of bamboo fibre, cotton pulp fiber and Modal fibre with after opener shredding and removal of impurities;
B. cylinder yarn is woven into the grey cloth that preparation makes socks;
C. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
D. described grey cloth is processed through over-cooking drift;
E. dyeing process is carried out by through over-cooking the grey cloth after drift;
F. the grey cloth after dyeing is carried out drying, pressing process through drying plant;
G. grey cloth is put into immersion treatment in antiseptic solution;
H. by the grey cloth after immersion treatment by cutting out and sewing and obtain composite fibre socks.
Further, described dyeing process is dyeed 20 minutes at 60 DEG C of temperature.
Further, the temperature that described drying and processing adopts is 70 DEG C ~ 80 DEG C.
Further, the time of described immersion treatment is 1 hour.
The invention has the beneficial effects as follows, a kind of antibacterial composite fibers socks manufacture craft of the present invention is through antimicrobial treatment, effectively can prevent staphylococcus aureus, growing of Candida albicans, Escherichia coli, aspergillus niger, aspergillus flavus, variable color aspergillus, Trichoderma viride, Penicillium citrinum etc. the bacteriums such as mould, socks are not stain by Institute of Micro-biology, remain water imbibition, the feature such as soft, there is excellent moisture absorbing and sweat releasing performance, outstanding resistance to elevated temperatures and the smelly blowdown performance of suction, environmental protection, long service life, and processing technology is simple, and production efficiency is high.
Detailed description of the invention
A. a yarn is made after the mixing of bamboo fibre, cotton pulp fiber and Modal fibre with after opener shredding and removal of impurities;
B. cylinder yarn is woven into the grey cloth that preparation makes socks;
C. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
D. described grey cloth is processed through over-cooking drift;
E. dyeing process is carried out by through over-cooking the grey cloth after drift;
F. the grey cloth after dyeing is carried out drying, pressing process through drying plant;
G. grey cloth is put into immersion treatment in antiseptic solution;
H. by the grey cloth after immersion treatment by cutting out and sewing and obtain composite fibre socks.
Further, dyeing process is dyeed 20 minutes at 60 DEG C of temperature.
Further, the temperature that drying and processing adopts is 70 DEG C ~ 80 DEG C.
Further, the time of immersion treatment is 1 hour.
With above-mentioned according to desirable embodiment of the present invention for enlightenment, by above-mentioned description, relevant staff in the scope not departing from this invention technological thought, can carry out various change and amendment completely.The technical scope of this invention is not limited to the content on description, must determine its technical scope according to right.
Claims (4)
1. an antibacterial composite fibers socks manufacture craft, is characterized in that, technological process is as follows:
A. a yarn is made after the mixing of bamboo fibre, cotton pulp fiber and Modal fibre with after opener shredding and removal of impurities;
B. cylinder yarn is woven into the grey cloth that preparation makes socks;
C. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
D. described grey cloth is processed through over-cooking drift;
E. dyeing process is carried out by through over-cooking the grey cloth after drift;
F. the grey cloth after dyeing is carried out drying, pressing process through drying plant;
G. grey cloth is put into immersion treatment in antiseptic solution;
H. by the grey cloth after immersion treatment by cutting out and sewing and obtain composite fibre socks.
2. a kind of antibacterial composite fibers socks manufacture craft according to claim 1, is characterized in that: described dyeing process is dyeed 20 minutes at 60 DEG C of temperature.
3. a kind of antibacterial composite fibers socks manufacture craft according to claim 1, is characterized in that: the temperature that described drying and processing adopts is 70 DEG C ~ 80 DEG C.
4. a kind of antibacterial composite fibers socks manufacture craft according to claim 1, is characterized in that: the time of described immersion treatment is 1 hour.