CN105231498A - Production process of antibacterial blended fiber socks - Google Patents
Production process of antibacterial blended fiber socks Download PDFInfo
- Publication number
- CN105231498A CN105231498A CN201510546876.0A CN201510546876A CN105231498A CN 105231498 A CN105231498 A CN 105231498A CN 201510546876 A CN201510546876 A CN 201510546876A CN 105231498 A CN105231498 A CN 105231498A
- Authority
- CN
- China
- Prior art keywords
- socks
- grey cloth
- gray fabric
- composite fibre
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production process of antibacterial blended fiber socks. After being mixed, bamboo fiber, cotton pulp fiber and polyester fiber are opened with an opener; the opened fibers are then made into cone yarns after impurity removal; the cone yarns are spun into gray fabric to be made into socks; the gray fabric is soaked in a hot water tank, and water-soluble threads are removed by flushing; the gray fabric is boiled and bleached; the gray fabric is soaked in antibacterial solution; the soaked gray fabric is cut and sewn to form blended fiber socks. According to the production process, antibacterial treatment is carried out, thus germ growth is effectively prevented, the socks are protected from contamination by microorganisms, features such as water retention and softness are retained, and the socks have excellent moisture-absorbing and sweat transfer performances, have outstanding high temperature resistance and outstanding stink-absorbing and foul-eliminating performances and are green and long in service life.
Description
Technical field
The present invention relates to socks and make field, especially a kind of antibacterial composite fibre socks manufacture craft.
Background technology
Socks are one of most important daily necessities of daily life.Socks take textile fabric as raw material, the fabric with loop construction be interweaved by three system yarns.The yarn of these three systems be hair respectively through, warp and weft yarn.Along with the development of science and technology, occurred again through compiling socks fabric, this socks looped pile consolidation jail, but form is relatively single.On market, the overwhelming majority is woven socks, and the shortcomings such as filoplume is more, feel is poor easily appear in obtained socks, and the service life of socks is not long, and manufacture craft is also comparatively complicated.Due to the easy moisture absorption of socks, easily corroded by various harmful bacteria breeding, as cleaned not in time, the fermentations of going bad such as the mushroom on socks fabric, grease, protein, bacterium can grow fast with geometric progression, socks are clamminess mouldy, produce peculiar smell, affect the health of people, if the amount reproduction of malignant bacteria, cause beriberi, the healthy living of harmful to human.After living standards of the people step into " fairly well-off " and " rich type ", the consumption idea of resident can change to some extent than ever and select, pursue and this has been human social development with the household textiles of green, environmental protection and health inexorable trend, therefore, the exploitation of anti-microbial type socks, emerge in large numbers the trend in epoch of also just having coincide, meet consumer's uphold nature, be particular about the good custom of life of health.
Summary of the invention
The technical problem to be solved in the present invention is: for overcoming above-mentioned Problems existing, provides a kind of environmental protection, soft comfortable one antibacterial composite fibre socks manufacture craft.
The technical solution adopted for the present invention to solve the technical problems is: a kind of antibacterial composite fibre socks manufacture craft, and technological process is as follows:
A. a yarn is made after the mixing of bamboo fibre, cotton pulp fiber and polyster fibre with after opener shredding and removal of impurities;
B. cylinder yarn is woven into the grey cloth that preparation makes socks;
C. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
D. described grey cloth is processed through over-cooking drift;
E. dyeing process is carried out by through over-cooking the grey cloth after drift;
F. the grey cloth after dyeing is carried out drying, pressing process through drying plant;
G. grey cloth is put into immersion treatment in antiseptic solution;
H. by the grey cloth after immersion treatment by cutting out and sewing and obtain composite fibre socks.
Further, described dyeing process is dyeed 20 minutes at 60 DEG C of temperature.
Further, the temperature that described drying and processing adopts is 70 DEG C ~ 80 DEG C.
Further, the time of described immersion treatment is 1 hour.
The invention has the beneficial effects as follows, one of the present invention antibacterial composite fibre socks manufacture craft is through antimicrobial treatment, effectively can prevent staphylococcus aureus, growing of Candida albicans, Escherichia coli, aspergillus niger, aspergillus flavus, variable color aspergillus, Trichoderma viride, Penicillium citrinum etc. the bacteriums such as mould, socks are not stain by Institute of Micro-biology, remain water imbibition, the feature such as soft, there is excellent moisture absorbing and sweat releasing performance, outstanding resistance to elevated temperatures and the smelly blowdown performance of suction, environmental protection, long service life, and processing technology is simple, and production efficiency is high.
Detailed description of the invention
A. a yarn is made after the mixing of bamboo fibre, cotton pulp fiber and polyster fibre with after opener shredding and removal of impurities;
B. cylinder yarn is woven into the grey cloth that preparation makes socks;
C. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
D. described grey cloth is processed through over-cooking drift;
E. dyeing process is carried out by through over-cooking the grey cloth after drift;
F. the grey cloth after dyeing is carried out drying, pressing process through drying plant;
G. grey cloth is put into immersion treatment in antiseptic solution;
H. by the grey cloth after immersion treatment by cutting out and sewing and obtain composite fibre socks.
Further, dyeing process is dyeed 20 minutes at 60 DEG C of temperature.
Further, the temperature that drying and processing adopts is 70 DEG C ~ 80 DEG C.
Further, the time of immersion treatment is 1 hour.
With above-mentioned according to desirable embodiment of the present invention for enlightenment, by above-mentioned description, relevant staff in the scope not departing from this invention technological thought, can carry out various change and amendment completely.The technical scope of this invention is not limited to the content on description, must determine its technical scope according to right.
Claims (4)
1. an antibacterial composite fibre socks manufacture craft, it is characterized in that, technological process is as follows:
A. a yarn is made after the mixing of bamboo fibre, cotton pulp fiber and polyster fibre with after opener shredding and removal of impurities;
B. cylinder yarn is woven into the grey cloth that preparation makes socks;
C. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
D. described grey cloth is processed through over-cooking drift;
E. dyeing process is carried out by through over-cooking the grey cloth after drift;
F. the grey cloth after dyeing is carried out drying, pressing process through drying plant;
G. grey cloth is put into immersion treatment in antiseptic solution;
H. by the grey cloth after immersion treatment by cutting out and sewing and obtain composite fibre socks.
2. one according to claim 1 antibacterial composite fibre socks manufacture craft, is characterized in that: described dyeing process is dyeed 20 minutes at 60 DEG C of temperature.
3. one according to claim 1 antibacterial composite fibre socks manufacture craft, is characterized in that: the temperature that described drying and processing adopts is 70 DEG C ~ 80 DEG C.
4. one according to claim 1 antibacterial composite fibre socks manufacture craft, is characterized in that: the time of described immersion treatment is 1 hour.