CN105220351A - A kind of suitable winding crape terylene warp-knitted face fabric of long acting antibiotic and processing technology thereof - Google Patents
A kind of suitable winding crape terylene warp-knitted face fabric of long acting antibiotic and processing technology thereof Download PDFInfo
- Publication number
- CN105220351A CN105220351A CN201510671149.7A CN201510671149A CN105220351A CN 105220351 A CN105220351 A CN 105220351A CN 201510671149 A CN201510671149 A CN 201510671149A CN 105220351 A CN105220351 A CN 105220351A
- Authority
- CN
- China
- Prior art keywords
- yarn
- warp
- twisting
- weft yarn
- face fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of suitable winding crape terylene warp-knitted face fabric and processing technology thereof of long acting antibiotic, comprise the first weft yarn twisting group technology, the second weft yarn twisting group technology, twist shaping, warping technology, warp-knitted face fabric weaving process, warp-knitted face fabric dyeing, warp-knitted face fabric finishing technique.The present invention can make that fabric TENSILE STRENGTH is under normal conditions large, percentage elongation is high, not yielding, enhances the third dimension of textiles, visual effect is better, have and paste little, the good springiness of skin, the advantages such as comfortable good and COLOR FASTNESS is good, also have permanent antibacterial, biocidal property simultaneously.
Description
[technical field]
The present invention relates to the technical field of textile technology, particularly a kind of suitable winding crape terylene warp-knitted face fabric of long acting antibiotic and the technical field of processing technology thereof.
[background technology]
Real silk, along winding crape, mainly applies composition: 2/20/22D mulberry silk 100%.Successively form through deep processings such as routing, heavy twist, preshrunk, environmental protection dyeing.Fabric construction adopts plain weave change, especially tatting is had to make the high twist adapting to silk, under the condition of front road longitude and latitude heavy twist, through tram distortion after dyeing and finishing contraction, the sense of cloth cover crape is obvious, outward appearance is in washing shape wrinkle, finished product is rich in nature and stretches, and intertwined point has and firmly, not easily loosens, takes off the feature split, and product is except having softness, smooth, ventilative, the advantage of easily washing, comfortableness is stronger, and drapability is better.With its crease effective, permeability is good, fabric appearance is beautiful, the feature such as soft seizes market sale focus.Real silk, along wrinkling comparatively large after winding crape wash water, can recover major part through steam ironing and after evening up.Fabric not only can dye but also can stamp, embroidery, gold stamping etc., was comparatively high-grade fashion material in summer.But real silk also exists expensive, easy yellowing along winding crape the shortcoming such as to fade.In addition, in existing fabric manufacturing process, often only use a kind of fiber as the warp thread of woven fabric, the fabric product form obtained, color, style are single, and added value is lower.
[summary of the invention]
Object of the present invention solves the problems of the prior art exactly, a kind of suitable winding crape terylene warp-knitted face fabric and processing technology thereof of long acting antibiotic are proposed, can make that fabric TENSILE STRENGTH is under normal conditions large, percentage elongation is high, not yielding, enhance the third dimension of textiles, visual effect is better, has and pastes little, the good springiness of skin, the advantages such as comfortable good and COLOR FASTNESS is good, also have permanent antibacterial, biocidal property simultaneously.
For achieving the above object, the present invention proposes a kind of suitable winding crape terylene warp-knitted face fabric of long acting antibiotic, comprise the first weft yarn, the second weft yarn, warp thread, described first weft yarn and the second weft yarn and warp thread alternately weave one by one, described first weft yarn comprises high convergency heart yarn and low shrinkage yarn, described high convergency heart yarn is positioned at center, and described low shrinkage yarn is wrapped in around high convergency heart yarn; Described low shrinkage yarn comprises middle sth. made by twisting single thread, high sth. made by twisting single thread, and described middle sth. made by twisting single thread and high single thread of twisting with the fingers are alternately arranged; Described first weft twist to from the sth. made by twisting of warp thread to different, the sth. made by twisting of described first weft yarn to from the sth. made by twisting of high convergency heart yarn, low shrinkage yarn to different.
As preferably, the specification of described first weft yarn is 75D/72F, and the specification of described second weft yarn is 100/96F, and the specification of described warp thread is 75D/72F.
As preferably, the compound fiber number of described high convergency heart yarn is 28/30D, and the compound fiber number of described low shrinkage yarn is 20/22D, and the compound fiber number of described high convergency heart yarn is greater than low shrinkage yarn.
As preferably, described first weft yarn is that Z twists with the fingers, and described warp thread is that S twists with the fingers, and described high convergency heart yarn and low shrinkage yarn are that S twists with the fingers.
As preferably, the quantity of described middle sth. made by twisting single thread is 4 strands, and the quantity that described height twists with the fingers single thread is 3 strands, and described middle sth. made by twisting single thread and high sth. made by twisting single thread interval are alternately arranged and are wrapped in outside high convergency heart yarn.
As preferably, described second weft yarn is by the silver plated fiber yarn of silver-plated antibiotic polyester fiber monofilament composite twist.
The present invention proposes a kind of processing technology of suitable winding crape terylene warp-knitted face fabric of long acting antibiotic, comprise the following steps successively:
A first weft yarn twisting group technology: adopt the silk fiber of different shrinkage to be main raw material, to wrap up the form of low shrinkage yarn outside high convergency heart yarn, design the twisting that middle sth. made by twisting single thread and high sth. made by twisting single thread interval to be alternately arranged by organizing conductive structure and be wrapped in around high convergency heart yarn.
B second weft yarn twisting group technology: adopt homodisperse silver-plated antibiotic polyester fiber to be main raw material, to wrap up the form of low shrinkage yarn outside high convergency heart yarn, design the twisting that middle sth. made by twisting single thread and high sth. made by twisting single thread interval to be alternately arranged by organizing conductive structure and be wrapped in around high convergency heart yarn.
C twist shaping: be placed in shaping box by the first weft yarn and the second weft yarn, spray high-temperature water vapor and set twist, temperature remains on 160 ~ 170 DEG C, cools certain hour subsequently again and completes twist shaping.
D warping technology:
D1 first weft yarn warping technology parameter: speed of beaming is 300 ~ 350m/min, tension in Warping: 6.20 ~ 7.82cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
D2 second weft yarn warping technology parameter: speed of beaming is 300 ~ 400m/min, tension in Warping: 7.20 ~ 9.60cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
E warp-knitted face fabric weaving process: by warp knitting machine, using the first weft yarn as rear comb, using the second weft yarn as front comb, adopts the mode of two combs through putting down tiltedly tissue to weave and forms fabric embryo cloth;
F warp-knitted face fabric dyeing: prepare working solution under room temperature, warp-knitted face fabric is devoted oneself to work in liquid, with 1.5 DEG C/min ramp to 60 DEG C, then adds dyeing auxiliaries AC-G105, insulation a period of time, takes out warp-knitted face fabric, dries after washing; Described working solution comprises each component of following ratio: black cationic dye: 3 ~ 4% (o.w.f), levelling agent: 0.2 ~ 0.5g/L, dyeing auxiliaries AC-G105:2 ~ 10g/L; The bath raio of described working solution is: 1:25, and the pH value of working solution is 5;
G warp-knitted face fabric finishing technique: adopt two padding process that roll of leaching two to carry out alkali decrement treatment to warp-knitted face fabric by alkaline dressing liquid, finally successively through preliminary drying, bake, wash, soap and stoving process.
Beneficial effect of the present invention: the present invention adopts the silk fiber of different shrinkage and silver-plated antibiotic polyester fiber to be that the first weft yarn of making of main raw material and the second weft yarn cross are knitted, can make that fabric TENSILE STRENGTH is under normal conditions large, percentage elongation is high, not yielding, enhance the third dimension of textiles, visual effect is better, have and paste little, the good springiness of skin, the advantages such as comfortable good and COLOR FASTNESS is good, also have permanent antibacterial, biocidal property simultaneously.
Feature of the present invention and advantage will be described in detail by reference to the accompanying drawings by embodiment.
[accompanying drawing explanation]
Fig. 1 is the process chart of the suitable winding crape terylene warp-knitted face fabric processing technology of a kind of long acting antibiotic of the present invention.
[detailed description of the invention]
Consult Fig. 1, the suitable winding crape terylene warp-knitted face fabric of a kind of long acting antibiotic of the present invention and, comprise the first weft yarn, the second weft yarn, warp thread, described first weft yarn and the second weft yarn and warp thread alternately weave one by one, described first weft yarn comprises high convergency heart yarn and low shrinkage yarn, described high convergency heart yarn is positioned at center, and described low shrinkage yarn is wrapped in around high convergency heart yarn, described low shrinkage yarn comprises middle sth. made by twisting single thread, high sth. made by twisting single thread, and described middle sth. made by twisting single thread and high single thread of twisting with the fingers are alternately arranged, described first weft twist to from the sth. made by twisting of warp thread to different, the sth. made by twisting of described first weft yarn to high convergency heart yarn, the sth. made by twisting of low shrinkage yarn is to difference, the specification of described first weft yarn is 75D/72F, the specification of described second weft yarn is 100/96F, the specification of described warp thread is 75D/72F, the compound fiber number of described high convergency heart yarn is 28/30D, the compound fiber number of described low shrinkage yarn is 20/22D, the compound fiber number of described high convergency heart yarn is greater than low shrinkage yarn, described first weft yarn is that Z twists with the fingers, described warp thread is that S twists with the fingers, described high convergency heart yarn and low shrinkage yarn are that S twists with the fingers, the quantity of described middle sth. made by twisting single thread is 4 strands, the quantity that described height twists with the fingers single thread is 3 strands, described middle sth. made by twisting single thread and high sth. made by twisting single thread interval are alternately arranged and are wrapped in outside high convergency heart yarn, described second weft yarn is by the silver plated fiber yarn of silver-plated antibiotic polyester fiber monofilament composite twist.
The processing technology of the suitable winding crape terylene warp-knitted face fabric of a kind of long acting antibiotic of the present invention, comprises the following steps successively:
A first weft yarn twisting group technology: adopt the silk fiber of different shrinkage to be main raw material, to wrap up the form of low shrinkage yarn outside high convergency heart yarn, design the twisting that middle sth. made by twisting single thread and high sth. made by twisting single thread interval to be alternately arranged by organizing conductive structure and be wrapped in around high convergency heart yarn.
B second weft yarn twisting group technology: adopt homodisperse silver-plated antibiotic polyester fiber to be main raw material, to wrap up the form of low shrinkage yarn outside high convergency heart yarn, design the twisting that middle sth. made by twisting single thread and high sth. made by twisting single thread interval to be alternately arranged by organizing conductive structure and be wrapped in around high convergency heart yarn.
C twist shaping: be placed in shaping box by the first weft yarn and the second weft yarn, spray high-temperature water vapor and set twist, temperature remains on 160 ~ 170 DEG C, cools certain hour subsequently again and completes twist shaping.
D warping technology:
D1 first weft yarn warping technology parameter: speed of beaming is 300 ~ 350m/min, tension in Warping: 6.20 ~ 7.82cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
D2 second weft yarn warping technology parameter: speed of beaming is 300 ~ 400m/min, tension in Warping: 7.20 ~ 9.60cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
E warp-knitted face fabric weaving process: by warp knitting machine, using the first weft yarn as rear comb, using the second weft yarn as front comb, adopts the mode of two combs through putting down tiltedly tissue to weave and forms fabric embryo cloth;
F warp-knitted face fabric dyeing: prepare working solution under room temperature, warp-knitted face fabric is devoted oneself to work in liquid, with 1.5 DEG C/min ramp to 60 DEG C, then adds dyeing auxiliaries AC-G105, insulation a period of time, takes out warp-knitted face fabric, dries after washing; Described working solution comprises each component of following ratio: black cationic dye: 3 ~ 4% (o.w.f), levelling agent: 0.2 ~ 0.5g/L, dyeing auxiliaries AC-G105:2 ~ 10g/L; The bath raio of described working solution is: 1:25, and the pH value of working solution is 5;
G warp-knitted face fabric finishing technique: adopt two padding process that roll of leaching two to carry out alkali decrement treatment to warp-knitted face fabric by alkaline dressing liquid, finally successively through preliminary drying, bake, wash, soap and stoving process.
The present invention can make that fabric TENSILE STRENGTH is under normal conditions large, percentage elongation is high, not yielding, enhances the third dimension of textiles, visual effect is better, have and paste little, the good springiness of skin, the advantages such as comfortable good and COLOR FASTNESS is good, also have permanent antibacterial, biocidal property simultaneously.
Above-described embodiment is to explanation of the present invention, is not limitation of the invention, anyly all belongs to protection scope of the present invention to the scheme after simple transformation of the present invention.
Claims (7)
1. the suitable winding crape terylene warp-knitted face fabric of a long acting antibiotic, it is characterized in that: comprise the first weft yarn, the second weft yarn, warp thread, described first weft yarn and the second weft yarn and warp thread alternately weave one by one, described first weft yarn comprises high convergency heart yarn and low shrinkage yarn, described high convergency heart yarn is positioned at center, and described low shrinkage yarn is wrapped in around high convergency heart yarn; Described low shrinkage yarn comprises middle sth. made by twisting single thread, high sth. made by twisting single thread, and described middle sth. made by twisting single thread and high single thread of twisting with the fingers are alternately arranged; Described first weft twist to from the sth. made by twisting of warp thread to different, the sth. made by twisting of described first weft yarn to from the sth. made by twisting of high convergency heart yarn, low shrinkage yarn to different.
2. the suitable winding crape terylene warp-knitted face fabric of a kind of long acting antibiotic as claimed in claim 1, it is characterized in that: the specification of described first weft yarn is 75D/72F, the specification of described second weft yarn is 100/96F, and the specification of described warp thread is 75D/72F.
3. the suitable winding crape terylene warp-knitted face fabric of a kind of long acting antibiotic as claimed in claim 1, it is characterized in that: the compound fiber number of described high convergency heart yarn is 28/30D, the compound fiber number of described low shrinkage yarn is 20/22D, and the compound fiber number of described high convergency heart yarn is greater than low shrinkage yarn.
4. the suitable winding crape terylene warp-knitted face fabric of a kind of long acting antibiotic as claimed in claim 1, is characterized in that: described first weft yarn is that Z twists with the fingers, and described warp thread is that S twists with the fingers, and described high convergency heart yarn and low shrinkage yarn are that S twists with the fingers.
5. the suitable winding crape terylene warp-knitted face fabric of a kind of long acting antibiotic as claimed in claim 1, it is characterized in that: the quantity of described middle sth. made by twisting single thread is 4 strands, the quantity that described height twists with the fingers single thread is 3 strands, and described middle sth. made by twisting single thread and high sth. made by twisting single thread interval are alternately arranged and are wrapped in outside high convergency heart yarn.
6. the suitable winding crape terylene warp-knitted face fabric of a kind of long acting antibiotic as claimed in claim 1, is characterized in that: described second weft yarn is by the silver plated fiber yarn of silver-plated antibiotic polyester fiber monofilament composite twist.
7. a processing technology for the suitable winding crape terylene warp-knitted face fabric of long acting antibiotic, is characterized in that: comprise the following steps successively:
(A) the first weft yarn twisting group technology: adopt the silk fiber of different shrinkage to be main raw material, to wrap up the form of low shrinkage yarn outside high convergency heart yarn, design the twisting that middle sth. made by twisting single thread and high sth. made by twisting single thread interval to be alternately arranged by organizing conductive structure and be wrapped in around high convergency heart yarn.
(B) the second weft yarn twisting group technology: adopt homodisperse silver-plated antibiotic polyester fiber to be main raw material, to wrap up the form of low shrinkage yarn outside high convergency heart yarn, design the twisting that middle sth. made by twisting single thread and high sth. made by twisting single thread interval to be alternately arranged by organizing conductive structure and be wrapped in around high convergency heart yarn.
(C) twist shaping: be placed in shaping box by the first weft yarn and the second weft yarn, spray high-temperature water vapor and set twist, temperature remains on 160 ~ 170 DEG C, cools certain hour subsequently again and completes twist shaping.
(D) warping technology:
(D1) the first weft yarn warping technology parameter: speed of beaming is 300 ~ 350m/min, tension in Warping: 6.20 ~ 7.82cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
(D2) the second weft yarn warping technology parameter: speed of beaming is 300 ~ 400m/min, tension in Warping: 7.20 ~ 9.60cN; Workshop temperature: 18 ~ 22 DEG C; Workshop relative humidity: 75% ~ 80%; Warping radical: front and back comb is 370; To entry mode: front and back comb is completely to be worn;
(E) warp-knitted face fabric weaving process: by warp knitting machine, using the first weft yarn as rear comb, using the second weft yarn as front comb, adopts the mode of two combs through putting down tiltedly tissue to weave and forms fabric embryo cloth;
(F) warp-knitted face fabric dyeing: prepare working solution under room temperature, warp-knitted face fabric is devoted oneself to work in liquid, with 1.5 DEG C/min ramp to 60 DEG C, then adds dyeing auxiliaries AC-G105, insulation a period of time, takes out warp-knitted face fabric, dries after washing; Described working solution comprises each component of following ratio: black cationic dye: 3 ~ 4% (o.w.f), levelling agent: 0.2 ~ 0.5g/L, dyeing auxiliaries AC-G105:2 ~ 10g/L; The bath raio of described working solution is: 1:25, and the pH value of working solution is 5;
(G) warp-knitted face fabric finishing technique: adopt two padding process that roll of leaching two to carry out alkali decrement treatment to warp-knitted face fabric by alkaline dressing liquid, finally successively through preliminary drying, bake, wash, soap and stoving process.