CN105199448A - Organosilicone modified photocatalyst nano coating and preparation method thereof - Google Patents
Organosilicone modified photocatalyst nano coating and preparation method thereof Download PDFInfo
- Publication number
- CN105199448A CN105199448A CN201510741821.5A CN201510741821A CN105199448A CN 105199448 A CN105199448 A CN 105199448A CN 201510741821 A CN201510741821 A CN 201510741821A CN 105199448 A CN105199448 A CN 105199448A
- Authority
- CN
- China
- Prior art keywords
- nano
- parts
- modified photocatalyst
- paint
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an organosilicone modified photocatalyst nano coating and a preparation method thereof. The organosilicone modified photocatalyst nano coating comprises raw materials in parts by weight as follows: absolute ethyl alcohol, epoxy silane, nano activated carbon, nano diatomite, nano titanium dioxide, nano negative ion powder, nano zinc oxide, rare-dispersed elements, glycerol, sodium benzoate, sodium hexametaphosphate, amino acid, vitamin C, a surfactant, distilled water and carboxyethyl cellulose. The preparation method of the organosilicone modified photocatalyst nano coating comprises steps as follows: low-speed stirring and mixing, ball milling, medium-speed stirring, drying, high-speed stirring, screening for preparation of powder, preparation of a solvent, mixing of the power and the solvent and preparation of the organosilicone modified photocatalyst nano coating.
Description
Technical field
The present invention relates to building material technical field, particularly relate to a kind of organic-silicon-modified Photocatalyst nano-paint and preparation method thereof.
Background technology
After interior decoration, the chemical pollutant such as ammonia of the benzene homologues in the formaldehyde in tackiness agent, paint, body of wall release can long-term slow releasing, constitutes a serious threat to indoor occupant health.People stays for some time and can feel dizzy, dizzy, breathes uncomfortable in room, directly affect the healthy of indoor occupant, so carrying out the comprehensive regulation to indoor environment after fitting up, is a urgent health engineering.
In prior art, improve indoor environment to remove ski dome, the products such as solid activated carbon, photocatalyst, dissolve formaldehyde enzyme are current more widely used products.Solid activated carbon mainly removes chemical pollutant by the mode of absorption, owing to not being oxidized, the chemical reaction such as decomposition, so elimination effect is uncertain.
The main component of photocatalyst is titanium dioxide.Electric charge can be produced under sunlight or uviolizing, react with the water molecules in air and oxygen molecule, produce negative oxygen ion and hydroxide radical free radical, the oxidation capacity that these material tools are superpower, ski dome material can be made oxidized, also the cell walls of virus and bacteria can be made to be destroyed, to reach the object removing indoor chemistry and biological pollution.This kind of medicament adopts the mode of tackiness agent that these nano particles are pasted onto body surface usually, forms thin film.But, the coefficient of thermal expansion and contraction of the coefficient of thermal expansion and contraction of this layer film and furniture and wall surface is impossible identical, because furniture and paint for wall vary, so common film technique can come off along with the prolongation film of time, after friction, film formation surface also can be destroyed, and causes medicament to lose efficacy.
Dissolve formaldehyde enzyme is the medicament of more common removing ski dome.In use procedure, in order to coordinate the reaction conditions of the reagent such as dissolve formaldehyde enzyme, need to adopt acidic solution environment.This kind of acid reagent needs to protect metal parts when spraying furniture, because the positions such as folding, screw, metal finish paint are after contact acid medicine, can produce corrosion, and the cost of labor doing to protect is more than three times of spraying cost of labor, and construction cost is high.In spraying process, produce a large amount of acid aerosol and fill the air whole room, have strong impulse smell, serious harm workmen's is healthy.
As can be seen here, remove at present the product of indoor environment chemistry, biological pollution, there is certain weak point, needing technical progress is improved.
Summary of the invention
The invention provides a kind of organic-silicon-modified Photocatalyst nano-paint and preparation method thereof.
The present invention realizes like this, a kind of organic-silicon-modified Photocatalyst nano-paint, following starting material are comprised: dehydrated alcohol 20-100 part according to parts by weight ratio, epoxy radicals silicone hydride 2-10 part, active carbon nanoparticles 6-8 part, nano diatomite 3-8 part, nano titanium oxide 8-20 part, nanometer anion powder 6-12 part, nano zine oxide 2-5 part, rare and scatter element 3-7 part, glycerol 9-15 part, Sodium Benzoate 5-15 part, Sodium hexametaphosphate 99 5-12 part, amino acid 0.5-1.2 part, vitamins C 0.3-0.8 part, tensio-active agent 1-3 part, distilled water 10-20 part and carboxyethyl cellulose 2-8 part.
Further, described organic-silicon-modified Photocatalyst nano-paint comprises following starting material according to parts by weight ratio: dehydrated alcohol 22 parts, epoxy radicals silicone hydride 2.2 parts, active carbon nanoparticles 6 parts, nano diatomite 5.5 parts, nano titanium oxide 15 parts, nanometer anion powder 7 parts, nano zine oxide 3.5 parts, rare and scatter element 4 parts, glycerol 12 parts, Sodium Benzoate 10 parts, Sodium hexametaphosphate 99 8 parts, amino acid/11 part, vitamins C 0.5 part, 2 parts, tensio-active agent, distilled water 15 parts and carboxyethyl cellulose 2 parts.
Further, described tensio-active agent is one or more the combination in polyoxyethylenated alcohol sodium sulfate, ethoxylated alkyl sulfate or alkyl glycoside.
Further, described rare and scatter element is the one in selenium, tellurium, germanium, gallium or indium.
Further, the model of described epoxy radicals silicone hydride is kh560 or kh550.
A kind of organic-silicon-modified Photocatalyst nano-paint, its preparation method is as follows:
Step one: stirring at low speed mixes;
According to each component that parts by weight ratio modulates, after dehydrated alcohol is mixed with epoxy radicals silicone hydride, active carbon nanoparticles, nano diatomite, nano titanium oxide, nanometer anion powder, nano zine oxide, rare and scatter element, glycerol, Sodium Benzoate, Sodium hexametaphosphate 99, amino acid, vitamins C and tensio-active agent are joined dehydrated alcohol mix with epoxy radicals silicone hydride after mixture in, then above-mentioned whole component is joined in stirrer to carry out stirring 0.5-1 hour under the low speed of 40-50r/min;
Step 2: ball milling;
Mixture after stirring in step one is put into ball mill and carries out ball milling, ball milling speed is 40-50r/min;
Step 3: moderate-speed mixer;
In step 2, after ball milling, then mixture is put into stirrer and mix with the moderate-speed mixer of 300-500r/min, churning time is 30-50 minute;
Step 4: dry;
After moderate-speed mixer, mixture is put into the dryer inner drying 1-1.5 hour of 100-150 degree Celsius;
Step 5: high-speed stirring;
After drying, then mixture is put into homogenizer and carry out high-speed stirring mixing with the rotating speed of 1500-3000r/min, churning time is 20-40 minute;
Step 6: pulvis is prepared in screening;
After high-speed stirring, adopted by mixture 100-150 eye mesh screen to remove foreign material, both obtained pulvis;
Step 7: prepare solvent;
Carboxyethyl cellulose is joined in distilled water, soak 5 days, obtained solvent for subsequent use;
Step 8: the mixing of pulvis and solvent;
The solvent of gained in the pulvis of gained in step 6 and step 7 is put into stirrer mix with the rotating speed stirring at low speed of 40-50r/min, churning time is 1.5-2 hour;
After stirring at low speed, then carry out moderate-speed mixer mixing with the rotating speed of 300-500r/min, churning time is 30-50 minute;
Step 9: prepare organic-silicon-modified Photocatalyst nano-paint;
Use high-shear emulsion machine to carry out dispersion treatment 20-40 minute the material after being uniformly mixed in step 8, adopt ultrasonic dispersing machine to carry out dispersion treatment 5-15 minute, be i.e. obtained organic-silicon-modified Photocatalyst nano-paint.
The advantage of a kind of organic-silicon-modified Photocatalyst nano-paint provided by the invention and preparation method thereof is: the present invention effectively can remove the chemical pollutant of finishing material release after interior decoration, also can the biological pollutant such as elimination virus bacterium, product has no irritating odor, there is no secondary pollution, do not need in construction process to protect, can not the parts such as corroding metal, construction cost can be reduced;
The present invention is directed to the uncertain problem of solid activated carbon sorption chemical pollution effects, the pioneering above-mentioned raw materials that adopts is prepared into organosilicon composite photo catalyst, the catalyzer such as active carbon nanoparticles, glycerol, nano titanium oxide, nano diatomite, nanometer anion powder, nano zine oxide, rare and scatter element and epoxy radicals silicone hydride are added in addition in manufacturing processed, chemical pollutant is adsorbed by silane coupling agent, thoroughly clears the pollution off;
The present invention initiates supramolecule without film-forming process, solves common use adhesive products and is easily destroyed in film forming situation, occur the problem of pollution rebound, realizes the object of permanent long-acting removing ski dome;
Product of the present invention is without the need to construction protection; for the problem of the existing acid environmental friendly indoor medicament corroding metal component generally used; succeed in developing weakly alkaline emulsion; can not corroding metal accessory; construction cost more than 70% can be reduced in construction process; and the problems such as the anti-Huang of body of wall can not be caused, also can not cause the problem that colo(u)r coating decolours.
Embodiment
In order to make object of the present invention, technical scheme and advantage clearly understand, below in conjunction with embodiment, the present invention is further elaborated.Should be appreciated that specific embodiment described herein only in order to explain the present invention, be not intended to limit the present invention.
Percentage composition in following embodiment if no special instructions, is mass percentage.
Embodiment 1
Get after 2g epoxy radicals silicone hydride kh560 and dehydrated alcohol 20g mixes, add active carbon nanoparticles 6g, nano diatomite 3g, nano titanium oxide 8g, nanometer anion powder 6g, nano zine oxide 2g, selenium 3g, glycerol 9g, Sodium Benzoate 5g, Sodium hexametaphosphate 99 5g, amino acid 0.5g, vitamins C 0.3g, ethoxylated alkyl sulfate 1g join in stirrer to stir 0.5 hour under the low speed of 40r/min, put into ball mill and carry out ball milling, ball milling speed is 40r/min; Put into stirrer again and mix 30 minutes with the moderate-speed mixer of 300r/min; Put into the dryer inner drying 1 hour of 100 degrees Celsius; Put into homogenizer high speed 1500r/min again and be uniformly mixed 20 minutes; Remove foreign material with 100 eye mesh screens, both obtain pulvis; Carboxyethyl cellulose 8g joins in 20g distilled water, soaks 5 days, obtained solvent for subsequent use; Above-mentioned pulvis and solvent for subsequent use are put into stirrer low speed 50r/min and is uniformly mixed 2 hours, then moderate-speed mixer mixing 500r/min is uniformly mixed 50 minutes; High-shear emulsion machine is used to carry out dispersion treatment 40 minutes the material after above-mentioned being uniformly mixed; Dispersion treatment is carried out 15 minutes, i.e. obtained organic-silicon-modified Photocatalyst nano-paint with ultrasonic dispersing machine.
Organic-silicon-modified Photocatalyst nano-paint prepared by the present embodiment, through verification experimental verification, he thoroughly can remove the formaldehyde of fitment process, benzene,toluene,xylene, ammonia, TVOC (total volatile organism etc., chemical pollutant.Process of the test is as follows:
Subjects is detect company through authority after finishing completes to detect between indoor formaldehyde, benzene,toluene,xylene, the overproof finishing back room of ammonia, then carries out the organic-silicon-modified Photocatalyst nano-paint obtained by even application the present embodiment to metope and furniture surfaces externally and internally.For the bibulous material such as bare board, carpet, 3 sprayings be carried out.Spraying terminates the dry 24-48 hour of rear venting.
The little company of again please detecting of spraying end 50 adopts identical method to detect, and detected result shows indoor without finishing pollution, meets environmental requirement.Test-results shows that product of the present invention can thoroughly remove the finishing pollutions such as indoor formaldehyde, benzene homologues, TVOC.
Using method of the present invention is as follows:
Brushing: use scrubbing brush or other instrument in place's brushings such as furniture surfaces externally and internally, metopes, dry 24-48 hour.
Embodiment 2
Get after 10g epoxy radicals silicone hydride kh560 and dehydrated alcohol 100g mixes, add active carbon nanoparticles 8, nano diatomite 8g, nano titanium oxide 20g, nanometer anion powder 12g, nano zine oxide 5g, tellurium 7g, glycerol 15g, Sodium Benzoate 15g, Sodium hexametaphosphate 99 12g, amino acid/11 2g, vitamins C 0.8g, polyoxyethylenated alcohol sodium sulfate 3g join in stirrer to stir 1 hour under the low speed of 50r/min, put into ball mill and carry out ball milling, ball milling speed is 0r/min; Put into stirrer again with the moderate-speed mixer of 500r/min mixing-50 minutes; Put into the dryer inner drying 1.5 hours of 50 degrees Celsius; Put into homogenizer high speed 3000r/min again and be uniformly mixed 40 minutes; Remove foreign material with 150 eye mesh screens, both obtain pulvis; 2g carboxyethyl cellulose is joined in 10g distilled water, soak 5 days, obtained solvent for subsequent use; Above-mentioned pulvis and solvent for subsequent use are put into stirrer low speed 40r/min and is uniformly mixed 1.5 hours, then moderate-speed mixer mixing 300r/min is uniformly mixed 30 minutes; High-shear emulsion machine is used to carry out dispersion treatment 20 minutes the material after above-mentioned being uniformly mixed; Dispersion treatment is carried out 5 minutes, i.e. obtained organic-silicon-modified Photocatalyst nano-paint with ultrasonic dispersing machine.
Organic-silicon-modified Photocatalyst nano-paint prepared by the present embodiment, through verification experimental verification, he thoroughly can remove the formaldehyde of fitment process, benzene,toluene,xylene, ammonia, TVOC (total volatile organism etc., chemical pollutant.Process of the test is as follows:
Subjects is detect company through authority after finishing completes to detect between indoor formaldehyde, benzene,toluene,xylene, the overproof finishing back room of ammonia, then carries out the organic-silicon-modified Photocatalyst nano-paint obtained by even application the present embodiment to metope and furniture surfaces externally and internally.For the bibulous material such as bare board, carpet, 3 sprayings be carried out.Spraying terminates the dry 24-48 hour of rear venting.
The little company of again please detecting of spraying end 50 adopts identical method to detect, and detected result shows indoor without finishing pollution, meets environmental requirement.Test-results shows that product of the present invention can thoroughly remove the finishing pollutions such as indoor formaldehyde, benzene homologues, TVOC.
Using method of the present invention is as follows:
Brushing: use scrubbing brush or other instrument in place's brushings such as furniture surfaces externally and internally, metopes, dry 24-48 hour;
Coating adds: add in water-borne coatings, generally can add according to 10% ratio.
Embodiment 3
Get after 2.2g epoxy radicals silicone hydride kh550 and dehydrated alcohol 22g mixes, add active carbon nanoparticles 6g, nano diatomite 5.5g, nano titanium oxide 15g, nanometer anion powder 7g, nano zine oxide 3.5g, germanium 4g, glycerol 12g, Sodium Benzoate 10g, Sodium hexametaphosphate 99 8g, amino acid/11 g, vitamins C 0.5g, ethoxylated alkyl sulfate 2g join in stirrer to stir 0.7 hour under the low speed of 45r/min, put into ball mill and carry out ball milling, ball milling speed is 45r/min; Put into stirrer again and mix 40 minutes with the moderate-speed mixer of 400r/min; Put into the dryer inner drying 1.2 hours of 120 degrees Celsius; Put into homogenizer high speed 2000r/min again and be uniformly mixed 30 minutes; Remove foreign material with 130 eye mesh screens, both obtain pulvis; 2g carboxyethyl cellulose is joined in 15g distilled water, soak 5 days, obtained solvent for subsequent use; Above-mentioned pulvis and solvent for subsequent use are put into stirrer low speed 45r/min and is uniformly mixed 2 hours, then moderate-speed mixer mixing 400r/min is uniformly mixed 40 minutes; High-shear emulsion machine is used to carry out dispersion treatment 30 minutes the material after above-mentioned being uniformly mixed; Dispersion treatment is carried out 10 minutes, i.e. obtained organic-silicon-modified Photocatalyst nano-paint with ultrasonic dispersing machine.
Organic-silicon-modified Photocatalyst nano-paint prepared by the present embodiment, through verification experimental verification, he thoroughly can remove the formaldehyde of fitment process, benzene,toluene,xylene, ammonia, TVOC (total volatile organism etc., chemical pollutant.Process of the test is as follows:
Subjects is detect company through authority after finishing completes to detect between indoor formaldehyde, benzene,toluene,xylene, the overproof finishing back room of ammonia, then carries out the organic-silicon-modified Photocatalyst nano-paint obtained by even application the present embodiment to metope and furniture surfaces externally and internally.For the bibulous material such as bare board, carpet, 3 sprayings be carried out.Spraying terminates the dry 24-48 hour of rear venting.
The little company of again please detecting of spraying end 50 adopts identical method to detect, and detected result shows indoor without finishing pollution, meets environmental requirement.Test-results shows that product of the present invention can thoroughly remove the finishing pollutions such as indoor formaldehyde, benzene homologues, TVOC.
Using method of the present invention is as follows:
Brushing: use scrubbing brush or other instrument in place's brushings such as furniture surfaces externally and internally, metopes, dry 24-48 hour;
Coating adds: add in water-borne coatings, generally can add according to 10% ratio.
Embodiment 4
Get after 5g epoxy radicals silicone hydride kh560 and dehydrated alcohol 55g mixes, add active carbon nanoparticles 7g, nano diatomite 7g, nano titanium oxide 10g, nanometer anion powder 9g, nano zine oxide 3g, gallium 5g, glycerol 11g, Sodium Benzoate 8g, Sodium hexametaphosphate 99 7g, amino acid 0.7g, vitamins C 0.7g, alkyl glycoside 1.5 join in stirrer to stir 0.6 hour under the low speed of 40r/min, put into ball mill and carry out ball milling, ball milling speed is 50r/min; Put into stirrer again and mix 35 minutes with the moderate-speed mixer of 350r/min; Put into the dryer inner drying 1.1 hours of 110 degrees Celsius; Put into homogenizer high speed 2500r/min again and be uniformly mixed 25 minutes; Remove foreign material with 120 eye mesh screens, both obtain pulvis; 6g carboxyethyl cellulose is joined in 17g distilled water, soak 5 days, obtained solvent for subsequent use; Above-mentioned pulvis and solvent for subsequent use are put into stirrer low speed 45r/min and is uniformly mixed 1.4 hours, then moderate-speed mixer mixing 350r/min is uniformly mixed 35 minutes; High-shear emulsion machine is used to carry out dispersion treatment 25 minutes the material after above-mentioned being uniformly mixed; Dispersion treatment is carried out 7 minutes, i.e. obtained organic-silicon-modified Photocatalyst nano-paint with ultrasonic dispersing machine.
Organic-silicon-modified Photocatalyst nano-paint prepared by the present embodiment, through verification experimental verification, he thoroughly can remove the formaldehyde of fitment process, benzene,toluene,xylene, ammonia, TVOC (total volatile organism etc., chemical pollutant.Process of the test is as follows:
Subjects is detect company through authority after finishing completes to detect between indoor formaldehyde, benzene,toluene,xylene, the overproof finishing back room of ammonia, then carries out the organic-silicon-modified Photocatalyst nano-paint obtained by even application the present embodiment to metope and furniture surfaces externally and internally.For the bibulous material such as bare board, carpet, 3 sprayings be carried out.Spraying terminates the dry 24-48 hour of rear venting.
The little company of again please detecting of spraying end 50 adopts identical method to detect, and detected result shows indoor without finishing pollution, meets environmental requirement.Test-results shows that product of the present invention can thoroughly remove the finishing pollutions such as indoor formaldehyde, benzene homologues, TVOC.
Using method of the present invention is as follows:
Brushing: use scrubbing brush or other instrument in place's brushings such as furniture surfaces externally and internally, metopes, dry 24-48 hour;
Coating adds: add in water-borne coatings, generally can add according to 10% ratio.
Embodiment 5
Get after 4g epoxy radicals silicone hydride kh560 and dehydrated alcohol 40g mixes, add active carbon nanoparticles 6.5g, nano diatomite 4g, nano titanium oxide 17g, nanometer anion powder 11g, nano zine oxide 4.5g, indium 4g, glycerol 11g, Sodium Benzoate 13g, Sodium hexametaphosphate 99 11g, amino acid 0.9g, vitamins C 0.4g, polyoxyethylenated alcohol sodium sulfate 2.5g join in stirrer to stir 0.7 hour under the low speed of 45r/min, put into ball mill and carry out ball milling, ball milling speed is 45r/min; Put into stirrer again and mix 45 minutes with the moderate-speed mixer of 450r/min; Put into the dryer inner drying 1.4 hours of 130 degrees Celsius; Put into homogenizer high speed 2300r/min again and be uniformly mixed 30 minutes; Remove foreign material with 140 eye mesh screens, both obtain pulvis; 4g carboxyethyl cellulose is joined in 13g distilled water, soak 5 days, obtained solvent for subsequent use; Above-mentioned pulvis and solvent for subsequent use are put into stirrer low speed 40r/min and is uniformly mixed 2 hours, then moderate-speed mixer mixing 450r/min is uniformly mixed 45 minutes; High-shear emulsion machine is used to carry out dispersion treatment 35 minutes the material after above-mentioned being uniformly mixed; Dispersion treatment is carried out 12 minutes, i.e. obtained organic-silicon-modified Photocatalyst nano-paint with ultrasonic dispersing machine.
Organic-silicon-modified Photocatalyst nano-paint prepared by the present embodiment, through verification experimental verification, he thoroughly can remove the formaldehyde of fitment process, benzene,toluene,xylene, ammonia, TVOC (total volatile organism etc., chemical pollutant.Process of the test is as follows:
Subjects is detect company through authority after finishing completes to detect between indoor formaldehyde, benzene,toluene,xylene, the overproof finishing back room of ammonia, then carries out the organic-silicon-modified Photocatalyst nano-paint obtained by even application the present embodiment to metope and furniture surfaces externally and internally.For the bibulous material such as bare board, carpet, 3 sprayings be carried out.Spraying terminates the dry 24-48 hour of rear venting.
The little company of again please detecting of spraying end 50 adopts identical method to detect, and detected result shows indoor without finishing pollution, meets environmental requirement.Test-results shows that product of the present invention can thoroughly remove the finishing pollutions such as indoor formaldehyde, benzene homologues, TVOC.
Using method of the present invention is as follows:
Brushing: use scrubbing brush or other instrument in place's brushings such as furniture surfaces externally and internally, metopes, dry 24-48 hour;
Coating adds: add in water-borne coatings, generally can add according to 10% ratio.
Embodiment 6
Get after 6g epoxy radicals silicone hydride kh550 and dehydrated alcohol 80g mixes, add active carbon nanoparticles 7.5g, nano diatomite 4.5g, nano titanium oxide 14g, nanometer anion powder 9g, nano zine oxide 4g, germanium 5g, glycerol 10g, Sodium Benzoate 12g, Sodium hexametaphosphate 99 10g, amino acid/11 .1g, vitamins C 0.6g, ethoxylated alkyl sulfate 1.5g join in stirrer to stir 0.7 hour under the low speed of 45r/min, put into ball mill and carry out ball milling, ball milling speed is 45r/min; Put into stirrer again and mix 40 minutes with the moderate-speed mixer of 400r/min; Put into the dryer inner drying 1.2 hours of 120 degrees Celsius; Put into homogenizer high speed 2000r/min again and be uniformly mixed 30 minutes; Remove foreign material with 130 eye mesh screens, both obtain pulvis; 5g carboxyethyl cellulose is joined in 12g distilled water, soak 5 days, obtained solvent for subsequent use; Above-mentioned pulvis and solvent for subsequent use are put into stirrer low speed 50r/min and is uniformly mixed 2 hours, then moderate-speed mixer mixing 500r/min is uniformly mixed 50 minutes; High-shear emulsion machine is used to carry out dispersion treatment 40 minutes the material after above-mentioned being uniformly mixed; Dispersion treatment is carried out 13 minutes, i.e. obtained organic-silicon-modified Photocatalyst nano-paint with ultrasonic dispersing machine.
Organic-silicon-modified Photocatalyst nano-paint prepared by the present embodiment, through verification experimental verification, he thoroughly can remove the formaldehyde of fitment process, benzene,toluene,xylene, ammonia, TVOC (total volatile organism etc., chemical pollutant.Process of the test is as follows:
Subjects is detect company through authority after finishing completes to detect between indoor formaldehyde, benzene,toluene,xylene, the overproof finishing back room of ammonia, then carries out the organic-silicon-modified Photocatalyst nano-paint obtained by even application the present embodiment to metope and furniture surfaces externally and internally.For the bibulous material such as bare board, carpet, 3 sprayings be carried out.Spraying terminates the dry 24-48 hour of rear venting.
The little company of again please detecting of spraying end 50 adopts identical method to detect, and detected result shows indoor without finishing pollution, meets environmental requirement.Test-results shows that product of the present invention can thoroughly remove the finishing pollutions such as indoor formaldehyde, benzene homologues, TVOC.
Using method of the present invention is as follows:
Brushing: use scrubbing brush or other instrument in place's brushings such as furniture surfaces externally and internally, metopes, dry 24-48 hour;
Coating adds: add in water-borne coatings, generally can add according to 10% ratio.
Embodiment 7
Get after 9g epoxy radicals silicone hydride kh550 and dehydrated alcohol 30g mixes, add active carbon nanoparticles 7g, nano diatomite 6g, nano titanium oxide 11g, nanometer anion powder 11g, nano zine oxide 4g, gallium 6g, glycerol 12g, Sodium Benzoate 6g, Sodium hexametaphosphate 99 6g, amino acid 0.6g, vitamins C 0.6g, ethoxylated alkyl sulfate 2g join in stirrer to stir 0.7 hour under the low speed of 45r/min, put into ball mill and carry out ball milling, ball milling speed is 45r/min; Put into stirrer again and mix 40 minutes with the moderate-speed mixer of 400r/min; Put into the dryer inner drying 1.2 hours of 120 degrees Celsius; Put into homogenizer high speed 2000r/min again and be uniformly mixed 30 minutes; Remove foreign material with 130 eye mesh screens, both obtain pulvis; 6g carboxyethyl cellulose is joined in 16g distilled water, soak 5 days, obtained solvent for subsequent use; Above-mentioned pulvis and solvent for subsequent use are put into stirrer low speed 50r/min and is uniformly mixed 2 hours, then moderate-speed mixer mixing 500r/min is uniformly mixed 50 minutes; High-shear emulsion machine is used to carry out dispersion treatment 40 minutes the material after above-mentioned being uniformly mixed; Dispersion treatment is carried out 14 minutes, i.e. obtained organic-silicon-modified Photocatalyst nano-paint with ultrasonic dispersing machine.
Organic-silicon-modified Photocatalyst nano-paint prepared by the present embodiment, through verification experimental verification, he thoroughly can remove the formaldehyde of fitment process, benzene,toluene,xylene, ammonia, TVOC (total volatile organism etc., chemical pollutant.Process of the test is as follows:
Subjects is detect company through authority after finishing completes to detect between indoor formaldehyde, benzene,toluene,xylene, the overproof finishing back room of ammonia, then carries out the organic-silicon-modified Photocatalyst nano-paint obtained by even application the present embodiment to metope and furniture surfaces externally and internally.For the bibulous material such as bare board, carpet, 3 sprayings be carried out.Spraying terminates the dry 24-48 hour of rear venting.
The little company of again please detecting of spraying end 50 adopts identical method to detect, and detected result shows indoor without finishing pollution, meets environmental requirement.Test-results shows that product of the present invention can thoroughly remove the finishing pollutions such as indoor formaldehyde, benzene homologues, TVOC.
Using method of the present invention is as follows:
Brushing: use scrubbing brush or other instrument in place's brushings such as furniture surfaces externally and internally, metopes, dry 24-48 hour;
Coating adds: add in water-borne coatings, generally can add according to 10% ratio.
The advantage of a kind of organic-silicon-modified Photocatalyst nano-paint provided by the invention and preparation method thereof is: the present invention effectively can remove the chemical pollutant of finishing material release after interior decoration, also can the biological pollutant such as elimination virus bacterium, product has no irritating odor, there is no secondary pollution, do not need in construction process to protect, can not the parts such as corroding metal, construction cost can be reduced;
The present invention is directed to the uncertain problem of solid activated carbon sorption chemical pollution effects, the pioneering above-mentioned raw materials that adopts is prepared into organosilicon composite photo catalyst, the catalyzer such as active carbon nanoparticles, glycerol, nano titanium oxide, nano diatomite, nanometer anion powder, nano zine oxide, rare and scatter element and epoxy radicals silicone hydride are added in addition in manufacturing processed, chemical pollutant is adsorbed by silane coupling agent, thoroughly clears the pollution off;
The present invention initiates supramolecule without film-forming process, solves common use adhesive products and is easily destroyed in film forming situation, occur the problem of pollution rebound, realizes the object of permanent long-acting removing ski dome;
Product of the present invention is without the need to construction protection; for the problem of the existing acid environmental friendly indoor medicament corroding metal component generally used; succeed in developing weakly alkaline emulsion; can not corroding metal accessory; construction cost more than 70% can be reduced in construction process; and the problems such as the anti-Huang of body of wall can not be caused, also can not cause the problem that colo(u)r coating decolours.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any amendments done within the spirit and principles in the present invention, equivalent replacement and improvement etc., all should be included within protection scope of the present invention.
Claims (6)
1. an organic-silicon-modified Photocatalyst nano-paint, it is characterized in that, following starting material are comprised: dehydrated alcohol 20-100 part according to parts by weight ratio, epoxy radicals silicone hydride 2-10 part, active carbon nanoparticles 6-8 part, nano diatomite 3-8 part, nano titanium oxide 8-20 part, nanometer anion powder 6-12 part, nano zine oxide 2-5 part, rare and scatter element 3-7 part, glycerol 9-15 part, Sodium Benzoate 5-15 part, Sodium hexametaphosphate 99 5-12 part, amino acid 0.5-1.2 part, vitamins C 0.3-0.8 part, tensio-active agent 1-3 part, distilled water 10-20 part and carboxyethyl cellulose 2-8 part.
2. the organic-silicon-modified Photocatalyst nano-paint of one according to claim 1, it is characterized in that, comprise following starting material according to parts by weight ratio: dehydrated alcohol 22 parts, epoxy radicals silicone hydride 2.2 parts, active carbon nanoparticles 6 parts, nano diatomite 5.5 parts, nano titanium oxide 15 parts, nanometer anion powder 7 parts, nano zine oxide 3.5 parts, rare and scatter element 4 parts, glycerol 12 parts, Sodium Benzoate 10 parts, Sodium hexametaphosphate 99 8 parts, amino acid/11 part, vitamins C 0.5 part, 2 parts, tensio-active agent, distilled water 15 parts and carboxyethyl cellulose 2 parts.
3. the organic-silicon-modified Photocatalyst nano-paint of one according to claim 1, is characterized in that, described tensio-active agent is one or more the combination in polyoxyethylenated alcohol sodium sulfate, ethoxylated alkyl sulfate or alkyl glycoside.
4. the organic-silicon-modified Photocatalyst nano-paint of one according to claim 1, is characterized in that, described rare and scatter element is the one in selenium, tellurium, germanium, gallium or indium.
5. the organic-silicon-modified Photocatalyst nano-paint of one according to claim 1, is characterized in that, the model of described epoxy radicals silicone hydride is kh560 or kh550.
6., according to the organic-silicon-modified Photocatalyst nano-paint of the one in Claims 1 to 5 described in any one, it is characterized in that, its preparation method is as follows:
Step one: stirring at low speed mixes;
According to each component that parts by weight ratio modulates, after dehydrated alcohol is mixed with epoxy radicals silicone hydride, active carbon nanoparticles, nano diatomite, nano titanium oxide, nanometer anion powder, nano zine oxide, rare and scatter element, glycerol, Sodium Benzoate, Sodium hexametaphosphate 99, amino acid, vitamins C and tensio-active agent are joined dehydrated alcohol mix with epoxy radicals silicone hydride after mixture in, then above-mentioned whole component is joined in stirrer to carry out stirring 0.5-1 hour under the low speed of 40-50r/min;
Step 2: ball milling;
Mixture after stirring in step one is put into ball mill and carries out ball milling, ball milling speed is 40-50r/min;
Step 3: moderate-speed mixer;
In step 2, after ball milling, then mixture is put into stirrer and mix with the moderate-speed mixer of 300-500r/min, churning time is 30-50 minute;
Step 4: dry;
After moderate-speed mixer, mixture is put into the dryer inner drying 1-1.5 hour of 100-150 degree Celsius;
Step 5: high-speed stirring;
After drying, then mixture is put into homogenizer and carry out high-speed stirring mixing with the rotating speed of 1500-3000r/min, churning time is 20-40 minute;
Step 6: pulvis is prepared in screening;
After high-speed stirring, adopted by mixture 100-150 eye mesh screen to remove foreign material, both obtained pulvis;
Step 7: prepare solvent;
Carboxyethyl cellulose is joined in distilled water, soak 5 days, obtained solvent for subsequent use;
Step 8: the mixing of pulvis and solvent;
The solvent of gained in the pulvis of gained in step 6 and step 7 is put into stirrer mix with the rotating speed stirring at low speed of 40-50r/min, churning time is 1.5-2 hour;
After stirring at low speed, then carry out moderate-speed mixer mixing with the rotating speed of 300-500r/min, churning time is 30-50 minute;
Step 9: prepare organic-silicon-modified Photocatalyst nano-paint;
Use high-shear emulsion machine to carry out dispersion treatment 20-40 minute the material after being uniformly mixed in step 8, adopt ultrasonic dispersing machine to carry out dispersion treatment 5-15 minute, be i.e. obtained organic-silicon-modified Photocatalyst nano-paint.