CN110270352A - A kind of composite photo catalyst and preparation method thereof - Google Patents
A kind of composite photo catalyst and preparation method thereof Download PDFInfo
- Publication number
- CN110270352A CN110270352A CN201810214080.9A CN201810214080A CN110270352A CN 110270352 A CN110270352 A CN 110270352A CN 201810214080 A CN201810214080 A CN 201810214080A CN 110270352 A CN110270352 A CN 110270352A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- mixture
- composite photo
- photo catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of composite photo catalysts and preparation method thereof, it is made of following parts by weight: 10-20 parts of nano-titanium dioxide, 4-10 parts of nano zine oxide, 6-12 parts of nano silica, 8-10 parts of active carbon nanoparticles, 3-8 parts of zinc sulphide, 5-9 parts of tungsten oxide, 4-8 parts of cadmium sulfide, 3-5 parts of platinum simple substance, 4-12 parts of sodium benzoate, 20-80 parts of dehydrated alcohol, 1-2 parts of auxiliary agent, 2-3 parts of surfactant, 10-15 parts of distilled water, the present invention is directed to the uncertain problem of solid activated carbon sorption chemical pollution effects, active carbon nanoparticles are added in the fabrication process, nano-titanium dioxide, nano zine oxide, the catalyst such as platinum, adsorb chemical pollutant by silane coupling agent, thoroughly remove pollutant, the change that the present invention can discharge finishing material after interior decoration Dissociated air state, surface adsorption state, internal combustion state that pollutant generates is learned effectively to be removed, permeated, be catalyzed, degraded, it can also be with biological pollutants such as elimination virus bacteriums.
Description
Technical field
The present invention relates to a kind of photocatalysts, more particularly, to a kind of composite photo catalyst and preparation method thereof.
Background technique
In the prior art, improve indoor environment to remove ski dome, solid activated carbon, photocatalyst, formaldehyde are molten
The products such as solution enzyme are current relatively widely used products.Chemical pollutant is mainly removed by way of absorption, due to not having
There are the chemical reactions such as generation oxidation, decomposition, so elimination effect is uncertain.
Photocatalyst is a kind of using Nano titanium dioxide as the total of the photosemiconductor material with photo-catalysis function of representative
Claim, it is coated on substrate surface, under the action of ultraviolet light and visible light, generates strong catalytic degradation function: can effectively drop
Solve toxic and harmful gas in air;It can effectively kill various bacteria, and the toxin that bacterium or fungi release can be decomposed and nothing
Evilization processing;It is also equipped with simultaneously except functions such as formaldehyde, deodorization, anti-pollution, purification air.The main component of photocatalyst is titanium dioxide
Titanium.The hydrone and oxygen molecule that can be generated in charge, with air under sunlight or ultraviolet light irradiation react, and produce
Raw negative oxygen ion and hydroxyl free radical, these substances have superpower oxidability, and ski dome substance can be made by oxygen
Change, the cell wall of virus and bacteria can also be made to be destroyed, achievees the purpose that remove indoor chemistry and biological pollution.This kind of medicament is logical
These nano particles are pasted onto body surface frequently with the mode of adhesive, form thin film.But the heat of this layer film
The coefficient of thermal expansion and contraction of swollen contraction coefficients and furniture and wall surface is impossible identical, because of furniture and paint for wall
Be it is multifarious, so common film technique can fall off with the extension film of time, film formation surface also can after friction
It is destroyed, medicament is caused to fail.
Currently, the clean-up effect of the substances such as existing composite photo catalyst PARA FORMALDEHYDE PRILLS(91,95), benzene, ammonia is not good enough, therefore provide newly
Composite photo catalyst and preparation method thereof.
Summary of the invention
The object of the present invention is to provide a kind of composite photo catalysts and preparation method thereof, to solve the problems of the prior art.
A kind of composite photo catalyst is made of following parts by weight: 10-20 parts of nano-titanium dioxide, 4-10 parts of nano zine oxide,
6-12 parts of nano silica, 8-10 parts of active carbon nanoparticles, 3-8 parts of zinc sulphide, 5-9 parts of tungsten oxide, 4-8 parts of cadmium sulfide, platinum list
3-5 parts of matter, 4-12 parts of sodium benzoate, 20-80 parts of dehydrated alcohol, 1-2 parts of auxiliary agent, 2-3 parts of surfactant, distilled water 10-15
Part.
It as a preferred technical solution of the present invention, is made of following parts by weight: 10 parts of nano-titanium dioxide, nano oxygen
Change 10 parts of zinc, 6 parts of nano silica, 10 parts of active carbon nanoparticles, 8 parts of zinc sulphide, 9 parts of tungsten oxide, 4 parts of cadmium sulfide, platinum simple substance 5
Part, 4 parts of sodium benzoate, 80 parts of dehydrated alcohol, 1 part of auxiliary agent, 3 parts of surfactant, 10 parts of distilled water.
It as a preferred technical solution of the present invention, is made of following parts by weight: 15 parts of nano-titanium dioxide, nano oxygen
Change 7 parts of zinc, 9 parts of nano silica, 9 parts of active carbon nanoparticles, 5 parts of zinc sulphide, 7 parts of tungsten oxide, 6 parts of cadmium sulfide, platinum simple substance 4
Part, 8 parts of sodium benzoate, 50 parts of dehydrated alcohol, 2 parts of auxiliary agent, 3 parts of surfactant, 13 parts of distilled water.
As a preferred technical solution of the present invention, the thickener is cellulose thickener.
As a preferred technical solution of the present invention, the tungsten oxide is tungstic acid.
As a preferred technical solution of the present invention, the auxiliary agent includes light stabilizer, thickener, dispersing agent and defoaming
Agent.
As a preferred technical solution of the present invention, the surfactant is neopelex, fatty acid
Glyceride, dioctyl succinate disulfonate acid or lauryl glucoside.
A kind of preparation method of composite photo catalyst, includes the following steps:
(1) by 15 parts of nano-titanium dioxides, 7 parts of nano zine oxides, 9 parts of nano silicas, 9 parts of active carbon nanoparticles, 5 parts
Zinc sulphide, 7 parts of tungsten oxides, 6 parts of cadmium sulfides, 4 parts of platinum simple substance, 50 parts of dehydrated alcohols, 2 parts of auxiliary agents, 3 parts of surfactant mixing are equal
It is even, it is added in blender, mixing speed 60-100r/min, stirs 1-2h, obtain the first mixture;
(2) the first mixture in step (1) is put into dryer, drying temperature is set as 80-120 degrees Celsius, dries
Dry 30-50min, obtains the second mixture;
(3) the second mixture in step (2) is put into blender and is stirred again, mixing speed 1500-
2000r/min stirs 50-60min, obtains third mixture;
(4) the third mixture in step (3) is crossed into 120-150 mesh, removes impurity, obtains pulvis;
(5) pulvis and 8 parts of sodium benzoates, 13 parts of distilled water are mixed to be put into blender and is stirred with the speed of 50-80r/min
80-100min is mixed, the 4th mixture is obtained;
(6) the 4th mixture is subjected to decentralized processing with ultrasonic dispersing machine, composite photo catalyst is made.
The beneficial effects of the present invention are: the present invention provides a kind of composite photo catalyst and preparation method thereof, the present invention is for solid
The uncertain problem of body activated carbon adsorption chemical contamination effect, in the fabrication process be added active carbon nanoparticles, nano-titanium dioxide,
The catalyst such as nano zine oxide, platinum, adsorb chemical pollutant by silane coupling agent, thoroughly remove pollutant.Energy of the present invention
The chemical pollutant discharged to finishing material after interior decoration is effectively removed, can also be with biological pollutions such as elimination virus bacteriums
Object, product have no irritating odor, and without secondary pollution, do not need to protect in work progress, will not corrode the components such as metal, can
Reduce construction cost.PARA FORMALDEHYDE PRILLS(91,95), benzene, ammonia, sulfur dioxide, carbon monoxide, nitrogen oxides etc. influence having for human health
Evil organic matter plays catharsis, and practical of the present invention is suitble to promote the use of.
Specific embodiment
A kind of composite photo catalyst is made of following parts by weight: 10-20 parts of nano-titanium dioxide, 4-10 parts of nano zine oxide,
6-12 parts of nano silica, 8-10 parts of active carbon nanoparticles, 3-8 parts of zinc sulphide, 5-9 parts of tungsten oxide, 4-8 parts of cadmium sulfide, platinum list
3-5 parts of matter, 4-12 parts of sodium benzoate, 20-80 parts of dehydrated alcohol, 1-2 parts of auxiliary agent, 2-3 parts of surfactant, distilled water 10-15
Part.
The thickener is cellulose thickener.
The tungsten oxide is tungstic acid.
The auxiliary agent includes light stabilizer, thickener, dispersing agent and defoaming agent.
The surfactant is neopelex, fatty glyceride, dioctyl succinate disulfonate acid or the moon
Osmanthus base glucoside.
The present invention is described further below with reference to embodiment:
Embodiment 1
A kind of composite photo catalyst is made of following parts by weight: 10 parts of nano-titanium dioxide, nano zine oxide 10 part, nanometer
6 parts of silica, 10 parts of active carbon nanoparticles, 8 parts of zinc sulphide, 9 parts of tungsten oxide, 4 parts of cadmium sulfide, 5 parts of platinum simple substance, sodium benzoate 4
Part, 80 parts of dehydrated alcohol, 1 part of auxiliary agent, 3 parts of surfactant, 10 parts of distilled water.
The tungsten oxide is tungstic acid, and the auxiliary agent includes light stabilizer, thickener, dispersing agent and defoaming agent, described
Surfactant is neopelex, fatty glyceride.
A kind of preparation method of composite photo catalyst, includes the following steps:
(1) by 10 parts of nano-titanium dioxides, 10 parts of nano zine oxides, 6 parts of nano silicas, 10 parts of active carbon nanoparticles, 8
Part zinc sulphide, 9 parts of tungsten oxides, 4 parts of cadmium sulfides, 5 parts of platinum simple substance, 80 parts of dehydrated alcohols, 1 part of auxiliary agent, 3 parts of surfactants mixing
Uniformly, it is added in blender, mixing speed 60r/min, stirs 1h, obtain the first mixture;
(2) the first mixture in step (1) is put into dryer, drying temperature is set as 80 degrees Celsius, drying
30min obtains the second mixture;
(3) the second mixture in step (2) is put into blender and is stirred again, mixing speed 1500r/min,
50min is stirred, third mixture is obtained;
(4) the third mixture in step (3) is crossed into 120 meshes, removes impurity, obtains pulvis;
(5) pulvis and 4 parts of sodium benzoates, 10 parts of distilled water are mixed to be put into blender and is stirred with the speed of 50r/min
80min obtains the 4th mixture;
(6) the 4th mixture is subjected to decentralized processing with ultrasonic dispersing machine, composite photo catalyst is made.
Embodiment 2
A kind of composite photo catalyst is made of following parts by weight: 20 parts of nano-titanium dioxide, 4 part, nanometer two of nano zine oxide
12 parts of silica, 8 parts of active carbon nanoparticles, 8 parts of zinc sulphide, 5 parts of tungsten oxide, 8 parts of cadmium sulfide, 3 parts of platinum simple substance, sodium benzoate 12
Part, 20 parts of dehydrated alcohol, 2 parts of auxiliary agent, 2 parts of surfactant, 15 parts of distilled water.
The tungsten oxide is tungstic acid, and the auxiliary agent includes light stabilizer, thickener, dispersing agent and defoaming agent, described
Surfactant is dioctyl succinate disulfonate acid, lauryl glucoside.
A kind of preparation method of composite photo catalyst, includes the following steps:
(1) by 20 parts of nano-titanium dioxides, 4 parts of nano zine oxides, 12 parts of nano silicas, 8 parts of active carbon nanoparticles, 8
Part zinc sulphide, 5 parts of tungsten oxides, 8 parts of cadmium sulfides, 3 parts of platinum simple substance, 20 parts of dehydrated alcohols, 2 parts of auxiliary agents, 2 parts of surfactants mixing
Uniformly, it is added in blender, mixing speed 100r/min, stirs 2h, obtain the first mixture;
(2) the first mixture in step (1) is put into dryer, drying temperature is set as 120 degrees Celsius, drying
50min obtains the second mixture;
(3) the second mixture in step (2) is put into blender and is stirred again, mixing speed 2000r/min,
60min is stirred, third mixture is obtained;
(4) the third mixture in step (3) is crossed into 150 meshes, removes impurity, obtains pulvis;
(5) pulvis and 12 parts of sodium benzoates, 15 parts of distilled water are mixed to be put into blender and is stirred with the speed of 80r/min
100min obtains the 4th mixture;
(6) the 4th mixture is subjected to decentralized processing with ultrasonic dispersing machine, composite photo catalyst is made.
Embodiment 3
A kind of composite photo catalyst is made of following parts by weight: 15 parts of nano-titanium dioxide, 7 part, nanometer two of nano zine oxide
9 parts of silica, 9 parts of active carbon nanoparticles, 5 parts of zinc sulphide, 7 parts of tungsten oxide, 6 parts of cadmium sulfide, 4 parts of platinum simple substance, 8 parts of sodium benzoate,
50 parts of dehydrated alcohol, 2 parts of auxiliary agent, 3 parts of surfactant, 13 parts of distilled water.
The tungsten oxide is tungstic acid, and the auxiliary agent includes light stabilizer, thickener, dispersing agent and defoaming agent, described
Surfactant is neopelex, lauryl glucoside.
A kind of preparation method of composite photo catalyst, includes the following steps:
(1) by 15 parts of nano-titanium dioxides, 7 parts of nano zine oxides, 9 parts of nano silicas, 9 parts of active carbon nanoparticles, 5 parts
Zinc sulphide, 7 parts of tungsten oxides, 6 parts of cadmium sulfides, 4 parts of platinum simple substance, 50 parts of dehydrated alcohols, 2 parts of auxiliary agents, 3 parts of surfactant mixing are equal
It is even, it is added in blender, mixing speed 80r/min, stirs 1.5h, obtain the first mixture;
(2) the first mixture in step (1) is put into dryer, drying temperature is set as 100 degrees Celsius, drying
40min obtains the second mixture;
(3) the second mixture in step (2) is put into blender and is stirred again, mixing speed 1800r/min,
55min is stirred, third mixture is obtained;
(4) the third mixture in step (3) is crossed into 120-150 mesh, removes impurity, obtains pulvis;
(5) pulvis and 8 parts of sodium benzoates, 13 parts of distilled water are mixed to be put into blender and is stirred with the speed of 65r/min
90min obtains the 4th mixture;
(6) the 4th mixture is subjected to decentralized processing with ultrasonic dispersing machine, composite photo catalyst is made.
The present invention provides a kind of composite photo catalyst and preparation method thereof, and the present invention is polluted for solid activated carbon sorption chemical
The catalysis such as active carbon nanoparticles, nano-titanium dioxide, nano zine oxide, platinum is added in the uncertain problem of effect in the fabrication process
Agent adsorbs chemical pollutant by silane coupling agent, thoroughly removes pollutant.The present invention can be to finishing material after interior decoration
Dissociated air state, surface adsorption state, the internal combustion state of the chemical pollutant generation of release are effectively removed, are permeated, are urged
Change, degradation, can also be had no irritating odor with the biological pollutants such as elimination virus bacterium, product, without secondary pollution, work progress
In do not need to protect, the components such as metal will not be corroded, construction cost, PARA FORMALDEHYDE PRILLS(91,95), benzene, ammonia, sulfur dioxide, an oxygen can be reduced
The harmful organic substance for changing the influence human health such as carbon, nitrogen oxides plays catharsis, and practical of the present invention is suitble to push away
It is wide to use.
The foregoing is merely one embodiment of the invention, are not intended to limit the present invention, all to use equivalent substitution or equivalent transformation
Mode technical solution obtained, fall within the scope of protection of the present invention.
Claims (7)
1. a kind of composite photo catalyst, which is characterized in that be made of following parts by weight: 10-20 parts of nano-titanium dioxide, nano oxidized
4-10 parts of zinc, 6-12 parts of nano silica, 8-10 parts of active carbon nanoparticles, 3-8 parts of zinc sulphide, 5-9 parts of tungsten oxide, cadmium sulfide 4-
8 parts, 3-5 parts of platinum simple substance, 4-12 parts of sodium benzoate, 20-80 parts of dehydrated alcohol, 1-2 parts of auxiliary agent, 2-3 parts of surfactant, distillation
10-15 parts of water.
2. a kind of composite photo catalyst according to claim 1, which is characterized in that be made of following parts by weight: nanometer two
10 parts of titanium oxide, 10 parts of nano zine oxide, 6 parts of nano silica, 10 parts of active carbon nanoparticles, 8 parts of zinc sulphide, 9 parts of tungsten oxide,
4 parts of cadmium sulfide, 5 parts of platinum simple substance, 4 parts of sodium benzoate, 80 parts of dehydrated alcohol, 1 part of auxiliary agent, 3 parts of surfactant, distilled water 10
Part.
3. a kind of composite photo catalyst according to claim 1, which is characterized in that be made of following parts by weight: nanometer two
15 parts of titanium oxide, 7 parts of nano zine oxide, 9 parts of nano silica, 9 parts of active carbon nanoparticles, 5 parts of zinc sulphide, 7 parts of tungsten oxide, sulphur
6 parts of cadmium, 4 parts of platinum simple substance, 8 parts of sodium benzoate, 50 parts of dehydrated alcohol, 2 parts of auxiliary agent, 3 parts of surfactant, 13 parts of distilled water.
4. a kind of composite photo catalyst according to claims 1-3, which is characterized in that the tungsten oxide is tungstic acid.
5. a kind of composite photo catalyst according to claims 1-3, which is characterized in that the auxiliary agent include light stabilizer,
Thickener, dispersing agent and defoaming agent.
6. a kind of composite photo catalyst according to claims 1-3, which is characterized in that the surfactant is dodecane
Base benzene sulfonic acid sodium salt, fatty glyceride, dioctyl succinate disulfonate acid or lauryl glucoside.
7. a kind of preparation method of composite photo catalyst as described in claims 1-6, which comprises the steps of:
(1) by 15 parts of nano-titanium dioxides, 7 parts of nano zine oxides, 9 parts of nano silicas, 9 parts of active carbon nanoparticles, 5 parts of vulcanizations
Zinc, 7 parts of tungsten oxides, 6 parts of cadmium sulfides, 4 parts of platinum simple substance, 50 parts of dehydrated alcohols, 2 parts of auxiliary agents, 3 parts of surfactants are uniformly mixed,
It is added in blender, mixing speed 60-100r/min, stirs 1-2h, obtain the first mixture;
(2) the first mixture in step (1) is put into dryer, drying temperature is set as 80-120 degrees Celsius, dries 30-
50min obtains the second mixture;
(3) the second mixture in step (2) is put into blender and is stirred again, mixing speed 1500-2000r/
Min stirs 50-60min, obtains third mixture;
(4) the third mixture in step (3) is crossed into 120-150 mesh, removes impurity, obtains pulvis;
(5) pulvis and 8 parts of sodium benzoates, 13 parts of distilled water are mixed to be put into blender and is stirred with the speed of 50-80r/min
80-100min obtains the 4th mixture;
(6) the 4th mixture is subjected to decentralized processing with ultrasonic dispersing machine, composite photo catalyst is made.