CN105198323A - 一种高延伸高强度聚合物水泥防水涂料 - Google Patents
一种高延伸高强度聚合物水泥防水涂料 Download PDFInfo
- Publication number
- CN105198323A CN105198323A CN201510708150.2A CN201510708150A CN105198323A CN 105198323 A CN105198323 A CN 105198323A CN 201510708150 A CN201510708150 A CN 201510708150A CN 105198323 A CN105198323 A CN 105198323A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof paint
- cement waterproof
- polymer cement
- strength polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高延伸高强度聚合物水泥防水涂料,其中,液料包括以下质量份数的组分:醋酸乙烯酯-乙烯共聚乳液1000~2000份,碳酸钙浆料湿法超细研磨后端酸性分散剂LX-7?1~5份,对苯二甲酸二辛酯增塑剂100~200份,有机硅油消泡剂5~20份,水100~200份,防腐剂(有效成分CMIT/MIT),2~10份;粉料包括以下质量份数的组分:32.5级白水泥500~1000份,石英粉500~1000份,硅灰石粉1000~1500,聚羧酸盐减水剂2~10份。本发明之聚合物水泥防水涂料具有很高的粘接强度、断裂延伸率和断裂拉伸强度,能有效避免由于建筑自身的变形而使防水层破裂的情况;本发明不含甲醛、VOC等物质,环保指标检测值为0,完全能满足民用防水要求,在民用防水上具有很好的前景。
Description
技术领域
本发明涉及一种聚合物水泥防水涂料,具体涉及一种高延伸高强度聚合物水泥防水涂料。
背景技术
聚合物水泥防水涂料又称JS防水涂料,施工简单,可以冷施工,且防水层厚度只有1.5~2.0mm,再加之属于无毒、无害、无污染绿色环保型水性涂料产品,,越来越受到人民的青睐,也是国家重点推荐的材料之一。其防水原理是有机聚合物乳液失水,形成具有粘结性、连续性的弹性膜层;水泥吸收乳液中的水而硬化,柔性聚合物与硬化体相互贯穿而牢固地粘接成一个坚固有弹性的防水层;柔性聚合物填充在水泥硬化体的空隙中,使水泥硬化体更加致密而富有弹性,聚合物失水后具有更好的延伸率,水泥硬化体又填充在聚合物中,使其具有更好的户外耐久性和更好的基层适应性。因此,JS防水涂料既具有一定的韧性,又具有很高的粘接力,同时还具有很持久的耐候性。
目前,JS防水涂料在使用中依然会出现渗漏情况,究其原因有以下几方面:(1)混凝土建筑出现裂缝,使防水膜破损而导致渗漏;(2)建筑物阴角处防水膜破损;(3)聚合物乳液触变性不好,使得在防水施工时出现流挂现象,导致建筑物表面不能形成完美的防水层保护膜;(4)防水涂料粘接性不好,使防水膜和建筑物表层出现空鼓,而导致防水膜易于脱落失去对建筑物的保护作用;(5)50℃热养护中因增塑剂挥发迁移而使得拉伸强度快速增长,产品寿命不长。因此,迫切需要从JS防水涂料性能和施工性能方面进行改良,提高JS防水涂料的结构强度和耐水耐候性,使其JS防水涂料不仅具有高断裂拉伸强度,而且也具有高断裂延伸率、高强粘接力和优良的耐水耐候性,攻克建筑抗渗难题,使混凝土空隙致密。
发明内容
本发明所要解决的技术问题是,提供一种高延伸高强度聚合物水泥防水涂料。
本发明解决其技术问题采用的技术方案是,一种高延伸高强度聚合物水泥防水涂料,液料包括以下质量份数的组分:
粉料包括以下质量份数的组分:
进一步,所述醋酸乙烯酯-乙烯共聚乳液为瓦克559ED乳液
进一步,所述分散剂为碳酸钙浆料湿法超细研磨后端酸性分散剂LX-7,是专门为90级以上超细高浓重质碳酸钙涂料而设计的新型阴离子分散剂。
进一步,所述消泡剂为有机硅油消泡剂。
进一步,所述增塑剂对苯二甲酸二辛酯
进一步,粉体原材料需具有一定的细度,其中,所述硅灰石粉为200目,所述石英粉为325目,所述32.5级白水泥为325目。
优选地,本发明之一种高延伸高强度JS防水涂料的制备方法,将醋酸乙烯酯-乙烯共聚乳液、分散剂、消泡剂、水、增塑剂和防腐剂复配成液料;将白水泥、石英粉、减水剂和硅灰石粉复配成粉料,然后按照10:8的液粉比搅拌混合配制成防水涂料,搅拌时可加入适量水配制成JS防水涂料。
本发明有益的技术效果是,(1)采用改进后的醋酸乙烯酯-乙烯共聚乳液,具有很好的流动性和触变性,不仅使得施工流畅而且还可很好的避免施工时防水层出现流淌流挂情况,因此本发明JS防水涂料具有良好的耐水性、耐候性、耐久性。(2)本发明柔性聚合物可充分填充在混凝土空隙中,使得防水层和混凝土之间具有很高的粘接强度,可达到1.5Mpa。(3)本发明显著提高了JS防水涂料膜自身的断裂拉伸强度和断裂延伸率,聚合物涂料在失水后具有较好的韧性和较大的抗断裂拉伸力,断裂延伸率可达到300%~500%,断裂拉伸强度可达到1.5~2.3MPa,可有效避免由于建筑自身的变形而使防水层破裂的情况。(4)本发明所采用原材料和助剂等均属于环保型材料,不含甲醛、VOC等物质,环保指标检测值为0,完全能满足民用防水要求,在民用防水上具有很好的前景。
具体实施方式
以下结合具体实施例对本发明作进一步详细说明。
实施例1
液料:取1400份醋酸乙烯酯-乙烯共聚,3份碳酸钙浆料湿法超细研磨后端酸性分散剂LX-7和7份有机硅油消泡剂,加入100份水,100份对苯二甲酸二辛酯增塑剂,1份防腐剂(有效成分CMIT/MIT)常温搅拌30分钟,混合均匀,备用。
粉料:取1000份200目的硅灰石粉、600份325目的石英粉、600份325目的32.5级白水泥和4份聚羧酸盐减水剂,常温搅拌0.5小时,混合均匀,备用。
将按照液料:粉料=10:8的比例将粉料加入到液料中,可加入适量水调节施工性能搅拌5分钟,混合均匀。
按照标准GB/T23445-2009I型标准测定其性能。测试实施例1制备的JS防水涂料产品的断裂延伸率为330%(≥200%),拉伸强度为2.0MPa(≥1.2MPa),其粘接强度达到1.3MPa(≥0.5MPa)左右,-10℃冷冻液下0.5h后沿10mm圆棒对弯无裂纹,不同条件处理下拉伸性能保持率均能达标。
实施例2
液料:取1400醋酸乙烯酯-乙烯共聚,2份碳酸钙浆料湿法超细研磨后端酸性分散剂LX-7和7份有机硅油消泡剂,加入100份水,140份对苯二甲酸二辛酯增塑剂,1份防腐剂(有效成分CMIT/MIT)常温搅拌30分钟,混合均匀,备用。
粉料:取1000份200目的硅灰石粉、600份325目的石英粉、600份325目的32.5级白水泥和4份聚羧酸盐减水剂,常温搅拌0.5小时,混合均匀,备用。
将按照液料:粉料=10:8的比例将粉料加入到液料中,可加入适量水调节施工性能搅拌5分钟,混合均匀。
按照标准GB/T23445-2009I型标准测定其性能。测试实施例2制备的JS防水涂料产品的断裂延伸率为460%(≥200%);拉伸强度为1.8MPa(≥1.2MPa),其粘接强度达到1.4MPa左右(≥0.5MPa)-10℃冷冻液下0.5h后沿10mm圆棒对弯无裂纹,不同条件处理下拉伸性能保持率均能达标。
实施例3
液料:取1600份醋酸乙烯酯-乙烯共聚,4份碳酸钙浆料湿法超细研磨后端酸性分散剂LX-7和14份有机硅油消泡剂,加入120份水,100对苯二甲酸二辛酯增塑剂,1份防腐剂(有效成分CMIT/MIT)常温搅拌30分钟,混合均匀,备用。
粉料:取1200份200目的硅灰石粉、700份325目的石英粉、700份325目的32.5级白水泥和4份聚羧酸盐减水剂,常温搅拌0.5小时,混合均匀。
将按照液料:粉料=10:8的比例将粉料加入到液料中,可加入适量水调节施工性能搅拌5分钟,混合均匀。
按照标准GB/T23445-2009测定其性能。测试实施例3制备的JS防水涂料产品的断裂延伸率为360%(≥200%);拉伸强度为2.3MPa(≥1.2MPa),粘接强度达到1.3MPa左右(≥0.5MPa),-10℃冷冻液下0.5h后沿10mm圆棒对弯无裂纹,不同条件处理下拉伸性能保持率均能达标。
Claims (7)
1.一种高延伸高强度聚合物水泥防水涂料,其特征在于,液料包括以下质量份数的组分:
粉料包括以下质量份数的组分:
。
2.根据权利要求1所述的高延伸高强度聚合物水泥防水涂料,其特征在于,所述醋酸乙烯酯-乙烯共聚乳液为瓦克生产的559ED乳液,该产品具有较高的耐水性、良好的耐粘连性和优异的触变性,使得产品施工时不会出现流挂等情况。
3.根据权利要求1所述的高延伸高强度聚合物水泥防水涂料,其特征在于,所述分散剂为碳酸钙浆料湿法超细研磨后端酸性分散剂LX-7,是专门为90级以上超细高浓重质碳酸钙涂料而设计的新型阴离子分散剂。
4.根据权利要求1所述的高延伸高强度聚合物水泥防水涂料,其特征在于,所述消泡剂为有机硅油消泡剂。
5.根据权利要求1所述的高延伸高强度聚合物水泥防水涂料,其特征在于,所述增塑剂为对苯二甲酸二辛酯。
6.根据权利要求1所述的高延伸高强度聚合物水泥防水涂料,其特征在于为聚羧酸盐减水剂。
7.根据权利要求1所述的高延伸高强度聚合物水泥防水涂料,其特征在于,所述硅灰石粉为200目,所述石英粉为325目,所述32.5级白水泥为325目。