CN103771806A - 一种混凝土裂缝修补防水涂料 - Google Patents

一种混凝土裂缝修补防水涂料 Download PDF

Info

Publication number
CN103771806A
CN103771806A CN201410025392.7A CN201410025392A CN103771806A CN 103771806 A CN103771806 A CN 103771806A CN 201410025392 A CN201410025392 A CN 201410025392A CN 103771806 A CN103771806 A CN 103771806A
Authority
CN
China
Prior art keywords
parts
concrete crack
concrete
waterproof coating
cracks
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410025392.7A
Other languages
English (en)
Inventor
刘绍贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd
Original Assignee
XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd filed Critical XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd
Priority to CN201410025392.7A priority Critical patent/CN103771806A/zh
Publication of CN103771806A publication Critical patent/CN103771806A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种混凝土裂缝修补防水涂料，它由以下重量比的组分组成：强度等级为52.5R的普通硅酸盐水泥62～68，甲酸钙0.5～1.5，纤维素醚0.25～0.75，可再分散性乳胶粉7～15，憎水剂1～2，石英砂28～38，玻璃短切丝1～2，填充料0.25～0.75，水35～45。本发明具有粘结力强、耐水性能，而且具有耐碱、无毒、无味、使用寿命长、绿色环保的优点，比高压注浆节省综合造价百分之六十以上，达到与混凝土同样的寿命，它能较好地修补10-20mm宽的新旧裂缝(例如石膏板，内外墙及屋面的裂缝修补)，混凝土、龟裂补缝，达到补缝、防渗的目的。

Description

一种混凝土裂缝修补防水涂料
技术领域
本发明涉及一种防水涂料，具体来说是一种混凝土裂缝修补防水涂料，属于建筑材料技术领域。 
背景技术
随着建筑装饰业的大力发展，由于建筑物出现混凝土裂缝是屡见不鲜的事情，原有混凝土裂缝处理的方法是：将双组份有机高分子防水涂料，按比例调配，用高压注浆机注入裂缝，渗透入岩体细小裂缝，产生聚合反应，形成固体加固，填充物发泡，但是，由于它是有机材料，在一定时间内会萎缩，因此会渗水，使用寿命短，增加维修成本。 
后来人们采用了涂料进行缝隙的修补，然而，现在常用的填缝修补涂料，使用寿命短，成本高，工作难度大，导致其使用寿命远远小于混凝土，用双组份高分子防水涂料高压注浆一段时间后，容易出现萎缩现象。而且，常见的填缝涂料，其由于没注重成分和性能之间的关系，往往导致注浆材料使用一段时间出现严重的渗水，严重影响了混凝土及钢筋的正常使用寿命，使用者无奈之中不得不将其重新修补。 
发明内容
本发明的目的在于克服现有混凝土填缝涂料不足之处，提供一种混凝土裂缝修补防水涂料，它具有一定延伸率，不开裂、粘结力强、耐水、耐碱、无毒、无味、与混凝土同寿命、比高压注浆节省综合造价百分之六十以上，绿色环保的优点，达到补缝、防渗的目的。 
本发明的目的是通过以下技术方案来实现的：一种混凝土裂缝修补防水涂料，其特征在于：它由以下重量比的组分组成： 
Figure BSA0000100548950000021
在具体实施例中，上述的组分的重量比多采用以下几种配比，分别是： 
(1)该混凝土裂缝修补防水涂料，其组分重量比为： 
Figure BSA0000100548950000022
Figure BSA0000100548950000031
(2)该混凝土裂缝修补防水涂料，其组分重量比为： 
Figure BSA0000100548950000032
(3)该混凝土裂缝修补防水涂料，其组分重量比为： 
Figure BSA0000100548950000033
期间，上述技术方案中，所述石英砂的颗粒大小为100～150目， 较佳选择为120目。 
并且，所采用的玻璃短切丝的长度为2～3mm。 
上述技术方案中，水泥能起到很好的胶凝作用； 
甲酸钙可调节涂料的凝结时间； 
纤维素醚的添加让涂料增加粘结力； 
可再分散性乳胶粉让其增加粘结性能，起防水作用； 
憎水剂具有很好的防水效果，阻止水的进入，采用现有的常见的憎水剂； 
石英砂主要起骨料的作用，增强挂涂层的强度； 
玻璃短切丝它防开裂、耐高低温、增加强度； 
填充料为常规的涂料填充材料； 
水用于对涂料起稀释作用。 
本发明所述的混凝土裂缝修补防水涂料，它与常规的混凝土填缝涂料相比，具有以下优点： 
本产品是由强度等级为52.5R的普通硅酸盐水泥、甲酸钙、纤维素醚、可再分散性乳胶粉、憎水剂、石英砂、玻璃短切丝、填充料、及水按一定重量比组成，它具有一定的弹性、粘结力强、耐水、耐碱、无毒、无味、使用寿命长、比高压注浆节省综合造价百分之六十以上，绿色环保的优点，达到与混凝土同样的寿命，它能较好地修补10—20mm宽的新旧裂缝(例如石膏板，石棉板，内外墙及屋面的裂缝修补)，混凝土、龟裂补缝，达到补缝、防渗的目的。 
具体实施方式
下面结合实施例进一步描述本发明的技术方案，但要求保护的范围并不局限于所述。 
实施例1 
本实施例所述的混凝土裂缝修补防水涂料，它由以下重量比的组分组成： 
Figure BSA0000100548950000051
实施例2 
本实施例所述的混凝土裂缝修补防水涂料，它由以下重量比的组分组成： 
Figure BSA0000100548950000061
实施例3 
本实施例所述的混凝土裂缝修补防水涂料，它由以下重量比的组分组成： 
Figure BSA0000100548950000062
实施例4 
本实施例所述的混凝土裂缝修补防水涂料，它由以下重量比的组分组成： 
Figure 20141002539271000021
Figure BSA0000100548950000071
实施例5 
本实施例所述的混凝土裂缝修补防水涂料，它由以下重量比的组分组成： 
Figure BSA0000100548950000072
对以上各实施例制得的混凝土裂缝修补防水涂料，对其进行物理性能检测，得下表： 
不透水性／Mpa 大于或等于0.9
试件抗渗压力／Mpa 大于或等于2.0
粘结强度／Mpa 大于或等于1.7
抗压强度(Mpa) 大于或等于35-42
从以上实施例及上表得知，本发明所述的混凝土裂缝修补防水涂料，其具有一定的弹性、粘结力强、耐水性能优，而且具有耐碱、无毒、无味、使用寿命长、绿色环保的优点，比高压注浆节省综合造价百分之六十以上，达到与混凝土同样的寿命，它能较好地修补10—20mm宽的新旧裂缝(例如石膏板，石棉板，内外墙及屋面的裂缝修补)，混凝土、龟裂补缝，达到补缝、防渗的目的。 

Claims (7)

1.一种混凝土裂缝修补防水涂料，其特征在于：它由以下重量比的组分组成：
Figure FSA0000100548940000011
2.根据权利要求1所述的混凝土裂缝修补防水涂料，其特征在于：它的组分重量比为：
Figure FSA0000100548940000012
3.根据权利要求1所述的混凝土裂缝修补防水涂料，其特征在于：它的组分重量比为：
Figure FSA0000100548940000021
4.根据权利要求1所述的混凝土裂缝修补防水涂料，其特征在于：它的组分重量比为：：
Figure FSA0000100548940000022
5.根据权利要求1至4任一权利要求所述的混凝土裂缝修补防水涂料，其特征在于：所述石英砂的颗粒大小为100～150目。
6.根据权利要求5所述的混凝土裂缝修补防水涂料，其特征在于：所述石英砂的颗粒大小为120目。
7.根据权利要求1至4任一权利要求所述的混凝土裂缝修补防水涂料，其特征在于：所述的玻璃短切丝的长度为2～3mm。
CN201410025392.7A 2014-01-21 2014-01-21 一种混凝土裂缝修补防水涂料 Pending CN103771806A (zh)