CN105176224A - Acid and alkali-resistant peelable blue glue - Google Patents
Acid and alkali-resistant peelable blue glue Download PDFInfo
- Publication number
- CN105176224A CN105176224A CN201510439550.8A CN201510439550A CN105176224A CN 105176224 A CN105176224 A CN 105176224A CN 201510439550 A CN201510439550 A CN 201510439550A CN 105176224 A CN105176224 A CN 105176224A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- alkali
- peelable blue
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses acid and alkali-resistant peelable blue glue. The acid and alkali-resistant peelable blue glue comprises the following components in parts by weight: 25-35 parts of vinyl chloride-vinyl acetate resin, 20-30 parts of modified acrylic resin, 5-12 parts of a plasticizer, 3-9 parts of silicon dioxide, 2-8 parts of a blue pigment, 5-15 parts of a flatting agent, 4-12 parts of a defoaming agent and 4-14 parts of a coalescing agent. According to the acid and alkali-resistant peelable blue glue prepared by the invention, by adding the coalescing agent, the compactness of the film can be enhanced, and the acid and alkali corrosion resistance of the film can be improved. The blue glue corroded by acid and alkali on the glass can be fully peeled in a large area; no residual glue is available on the peeled glass; and the film is not worn.
Description
Technical field
The present invention relates to peelable glue technical field, particularly relate to a kind of acid and alkali-resistance peelable blue gel.
Background technology
Along with developing rapidly of information technology and flat panel display technology, the application of touch-screen is more and more general.The large Referral information system to public place, little of PC, panel computer, mobile phone, touch-screen is closely bound up with our life.
In production touch-screen process, need the protection ITO layer of touch-screen being carried out to acid and alkali corrosion in specific operation, after this operation, need protective membrane to peel off to carry out subsequent processing.Therefore, in today that touch-screen demand is growing, peel off being easy to, the demand with the peelable blue gel of acid-alkali-corrosive-resisting performance becomes more urgent.
But it is poor that peelable blue gel in the market exists resistance to acids and bases, the rete tensile strength after corrosion reduces, the deficiency of easily tearing during stripping.
Summary of the invention
The object of the invention is to overcome the deficiency that above-mentioned prior art exists, provide that a kind of acid-proof alkaline is excellent, tensile strength is high, without the peelable blue gel of cull.
For achieving the above object, the present invention is achieved by the following technical solutions:
A kind of acid and alkali-resistance peelable blue gel, meter comprises following component by weight: vinyl chloride-vinyl acetate resin 25 ~ 35 parts, acrylic resin modified 20 ~ 30 parts, 5 ~ 12 parts, softening agent, silicon-dioxide 3 ~ 9 parts, blue pigments 2 ~ 8 parts, flow agent 5 ~ 15 parts, defoamer 4 ~ 12 parts, film coalescence aid 4 ~ 14 parts.
Preferably, described acrylic resin modified be any one in organic fluorinated silicone modified acrylic resin, epoxy modified acrylic resin, hydroxyl modification acrylic resin.
Preferably, described softening agent is any one in dioctyl phthalate (DOP), dibutyl phthalate, diethyl phthalate.
Preferably, described flow agent is any one in polydimethylsiloxane, isophorone, diacetone alcohol.
Preferably, described defoamer is any one in polypropylene glycerol aether, polyoxypropylene, silicone emulsion.
Preferably, described film coalescence aid is any one in alcohol ester 12, propandiol butyl ether, 1-Methoxy-2-propyl acetate.
Beneficial effect of the present invention:
Acid and alkali-resistance peelable blue gel prepared by the present invention, adds film coalescence aid, can increase the density of rete, improves the acid-alkali-corrosive-resisting performance of rete.Glass can realize big area after acid and alkali corrosion peel off completely, peel off without cull on rear glass, and rete can not be torn.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.Following examples will contribute to those skilled in the art and understand the present invention further, but not limit the present invention in any form.It should be pointed out that to those skilled in the art, without departing from the inventive concept of the premise, some distortion and improvement can also be made.These all belong to protection scope of the present invention.
A kind of acid and alkali-resistance peelable blue gel, meter comprises following component by weight: vinyl chloride-vinyl acetate resin 25 ~ 35 parts, acrylic resin modified 20 ~ 30 parts, 5 ~ 12 parts, softening agent, silicon-dioxide 3 ~ 9 parts, blue pigments 2 ~ 8 parts, flow agent 5 ~ 15 parts, defoamer 4 ~ 12 parts, film coalescence aid 4 ~ 14 parts.
Acid and alkali-resistance peelable blue gel prepared by the present invention, have acid-proof alkaline excellence, tensile strength high, without advantages such as culls.
Embodiment 1
Acid and alkali-resistance peelable blue gel of the present invention, meter comprises following component by weight: vinyl chloride-vinyl acetate resin 25 parts, organic fluorinated silicone modified acrylic resin 30 parts, dioctyl phthalate (DOP) 5 parts, silicon-dioxide 9 parts, blue pigments 2 parts, polydimethylsiloxane 15 parts, polypropylene glycerol aether 4 parts, alcohol ester 12 parts.
Embodiment 2
Acid and alkali-resistance peelable blue gel of the present invention, meter comprises following component by weight: vinyl chloride-vinyl acetate resin 35 parts, epoxy modified acrylic resin 20 parts, dibutyl phthalate 12 parts, silicon-dioxide 3 parts, blue pigments 8 parts, isophorone 5 parts, polyoxypropylene 12 parts, propandiol butyl ether 4 parts.
Embodiment 3
Acid and alkali-resistance peelable blue gel of the present invention, meter comprises following component by weight: vinyl chloride-vinyl acetate resin 29 parts, hydroxyl modification acrylic resin 25 parts, diethyl phthalate 8 parts, silicon-dioxide 6 parts, blue pigments 5 parts, diacetone alcohol 9 parts, silicone emulsion 8 parts, 1-Methoxy-2-propyl acetate 9 parts.
Embodiment 4
Acid and alkali-resistance peelable blue gel of the present invention, meter comprises following component by weight: vinyl chloride-vinyl acetate resin 27 parts, epoxy modified acrylic resin 22 parts, dibutyl phthalate 7 parts, silicon-dioxide 4 parts, blue pigments 3 parts, isophorone 7 parts, polyoxypropylene 6 parts, propandiol butyl ether 6 parts.
Embodiment 5
Acid and alkali-resistance peelable blue gel of the present invention, meter comprises following component by weight: vinyl chloride-vinyl acetate resin 33 parts, hydroxyl modification acrylic resin 28 parts, diethyl phthalate 10 parts, silicon-dioxide 7 parts, blue pigments 6 parts, diacetone alcohol 12 parts, silicone emulsion 9 parts, 1-Methoxy-2-propyl acetate 11 parts.
Embodiment 6
Acid and alkali-resistance peelable blue gel of the present invention, meter comprises following component by weight: vinyl chloride-vinyl acetate resin 25 parts, organic fluorinated silicone modified acrylic resin 23 parts, dioctyl phthalate (DOP) 12 parts, silicon-dioxide 5 parts, blue pigments 6 parts, polydimethylsiloxane 15 parts, polypropylene glycerol aether 4 parts, alcohol ester 12 parts.
Performance test
Basic mechanical design feature of the present invention is as shown in table 1:
Table 1
As can be seen from Table 1, acid and alkali-resistance peelable blue gel prepared by the present invention, have acid-proof alkaline excellence, tensile strength high, without advantages such as culls.
Above specific embodiments of the invention are described.It is to be appreciated that the present invention is not limited to above-mentioned particular implementation, those skilled in the art can make various distortion or amendment within the scope of the claims, and this does not affect flesh and blood of the present invention.
Claims (6)
1. an acid and alkali-resistance peelable blue gel, it is characterized in that, by weight meter comprise following component: vinyl chloride-vinyl acetate resin 25 ~ 35 parts, acrylic resin modified 20 ~ 30 parts, 5 ~ 12 parts, softening agent, silicon-dioxide 3 ~ 9 parts, blue pigments 2 ~ 8 parts, flow agent 5 ~ 15 parts, defoamer 4 ~ 12 parts, film coalescence aid 4 ~ 14 parts.
2. acid and alkali-resistance peelable blue gel according to claim 1, is characterized in that: described acrylic resin modified be organic fluorinated silicone modified acrylic resin, epoxy modified acrylic resin, any one in hydroxyl modification acrylic resin.
3. acid and alkali-resistance peelable blue gel according to claim 1, is characterized in that: described softening agent is any one in dioctyl phthalate (DOP), dibutyl phthalate, diethyl phthalate.
4. acid and alkali-resistance peelable blue gel according to claim 1, is characterized in that: described flow agent is any one in polydimethylsiloxane, isophorone, diacetone alcohol.
5. acid and alkali-resistance peelable blue gel according to claim 1, is characterized in that: described defoamer is any one in polypropylene glycerol aether, polyoxypropylene, silicone emulsion.
6. acid and alkali-resistance peelable blue gel according to claim 1, is characterized in that: described film coalescence aid is any one in alcohol ester 12, propandiol butyl ether, 1-Methoxy-2-propyl acetate.