CN105176124A - Mouldproof additive used for processing wood-plastic floors - Google Patents
Mouldproof additive used for processing wood-plastic floors Download PDFInfo
- Publication number
- CN105176124A CN105176124A CN201510595304.1A CN201510595304A CN105176124A CN 105176124 A CN105176124 A CN 105176124A CN 201510595304 A CN201510595304 A CN 201510595304A CN 105176124 A CN105176124 A CN 105176124A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- add
- mouldproof
- supersound process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a mouldproof additive used for processing wood-plastic floors, relating to the technical field of floor processing. The mouldproof additive is prepared from the following raw materials in parts by weight: 10-15 parts of nano copper oxide, 6-10 parts of nano titanium dioxide, 90-100 parts of zeolite powder, 45-50 parts of soda lime, 25-30 parts of modified gypsum powder, 15-20 parts of dried alum, 12-18 parts of traditional Chinese medicine extract, 12-18 parts of sodium chloride, 10-15 parts of chitin, 10-15 parts of activated carbon, 8-12 parts of mirabilite, 6-10 parts of chilli powder, 5-8 parts of iron powder, 5-8 parts of Chinese prickly ash powder, 40-50 parts of ethanol and 500-600 parts of water. The prepared mouldproof additive has the characteristics of light and fragrant taste, safety and environment friendliness, can be used for effectively mouldproofing the floors and improving the indoor air quality, can be directly added to floor manufacturing raw materials when being used, and has good and durable mouldproof effects.
Description
Technical field:
The present invention relates to floor processing technique field, be specifically related to a kind of wood-plastic floor board processing mildewproof additive.
Background technology:
Wood-plastic floor board is a kind of novel environment-friendly wood-plastic composite material products, be composited primarily of wood powder (vegetable fibre) and thermoplastic macromolecule material and processing aid etc., the high-tech green material made through die apparatus heating extrusion moulding again after mixing, have performance and the feature of timber and plastics concurrently, the novel mixed tech materials of offering a high price of timber and plastics can be substituted.Wood-plastic floor board is the floor made from wood plastic composite, have the woodiness touch the same with timber and processing characteristics, use common instrument to get final product sawing, boring, upper nail, there is the Waterproof corrosion performance of plastics simultaneously, make it become a kind of excellent property and very durable house decorative material.Mildew-resistant process is a critical process in the course of processing of floor, and traditional diamond-making technique sprays a coating at floor surface, can not only beautify flooring look like this, can also play mildew-proof function.But containing volatile chemical in most of coating, certain potential safety hazard is existed to HUMAN HEALTH.
Summary of the invention:
Technical problem to be solved by this invention is to provide a kind of safety and environmental protection, Be very effective and lasting wood-plastic floor board processing mildewproof additive.
Technical problem to be solved by this invention adopts following technical scheme to realize:
A kind of wood-plastic floor board processing mildewproof additive, be made up of the raw material of following parts by weight:
Nano cupric oxide 10-15 part, nano titanium oxide 6-10 part, zeolite powder 90-100 part, soda-lime 45-50 part, modified landplaster 25-30 part, alumen 15-20 part, Chinese medical extract 12-18 part, sodium-chlor 12-18 part, chitin 10-15 part, gac 10-15 part, saltcake 8-12 part, red chilly powder 6-10 part, iron powder 5-8 part, zanthoxylum powder 5-8 part, ethanol 40-50 part, water 500-600 part;
Its preparation method is as follows:
(1) add in ethanol by nano cupric oxide and nano titanium oxide, supersound process 5-10min under ultrasonic frequency 22kHz, power 100W, then adds zeolite powder and soda-lime, continues supersound process 10-15min, obtains material I;
(2) alumen and mirabilite powder are broken into powder, are then heated to the 80-90 DEG C of 10-15min that stir-fries, mix with chitin, red chilly powder and zanthoxylum powder again after room temperature is down in cooling, obtain material II;
(3) be dissolved in the water by sodium-chlor, then add material II, supersound process 15-20min under ultrasonic frequency 22kHz, power 100W, obtains material III;
(4) in material III, add material I, modified landplaster, Chinese medical extract, gac and iron powder, add in ball mill after fully mixing, be milled to fineness and be less than 0.1mm, then after lyophilize, pulverize 100-120 mesh sieve.
Described modified landplaster is obtained through chitosan and nanometer aluminum chloride modified by terra alba, its preparation method is first scattered in 70-80 part ethanol by 30-35 part terra alba and 8-12 part chitosan, then supersound process 20-30min under ultrasonic frequency 22kHz, power 100W, filter, washing, filter residue is dried afterwards and 5-8 part nanometer aluminum chloride adds in ball mill, ball milling 30-45min.
Described Chinese medical extract is made up of the raw material of following parts by weight: Ginkgo Leaf 25-30 part, leaf of bamboo 25-30 part, taraxacum 20-25 part, Herba Houttuyniae 20-25 part, purslane 18-22 part, Japanese Honeysuckle 18-22 part, Folium Eucalypti Robustae 15-20 part, bark of eucommia 15-20 part, balsam pear 12-18 part, dried orange peel 12-15 part, wormwood 10-15 part, Herba Andrographis 8-12 part, tea seed 5-8 part, castor seeds 5-8 part, peppermint 3-6 part, its preparation method is: will add in extractor after all herbal medicine choppings, add 2-3 times of water gaging again, be heated to boiling state insulation 45-60min, filter, filtrate is condensed into paste, then send into freeze drier and carry out drying, cross 100-120 mesh sieve after crushed.
The invention has the beneficial effects as follows: the present invention take zeolite powder as main raw material, be aided with nano cupric oxide, nano titanium oxide and other multiple auxiliary agents with mildew-proof function, obtained mildewproof additive has the feature of fragrant taste, safety and environmental protection, can effective mildew-resistant be carried out to floor and improve IAQ (indoor air quality), directly this additive can be added floor during use makes in raw material, and anti-mold effect is good and lasting.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
The preparation of modified landplaster: first 35 parts of terra albas and 10 parts of chitosans are scattered in 80 parts of ethanol, then supersound process 30min under ultrasonic frequency 22kHz, power 100W, filters, washing, filter residue adds in ball mill with 6 parts of nanometer aluminum chloride after drying, ball milling 45min.
The preparation of Chinese medical extract: will add in extractor after 30 parts of Ginkgo Leaves, 25 parts of leaf of bamboves, 25 portions of taraxacums, 20 portions of Herba Houttuyniaes, 20 portions of purslanes, 18 portions of Japanese Honeysuckles, 15 portions of Folium Eucalypti Robustae, 15 parts of barks of eucommia, 15 portions of balsam pears, 12 parts of dried orange peels, 12 parts of wormwoods, 10 parts of Herba Andrographis, 8 parts of tea seeds, 6 parts of castor seedss and 4 parts of peppermint choppings, add 480 parts of water again, be heated to boiling state insulation 60min, filter, filtrate is condensed into paste, then send into freeze drier and carry out drying, cross 120 mesh sieves after crushed.
Embodiment 1
(1) add in 40 parts of ethanol by 10 parts of nano cupric oxides and 6 parts of nano titanium oxides, supersound process 10min under ultrasonic frequency 22kHz, power 100W, then adds 100 parts of zeolite powders and 45 parts of soda-lime, continues supersound process 15min, obtains material I;
(2) 15 parts of alumens and 8 parts of mirabilite powders are broken into powder, are then heated to the 80-90 DEG C of 15min that stir-fries, mix with 15 parts of chitins, 6 portions of red chilly powders and 5 parts of zanthoxylum powders again after room temperature is down in cooling, obtain material II;
(3) be dissolved in 500 parts of water by 12 parts of sodium-chlor, then add material II, supersound process 20min under ultrasonic frequency 22kHz, power 100W, obtains material III;
(4) in material III, add material I, 25 parts of modified landplasters, 12 parts of Chinese medical extracts, 15 parts of gacs and 5 parts of iron powders, add after fully mixing in ball mill, be milled to fineness and be less than 0.1mm, then after lyophilize, pulverize 120 mesh sieves.
Embodiment 2
(1) add in 45 parts of ethanol by 15 parts of nano cupric oxides and 8 parts of nano titanium oxides, supersound process 10min under ultrasonic frequency 22kHz, power 100W, then adds 95 parts of zeolite powders and 45 parts of soda-lime, continues supersound process 15min, obtains material I;
(2) 20 parts of alumens and 10 parts of mirabilite powders are broken into powder, are then heated to the 80-90 DEG C of 15min that stir-fries, mix with 12 parts of chitins, 8 portions of red chilly powders and 6 parts of zanthoxylum powders again after room temperature is down in cooling, obtain material II;
(3) be dissolved in 550 parts of water by 15 parts of sodium-chlor, then add material II, supersound process 20min under ultrasonic frequency 22kHz, power 100W, obtains material III;
(4) in material III, add material I, 25 parts of modified landplasters, 15 parts of Chinese medical extracts, 10 parts of gacs and 6 parts of iron powders, add after fully mixing in ball mill, be milled to fineness and be less than 0.1mm, then after lyophilize, pulverize 120 mesh sieves.
Embodiment 3
(1) 15 parts of nano cupric oxides and 10 parts of nano titanium oxides are added in 50 parts of ethanol, supersound process 10min under ultrasonic frequency 22kHz, power 100W, then add 100 parts of zeolite powders and 50 parts of soda-lime, continue supersound process 15min, obtain material I;
(2) 20 parts of alumens and 8 parts of mirabilite powders are broken into powder, are then heated to the 80-90 DEG C of 15min that stir-fries, mix with 15 parts of chitins, 10 portions of red chilly powders and 5 parts of zanthoxylum powders again after room temperature is down in cooling, obtain material II;
(3) be dissolved in 600 parts of water by 18 parts of sodium-chlor, then add material II, supersound process 20min under ultrasonic frequency 22kHz, power 100W, obtains material III;
(4) in material III, add material I, 30 parts of modified landplasters, 12 parts of Chinese medical extracts, 10 parts of gacs and 8 parts of iron powders, add after fully mixing in ball mill, be milled to fineness and be less than 0.1mm, then after lyophilize, pulverize 120 mesh sieves.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (1)
1. a wood-plastic floor board processing mildewproof additive, is characterized in that, is made up of the raw material of following parts by weight:
Nano cupric oxide 10-15 part, nano titanium oxide 6-10 part, zeolite powder 90-100 part, soda-lime 45-50 part, modified landplaster 25-30 part, alumen 15-20 part, Chinese medical extract 12-18 part, sodium-chlor 12-18 part, chitin 10-15 part, gac 10-15 part, saltcake 8-12 part, red chilly powder 6-10 part, iron powder 5-8 part, zanthoxylum powder 5-8 part, ethanol 40-50 part, water 500-600 part;
Its preparation method is as follows:
(1) add in ethanol by nano cupric oxide and nano titanium oxide, supersound process 5-10min under ultrasonic frequency 22kHz, power 100W, then adds zeolite powder and soda-lime, continues supersound process 10-15min, obtains material I;
(2) alumen and mirabilite powder are broken into powder, are then heated to the 80-90 DEG C of 10-15min that stir-fries, mix with chitin, red chilly powder and zanthoxylum powder again after room temperature is down in cooling, obtain material II;
(3) be dissolved in the water by sodium-chlor, then add material II, supersound process 15-20min under ultrasonic frequency 22kHz, power 100W, obtains material III;
(4) in material III, add material I, modified landplaster, Chinese medical extract, gac and iron powder, add in ball mill after fully mixing, be milled to fineness and be less than 0.1mm, then after lyophilize, pulverize 100-120 mesh sieve;
Described modified landplaster is obtained through chitosan and nanometer aluminum chloride modified by terra alba, its preparation method is first scattered in 70-80 part ethanol by 30-35 part terra alba and 8-12 part chitosan, then supersound process 20-30min under ultrasonic frequency 22kHz, power 100W, filter, washing, filter residue is dried afterwards and 5-8 part nanometer aluminum chloride adds in ball mill, ball milling 30-45min;
Described Chinese medical extract is made up of the raw material of following parts by weight: Ginkgo Leaf 25-30 part, leaf of bamboo 25-30 part, taraxacum 20-25 part, Herba Houttuyniae 20-25 part, purslane 18-22 part, Japanese Honeysuckle 18-22 part, Folium Eucalypti Robustae 15-20 part, bark of eucommia 15-20 part, balsam pear 12-18 part, dried orange peel 12-15 part, wormwood 10-15 part, Herba Andrographis 8-12 part, tea seed 5-8 part, castor seeds 5-8 part, peppermint 3-6 part, its preparation method is: will add in extractor after all herbal medicine choppings, add 2-3 times of water gaging again, be heated to boiling state insulation 45-60min, filter, filtrate is condensed into paste, then send into freeze drier and carry out drying, cross 100-120 mesh sieve after crushed.