CN109135179A - A kind of preparation method of the moisture-proof wood veneer of insect prevention - Google Patents
A kind of preparation method of the moisture-proof wood veneer of insect prevention Download PDFInfo
- Publication number
- CN109135179A CN109135179A CN201810965432.4A CN201810965432A CN109135179A CN 109135179 A CN109135179 A CN 109135179A CN 201810965432 A CN201810965432 A CN 201810965432A CN 109135179 A CN109135179 A CN 109135179A
- Authority
- CN
- China
- Prior art keywords
- wood veneer
- parts
- powder
- moisture
- finished product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods of the moisture-proof wood veneer of insect prevention, comprising the following steps: A, takes masson pine bark, is ground into pine powder；B, beech wood shavings are taken, beech powder is ground into；C, pine powder is put into agitator with beech powder uniformly to mix, distilled water stirring is added, sequentially adds camphorwood powder, mica powder, nano alumina powder and glass fibre in whipping process；D, fire retardant, adhesive and desiccant are added sequentially to agitator stirring, lead to nitrogen in whipping process；E, the obtained material of step D is poured into mold, with molding machine compression moulding, demoulds to obtain wood veneer semi-finished product；F, the wood veneer semi-finished product in step E are put into baking oven and carry out drying and processing, obtain wood veneer finished product.There is good vermins-proof effect and dampproof effect through wood veneer produced by the present invention.
Description
Technical field
The present invention relates to the preparation process that a kind of collose attaches together decoration panel, especially a kind of moisture-proof wood veneer of insect prevention
Preparation method.
Background technique
Common decoration panel is divided into natural wood veneer decoration panel and artificial veneer decoration panel, due to natural wood veneer
The cost of raw material is high, and performance is single, currently, being the main side of decoration panel development to the research of artificial veneer decoration panel
To the output of artificial veneer decoration panel is also cumulative year after year, and the preparation of existing artificial veneer decoration panel is commonly several originals
Hot-forming, simple process after material mixing, it is poor to the treatment effect of insect prevention, hair is easy inside artificial veneer decoration panel obtained
Infested moth, its surface is easy to give birth to various insect ovum after prolonged use, not only influences aesthetic measure, but also to indoor ring
Border will cause pollution；Decoration panel is chiefly used in interior decoration, and in the plum rain season in southern July in June-, air humidity is big, existing wood
Poor to moisture-proof treatment effect in decoration panel preparation process, indoor wood veneer is easy to become moist through, and then mouldy or swollen
It splits, influences beauty.Therefore, a kind of preparation method of moisture-proof wood veneer of insect prevention is needed, to prepare with insect prevention moisture-proof role
Wood veneer.
Summary of the invention
The object of the present invention is to provide a kind of preparation methods of the moisture-proof wood veneer of insect prevention.Through wood produced by the present invention
Decoration panel has good vermins-proof effect and dampproof effect.
Technical solution of the present invention: a kind of preparation method of the moisture-proof wood veneer of insect prevention, each raw material in terms of mass parts, including
Following steps:
A, 45 parts of masson pine barks are taken, 0.5-1.5h is impregnated with the sodium hydroxide solution that mass fraction is 20-30%, uses distilled water
It cleans, and dries, be ground into pine powder；
B, 20 parts of beech wood shavings are taken, 1-1.5h is impregnated with the sodium hydroxide solution that mass fraction is 15-20%, uses distilled water
It cleans, and dries, be ground into beech powder；
C, the pine powder in step A is put into agitator with the beech powder in step B uniformly to mix, 12 parts of distilled water is added
Stirring, stirs into starchiness mixture, 2 parts of camphorwood powders, 6 parts of mica powders, 1.1 parts of nano aluminium oxides is sequentially added in whipping process
Powder and 1.8 parts of glass fibres, mixing speed 1800-2200r/min, mixing time 30-50min；
D, 7 parts of fire retardants, 9 parts of adhesives and 6.5 parts of desiccant are added sequentially to agitator stirring, led in whipping process
Nitrogen, being kept stirring temperature within the barrel is 40-50 DEG C, mixing speed 2000-2400r/min, mixing time 35-45min；
E, the obtained material of step D is poured into mold, with molding machine compression moulding, pressing pressure 2.5-3.5Mpa,
Press temperature is 35-45 DEG C, pressing time 4-6h, demoulds to obtain wood veneer semi-finished product；
F, the wood veneer semi-finished product in step E are put into baking oven and carry out drying and processing, oven temperature is 60-80 DEG C, is dried
A length of 5-8h, obtains wood veneer finished product when dry.
In a kind of preparation method of the moisture-proof wood veneer of insect prevention above-mentioned, the moisture content of the wood veneer semi-finished product is 4-
8%, the moisture content of wood veneer finished product is 0.5-0.9%.
In a kind of preparation method of the moisture-proof wood veneer of insect prevention above-mentioned, the fire retardant includes magnesia, aluminium hydroxide
And zinc borate, the weight part ratio of magnesia, aluminium hydroxide and zinc borate are 1:1.2:0.8.
In a kind of preparation method of the moisture-proof wood veneer of insect prevention above-mentioned, described adhesive is 563 urea-formaldehyde resin adhesives.
In a kind of preparation method of the moisture-proof wood veneer of insect prevention above-mentioned, the desiccant is active carbon desiccant, activity
The mesh number of charcoal desiccant is 200-400 mesh.
In a kind of preparation method of the moisture-proof wood veneer of insect prevention above-mentioned, the mesh number of the pine powder and beech powder is
300-500 mesh.
Compared with prior art, the present invention is ground into powder, makes its tool using masson pine bark and beech wood shavings as substrate
There is good degree of mixing, distilled water is added and is stirred, properly mixed camphorwood powder, mica are sequentially added in whipping process
Powder, nano alumina powder and glass fibre, each ingredient can be sufficiently mixed；Camphorwood powder smell is refrigerant and strong, has anti-
Worm is mothproof, drives mould moisture-proof effect；Mica powder has good elasticity and toughness as a kind of excellent additive；It is suitable to receive
Rice alumina powder can reduce the generation of electrostatic charge, avoid moisture absorption；Glass fibre increases as a kind of inorganic non-metallic material
Strong material mechanical strength with higher, can be improved the integral strength of wood veneer, also have stronger insulating properties and heat-resisting
Property；It is finished to above-mentioned raw materials mixing, sequentially adds properly mixed fire retardant, adhesive and desiccant under logical condition of nitrogen gas,
The safe mixing under protective gas of each auxiliary agent, and its respective effect is played, molding machine compression moulding is then used, is taken off
Mould obtains wood veneer semi-finished product, and wood veneer semi-finished product are finally put into baking oven and carry out drying and processing, wood veneer finished product is obtained, obtains
The finished product moisture content arrived is 0.5-0.9%, and active carbon desiccant therein restores drying capacity again, moreover it is possible to effectively adsorb different
Taste, dampproof effect are good；Camphorwood powder after mixing is dispersed between pine powder and beech powder, can make wood veneer tool obtained
There is good Anti-moth-eating effect.
In addition, the step for addition fire retardant, can make wood veneer obtained have certain flame retardant effect.
To sum up, there is good vermins-proof effect and dampproof effect through wood veneer produced by the present invention.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1: a kind of preparation method of the moisture-proof wood veneer of insect prevention, each raw material is in terms of mass parts, comprising the following steps:
A, 45 parts of masson pine barks are taken, 0.5h is impregnated with the sodium hydroxide solution that mass fraction is 20-30%, is washed with distillation
Only, it and dries, is ground into pine powder；
B, 20 parts of beech wood shavings are taken, 1h is impregnated with the sodium hydroxide solution that mass fraction is 15-20%, is washed with distillation
Only, it and dries, is ground into beech powder；
C, the pine powder in step A is put into agitator with the beech powder in step B uniformly to mix, 12 parts of distilled water is added
Stirring, stirs into starchiness mixture, 2 parts of camphorwood powders, 6 parts of mica powders, 1.1 parts of nano aluminium oxides is sequentially added in whipping process
Powder and 1.8 parts of glass fibres, mixing speed 1800r/min, mixing time 30min；
D, 7 parts of fire retardants, 9 parts of adhesives and 6.5 parts of desiccant are added sequentially to agitator stirring, led in whipping process
Nitrogen, being kept stirring temperature within the barrel is 40 DEG C, mixing speed 2000r/min, mixing time 35min；
E, the obtained material of step D is poured into mold, with molding machine compression moulding, pressing pressure 2.5Mpa, compacting
Temperature is 35 DEG C, pressing time 4h, demoulds to obtain wood veneer semi-finished product；
F, the wood veneer semi-finished product in step E are put into baking oven and carry out drying and processing, oven temperature is 60 DEG C, when drying
A length of 5h obtains wood veneer finished product.
The moisture content of the wood veneer semi-finished product is 4-8%, and the moisture content of wood veneer finished product is 0.5-0.9%.
The fire retardant includes magnesia, aluminium hydroxide and zinc borate, the parts by weight of magnesia, aluminium hydroxide and zinc borate
Number ratio is 1:1.2:0.8.
Described adhesive is 563 urea-formaldehyde resin adhesives.
The desiccant is active carbon desiccant, and the mesh number of active carbon desiccant is 300 mesh.
The mesh number of the pine powder and beech powder is 400 mesh.
Embodiment 2: a kind of preparation method of the moisture-proof wood veneer of insect prevention, each raw material is in terms of mass parts, comprising the following steps:
A, 45 parts of masson pine barks are taken, 1.5h is impregnated with the sodium hydroxide solution that mass fraction is 20-30%, is washed with distillation
Only, it and dries, is ground into pine powder；
B, 20 parts of beech wood shavings are taken, 1.5h is impregnated with the sodium hydroxide solution that mass fraction is 15-20%, is washed with distillation
Only, it and dries, is ground into beech powder；
C, the pine powder in step A is put into agitator with the beech powder in step B uniformly to mix, 12 parts of distilled water is added
Stirring, stirs into starchiness mixture, 2 parts of camphorwood powders, 6 parts of mica powders, 1.1 parts of nano aluminium oxides is sequentially added in whipping process
Powder and 1.8 parts of glass fibres, mixing speed 2200r/min, mixing time 50min；
D, 7 parts of fire retardants, 9 parts of adhesives and 6.5 parts of desiccant are added sequentially to agitator stirring, led in whipping process
Nitrogen, being kept stirring temperature within the barrel is 40-50 DEG C, mixing speed 2400r/min, mixing time 45min；
E, the obtained material of step D is poured into mold, with molding machine compression moulding, pressing pressure 3.5Mpa, compacting
Temperature is 45 DEG C, pressing time 6h, demoulds to obtain wood veneer semi-finished product；
F, the wood veneer semi-finished product in step E are put into baking oven and carry out drying and processing, oven temperature is 80 DEG C, when drying
A length of 8h obtains wood veneer finished product.
The moisture content of the wood veneer semi-finished product is 4-8%, and the moisture content of wood veneer finished product is 0.5-0.9%.
The fire retardant includes magnesia, aluminium hydroxide and zinc borate, the parts by weight of magnesia, aluminium hydroxide and zinc borate
Number ratio is 1:1.2:0.8.
Described adhesive is 563 urea-formaldehyde resin adhesives.
The desiccant is active carbon desiccant, and the mesh number of active carbon desiccant is 300 mesh.
The mesh number of the pine powder and beech powder is 400 mesh.
Embodiment 3: a kind of preparation method of the moisture-proof wood veneer of insect prevention, each raw material is in terms of mass parts, comprising the following steps:
A, 45 parts of masson pine barks are taken, 1h is impregnated with the sodium hydroxide solution that mass fraction is 20-30%, is cleaned with distilled water,
And dry, it is ground into pine powder；
B, 20 parts of beech wood shavings are taken, 1.2h is impregnated with the sodium hydroxide solution that mass fraction is 15-20%, is washed with distillation
Only, it and dries, is ground into beech powder；
C, the pine powder in step A is put into agitator with the beech powder in step B uniformly to mix, 12 parts of distilled water is added
Stirring, stirs into starchiness mixture, 2 parts of camphorwood powders, 6 parts of mica powders, 1.1 parts of nano aluminium oxides is sequentially added in whipping process
Powder and 1.8 parts of glass fibres, mixing speed 2000r/min, mixing time 40min；
D, 7 parts of fire retardants, 9 parts of adhesives and 6.5 parts of desiccant are added sequentially to agitator stirring, led in whipping process
Nitrogen, being kept stirring temperature within the barrel is 45 DEG C, mixing speed 2200r/min, mixing time 40min；
E, the obtained material of step D is poured into mold, with molding machine compression moulding, pressing pressure 3Mpa, compacting temperature
Degree is 40 DEG C, pressing time 5h, demoulds to obtain wood veneer semi-finished product；
F, the wood veneer semi-finished product in step E are put into baking oven and carry out drying and processing, oven temperature is 70 DEG C, when drying
A length of 6h obtains wood veneer finished product.
The moisture content of the wood veneer semi-finished product is 4-8%, and the moisture content of wood veneer finished product is 0.5-0.9%.
The fire retardant includes magnesia, aluminium hydroxide and zinc borate, the parts by weight of magnesia, aluminium hydroxide and zinc borate
Number ratio is 1:1.2:0.8.
Described adhesive is 563 urea-formaldehyde resin adhesives.
The desiccant is active carbon desiccant, and the mesh number of active carbon desiccant is 300 mesh.
The mesh number of the pine powder and beech powder is 400 mesh.
A kind of moisture-proof wood veneer of insect prevention, which is characterized in that comprise the following components in parts by weight: masson pine bark, 45 parts；Beech
Wood shavings, 20 parts；Camphorwood powder, 2 parts；Mica powder, 6 parts；Nano alumina powder, 1.1 parts；Glass fibre, 1.8 parts；Fire retardant, 7 parts；
Adhesive, 9 parts；Desiccant, 6.5 parts.
The fire retardant includes magnesia, aluminium hydroxide and zinc borate, the parts by weight of magnesia, aluminium hydroxide and zinc borate
Number ratio is 1:1.2:0.8.
Described adhesive is 563 urea-formaldehyde resin adhesives.
The desiccant is active carbon desiccant, and the mesh number of active carbon desiccant is 300 mesh.
Claims (6)
1. a kind of preparation method of the moisture-proof wood veneer of insect prevention, which is characterized in that each raw material is in terms of mass parts, including following step
It is rapid:
A, 45 parts of masson pine barks are taken, 0.5-1.5h is impregnated with the sodium hydroxide solution that mass fraction is 20-30%, is washed with distillation
Only, it and dries, is ground into pine powder；
B, 20 parts of beech wood shavings are taken, 1-1.5h is impregnated with the sodium hydroxide solution that mass fraction is 15-20%, is washed with distillation
Only, it and dries, is ground into beech powder；
C, the pine powder in step A is put into agitator with the beech powder in step B uniformly to mix, 12 parts of distilled water is added and stir
It mixes, stirs into starchiness mixture, 2 parts of camphorwood powders, 6 parts of mica powders, 1.1 parts of nano alumina powders are sequentially added in whipping process
With 1.8 parts of glass fibres, mixing speed 1800-2200r/min, mixing time 30-50min；
D, 7 parts of fire retardants, 9 parts of adhesives and 6.5 parts of desiccant are added sequentially to agitator stirring, lead to nitrogen in whipping process
Gas, being kept stirring temperature within the barrel is 40-50 DEG C, mixing speed 2000-2400r/min, mixing time 35-45min；
E, the obtained material of step D is poured into mold, with molding machine compression moulding, pressing pressure 2.5-3.5Mpa, compacting
Temperature is 35-45 DEG C, pressing time 4-6h, demoulds to obtain wood veneer semi-finished product；
F, the wood veneer semi-finished product in step E are put into baking oven and carry out drying and processing, oven temperature is 60-80 DEG C, when drying
A length of 5-8h obtains wood veneer finished product.
2. a kind of preparation method of the moisture-proof wood veneer of insect prevention according to claim 1, it is characterised in that: the wood facing
The moisture content of boards half-finished product is 4-8%, and the moisture content of wood veneer finished product is 0.5-0.9%.
3. a kind of preparation method of the moisture-proof wood veneer of insect prevention according to claim 1, it is characterised in that: the fire retardant
Including magnesia, aluminium hydroxide and zinc borate, the weight part ratio of magnesia, aluminium hydroxide and zinc borate is 1:1.2:0.8.
4. a kind of preparation method of the moisture-proof wood veneer of insect prevention according to claim 1, it is characterised in that: described adhesive
For 563 urea-formaldehyde resin adhesives.
5. a kind of preparation method of the moisture-proof wood veneer of insect prevention according to claim 1, it is characterised in that: the desiccant
For active carbon desiccant, the mesh number of active carbon desiccant is 200-400 mesh.
6. a kind of preparation method of the moisture-proof wood veneer of insect prevention according to claim 1, it is characterised in that: the pine powder
Mesh number with beech powder is 300-500 mesh.